CN105176028A - 一种汽车内饰用抵抗紫外老化的复合材料及其制备方法 - Google Patents

一种汽车内饰用抵抗紫外老化的复合材料及其制备方法 Download PDF

Info

Publication number
CN105176028A
CN105176028A CN201510609874.1A CN201510609874A CN105176028A CN 105176028 A CN105176028 A CN 105176028A CN 201510609874 A CN201510609874 A CN 201510609874A CN 105176028 A CN105176028 A CN 105176028A
Authority
CN
China
Prior art keywords
parts
minutes
composite material
ultraviolet
speed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510609874.1A
Other languages
English (en)
Inventor
陈峻
章云
张娉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUHU HUANRUI AUTO INTERIOR DECORATION CO Ltd
Original Assignee
WUHU HUANRUI AUTO INTERIOR DECORATION CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUHU HUANRUI AUTO INTERIOR DECORATION CO Ltd filed Critical WUHU HUANRUI AUTO INTERIOR DECORATION CO Ltd
Priority to CN201510609874.1A priority Critical patent/CN105176028A/zh
Publication of CN105176028A publication Critical patent/CN105176028A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种汽车内饰用抵抗紫外老化的复合材料，由下列重量份的原料制备制成：聚乳酸100-103、纳米三氧化二锑3.5-4、十溴二苯乙烷10-11、SEBS25-27、红麻纤维60-62、氧化铈4-5、纳米氧化锌7-8、苯并三唑0.8-1、硅烷偶联剂KH5700.6-0.7、硬酯酸单甘油酯1-1.3、明胶5-6、水适量、聚磷酸铵1-1.4、EVA乳液6-7.4。本发明将混合纤维浸渍在含有改性后的氧化铈、纳米氧化锌、苯并三唑中，三者协同作用，覆盖在混合纤维表面以及孔隙中，提高了混合纤维的抗紫外线的效果，同时内含硬酯酸单甘油酯等润滑成分，使得后续挤出造粒工艺更加流畅，从而提高了加工性。

