CN105176181A - Letterpress printing ink for plastic packaging bag and preparation method of letterpress printing ink - Google Patents
Letterpress printing ink for plastic packaging bag and preparation method of letterpress printing ink Download PDFInfo
- Publication number
- CN105176181A CN105176181A CN201510589439.7A CN201510589439A CN105176181A CN 105176181 A CN105176181 A CN 105176181A CN 201510589439 A CN201510589439 A CN 201510589439A CN 105176181 A CN105176181 A CN 105176181A
- Authority
- CN
- China
- Prior art keywords
- parts
- printing ink
- letterpress printing
- packaging bag
- plastic packaging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to letterpress printing ink for a plastic packaging bag and a preparation method of the letterpress printing ink. The letterpress printing ink comprises the following components in parts by mass: 20-32 parts of nitrile rubber, 3-6 parts of aluminum silver powder, 2-5 parts of phthalocyanine green G, 25-48 parts of fine-blenched linseed oil, 8-15 parts of dibutyl phthalate, 9-18 parts of acetic ether, 5-13 parts of ethylene glycol butyl ether, 2-9 parts of polyester modified dimethyl siloxane, 10-20 parts of eugenol, 3-8 parts of 2-ethylhexoic acid and 6-14 parts of terpilenol. The letterpress printing ink provided by the invention has excellent friction resistance, skinning difficulty and aging resistance; after being printed to the surface of the plastic packaging bag, the ink is high in drying speed, difficult to fade and high in glossiness and can play well identifying and advertising effects.
Description
Technical field
The present invention relates to field of packaging material, particularly relate to a kind of plastic packaging bag letterpress printing ink and preparation method thereof.
Background technology
Plastic packaging bag is a kind of is starting material with plastics, for the production of the packing bag of various articles for use in life, is widely used in daily life and industrial production.Although plastic packaging bag has certain harm to environment, rate of utilization is still higher at present.In use, need at plastic packaging bag surface printing ink, identify again, the effect such as publicity.But at present the problem of the ink ubiquity that uses of plastic packaging bag surface not rub resistance, fugitive color, color difference, can not play the effect of well mark and publicity.
Summary of the invention
the technical problem solved:the shortcoming of the ink used for existing plastic packaging bag surface not rub resistance, fugitive color, color difference, the invention provides a kind of plastic packaging bag letterpress printing ink and preparation method thereof.
technical scheme:a kind of plastic packaging bag letterpress printing ink, in mass parts containing following composition: paracril 20 ~ 32 parts, 3 ~ 6 parts, aluminium silver powder, Phthalocyanine Green G 2 ~ 5 parts, essence drift oleum lini 25 ~ 48 parts, dibutyl phthalate 8 ~ 15 parts, vinyl acetic monomer 9 ~ 18 parts, butyl glycol ether 5 ~ 13 parts, polyester modification dimethyl siloxane 2 ~ 9 parts, Eugenol 10 ~ 20 parts, 2 ethyl hexanoic acid 3 ~ 8 parts, Terpineol 350 6 ~ 14 parts.
A kind of plastic packaging bag letterpress printing ink described above, in mass parts containing following composition: paracril 22 ~ 30 parts, 3.5 ~ 5.5 parts, aluminium silver powder, Phthalocyanine Green G 3 ~ 4 parts, essence drift oleum lini 28 ~ 45 parts, dibutyl phthalate 9 ~ 13 parts, vinyl acetic monomer 11 ~ 16 parts, butyl glycol ether 7 ~ 12 parts, polyester modification dimethyl siloxane 3 ~ 8 parts, Eugenol 12 ~ 18 parts, 2 ethyl hexanoic acid 4 ~ 7 parts, Terpineol 350 7 ~ 12 parts.
