CN105198227A - Frosted glass production process - Google Patents
Frosted glass production process Download PDFInfo
- Publication number
- CN105198227A CN105198227A CN201510448082.0A CN201510448082A CN105198227A CN 105198227 A CN105198227 A CN 105198227A CN 201510448082 A CN201510448082 A CN 201510448082A CN 105198227 A CN105198227 A CN 105198227A
- Authority
- CN
- China
- Prior art keywords
- glass
- drying
- dry
- printing
- oven
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a frosted glass production process. According to the process, through control of the time for drying after development and the moisture content after drying, an image can be better formed on frosted glass; due to the components of frosting paste, the produced frosted glass can have a good texture. Therefore, the frosted glass produced according to the process has the advantages of being good in texture, high in quality and broad in market prospect.
Description
Technical field
The present invention relates to the production technique of glass, particularly relate to a kind of production technique of mat glass.
Background technology
Mat glass is different from sand blasting glass.Sand blasting glass under the effect of pressurized air or mechanical force, is directly injected to glass surface with silicon carbide or quartz sand, makes glass surface produce rough surface and the glass produced; Mat glass is also emulsifying glass, and it is the glass produced with chemical corrosion method etching glass surface.Mat glass product, with the texture of its uniqueness and finishing effect, has now been widely used in office building, auditoriums, hotels and house decoration.
Summary of the invention
The invention provides a kind of production technique of mat glass.For realizing object of the present invention, technical scheme of the present invention is as follows:
A production technique for mat glass, its concrete steps are:
(1) processing of silk screen plate
Select the polyester monofilament printing screen cloth of 0.15-0.18mm as required, then clean, then carry out drying and processing, the temperature of oven dry is 60-70 DEG C
(2) gluing
Polyester monofilament printing screen cloth after drying is carried out gluing process by tackiness agent, and then put and dry in an oven, the temperature of oven dry is 70-90 DEG C;
(3) stretch tight net
The net machine that stretches tight is utilized to be fixed on screen frame the polyester monofilament printing screen cloth after gluing;
(4) exposure and development
Polyester monofilament printing screen cloth on screen frame is coated exposure agent expose, the time shutter is 1-2h, then spray development agent on polyester monofilament printing screen cloth, and development forms silk screen printing forme after drying;
(5) cutting, the edging of glass
As required by the size that ball mill will be chosen glass cutting and becomes suitable, then polished in its corner;
(6) clean
With tap water, glass sparge is clean, then soak with acetone mixture, then use washed with de-ionized water, finally put dry in an oven, the temperature of baking oven is 60-80 DEG C;
(7) print
Be fixed on screen printing table by dried screen printing forme and glass, by scraping frosting cream with scraper plate, the frosting cream leaked down through silk screen plate forms pattern on glass;
(8) cleaning, drying
By the glass washed with de-ionized water after printing, then put dry in an oven, the temperature of baking oven is 50-60 DEG C, and the dry time is 1-2h;
(9) check
To thoroughly clean and dry the glass that frosting is good, check, pack, dispatch from the factory.
Preferably, the time of described step (4) development post-drying is 1-2h, and after drying, moisture content is 2-4%.
Preferably, in described step (7) frosting cream consist of hydrogen fluoride ammonia, ammonium fluoride, sodium bifluoride, Sodium Fluoride, sulfate of ammoniac, hydrofluoric acid and methylcellulose gum, the massfraction of described frosting cream is 20-40%.
Beneficial effect: the production technique that the invention provides a kind of mat glass, the control of the time of described development post-drying and the rear moisture content of oven dry, can make glass forms image better, the composition of described frosting cream, the mat glass texture produced can be made good.With the mat glass of this kind of explained hereafter, there is the advantage that texture is good, product are of fine quality, there are wide market outlook.
Embodiment
The technique means realized for making the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with embodiment, setting forth the present invention further.
