CN105155807A - Multifunctional moisture-proof pad - Google Patents
Multifunctional moisture-proof pad Download PDFInfo
- Publication number
- CN105155807A CN105155807A CN201510387260.3A CN201510387260A CN105155807A CN 105155807 A CN105155807 A CN 105155807A CN 201510387260 A CN201510387260 A CN 201510387260A CN 105155807 A CN105155807 A CN 105155807A
- Authority
- CN
- China
- Prior art keywords
- proof pad
- material layer
- puigging
- moisture
- pad according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a home decoration articles for daily use, in particular to a multifunctional moisture-proof pad which comprises a sound-insulation layer and a plurality of support units. The support units are positioned under the sound-insulation layer; channels are formed by gaps among the support units; the widths of the support units range from 1mm to 1000mm; the heights of the support units range from 0.3mm to 39mm; the distances among the adjacent support units range from 0.5mm to 500mm; the thickness of the sound-insulation layer ranges from 0.02mm to 40mm; the support units are cylinders or cuboids or trapezoids or polygonal columns or special-shaped curved solids. The multifunctional moisture-proof pad has the advantages that air can be effectively circulated, moisture-proof, mildew-proof, sound-insulation and noise reduction effects can be realized, users feel comfortable on the feet, and the multifunctional moisture-proof pad is particularly suitable to be laid underneath floors or carpets.
Description
Technical field
The present invention relates to a kind of house ornamentation daily necessities, particularly relate to a kind of Multi-functional moisture-proof pad.
Background technology
The two sides of existing moistureproof cushion product is all smooth; after Floor Covering completes; although prevent the impact of moisture on floor on ground; protect floor; but because cement floor has been hermetic with outside, the moisture on ground has been retained in cement floor, cannot get rid of always; if under wet conditions can mouldy, breed bacteria below moistureproof cushion of long duration. moistureproof cushion occurs aging or damaged, and the moisture on ground, the bacterium grown can affect use and the family health care on floor.Existing moistureproof cushion must select when installation the ground cushion that kind is good, and when installing, moistureproof cushion can not have breakage, installs and needs extreme care.Because the width of ground cushion is all generally 1 meter-1.5 meters, time ground cushion is installed, the bonding of aging adhesive tape must be not easy good for the gap viscosity of ground cushion, otherwise gap place has moisture affects floor.Inconvenience is very installed, cost is higher.
In addition, the shortcoming having soundproof effect not good between existing residenter house is gone downstairs, the cement board of floor and the floor be layered on cement board is only relied on to be difficult to reach the effect of abundant sound insulation, and the single differentiation to high frequency noise and low frequency noise of traditional product, the different noise fully stopping each frequency, thus affect the quality of life between resident.
CN100591261C (2010-2-24) discloses a kind of composite floor cushion, but it mainly solves the problem that ground cushion thoroughly can not pick people's sole dirt, for being laid on floor, does not relate to the problem such as sound insulation or protection against the tide simultaneously.
Summary of the invention
The object of this invention is to provide a kind of can air circulation effectively, moistureproof and mildewproof, sound insulation and noise reduction, comfortable foot feeling the Multi-functional moisture-proof pad being particularly suitable for being laid under floor or carpet.
Above-mentioned technical purpose of the present invention is achieved by the following technical programs:
A kind of Multi-functional moisture-proof pad, it comprises puigging and is positioned at the multiple support units below described puigging;
The space formed between described support unit forms passage;
The width of described support unit is 1-1000mm;
The height of described support unit is 0.3-39mm;
Spacing between adjacent supports unit is 0.5-500mm;
Described puigging thickness is 0.02-40mm;
Described support unit is cylinder, cuboid, prismatoid, polygon cylinder or different in nature curved body.