A kind of plastic packaging bag letterpress printing ink described above, in mass parts containing following composition: paracril 24 parts, 4 parts, aluminium silver powder, Phthalocyanine Green G 3.2 parts, essence drift oleum lini 33 parts, dibutyl phthalate 10 parts, vinyl acetic monomer 12 parts, butyl glycol ether 8 parts, polyester modification dimethyl siloxane 4 parts, Eugenol 13 parts, 2 ethyl hexanoic acid 5 parts, Terpineol 350 8 parts.
A kind of plastic packaging bag letterpress printing ink described above, in mass parts containing following composition: paracril 26 parts, 4.5 parts, aluminium silver powder, Phthalocyanine Green G 3.5 parts, essence drift oleum lini 42 parts, dibutyl phthalate 11 parts, vinyl acetic monomer 13 parts, butyl glycol ether 9.5 parts, polyester modification dimethyl siloxane 5.5 parts, Eugenol 15 parts, 2 ethyl hexanoic acid 5.5 parts, Terpineol 350 10 parts.
The preparation method of a kind of plastic packaging bag letterpress printing ink described above, the step of this preparation method is as follows:
The first step: add in agitator by paracril, essence drift oleum lini, Terpineol 350, Heating temperature to 170 ~ 190 DEG C, stir fusing, mix;
Second step: be cooled to 90 ~ 110 DEG C, then adds dibutyl phthalate, vinyl acetic monomer, butyl glycol ether, polyester modification dimethyl siloxane, Eugenol, 2 ethyl hexanoic acid, is uniformly mixed;
3rd step: finally add aluminium silver powder and phthalocyanine green, be down to room temperature after mixing, obtains plastic packaging bag letterpress printing ink.
Heating temperature to 180 DEG C in the first step described above.
100 DEG C are cooled in second step described above.
beneficial effect:a kind of plastic packaging bag letterpress printing ink provided by the invention and preparation method thereof, this ink has excellent rub resistance, not easily skinning and aging-resistant performance, be printed on the surface of plastic packaging bag, the rate of drying of ink soon, not fugitive color, the glossiness of ink is high, can play well mark and propaganda function.
Embodiment
embodiment 1
A kind of plastic packaging bag letterpress printing ink, in mass parts containing following composition: paracril 20 parts, 3 parts, aluminium silver powder, Phthalocyanine Green G 2 parts, essence drift oleum lini 25 parts, dibutyl phthalate 8 parts, vinyl acetic monomer 9 parts, butyl glycol ether 5 parts, polyester modification dimethyl siloxane 2 parts, Eugenol 10 parts, 2 ethyl hexanoic acid 3 parts, Terpineol 350 6 parts.
A preparation method for plastic packaging bag letterpress printing ink, the step of this preparation method is as follows:
The first step: add in agitator by paracril, essence drift oleum lini, Terpineol 350, Heating temperature to 170 DEG C, stirs fusing, mix;
Second step: be cooled to 90 DEG C, then adds dibutyl phthalate, vinyl acetic monomer, butyl glycol ether, polyester modification dimethyl siloxane, Eugenol, 2 ethyl hexanoic acid, is uniformly mixed;
3rd step: finally add aluminium silver powder and phthalocyanine green, be down to room temperature after mixing, obtains plastic packaging bag letterpress printing ink.
embodiment 2
A kind of plastic packaging bag letterpress printing ink, in mass parts containing following composition: paracril 32 parts, 6 parts, aluminium silver powder, Phthalocyanine Green G 5 parts, essence drift oleum lini 48 parts, dibutyl phthalate 15 parts, vinyl acetic monomer 18 parts, butyl glycol ether 13 parts, polyester modification dimethyl siloxane 9 parts, Eugenol 20 parts, 2 ethyl hexanoic acid 8 parts, Terpineol 350 14 parts.
