CN105170088B - 制备含油污泥基活性炭水处理剂的方法 - Google Patents

制备含油污泥基活性炭水处理剂的方法 Download PDF

Info

Publication number
CN105170088B
CN105170088B CN201510669997.4A CN201510669997A CN105170088B CN 105170088 B CN105170088 B CN 105170088B CN 201510669997 A CN201510669997 A CN 201510669997A CN 105170088 B CN105170088 B CN 105170088B
Authority
CN
China
Prior art keywords
oily sludge
activated carbon
water treatment
treatment agent
matrix activated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510669997.4A
Other languages
English (en)
Other versions
CN105170088A (zh
Inventor
张宏哲
牟桂琴
唐晓丽
张志远
郭亚逢
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Petroleum and Chemical Corp
Sinopec Qingdao Safety Engineering Institute
Original Assignee
China Petroleum and Chemical Corp
Sinopec Qingdao Safety Engineering Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China Petroleum and Chemical Corp, Sinopec Qingdao Safety Engineering Institute filed Critical China Petroleum and Chemical Corp
Priority to CN201510669997.4A priority Critical patent/CN105170088B/zh
Publication of CN105170088A publication Critical patent/CN105170088A/zh
Application granted granted Critical
Publication of CN105170088B publication Critical patent/CN105170088B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种制备含油污泥基活性炭水处理剂的方法，主要解决现有技术中尚无制备含油污泥基活性炭水处理剂的方法的问题。本发明通过采用一种制备含油污泥基活性炭水处理剂的方法，包括如下步骤：(1)将含油污泥基活性炭、无机聚合氯化铝、石灰、明矾按照一定比例混合均匀；(2)在硅胶溶液中加入水配成硅溶胶粘结剂，然后加入到步骤(1)中的样品中，充分混合后放置于60‑100℃的干燥箱中进行空气预氧化，降温的样品在氮气气氛下升温至300‑500℃，恒温焙烧1‑3小时，降温后即可得到所述水处理剂的技术方案较好地解决了上述问题，可用于水处理剂制备中。

