CN105176205A - High-flexibility high-adhesive-force diatom-ooze coating material - Google Patents
High-flexibility high-adhesive-force diatom-ooze coating material Download PDFInfo
- Publication number
- CN105176205A CN105176205A CN201510571167.8A CN201510571167A CN105176205A CN 105176205 A CN105176205 A CN 105176205A CN 201510571167 A CN201510571167 A CN 201510571167A CN 105176205 A CN105176205 A CN 105176205A
- Authority
- CN
- China
- Prior art keywords
- parts
- high tenacity
- cotton
- supersound process
- ooze coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-flexibility high-adhesive-force diatom-ooze coating material. The high-flexibility high-adhesive-force diatom-ooze coating material comprises the following raw materials: 30 to 35 parts of diatom ooze, 13 to 17 parts of high-flexibility fiber material, 10 to 15 parts of talcum powder, 4 to 7 parts of active carbon, 3 to 5 parts of sea-foam stone powder, 3 to 6 parts of binder, 1.2 to 1.5 parts of leveling agent, 0.3 to 0.6 parts of leveling additive, 1.2 to 1.5 parts of thickening agent, 1.4 to 1.7 parts of mould inhibitor, 1.5 to 1.8 parts of film forming additive, 2.2 to 2.6 parts of dispersing agent and 40 to 50 parts of deionized water. The high-flexibility high-adhesive-force diatom-ooze coating material has characteristics of high flexibility and high adhesive force, also has good heat preservation and moisturizing performance and is a novel diatom ooze coating material.
Description
Technical field
The present invention relates to diatom ooze coating technical field, particularly relate to a kind of high tenacity high adhesive force diatom ooze coating.
Background technology
Along with people's environmental consciousness strengthens day by day, diatom ooze coating is widely used in house ornamentation field further as a kind of new coating.Diatom ooze coating has functions such as regulating humidity, fire protection flame retarding, deodorization and sterilization, its composition is a kind of rule, is fitly arranged in circle or the micrometer level porous material of aciculiform, porosity is up to 90%, the minute aperture number ratio charcoal of its unit surface also will have more thousands of times, has extremely strong physical adsorption performance and ion-exchange performance; But often face drying in diatom ooze coating process, the phenomenon such as fracture, fragmentation that external impact causes, therefore, develop a kind of high tenacity, high adhesion property diatom ooze coating very necessary.
Summary of the invention
Based on the technical problem that background technology exists, the present invention proposes a kind of high tenacity high adhesive force diatom ooze coating, have the feature of high tenacity and high adhesive force, also have excellent heat and moisture preserving performance, is a kind of novel diatom ooze coating.
A kind of high tenacity high adhesive force diatom ooze coating that the present invention proposes, its raw material comprises by weight: diatomite 30-35 part, high tenacity cotton fibre material 13-17 part, talcum powder 10-15 part, gac 4-7 part, sepiolite powder 3-5 part, binding agent 3-6 part, flow agent 1.2-1.5 part, flow assistants 0.3-0.6 part, thickening material 1.2-1.5 part, mould inhibitor 1.4-1.7 part, film coalescence aid 1.5-1.8 part, dispersion agent 2.2-2.6 part, deionized water 40-50 part.
Preferably, diatomite, high tenacity cotton fibre material, talcous weight ratio are 32-33:14-15:12-14.
Preferably, its raw material comprises by weight: diatomite 32-33 part, high tenacity cotton fibre material 14-15 part, talcum powder 12-14 part, gac 5-6 part, sepiolite powder 3.5-4 part, binding agent 4-5 part, flow agent 1.3-1.4 part, flow assistants 0.4-0.5 part, thickening material 1.3-1.4 part, mould inhibitor 1.5-1.6 part, film coalescence aid 1.6-1.7 part, dispersion agent 2.3-2.4 part, deionized water 43-45 part.
Preferably, talcous order number is 700-800 order.
Preferably, the preparation method of high tenacity cotton fibre material is: stir dropping in mixing solutions after cotton combing fragmentation, wherein mixing solutions is mixed to get by aqueous propanol solution and aqueous sodium hydroxide solution, and standing squeezing drains, broken, agingly obtains prefibers; Prefibers, prefabricated infiltration material, deionized water are carried out supersound process after mixing, obtains infiltrating rear cotton fiber; Then cotton fiber after infiltration is left standstill, dry, obtain high tenacity cotton fibre material.