Description

一种汽车内饰用抵抗紫外老化的复合材料及其制备方法
技术领域
本发明涉及汽车内饰材料技术领域，尤其涉及一种汽车内饰用抵抗紫外老化的复合材料及其制备方法。
背景技术
轿车的内饰件一般是指轿车车厢的隔板、门内装饰板、仪表板总成、扶手、地毯等零部件和材料。相对于车上其它部件而言，它们对车辆的运行性能没有什么影响，但其面目一览无遗，代表了整部车子的形象，孰优孰劣，决定着轿车的声誉和档次，决定着人们选择轿车的意向。另外，对于轿车来讲，虽然内饰件只是一些辅助性的零配件，但它们要承担起减振、隔热、吸音和遮音等功能，对轿车的舒适性起到十分重要的作用。汽车产业在世界各地蓬勃发展的同时，也带来环境污染和能源短缺两大严重的负面影响。据调查，石油消费品中多达35%是作为汽车的燃料被使用，随着石油资源的过度消耗，使得汽车行业必须进行相应的调整，轻量化和节能环保成为国际汽车工业研究的主题。
可生物降解高分子及其制品是近些年来各国科学家研究、开发、生产的热点，发达国家不光政府大量资金投入，还对大公司、科研机构及大学研究部门投入大量的人物力资源进行研发。由于聚乳酸具有优良的生物降解性和生物相容性，在环境中最终分解为二氧化碳和水，对环境没有污染，因此成为降解材料的研究热点之一。聚乳酸树脂来源于非石油基的生物原料，又具有良好的综合性能，受到了汽车业界的重视和青睐，丰田、三菱、马自达等日本公司已经率先在其品牌汽车上应用聚乳酸内饰产品，国内如奇瑞汽车也在开发车用聚乳酸产品。然而由于聚乳酸树脂结晶速度很慢，成型制品收缩率大，本身质脆，加工热稳定性差，以及制品耐久性差等缺点，限制了其作为工程塑料的应用。因此，迫切需要对绿色塑料聚乳酸树脂进行增强增韧、耐热等多元复合改性研究。再加上汽车火灾现象频繁出现，私家车火灾呈上升趋势，汽车火灾的原因一方面是由于汽车自身技术水平参差不齐，另一方面汽车自身所使用结构材料中有一部分为易燃材料，包括汽车内饰用高分子材料聚丙烯、聚碳酸酯以及可降解材料聚乳酸等。因此，还需要去聚乳酸材料的阻燃性进行改性。同时由于汽车噪音在行驶过程中给车内人员带来很大的影响，直接关系到车内人员的健康。所以，汽车噪音就成为了衡量汽车自身机械性能和舒适性能品质的重要标准。所以，急需发明一种兼具环保、阻燃、吸音等功能的汽车内饰材料。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种汽车内饰用抵抗紫外老化的复合材料及其制备方法。
本发明是通过以下技术方案实现的：
一种汽车内饰用抵抗紫外老化的复合材料，由下列重量份的原料制备制成：聚乳酸100-103、纳米三氧化二锑3.5-4、十溴二苯乙烷10-11、SEBS25-27、红麻纤维60-62、氧化铈4-5、纳米氧化锌7-8、苯并三唑0.8-1、硅烷偶联剂KH5700.6-0.7、硬酯酸单甘油酯1-1.3、明胶5-6、水适量、聚磷酸铵1-1.4、EVA乳液6-7.4。
所述一种汽车内饰用抵抗紫外老化的复合材料，由以下具体步骤制成：
（1）将聚乳酸在真空干燥箱中80℃干燥10小时待用，纳米三氧化二锑、十溴二苯乙烷分别烘箱中60℃下干燥5小时和8小时待用；将干燥后的物料放入高速搅拌机中，以1000转/分的速度搅拌10分钟后，加入SEBS，继续搅拌10分钟后将混合物料送入双螺杆挤出机中在175℃的温度，螺杆转速为150转/分的工艺条件下挤出造粒，得到改性聚乳酸母粒；
（2）将改性聚乳酸母粒送入螺杆纺丝机中进行共混熔融并挤出纺丝（控制螺杆挤出速度为250转/分，喷丝熔体温度控制在200℃），然后将喷出的初纤维经水浴冷却，控制水浴温度在20℃，水浴冷却后将纤维用120-130℃的热风干燥，即得改性聚乳酸纤维；将红麻纤维进行开松处理，处理后的红麻纤维与改性聚乳酸纤维进行混纺并条，得到混合纤维条；
（3）将氧化铈与纳米氧化锌放入高速混合机中，边搅拌将硅烷偶联剂KH570喷洒在粉体表面，继续以1000转/分的速度搅拌10分钟后出料待用；将将明胶放入搅拌釜中，加入30倍量的水，静置溶胀30分钟后加热至完全溶解，冷却至室温后加入EVA乳液、聚磷酸铵，超声处理25分钟，使物料分散均匀，然后继续加入上述处理后的物料以及其余剩余成分，继续以300转/分的速度搅拌45分钟，即得浸渍浆料；
（4）将步骤（2）得到的混合纤维条放入浸渍浆料中处理30分钟后取出，放入鼓风干燥箱中，以90℃的温度干燥至含水量小于0.2%，然后将干燥的混合纤维条导入双螺杆挤出机，控制挤出温度为170℃，挤出造粒即得本发明材料。
本发明的优点是：本发明首先添加纳米三氧化二锑，在聚合物材料中的分散好，能在燃烧表面形成壳层，起到隔热和阻隔可燃气体向燃烧表面迁移的作用；协同十溴二苯乙烷的添加，与纳米三氧化二锑反应生成的三溴化锑，进一步减缓或终止燃烧反应，起到良好的阻燃效果，提高了聚合物的冲击强度、断裂伸长率、流动速率，具有良好的成型加工性。同时将SEBS作为聚乳酸的增韧剂，使得制成的改性聚乳酸纤维具有很好的韧性，同时能极大的提升材料的冲击强度。
本发明将混合纤维浸渍在含有改性后的氧化铈、纳米氧化锌、苯并三唑中，三者协同作用，覆盖在混合纤维表面以及孔隙中，提高了混合纤维的抗紫外线的效果，同时内含硬酯酸单甘油酯等润滑成分，使得后续挤出造粒工艺更加流畅，从而提高了加工性。本发明材料制成的汽车内饰件抗紫外老化，使用寿命长。
具体实施方式
一种汽车内饰用抵抗紫外老化的复合材料，由下列重量份（公斤）的原料制备制成：聚乳酸100、纳米三氧化二锑3.5、十溴二苯乙烷10、SEBS25、红麻纤维60、氧化铈4、纳米氧化锌7、苯并三唑0.8、硅烷偶联剂KH5700.6、硬酯酸单甘油酯1、明胶5、水适量、聚磷酸铵1、EVA乳液6。
所述一种汽车内饰用抵抗紫外老化的复合材料，由以下具体步骤制成：
（1）将聚乳酸在真空干燥箱中80℃干燥10小时待用，纳米三氧化二锑、十溴二苯乙烷分别烘箱中60℃下干燥5小时和8小时待用；将干燥后的物料放入高速搅拌机中，以1000转/分的速度搅拌10分钟后，加入SEBS，继续搅拌10分钟后将混合物料送入双螺杆挤出机中在175℃的温度，螺杆转速为150转/分的工艺条件下挤出造粒，得到改性聚乳酸母粒；
（2）将改性聚乳酸母粒送入螺杆纺丝机中进行共混熔融并挤出纺丝（控制螺杆挤出速度为250转/分，喷丝熔体温度控制在200℃），然后将喷出的初纤维经水浴冷却，控制水浴温度在20℃，水浴冷却后将纤维用120℃的热风干燥，即得改性聚乳酸纤维；将红麻纤维进行开松处理，处理后的红麻纤维与改性聚乳酸纤维进行混纺并条，得到混合纤维条；
（3）将氧化铈与纳米氧化锌放入高速混合机中，边搅拌将硅烷偶联剂KH570喷洒在粉体表面，继续以1000转/分的速度搅拌10分钟后出料待用；将将明胶放入搅拌釜中，加入30倍量的水，静置溶胀30分钟后加热至完全溶解，冷却至室温后加入EVA乳液、聚磷酸铵，超声处理25分钟，使物料分散均匀，然后继续加入上述处理后的物料以及其余剩余成分，继续以300转/分的速度搅拌45分钟，即得浸渍浆料；
（4）将步骤（2）得到的混合纤维条放入浸渍浆料中处理30分钟后取出，放入鼓风干燥箱中，以90℃的温度干燥至含水量小于0.2%，然后将干燥的混合纤维条导入双螺杆挤出机，控制挤出温度为170℃，挤出造粒即得本发明材料。
本发明材料可以直接经过注塑机注塑成型，制成各种汽车内饰件。本发明制成的材料经过检测，阻燃性能达到UL-94V-0级，弯曲强度为102.6MPa，冲击强度为109.4J/m。