A preparation method for plastic packaging bag letterpress printing ink, the step of this preparation method is as follows:
The first step: add in agitator by paracril, essence drift oleum lini, Terpineol 350, Heating temperature to 190 DEG C, stirs fusing, mix;
Second step: be cooled to 110 DEG C, then adds dibutyl phthalate, vinyl acetic monomer, butyl glycol ether, polyester modification dimethyl siloxane, Eugenol, 2 ethyl hexanoic acid, is uniformly mixed;
3rd step: finally add aluminium silver powder and phthalocyanine green, be down to room temperature after mixing, obtains plastic packaging bag letterpress printing ink.
embodiment 3
A kind of plastic packaging bag letterpress printing ink, in mass parts containing following composition: paracril 30 parts, 5.5 parts, aluminium silver powder, Phthalocyanine Green G 4 parts, essence drift oleum lini 45 parts, dibutyl phthalate 13 parts, vinyl acetic monomer 16 parts, butyl glycol ether 12 parts, polyester modification dimethyl siloxane 8 parts, Eugenol 18 parts, 2 ethyl hexanoic acid 7 parts, Terpineol 350 12 parts.
A preparation method for plastic packaging bag letterpress printing ink, the step of this preparation method is as follows:
The first step: add in agitator by paracril, essence drift oleum lini, Terpineol 350, Heating temperature to 180 DEG C, stirs fusing, mix;
Second step: be cooled to 100 DEG C, then adds dibutyl phthalate, vinyl acetic monomer, butyl glycol ether, polyester modification dimethyl siloxane, Eugenol, 2 ethyl hexanoic acid, is uniformly mixed;
3rd step: finally add aluminium silver powder and phthalocyanine green, be down to room temperature after mixing, obtains plastic packaging bag letterpress printing ink.
embodiment 4
A kind of plastic packaging bag letterpress printing ink, in mass parts containing following composition: paracril 24 parts, 4 parts, aluminium silver powder, Phthalocyanine Green G 3.2 parts, essence drift oleum lini 33 parts, dibutyl phthalate 10 parts, vinyl acetic monomer 12 parts, butyl glycol ether 8 parts, polyester modification dimethyl siloxane 4 parts, Eugenol 13 parts, 2 ethyl hexanoic acid 5 parts, Terpineol 350 8 parts.
A preparation method for plastic packaging bag letterpress printing ink, the step of this preparation method is as follows:
The first step: add in agitator by paracril, essence drift oleum lini, Terpineol 350, Heating temperature to 180 DEG C, stirs fusing, mix;
Second step: be cooled to 100 DEG C, then adds dibutyl phthalate, vinyl acetic monomer, butyl glycol ether, polyester modification dimethyl siloxane, Eugenol, 2 ethyl hexanoic acid, is uniformly mixed;
3rd step: finally add aluminium silver powder and phthalocyanine green, be down to room temperature after mixing, obtains plastic packaging bag letterpress printing ink.
embodiment 5
A kind of plastic packaging bag letterpress printing ink, in mass parts containing following composition: paracril 26 parts, 4.5 parts, aluminium silver powder, Phthalocyanine Green G 3.5 parts, essence drift oleum lini 42 parts, dibutyl phthalate 11 parts, vinyl acetic monomer 13 parts, butyl glycol ether 9.5 parts, polyester modification dimethyl siloxane 5.5 parts, Eugenol 15 parts, 2 ethyl hexanoic acid 5.5 parts, Terpineol 350 10 parts.
A preparation method for plastic packaging bag letterpress printing ink, the step of this preparation method is as follows:
The first step: add in agitator by paracril, essence drift oleum lini, Terpineol 350, Heating temperature to 180 DEG C, stirs fusing, mix;
Second step: be cooled to 100 DEG C, then adds dibutyl phthalate, vinyl acetic monomer, butyl glycol ether, polyester modification dimethyl siloxane, Eugenol, 2 ethyl hexanoic acid, is uniformly mixed;
3rd step: finally add aluminium silver powder and phthalocyanine green, be down to room temperature after mixing, obtains plastic packaging bag letterpress printing ink.