Mat of the present invention directly can lay use, such as, for outdoor goods, also can use in interior decoration, preferably be laid on below floor or carpet.Puigging of the present invention can be one deck or two-layer above structure; Puigging is preferably smooth, is convenient at laying floor above; Certainly, in order to anti-skidding or increase feel or strengthen attractive in appearance, also puigging end face can be processed into level and smooth dapple structure.Mat soundproof effect of the present invention and feel good, can make noise minimization when people walk on floor, sound-absorbing reaches 5 decibels; And can make the minimum sound that next room or downstairs room are heard, sound insulation reaches 10 decibels.Folding, transport or selling of mat of the present invention is also convenient in the setting of passage, does not produce impression when mat is folded, when transporting or sell to take volume little, overallly high-endly to improve grade, also enhances air circulation circulating function simultaneously.
The space formed between support unit forms passage, the earth's surface thermogenetic hot gas that wets can flow upward, the water moisture lower from the temperature on floor is walked toward below, enter first passage and flow wherein, according to aerodynamic principle, can flow in first passage after air meets, the higher convection velocity of temperature is faster, the heat taken away and aqueous vapor more, the heat taken away and aqueous vapor upwards derive discharge by mat and space reserved between the walls, thus realize air circulation, reach the heat radiation dehumidifying object of moistureproof and mildewproof and the temperature adjuster object of constant temperature, in order to avoid too high or too low for temperature, moist or mould damages floor.
Spacing between the width of support unit and/or adjacent supports unit can not too greatly can not be too little, otherwise when people directly walks on the floor above mat or above mat, can make first passage shutoff, or air circulation is not smooth, thus above-mentioned functions is disappeared; Meanwhile, the height of support unit can not too greatly can not be too little, and too conference increases cost of production; Too littlely can reduce overall feel, reduce mat intensity, and the air circulation of first passage can be affected, even can make first passage shutoff.
Be different from the single differentiation to high frequency noise and low frequency noise of traditional product, the present invention is a transboundary product efficiently.Press test result on year-on-year basis, this invention product can improve more than 2 times than the sound insulation and noise reduction rate of original traditional product; Meanwhile, be arranged on the compound moisture sealer of top layer, make sound insulating pad possess high anti-property and feel.As preferably, described puigging thickness is 0.3-40mm.
As preferably, described puigging upper surface or soffit are provided with nanometer silver antimicrobial mildew-resistant grain or nanometer silver antimicrobial mildew-resistant layer.
Antibacterial and mouldproof component especially nanometer silver antimicrobial mildew-resistant grain or nanometer silver antimicrobial mildew-resistant layer is set, growing of mould can be prevented from source further.
As preferably, described puigging is one or more in full open aperture foamed material layer or closed cell foamed material layer or half perforate foamed material layer.
If communicate between hole, be then called perforate.Full open aperture expanded material refers to and all communicates between the hole in material.If each hole and surrounding hole separate completely, be then called closed pore.If hole half perforate semi-closure hole, be then called half perforate foamed material layer.
Set of the present invention half perforate expanded material and full open aperture expanded material or the advantage of cork in sound insulation and noise reduction, adopt MULTILAYER COMPOSITE technology, effectively overcome the shortcoming of each material itself, can solve the noise as high frequency, low frequency, make it effective sound insulation and noise reduction, effectively reduce the noise between floor, can reduce and obviously improve 95% from impact sound (knock that high-heeled shoes or other hard object produce) upstairs, thus improve quality of the life.
As preferably, be provided with waterproofing membrane layer above described puigging, described waterproofing membrane layer is the moistureproof ply of paper of PE rete or aluminum membranous layer or metal.Thus the moistureproof and mildewproof performance on further enhancing floor, soundproof effect and feel.
As preferably, described puigging and described support column are composited by heating compound or glue; Or formed by hot melt roll-in.The product especially uniformity of first passage or second channel and the stability of performance can be improved like this.
