CN105174807A - 一种填缝剂耐候性稳定剂和制备方法 - Google Patents
一种填缝剂耐候性稳定剂和制备方法 Download PDFInfo
- Publication number
- CN105174807A CN105174807A CN201510597423.0A CN201510597423A CN105174807A CN 105174807 A CN105174807 A CN 105174807A CN 201510597423 A CN201510597423 A CN 201510597423A CN 105174807 A CN105174807 A CN 105174807A
- Authority
- CN
- China
- Prior art keywords
- parts
- weather resistance
- stabilizing agent
- spackling
- vinyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种填缝剂耐候性稳定剂,按质量份数包括乙烯-醋酸乙烯共聚物2-3份、玻化微珠8-12份、丙烯酸树脂1-1.5份、羟丙基甲基纤维素3-6份、无机铝盐防水剂1-1.3份、硅酸镁铝0.5-1.5份、107有机硅胶1.5-1.9份。将乙烯-醋酸乙烯共聚物和丙烯酸树脂,超声分散0.5-1h后加入有无机铝盐防水剂、硅酸镁铝和107有机硅胶,高速搅拌分散1-1.5h,最后加入玻化微珠和羟丙基甲基纤维素,缓慢降至室温即得。
Description
技术领域
本发明涉及一种建筑用填缝剂,具体说是一种填缝剂耐候性稳定剂和制备方法。
背景技术
由于填缝剂能完美的修补地表面的开裂或破损,还可自行配制颜色丰富色彩丰富,因而越来越受客人青睐。而现有的填缝剂大都采用水泥制备,配以水泥常用的添加剂,存在耐环境、环保上的缺陷,在应用场合和使用安全、寿命长局限性大。
发明内容
针对现有技术的不足,本发明提供了一种耐环境、环保的填缝剂耐候性稳定剂和制备方法。
本发明采用的技术方案是:一种填缝剂耐候性稳定剂,按质量份数包括乙烯-醋酸乙烯共聚物2-3份、玻化微珠8-12份、丙烯酸树脂1-1.5份、羟丙基甲基纤维素3-6份、无机铝盐防水剂1-1.3份、硅酸镁铝0.5-1.5份、107有机硅胶1.5-1.9份。
一种填缝剂耐候性稳定剂制备方法,包括以下步骤:(1)将乙烯-醋酸乙烯共聚物和丙烯酸树脂,超声分散0.5-1h后加入有无机铝盐防水剂、硅酸镁铝和107有机硅胶,高速搅拌分散1-1.5h,最后加入玻化微珠和羟丙基甲基纤维素,缓慢降至室温即得。
采用上述技术方案后,本发明的有益效果是:在填缝剂的中增加107有机硅橡胶,能够有效增强填缝剂的憎水性和憎水迁移性,使得填缝剂具有自清洁性,不易附着灰尘,保证了填缝剂的使用效果。乙烯-醋酸乙烯共聚物提高耐水性,其密闭泡孔结构、不吸水、防潮、耐水性能良好,提高耐腐蚀性:耐海水、油脂、酸、碱等化学品腐蚀,抗菌、无毒、无味、无污染,便于进行剪裁加工,具有良好的防震、缓冲性能,隔热,保温防寒及低温性能优异,可耐严寒和曝晒。玻化微珠作为填充骨料,进一步提高其绝热﹑防火﹑吸音﹑保温性能。填充骨料和绝热﹑防火﹑吸音﹑保温材料。丙烯酸树脂有效促进户外抗老化性能.羟丙基甲基纤维素作为增强剂、保水剂能使浆料在涂抹后不会因干得太快而龟裂,同时增强硬化后强度。无机铝盐防水剂提高其防水性能,结合硅酸镁铝悬浮增稠,同时提高填缝剂稳定性,确保使用安全卫生。
具体实施方式
以下结合实施例对本发明作进一步说明。
实施例一
一种填缝剂耐候性稳定剂,按质量份数包括乙烯-醋酸乙烯共聚物2份、玻化微珠8份、丙烯酸树脂1份、羟丙基甲基纤维素3份、无机铝盐防水剂1份、硅酸镁铝0.5份、107有机硅胶1.5份。
实施例二
一种填缝剂耐候性稳定剂,按质量份数包括乙烯-醋酸乙烯共聚物3份、玻化微珠12份、丙烯酸树脂1.5份、羟丙基甲基纤维素6份、无机铝盐防水剂1.3份、硅酸镁铝1.5份、107有机硅胶1.9份。
实施例三
一种填缝剂耐候性稳定剂,按质量份数包括乙烯-醋酸乙烯共聚物2.5份、玻化微珠11份、丙烯酸树脂1.35份、羟丙基甲基纤维素5份、无机铝盐防水剂1.2份、硅酸镁铝1.2份、107有机硅胶1.8份。
上述填缝剂耐候性稳定剂制备方法,包括以下步骤:(1)将乙烯-醋酸乙烯共聚物和丙烯酸树脂,超声分散0.5-1h后加入有无机铝盐防水剂、硅酸镁铝和107有机硅胶,高速搅拌分散1-1.5h,最后加入玻化微珠和羟丙基甲基纤维素,缓慢降至室温即得。
Claims (2)
1.一种填缝剂耐候性稳定剂,其特征在于:按质量份数包括乙烯-醋酸乙烯共聚物2-3份、玻化微珠8-12份、丙烯酸树脂1-1.5份、羟丙基甲基纤维素3-6份、无机铝盐防水剂1-1.3份、硅酸镁铝0.5-1.5份、107有机硅胶1.5-1.9份。
2.一种填缝剂耐候性稳定剂制备方法,包括以下步骤:(1)将乙烯-醋酸乙烯共聚物和丙烯酸树脂,超声分散0.5-1h后加入有无机铝盐防水剂、硅酸镁铝和107有机硅胶,高速搅拌分散1-1.5h,最后加入玻化微珠和羟丙基甲基纤维素,缓慢降至室温即得。