By ink printing provided by the invention on plastic packaging bag, the time of drying of this ink, rub resistance number of times was higher than 1600 times, and the temper(ing) time, meanwhile, the glossiness of ink was high higher than 800h within 20s, mark and good decorating effect.
Above the embodiment of the present invention is described in detail, for one of ordinary skill in the art, according to the thought of the embodiment of the present invention, all will change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.
Claims (7)
1. a plastic packaging bag letterpress printing ink, to it is characterized in that in mass parts containing following composition: paracril 20 ~ 32 parts, 3 ~ 6 parts, aluminium silver powder, Phthalocyanine Green G 2 ~ 5 parts, essence drift oleum lini 25 ~ 48 parts, dibutyl phthalate 8 ~ 15 parts, vinyl acetic monomer 9 ~ 18 parts, butyl glycol ether 5 ~ 13 parts, polyester modification dimethyl siloxane 2 ~ 9 parts, Eugenol 10 ~ 20 parts, 2 ethyl hexanoic acid 3 ~ 8 parts, Terpineol 350 6 ~ 14 parts.
2. a kind of plastic packaging bag letterpress printing ink according to claim 1, to it is characterized in that in mass parts containing following composition: paracril 22 ~ 30 parts, 3.5 ~ 5.5 parts, aluminium silver powder, Phthalocyanine Green G 3 ~ 4 parts, essence drift oleum lini 28 ~ 45 parts, dibutyl phthalate 9 ~ 13 parts, vinyl acetic monomer 11 ~ 16 parts, butyl glycol ether 7 ~ 12 parts, polyester modification dimethyl siloxane 3 ~ 8 parts, Eugenol 12 ~ 18 parts, 2 ethyl hexanoic acid 4 ~ 7 parts, Terpineol 350 7 ~ 12 parts.
3. a kind of plastic packaging bag letterpress printing ink according to claim 1, to it is characterized in that in mass parts containing following composition: paracril 24 parts, 4 parts, aluminium silver powder, Phthalocyanine Green G 3.2 parts, essence drift oleum lini 33 parts, dibutyl phthalate 10 parts, vinyl acetic monomer 12 parts, butyl glycol ether 8 parts, polyester modification dimethyl siloxane 4 parts, Eugenol 13 parts, 2 ethyl hexanoic acid 5 parts, Terpineol 350 8 parts.
4. a kind of plastic packaging bag letterpress printing ink according to claim 1, to it is characterized in that in mass parts containing following composition: paracril 26 parts, 4.5 parts, aluminium silver powder, Phthalocyanine Green G 3.5 parts, essence drift oleum lini 42 parts, dibutyl phthalate 11 parts, vinyl acetic monomer 13 parts, butyl glycol ether 9.5 parts, polyester modification dimethyl siloxane 5.5 parts, Eugenol 15 parts, 2 ethyl hexanoic acid 5.5 parts, Terpineol 350 10 parts.
5. the preparation method of a kind of plastic packaging bag letterpress printing ink according to claim 1, is characterized in that the step of this preparation method is as follows:
The first step: add in agitator by paracril, essence drift oleum lini, Terpineol 350, Heating temperature to 170 ~ 190 DEG C, stir fusing, mix;
Second step: be cooled to 90 ~ 110 DEG C, then adds dibutyl phthalate, vinyl acetic monomer, butyl glycol ether, polyester modification dimethyl siloxane, Eugenol, 2 ethyl hexanoic acid, is uniformly mixed;
3rd step: finally add aluminium silver powder and phthalocyanine green, be down to room temperature after mixing, obtains plastic packaging bag letterpress printing ink.
6. the preparation method of a kind of plastic packaging bag letterpress printing ink according to claim 5, is characterized in that: Heating temperature to 180 DEG C in the described the first step.
7. the preparation method of a kind of plastic packaging bag letterpress printing ink according to claim 5, is characterized in that: be cooled to 100 DEG C in described second step.