As preferably, described full open aperture foamed material layer is full open aperture EPDM foam sponge layer, EPE pearl wool, PU foaming, SBR foaming or the PE modified insulation material layer of full open aperture; Described half perforate foamed material layer is half perforate EPDM foam sponge layer or half perforate PVC foam material layer; Described closed cell foamed material layer is EPS foaming, EPE, IXPE, XPE, rubber expanded material, EVA material layer or closed-cell polyethylene modification insulation material layer.
EPE is expandability polyethylene, also known as expanded polyethylene foam, is non-crosslinked hole-closing structure.
IXPE is chemistry (physics) crosslinked polyethylene foam sheet.XPE and processes for chemically crosslinked polyethylene expanded material.EVA is ethylene-vinyl acetate copolymer.
More preferably, the preparation method of described PE modified sound insulation materials comprises the following steps successively:
(1) raw material prepares: polyethylene 30-75 part, Zinc Oxide 10-40 part, magnesia 8-25 part, glass fiber 10-15 part, peroxidating two different phenylpropyl alcohol crosslinking agent 0.8-1.5 part, stearic acid active lubricant 1-2 part;
(2) just mix: described crosslinking agent, Zinc Oxide, magnesia and glass fiber are mixed, obtain just mixed reactant;
(3) entirely mix: the described reactant and described polyethylene and mix lubricant of just mixing is obtained complete dark compound;
(4) banburying is shaping: by described complete dark compound temperature be 160-180 DEG C, pressure be 40-50MPa under banburying shaping.
The present invention adopts Zinc Oxide, magnesia and glass fiber filling-modified in polyethylene, can assist the noise solving as high frequency, low frequency further, make it effective sound insulation and noise reduction; Improve dimensional stability simultaneously.
As preferably, described support unit is cylinder, rectangular shaped post or polygon cylinder.
By the connectivity structure of passage and air through hole, air self-cycle structure can be formed, be convenient to discharge moisture.Especially, the earth's surface thermogenetic hot gas that wets can flow upward, the water moisture lower from the temperature on floor is walked toward below, also flowed wherein by passage, according to aerodynamic principle, can flow in the channel after air meets, the higher convection velocity of temperature is faster, the heat taken away and aqueous vapor more, the heat taken away and aqueous vapor upwards derive discharge by mat and space reserved between the walls, thus realize the heat radiation dehumidifying object of mildew-resistant and the temperature adjuster system of constant temperature, in order to avoid damage floor too high or too low for temperature.
As preferably, be provided with in described passage or be connected with dryer.
More electedly, described dryer is connected with external control box; Blower fan, heater and for accommodating and protect the elastic protecting sleeve of described blower fan and heater is provided with in described dryer; Controller, time switch and attaching plug is mounted with in described control box.
When needs work, plug in, open time switch timing, dryer is started working, and blower fan makes the moisture in passage discharge; When temperature is lower or humidity is larger, start heater, make condensing drip be heated as steam to discharge, meanwhile, when running into rainy weather, floor itself is than when being easier to make moist breed bacteria, start heater, according to pasteurization principle, add blowing hot wind by heater and keep a period of time, most harmful bacteria in floor can be killed.
Present invention also offers a kind of installation and application of Multi-functional moisture-proof pad, comprise the following steps:
(1) ground even level, totally drying is guaranteed;
(2) eliminating steam, is compressed by the puigging of described mat upward; Laying floor on described mat;
(3) floor and wall or between floor and ground the circulation space of reserved 0.5-5mm to provide air circulation.
By the specific ground cushion of the present invention and mounting method, air under floor can be made to keep continuing exchange and eliminate the steam from floor.
As preferably, described circulation space is arranged on the nearest described passage of distance wall or ground.
The heat of discharging after being convenient to cross-ventilation and steam, in the circulation of passage Inner eycle, are finally collected to the nearest described passage of distance wall or ground, finally discharge from the nearest described passage of distance wall or ground.Certainly, in order to improve circulation effect, preferably discharge blower fan can also be communicated with on the nearest described passage of distance wall or ground.