Preferably, the preparation method of high tenacity cotton fibre material is: stir dropping in mixing solutions after cotton combing fragmentation, wherein mixing solutions is mixed to get by the aqueous sodium hydroxide solution of massfraction to be the aqueous propanol solution of 15-20wt% and massfraction be 22-25wt%, squeeze after leaving standstill 2-3h and drain, fragmentation, agingly obtains prefibers; Prefibers, prefabricated infiltration material, deionized water are carried out supersound process after mixing, obtains infiltrating rear cotton fiber, the frequency of supersound process is 55-60KHz, and the power of supersound process is 120-150W, and the time of supersound process is 25-30min; Then cotton fiber after infiltration is left standstill, dry, obtain high tenacity cotton fibre material.
Preferably, the preparation method of high tenacity cotton fibre material is: stir dropping in mixing solutions after the fragmentation of 10-15 part cotton combing by weight, wherein mixing solutions is mixed to get by the aqueous sodium hydroxide solution of 5-8 part massfraction to be the aqueous propanol solution of 15-20wt% and 30-40 part massfraction be 22-25wt%, squeeze after leaving standstill 2-3h and drain, fragmentation, agingly obtains prefibers; 20-25 part prefibers, the prefabricated infiltration material of 8-10 part, 32-35 part deionized water are carried out supersound process after mixing, obtain infiltrating rear cotton fiber, the frequency of supersound process is 55-60KHz, and the power of supersound process is 120-150W, and the time of supersound process is 25-30min; Then cotton fiber after infiltration is left standstill, dry, obtain high tenacity cotton fibre material.
The present invention is with the diatomite of specified proportion, high tenacity cotton fibre material, talcum powder is as major ingredient, substantially increase sticking power of the present invention, toughness, in the preparation process of wherein high tenacity cotton fibre material, the soda cellulose that gossypin is formed through certain concentration sodium hydroxide and the process of propyl alcohol mixing solutions, cotton fibre welds tactile hemicellulose, impurity, add the wettability of cotton fibre, reduce the diameter of cotton fibre, can be cross-linked with unclassified stores big area, the simultaneous swelling gossypin that makes is loose gradually, expand the area of cotton fibre, thus substantially increase snappiness of the present invention and intensity, the propanol solution of adding can reduce the solubleness of sodium hydroxide, impels cotton fibre to absorb hydroxide ion, thus accelerates the swelling of cotton fibre, after prefibers, prefabricated infiltration material, deionized water being carried out the infiltration that supersound process obtains after mixing, cotton fiber has excellent wetting ability, splendid snappiness, and the cavatition of supersound process can accelerate the fusion between prefibers and styrene-butadiene latex, gelatin, polyvinyl alcohol, is conducive to the even combination of unclassified stores in high tenacity cotton fibre material and the present invention, thus greatly improves toughness of the present invention and intensity, meanwhile, the interpolation of high tenacity cotton fibre material, can improve heat and moisture preserving performance of the present invention further, the interpolation of gac, can after the present invention uses, and energy and diatomite coordinate particle, obnoxious flavour in absorbed air, thus improve environmental-protecting performance of the present invention, and the interpolation of sepiolite powder, energy and high tenacity cotton fibre material coordinate, and improve intensity of the present invention and toughness.
Embodiment
Below, by specific embodiment, technical scheme of the present invention is described in detail.
Embodiment 1
A kind of high tenacity high adhesive force diatom ooze coating that the present invention proposes, its raw material comprises by weight: 35 parts, diatomite, high tenacity cotton fibre material 13 parts, 700 object talcum powder 15 parts, gac 4 parts, sepiolite powder 5 parts, binding agent 3 parts, flow agent 1.5 parts, flow assistants 0.3 part, thickening material 1.5 parts, mould inhibitor 1.4 parts, film coalescence aid 1.8 parts, dispersion agent 2.2 parts, deionized water 50 parts;
The preparation method of high tenacity cotton fibre material is: stir dropping in mixing solutions after 15 parts of cotton combing fragmentations by weight, wherein mixing solutions is mixed to get by the aqueous sodium hydroxide solution of 5 parts of massfractions to be the aqueous propanol solution of 20wt% and 30 parts of massfractions be 25wt%, squeeze after leaving standstill 2h and drain, fragmentation, agingly obtains prefibers; 25 parts of prefibers, 8 parts of prefabricated infiltration materials, 35 parts of deionized waters are carried out supersound process after mixing, and obtain infiltrating rear cotton fiber, the frequency of supersound process is 55KHz, and the power of supersound process is 150W, and the time of supersound process is 25min; Then cotton fiber after infiltration is left standstill, dry, obtain high tenacity cotton fibre material.