Description

制备含油污泥基活性炭水处理剂的方法
技术领域
本发明涉及一种制备含油污泥基活性炭水处理剂的方法。
背景技术
粉状活性炭吸附处置污水中的有机污染物是一项成熟的技术，该方法具有简单，操作方便，吸附速度快，吸附能力强的优点。但由于活性炭粉的再生困难，往往只能使用一次，因此成本较高。故一般多用于废水的深度处理(三级处理)。但也有作为一级处理的辅助工序，这种情况要求吸附剂便宜，处理效率一般不高。因此，开发处理效果好、吸附效率高、廉价易得的活性炭吸附剂成为该技术大面积推广的关键。
含油污泥是石化行业生产过程中不可避免的一种副产物，含油污泥中的有机物化合物和无机化合物会在热解过程中发生一系列复杂的化学变化和物理变化，生成碳基材料和挥发分有机物。虽然由含油污泥制得的活性炭性能并不高，实际应用还较少，但因其价格低廉、含碳率高、材料易得、原料充足且绿色无毒而日益受到青睐。以含油污泥为原料所制得的碳基吸附材料具有发达的微孔结构和较大的比表面积，这种碳基吸附材料对印染废水、含重金属废水均具有很好的处理效果。
发明内容
本发明所要解决的技术问题是现有技术中尚无制备含油污泥基活性炭水处理剂的方法的问题，提供一种新的制备含油污泥基活性炭水处理剂的方法。该方法用于水处理剂制备中，可以达到对泄漏物吸附、分离、无害化处理的目的。
为解决上述问题，本发明采用的技术方案如下：一种制备含油污泥基活性炭水处理剂的方法，包括如下步骤：(1)将含油污泥基活性炭、无机聚合氯化铝、石灰、明矾按照一定比例混合均匀；(2)在硅胶溶液中加入水配成硅溶胶粘结剂，然后加入到步骤(1)中的样品中，充分混合后放置于60-100℃的干燥箱中进行空气预氧化，降温的样品在氮气气氛下升温至300-500℃，恒温焙烧1-3小时，降温后即可得到所述水处理剂；其中，含油污泥基活性炭、无机聚合氯化铝、石灰、明矾、硅溶胶的重量比为70-100：30-50：20-40：10-20：30-60。
上述技术方案中，优选地，空气预氧化时间为：6-12h。
本发明提供一种利用含油污泥基活性炭制备水处理剂的方法，由于含油污泥中含有较多的碳，具备了制备活性炭的客观条件。含油污泥价格低廉、含碳率高、材料易得、原料充足且绿色无毒而日益受到青睐。以含油污泥基活性炭为原料所制得的活性炭均具有发达的微孔结构和较大的比表面积，通过定向调控活性炭孔径分布和表面官能团，可以达到对泄漏物吸附、分离、无害化处理的目的，取得了较好的技术效果。
下面通过实施例对本发明作进一步的阐述，但不仅限于本实施例。
具体实施方式
【实施例1】
含油污泥基活性炭(粒度为100目,比表面积为674m2/g)70g、无机聚合氯化铝30g、石灰(粒度为150目)20g、明矾10g、硅溶胶30g、水适量。
按照以下步骤制备水处理剂：(1)将含油污泥基活性炭、无机聚合氯化铝、石灰、明矾按照一定比例混合均匀；(2)称称取30g硅胶溶液，加入30g水配成粘结剂，然后加入到步骤(1)中的样品中，充分混合后的放置于80℃干燥箱中空气预氧化8h，自然降温后取出；(3)将预氧化后的样品在氮气气氛下以5℃/min升温至400℃，恒温2小时进行焙烧，自然降温后取出即可。
将水处理剂用于净化成品油库含油污水，500ml，化学需氧量(COD)为2374，加入2.5g水处理剂，搅拌均匀后，沉淀反应3h，COD去除率为72.1％。
【实施例2】
含油污泥基活性炭(粒度为100目,比表面积为674m2/g)70g、无机聚合氯化铝40g、石灰(粒度为150目)30g、明矾20g、硅溶胶40g、水适量。
按照以下步骤制备水处理剂：(1)将含油污泥基活性炭、无机聚合氯化铝、石灰、明矾按照一定比例混合均匀；(2)称称取40g硅胶溶液，加入40g水配成粘结剂，然后加入到步骤(1)中的样品中，充分混合后的放置于80℃干燥箱中空气预氧化8h，自然降温后取出；(3)将预氧化后的样品在氮气气氛下以5℃/min升温至400℃，恒温2小时进行焙烧，自然降温后取出即可。
将水处理剂用于净化成品油库含油污水，500ml，COD为2374，加入2.5g水处理剂，搅拌均匀后，沉淀反应3h，COD去除率为84.1％。
【实施例3】
含油污泥基活性炭(粒度为100目,比表面积为674m2/g)80g、无机聚合氯化铝40g、石灰(粒度为150目)20g、明矾10g、硅溶胶30g、水适量。
按照以下步骤制备水处理剂：(1)将含油污泥基活性炭、无机聚合氯化铝、石灰、明矾按照一定比例混合均匀；(2)称称取30g硅胶溶液，加入30g水配成粘结剂，然后加入到步骤(1)中的样品中，充分混合后的放置于80℃干燥箱中空气预氧化12h，自然降温后取出；(3)将预氧化后的样品在氮气气氛下以5℃/min升温至400℃，恒温2小时进行焙烧，自然降温后取出即可。
将水处理剂用于净化成品油库含油污水，500ml，COD为2374，加入2.5g水处理剂，搅拌均匀后，沉淀反应3h，COD去除率为93.1％。
显然，本发明的利用含油污泥基活性炭制备水处理剂的方法，以含油污泥基活性炭为原料所制得的活性炭均具有发达的微孔结构和较大的比表面积，通过定向调控活性炭孔径分布和表面官能团，可以达到对泄漏物吸附、分离、无害化处理的目的，取得了较好的技术效果。

Claims (1)

1.一种制备含油污泥基活性炭水处理剂的方法，包括如下步骤：(1)将含油污泥基活性炭、无机聚合氯化铝、石灰、明矾按照一定比例混合均匀；(2)在硅胶溶液中加入水配成硅溶胶粘结剂，然后加入到步骤(1)中的样品中，充分混合后放置于60-100℃的干燥箱中进行空气预氧化，降温的样品在氮气气氛下升温至300-500℃，恒温焙烧1-3小时，降温后即可得到所述水处理剂；其中，含油污泥基活性炭、无机聚合氯化铝、石灰、明矾、硅溶胶的重量比为70-100：30-50：20-40：10-20：30-60；空气预氧化时间为：6-12h。
CN201510669997.4A 2015-10-13 2015-10-13 制备含油污泥基活性炭水处理剂的方法 Active CN105170088B (zh)