In sum, the present invention has following beneficial effect: can air circulation effectively, moistureproof and mildewproof, sound insulation and noise reduction, comfortable foot feeling.
Accompanying drawing explanation
Fig. 1 is one of Multi-functional moisture-proof pad cross-sectional schematic of the present invention;
Fig. 2 is one of Multi-functional moisture-proof pad lateral view of the present invention;
Fig. 3 is one of Multi-functional moisture-proof pad cross-sectional schematic of the present invention;
Fig. 4 is one of Multi-functional moisture-proof pad lateral view of the present invention;
Fig. 5 is one of Multi-functional moisture-proof pad cross-sectional schematic of the present invention;
Fig. 6 is that Multi-functional moisture-proof pad of the present invention analyses and observe one of upward view;
Fig. 7 is the dryer schematic diagram in Multi-functional moisture-proof pad of the present invention
Fig. 8 is one of Multi-functional moisture-proof pad scheme of installation of the present invention;
Fig. 9 is that Multi-functional moisture-proof pad of the present invention installs elevation.
Detailed description of the invention
Below in conjunction with accompanying drawing, the present invention is described in further detail.
As shown in Fig. 1-Fig. 9, multiple support units 20 that Multi-functional moisture-proof pad comprises puigging 1 and is positioned at below puigging 1, the space formed between support unit 20 forms passage 23, the width of support unit 20 is 1-1000mm, the height of support unit 20 is 0.3-39mm, spacing between adjacent supports unit 20 is 0.5-500mm, the earth's surface thermogenetic hot gas that wets can flow upward, the water moisture lower from the temperature on floor is walked toward below, admission passage also flows wherein, according to aerodynamic principle, can flow in the channel after air meets, the higher convection velocity of temperature is faster, the heat taken away and aqueous vapor more, the heat taken away and aqueous vapor upwards derive discharge by mat and space reserved between the walls, thus realize air circulation, reach the heat radiation dehumidifying object of moistureproof and mildewproof and the temperature adjuster object of constant temperature, in order to avoid too high or too low for temperature, moist or mould damages floor.
In order to strengthen the moistureproof and mildewproof performance on floor, soundproof effect and feel further, be provided with waterproofing membrane layer above puigging 1, waterproofing membrane layer is PE rete or aluminum membranous layer or the moistureproof ply of paper of metal.
For preventing growing of mould from source, antibacterial and mouldproof component especially nanometer silver antimicrobial mildew-resistant grain or nanometer silver antimicrobial mildew-resistant layer being set thereon, such as, on puigging 1 upper surface or soffit, being provided with nanometer silver antimicrobial mildew-resistant grain or nanometer silver antimicrobial mildew-resistant layer 3.
In order to improve the product especially uniformity of passage and the stability of performance, inventor does not adopt existing integrated compression method, but is composited by glue by puigging 1; Or formed by hot melt roll-in.
Puigging 1 can be one deck or two-layer above structure, the material of puigging 1 can select in full open aperture foamed material layer or closed cell foamed material layer or half perforate foamed material layer one or more.
If communicate between hole, be then called perforate.Full open aperture expanded material refers to and all communicates between the hole in material.If each hole and surrounding hole separate completely, be then called closed pore.If hole half perforate semi-closure hole, be then called half perforate foamed material layer.
Full open aperture foamed material layer is full open aperture EPDM foam sponge layer, EPE pearl wool, PU foaming, SBR foaming or the PE modified insulation material layer of full open aperture; Half perforate foamed material layer is half perforate EPDM foam sponge layer or half perforate PVC foam material layer; Closed cell foamed material layer is EPS foaming, EPE, IXPE, XPE, rubber expanded material, EVA material layer or closed-cell polyethylene modification insulation material layer.