Embodiment 2
A kind of high tenacity high adhesive force diatom ooze coating that the present invention proposes, its raw material comprises by weight: 30 parts, diatomite, high tenacity cotton fibre material 17 parts, 800 object talcum powder 10 parts, gac 7 parts, sepiolite powder 3 parts, binding agent 6 parts, flow agent 1.2 parts, flow assistants 0.6 part, thickening material 1.2 parts, mould inhibitor 1.7 parts, film coalescence aid 1.5 parts, dispersion agent 2.6 parts, deionized water 40 parts;
The preparation method of high tenacity cotton fibre material is: stir dropping in mixing solutions after 10 parts of cotton combing fragmentations by weight, wherein mixing solutions is mixed to get by the aqueous sodium hydroxide solution of 8 parts of massfractions to be the aqueous propanol solution of 15wt% and 40 parts of massfractions be 22wt%, squeeze after leaving standstill 3h and drain, fragmentation, agingly obtains prefibers; 20 parts of prefibers, 10 parts of prefabricated infiltration materials, 32 parts of deionized waters are carried out supersound process after mixing, and obtain infiltrating rear cotton fiber, the frequency of supersound process is 60KHz, and the power of supersound process is 120W, and the time of supersound process is 30min; Then cotton fiber after infiltration is left standstill, dry, obtain high tenacity cotton fibre material.
Embodiment 3
A kind of high tenacity high adhesive force diatom ooze coating that the present invention proposes, its raw material comprises by weight: 33 parts, diatomite, high tenacity cotton fibre material 14 parts, 750 object talcum powder 14 parts, gac 5 parts, sepiolite powder 4 parts, binding agent 4 parts, flow agent 1.4 parts, flow assistants 0.4 part, thickening material 1.4 parts, mould inhibitor 1.5 parts, film coalescence aid 1.7 parts, dispersion agent 2.3 parts, deionized water 45 parts;
The preparation method of high tenacity cotton fibre material is: stir dropping in mixing solutions after 13 parts of cotton combing fragmentations by weight, wherein mixing solutions is mixed to get by the aqueous sodium hydroxide solution of 6 parts of massfractions to be the aqueous propanol solution of 18wt% and 33 parts of massfractions be 24wt%, squeeze after leaving standstill 2.2h and drain, fragmentation, agingly obtains prefibers; 23 parts of prefibers, 8.5 parts of prefabricated infiltration materials, 34 parts of deionized waters are carried out supersound process after mixing, and obtain infiltrating rear cotton fiber, the frequency of supersound process is 56KHz, and the power of supersound process is 140W, and the time of supersound process is 26min; Then cotton fiber after infiltration is left standstill, dry, obtain high tenacity cotton fibre material.
Embodiment 4
A kind of high tenacity high adhesive force diatom ooze coating that the present invention proposes, its raw material comprises by weight: 32 parts, diatomite, high tenacity cotton fibre material 15 parts, 800 object talcum powder 12 parts, gac 6 parts, sepiolite powder 3.5 parts, binding agent 5 parts, flow agent 1.3 parts, flow assistants 0.5 part, thickening material 1.3 parts, mould inhibitor 1.6 parts, film coalescence aid 1.6 parts, dispersion agent 2.4 parts, deionized water 43 parts;
The preparation method of high tenacity cotton fibre material is: stir dropping in mixing solutions after 12 parts of cotton combing fragmentations by weight, wherein mixing solutions is mixed to get by the aqueous sodium hydroxide solution of 7 parts of massfractions to be the aqueous propanol solution of 16wt% and 38 parts of massfractions be 23wt%, squeeze after leaving standstill 2.5h and drain, fragmentation, agingly obtains prefibers; 22 parts of prefibers, 9 parts of prefabricated infiltration materials, 33 parts of deionized waters are carried out supersound process after mixing, and obtain infiltrating rear cotton fiber, the frequency of supersound process is 58KHz, and the power of supersound process is 130W, and the time of supersound process is 28min; Then cotton fiber after infiltration is left standstill, dry, obtain high tenacity cotton fibre material.