Claims (2)

1.一种汽车内饰用抵抗紫外老化的复合材料，其特征在于，由下列重量份的原料制备制成：聚乳酸100-103、纳米三氧化二锑3.5-4、十溴二苯乙烷10-11、SEBS25-27、红麻纤维60-62、氧化铈4-5、纳米氧化锌7-8、苯并三唑0.8-1、硅烷偶联剂KH5700.6-0.7、硬酯酸单甘油酯1-1.3、明胶5-6、水适量、聚磷酸铵1-1.4、EVA乳液6-7.4。
2.根据权利要求1所述一种汽车内饰用抵抗紫外老化的复合材料，其特征在于，由以下具体步骤制成：
（1）将聚乳酸在真空干燥箱中80℃干燥10小时待用，纳米三氧化二锑、十溴二苯乙烷分别烘箱中60℃下干燥5小时和8小时待用；将干燥后的物料放入高速搅拌机中，以1000转/分的速度搅拌10分钟后，加入SEBS，继续搅拌10分钟后将混合物料送入双螺杆挤出机中在175℃的温度，螺杆转速为150转/分的工艺条件下挤出造粒，得到改性聚乳酸母粒；
（2）将改性聚乳酸母粒送入螺杆纺丝机中进行共混熔融并挤出纺丝（控制螺杆挤出速度为250转/分，喷丝熔体温度控制在200℃），然后将喷出的初纤维经水浴冷却，控制水浴温度在20℃，水浴冷却后将纤维用120-130℃的热风干燥，即得改性聚乳酸纤维；将红麻纤维进行开松处理，处理后的红麻纤维与改性聚乳酸纤维进行混纺并条，得到混合纤维条；
（3）将氧化铈与纳米氧化锌放入高速混合机中，边搅拌将硅烷偶联剂KH570喷洒在粉体表面，继续以1000转/分的速度搅拌10分钟后出料待用；将将明胶放入搅拌釜中，加入30倍量的水，静置溶胀30分钟后加热至完全溶解，冷却至室温后加入EVA乳液、聚磷酸铵，超声处理25分钟，使物料分散均匀，然后继续加入上述处理后的物料以及其余剩余成分，继续以300转/分的速度搅拌45分钟，即得浸渍浆料；
（4）将步骤（2）得到的混合纤维条放入浸渍浆料中处理30分钟后取出，放入鼓风干燥箱中，以90℃的温度干燥至含水量小于0.2%，然后将干燥的混合纤维条导入双螺杆挤出机，控制挤出温度为170℃，挤出造粒即得本发明材料。
CN201510609874.1A 2015-09-23 2015-09-23 一种汽车内饰用抵抗紫外老化的复合材料及其制备方法 Pending CN105176028A (zh)