Support unit 20 can be cylinder, rectangular shaped post or polygon cylinder.Such as Fig. 1, Fig. 2 are pentagon cylinder; Fig. 3, Fig. 4 are cylinder; Fig. 5, Fig. 6 are rectangular shaped post.The heat taken away and aqueous vapor upwards derive discharge by mat and space reserved between the walls, thus realize the heat radiation dehumidifying object of mildew-resistant and the temperature adjuster system of constant temperature, in order to avoid damage floor too high or too low for temperature.
In order to tackle the special climate environment such as the comparatively large or rainy weather of the lower or humidity of temperature, invention is expected arranging passage 23 in or connection dryer 26, and dryer 26 connects external control box 27; When needs work, plug in, open time switch timing, dryer is started working, and blower fan 262 makes the moisture in first passage or second channel discharge; Start heater 262, make condensing drip be heated as steam to discharge, such as when running into rainy weather, floor itself is than when being easier to make moist breed bacteria, start heater 262, according to pasteurization principle, add blowing hot wind by heater and keep a period of time, most harmful bacteria in floor can be killed.
Blower fan 261, heater 262 and for accommodating and protection blower fan 261 and the elastic protecting sleeve 263 of heater 262 is provided with in dryer 26; Controller, time switch and attaching plug is mounted with in control box 27.
Embodiment one
Multiple support units 20 that Multi-functional moisture-proof pad comprises puigging 1 and is positioned at below puigging 1; The space formed between support unit 20 forms passage 23; The width of support unit 20 is 4mm; The height of support unit 20 is 1.5mm; Spacing between adjacent supports unit 20 is 4mm; Puigging 1 thickness is 1.5mm.Puigging 1 adopts full open aperture EPDM foam sponge layer, and supporting layer adopts half perforate PVC foam material layer.
When installing and using, take following steps:
1 guarantees ground even level, totally drying;
2 by the puigging 1 of mat upward, compresses and get rid of steam; Laying floor on mat;
3 floor 4 and wall 5 or between floor and ground the circulation space of reserved 1.5mm to provide air circulation.
Circulation space is arranged on the nearest second channel 24 of distance wall or ground.In order to improve circulation effect, the nearest second channel of distance wall or ground being arranged or connects dryer 26.
Transaudient and sound insulation test is carried out in the standard room of 10 square metres.
Table 1
IIC (impact acoustical ratings) is according to Standard, carry out the measurement of the level difference of each frequency range, the result directly evaluating out according to ISO sound insulation appraisal curve is sound insulation class (or weighted transmission loss), and this value does not comprise the corrections such as wall area, sound receiving room's absorption, flanking sound transmission loss; Therefore sound insulation class is commonly used to the actual defening effect between description two adjacent room.Impact sound insulation test according to the test of American society association ASTM49209 method, impact acoustical ratings according to American society association ASTME989 standard grading.IIC higher grade, and sound insulation property is better.
Table 2
Experimental data illustrates:
The sound insulation factor of carrying out each frequency range in laboratory or scene that refers to STC (STC) after detecting again according to measuring after body of wall revises by the factor such as absorption, flanking sound transmission of sound area, sound receiving room, again according to the result that ISO sound insulation appraisal curve is evaluated out, be generally used for the sound insulation property evaluating building unit.The classification of STC method of testing STC is according to American society association ASTME413-04 standard grading.STC higher grade, and sound insulation property is better.
Transaudient test is room temperature 11 DEG C, and relative humidity is carried out for 71% time.
As can be seen from Table 2, ground cushion of the present invention can effectively completely cut off high frequency noise and low frequency noise.And common market ground cushion does not only possess this function, and STC is generally less than 50.
Antibacterial and mouldproof effect detection: act on more than 6 months, is more than 95% to the antibiotic rate of staphylococcus aureus, reaches more than 93% to colibacillary antibiotic rate; Mildew-resistant grade is 0 grade, without Signs of Mould.