The above; be only the present invention's preferably embodiment; but protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to according to technical scheme of the present invention and inventive concept thereof and replace or change, all should be encompassed within protection scope of the present invention.
Claims (7)
1. a high tenacity high adhesive force diatom ooze coating, is characterized in that, its raw material comprises by weight: diatomite 30-35 part, high tenacity cotton fibre material 13-17 part, talcum powder 10-15 part, gac 4-7 part, sepiolite powder 3-5 part, binding agent 3-6 part, flow agent 1.2-1.5 part, flow assistants 0.3-0.6 part, thickening material 1.2-1.5 part, mould inhibitor 1.4-1.7 part, film coalescence aid 1.5-1.8 part, dispersion agent 2.2-2.6 part, deionized water 40-50 part.
2. high tenacity high adhesive force diatom ooze coating according to claim 1, it is characterized in that, diatomite, high tenacity cotton fibre material, talcous weight ratio are 32-33:14-15:12-14.
3. high tenacity high adhesive force diatom ooze coating according to claim 1 or 2, it is characterized in that, its raw material comprises by weight: diatomite 32-33 part, high tenacity cotton fibre material 14-15 part, talcum powder 12-14 part, gac 5-6 part, sepiolite powder 3.5-4 part, binding agent 4-5 part, flow agent 1.3-1.4 part, flow assistants 0.4-0.5 part, thickening material 1.3-1.4 part, mould inhibitor 1.5-1.6 part, film coalescence aid 1.6-1.7 part, dispersion agent 2.3-2.4 part, deionized water 43-45 part.
4. high tenacity high adhesive force diatom ooze coating according to any one of claim 1-3, is characterized in that, talcous order number is 700-800 order.
5. high tenacity high adhesive force diatom ooze coating according to any one of claim 1-4, it is characterized in that, the preparation method of high tenacity cotton fibre material is: stir dropping in mixing solutions after cotton combing fragmentation, wherein mixing solutions is mixed to get by aqueous propanol solution and aqueous sodium hydroxide solution, standing squeezing drains, fragmentation, agingly obtains prefibers; Prefibers, prefabricated infiltration material, deionized water are carried out supersound process after mixing, obtains infiltrating rear cotton fiber; Then cotton fiber after infiltration is left standstill, dry, obtain high tenacity cotton fibre material.
6. high tenacity high adhesive force diatom ooze coating according to any one of claim 1-5, it is characterized in that, the preparation method of high tenacity cotton fibre material is: stir dropping in mixing solutions after cotton combing fragmentation, wherein mixing solutions is mixed to get by the aqueous sodium hydroxide solution of massfraction to be the aqueous propanol solution of 15-20wt% and massfraction be 22-25wt%, squeeze after leaving standstill 2-3h and drain, fragmentation, agingly obtains prefibers; Prefibers, prefabricated infiltration material, deionized water are carried out supersound process after mixing, obtains infiltrating rear cotton fiber, the frequency of supersound process is 55-60KHz, and the power of supersound process is 120-150W, and the time of supersound process is 25-30min; Then cotton fiber after infiltration is left standstill, dry, obtain high tenacity cotton fibre material.
7. high tenacity high adhesive force diatom ooze coating according to any one of claim 1-6, it is characterized in that, the preparation method of high tenacity cotton fibre material is: stir dropping in mixing solutions after the fragmentation of 10-15 part cotton combing by weight, wherein mixing solutions is mixed to get by the aqueous sodium hydroxide solution of 5-8 part massfraction to be the aqueous propanol solution of 15-20wt% and 30-40 part massfraction be 22-25wt%, squeeze after leaving standstill 2-3h and drain, fragmentation, agingly obtains prefibers; 20-25 part prefibers, the prefabricated infiltration material of 8-10 part, 32-35 part deionized water are carried out supersound process after mixing, obtain infiltrating rear cotton fiber, the frequency of supersound process is 55-60KHz, and the power of supersound process is 120-150W, and the time of supersound process is 25-30min; Then cotton fiber after infiltration is left standstill, dry, obtain high tenacity cotton fibre material.