A production technique for mat glass, its concrete steps are:
(1) processing of silk screen plate
Select the polyester monofilament printing screen cloth of 0.165mm as required, then clean, then carry out drying and processing, the temperature of oven dry is 65 DEG C
(2) gluing
Polyester monofilament printing screen cloth after drying is carried out gluing process by tackiness agent, and then put and dry in an oven, the temperature of oven dry is 80 DEG C;
(3) stretch tight net
The net machine that stretches tight is utilized to be fixed on screen frame the polyester monofilament printing screen cloth after gluing;
(4) exposure and development
Polyester monofilament printing screen cloth on screen frame is coated exposure agent expose, time shutter is 1.5h, then spray development agent on polyester monofilament printing screen cloth, and development forms silk screen printing forme after drying, the time of development post-drying is 1.5h, and after drying, moisture content is 3%;
(5) cutting, the edging of glass
As required by the size that ball mill will be chosen glass cutting and becomes suitable, then polished in its corner;
(6) clean
With tap water, glass sparge is clean, then soak with acetone mixture, then use washed with de-ionized water, finally put dry in an oven, the temperature of baking oven is 70 DEG C;
(7) print
Dried screen printing forme and glass are fixed on screen printing table, by scraping frosting cream with scraper plate, the frosting cream leaked down through silk screen plate forms pattern on glass, frosting cream consist of hydrogen fluoride ammonia, ammonium fluoride, sodium bifluoride, Sodium Fluoride, sulfate of ammoniac, hydrofluoric acid and methylcellulose gum, the massfraction of described frosting cream is 30%;
(8) cleaning, drying
By the glass washed with de-ionized water after printing, then put dry in an oven, the temperature of baking oven is 55 DEG C, and the dry time is 1.5h;
(9) check
To thoroughly clean and dry the glass that frosting is good, check, pack, dispatch from the factory.
The invention provides a kind of production technique of mat glass, time of described development post-drying and the control of moisture content after drying, can make glass forms image better, the composition of described frosting cream, and the mat glass texture produced can be made good.With the mat glass of this kind of explained hereafter, there is the advantage that texture is good, product are of fine quality, there are wide market outlook.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize specification sheets of the present invention and content to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (3)
1. a production technique for mat glass, is characterized in that, its concrete steps are:
(1) processing of silk screen plate
Select the polyester monofilament printing screen cloth of 0.15-0.18mm as required, then clean, then carry out drying and processing, the temperature of oven dry is 60-70 DEG C;
(2) gluing
Polyester monofilament printing screen cloth after drying is carried out gluing process by tackiness agent, and then put and dry in an oven, the temperature of oven dry is 70-90 DEG C;
(3) stretch tight net
The net machine that stretches tight is utilized to be fixed on screen frame the polyester monofilament printing screen cloth after gluing;
(4) exposure and development
Polyester monofilament printing screen cloth on screen frame is coated exposure agent expose, the time shutter is 1-2h, then spray development agent on polyester monofilament printing screen cloth, and development forms silk screen printing forme after drying;
(5) cutting, the edging of glass
As required by the size that ball mill will be chosen glass cutting and becomes suitable, then polished in its corner;
(6) clean
With tap water, glass sparge is clean, then soak with acetone mixture, then use washed with de-ionized water, finally put dry in an oven, the temperature of baking oven is 60-80 DEG C;
(7) print
Be fixed on screen printing table by dried screen printing forme and glass, by scraping frosting cream with scraper plate, the frosting cream leaked down through silk screen plate forms pattern on glass;
(8) cleaning, drying
By the glass washed with de-ionized water after printing, then put dry in an oven, the temperature of baking oven is 50-60 DEG C, and the dry time is 1-2h;
(9) check
To thoroughly clean and dry the glass that frosting is good, check, pack, dispatch from the factory.
2. the production technique of a kind of mat glass according to claim 1, is characterized in that, the time of described step (4) development post-drying is 1-2h, and after drying, moisture content is 2-4%.
3. the production technique of a kind of mat glass according to claim 1, it is characterized in that, in described step (7) frosting cream consist of hydrogen fluoride ammonia, ammonium fluoride, sodium bifluoride, Sodium Fluoride, sulfate of ammoniac, hydrofluoric acid and methylcellulose gum, the massfraction of described frosting cream is 20-40%.