Embodiment two
Multiple support units 20 that Multi-functional moisture-proof pad comprises puigging 1 and is positioned at below puigging 1; The space formed between support unit 20 forms passage 23; The width of support unit 20 is 10mm; The height of support unit 20 is 10mm; Spacing between adjacent supports unit 20 is 40mm; Puigging 1 thickness is 40mm.Puigging 1 adopts closed pore IXPE layer, and supporting layer adopts closed-cell polyethylene modification insulation material layer.Puigging 1 upper surface or soffit are provided with nanometer silver antimicrobial mildew-resistant grain or nanometer silver antimicrobial mildew-resistant layer 3.
The preparation method of PE modified sound insulation materials comprises the following steps successively:
(1) raw material prepares: polyethylene 30 parts, Zinc Oxide 10 parts, 8 parts, magnesia, glass fiber 10 parts, the different phenylpropyl alcohol crosslinking agent of peroxidating two 0.8 part, stearic acid active lubricant 1 part;
(2) just mix: described crosslinking agent, Zinc Oxide, magnesia and glass fiber are mixed, obtain just mixed reactant;
(3) entirely mix: the described reactant and described polyethylene and mix lubricant of just mixing is obtained complete dark compound;
(4) banburying is shaping: by described complete dark compound temperature be 160 DEG C, pressure be 40MPa under banburying shaping.
When installing and using, take following steps:
1 guarantees ground even level, totally drying;
2 by the puigging 1 of mat upward, compresses and get rid of steam; Laying floor on mat; 3 floor and wall or between floor and ground the circulation space of reserved 0.5mm to provide air circulation.
Antibacterial and mouldproof effect detection: act on more than 6 months, is more than 96% to the antibiotic rate of staphylococcus aureus, reaches more than 94% to colibacillary antibiotic rate; Mildew-resistant grade is 0 grade, without Signs of Mould.
Embodiment three
Multiple support units 20 that Multi-functional moisture-proof pad comprises puigging 1 and is positioned at below puigging 1; The space formed between support unit 20 forms passage 23; The width of support unit 20 is 1000mm; The height of support unit 20 is 39mm; Spacing between adjacent supports unit 20 is 500mm; Puigging 1 thickness is 30mm.
Puigging 1 adopts closed-cell polyethylene modification insulation material layer, and supporting layer adopts half perforate EPDM foam sponge layer.
The preparation method of PE modified sound insulation materials comprises the following steps successively:
(1) raw material prepares: polyethylene 75 parts, Zinc Oxide 40 parts, 25 parts, magnesia, glass fiber 15 parts, the different phenylpropyl alcohol crosslinking agent of peroxidating two 1.5 parts, stearic acid active lubricant 2 parts;
(2) just mix: above-mentioned crosslinking agent, Zinc Oxide, magnesia and glass fiber are mixed, obtain just mixed reactant;
(3) entirely mix: the described reactant and described polyethylene and mix lubricant of just mixing is obtained complete dark compound;
(4) banburying is shaping: by described complete dark compound temperature be 180 DEG C, pressure be 50MPa under banburying shaping.
When installing and using, take following steps:
1 guarantees ground even level, totally drying;
2 by the puigging 1 of mat upward, compresses and get rid of steam; Laying floor on mat;
3 floor and wall or between floor and ground the circulation space of reserved 5mm to provide air circulation.
Antibacterial and mouldproof effect detection: act on more than 6 months, is more than 97% to the antibiotic rate of staphylococcus aureus, reaches more than 95% to colibacillary antibiotic rate; Mildew-resistant grade is 0 grade, without Signs of Mould.
Embodiment four
Multiple support units 20 that Multi-functional moisture-proof pad comprises puigging 1 and is positioned at below puigging 1; The space formed between support unit 20 forms passage 23; The width of support unit 20 is 1mm; The height of support unit 20 is 0.3mm; Spacing between adjacent supports unit 20 is 0.5mm; Puigging 1 thickness is 6mm.
Puigging 1 adopts closed-cell polyethylene modification insulation material layer, and supporting layer adopts closed pore EVA material layer.
The preparation method of PE modified sound insulation materials comprises the following steps successively:
(1) raw material prepares: polyethylene 45 parts, Zinc Oxide 30 parts, 15 parts, magnesia, glass fiber 12 parts, the different phenylpropyl alcohol crosslinking agent of peroxidating two 1 part, stearic acid active lubricant 1.5 parts;
(2) just mix: described crosslinking agent, Zinc Oxide, magnesia and glass fiber are mixed, obtain just mixed reactant;
(3) entirely mix: the described reactant and described polyethylene and mix lubricant of just mixing is obtained complete dark compound;
(4) banburying is shaping: by described complete dark compound temperature be 170 DEG C, pressure be 45MPa under banburying shaping.
Antibacterial and mouldproof effect detection: act on more than 6 months, is more than 98% to the antibiotic rate of staphylococcus aureus, reaches more than 96% to colibacillary antibiotic rate; Mildew-resistant grade is 0 grade, without Signs of Mould.
This specific embodiment is only explanation of the invention; it is not limitation of the present invention; those skilled in the art can make to the present embodiment the amendment not having creative contribution as required after reading this manual, as long as but be all subject to the protection of Patent Law in right of the present invention.
Claims (10)
1. a Multi-functional moisture-proof pad, is characterized in that: it comprises puigging (1) and is positioned at multiple support units (20) of described puigging (1) below;
The space formed between described support unit (20) forms passage (23);
The width of described support unit (20) is 1-1000mm;
The height of described support unit (20) is 0.3-39mm;
Spacing between described adjacent supports unit (20) is 0.5-500mm;
Described puigging (1) thickness is 0.02-40mm;
Described support unit (20) is cylinder, cuboid, prismatoid, polygon cylinder or different in nature curved body.
2. a kind of Multi-functional moisture-proof pad according to claim 1, is characterized in that: described puigging (1) upper surface or soffit are provided with nanometer silver antimicrobial mildew-resistant grain or nanometer silver antimicrobial mildew-resistant layer (3).
3. a kind of Multi-functional moisture-proof pad according to claim 1, is characterized in that: described puigging (1) is one or more in full open aperture foamed material layer or closed cell foamed material layer or half perforate foamed material layer.
4. a kind of Multi-functional moisture-proof pad according to claim 2, is characterized in that: the spacing of described passage (23) is 0.8-8mm.
5. a kind of Multi-functional moisture-proof pad according to claim 3, is characterized in that: described full open aperture foamed material layer is full open aperture EPDM foam sponge layer, EPE pearl wool, PU foaming, SBR foaming or the PE modified insulation material layer of full open aperture.
6. a kind of Multi-functional moisture-proof pad according to claim 5, is characterized in that: described half perforate foamed material layer is half perforate EPDM foam sponge layer or half perforate PVC foam material layer.
7. a kind of Multi-functional moisture-proof pad according to claim 5, is characterized in that: described closed cell foamed material layer is EPS foaming, EPE, IXPE, XPE, rubber expanded material, EVA material layer or closed-cell polyethylene modification insulation material layer.
8. moistureproof cushion a kind of Multi-functional moisture-proof pad according to claim 5, is characterized in that: be provided with or be connected with dryer (26) in described passage (23).
9. a kind of Multi-functional moisture-proof pad according to claim 6, is characterized in that: described dryer (26) is connected with external control box (27); Blower fan (261), heater (262) and for accommodating and protect the elastic protecting sleeve (263) of described blower fan (261) and heater (262) is provided with in described dryer (26); Described control box is mounted with controller, time switch and attaching plug in (27).
10. a kind of Multi-functional moisture-proof pad according to any one of claim 1-9, is characterized in that: described puigging (1) top is provided with waterproofing membrane layer (0), and described waterproofing membrane layer is the moistureproof ply of paper of PE rete or aluminum membranous layer or metal.