CN105149357A - 无缝钢管定径机轧辊滑板及其制备方法 - Google Patents
无缝钢管定径机轧辊滑板及其制备方法 Download PDFInfo
- Publication number
- CN105149357A CN105149357A CN201510474461.7A CN201510474461A CN105149357A CN 105149357 A CN105149357 A CN 105149357A CN 201510474461 A CN201510474461 A CN 201510474461A CN 105149357 A CN105149357 A CN 105149357A
- Authority
- CN
- China
- Prior art keywords
- sliding plate
- seamless steel
- slide plate
- graphite
- copper powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种机轧辊滑板，具体涉及一种无缝钢管定径机轧辊滑板及其制备方法。所述滑板由如下重量百分数的原料制成：聚四氟乙烯40-55％；铜粉35-50％；石墨10-15％。本发明所述滑板采用聚四氟乙烯添加铜粉和石墨制成，具有较高的耐温性，优良的自润滑性，较高的压缩强度、硬度等机械物理性能；采用了大量的聚四氟乙烯作填充材质，在不用润滑剂的情况下也大大改善了断裂和脱落的现象，从而延长了滑板的使用寿命；所述制备方法工艺简单、易于实现工业化生产。
Description
技术领域
本发明涉及一种机轧辊滑板，具体涉及一种无缝钢管定径机轧辊滑板及其制备方法。
背景技术
现有技术中，前轧辊滑板采用纯铜板制作，由于铜板韧性较差，在使用时需要添加一定量的黄油进行润滑，即便如此，纯铜板制作的前轧辊滑板在使用中还是很容易出现断裂、脱落等现象，严重影响其正常使用。
发明内容
针对现有技术的不足，本发明的目的是提供一种无缝钢管定径机轧辊滑板，具有较高的耐温性，优良的自润滑性，较高的压缩强度和硬度；本发明同时提供其制备方法，工艺简单、易于实现工业化生产。
本发明所述的无缝钢管定径机轧辊滑板，由如下重量百分数的原料制成：
聚四氟乙烯40-55％；
铜粉35-50％；
石墨10-15％。
所述的原料组成优选为：
聚四氟乙烯45％；
铜粉40％；
石墨15％。
所述的无缝钢管定径机轧辊滑板的制备方法，包括如下步骤：
(1)将聚四氟乙烯、铜粉、石墨球磨至800-1000目，加入高速混料机中混合均匀；
(2)将混匀的原料于20-25℃下加入到压模机中加压成型；
(3)烧结：将步骤(2)得到的成型后原料进行烧结，6-10小时升温至375-385℃，保温10-15小时，再降温至320-330℃，保温2-4小时，自然降温，得所述机轧辊滑板。综上所述，本发明的有益效果如下：
(1)本发明所述滑板采用聚四氟乙烯添加铜粉和石墨制成，具有较高的耐温性，优良的自润滑性，较高的压缩强度、硬度等机械物理性能。
(2)原料中采用了大量的聚四氟乙烯作填充材质，借由聚四氟乙烯材质的柔韧性和填充料的硬度，在不用润滑剂的情况下也大大改善了断裂和脱落的现象，从而延长了滑板的使用寿命。
(3)所述的制备方法，工艺简单、易于实现工业化生产。
具体实施方式
下面结合实施例对本发明做进一步说明。
实施例中用到的所有原料除特殊说明外，均为市购。
实施例1
原料配比：聚四氟乙烯45kg，铜粉40kg，石墨15kg。
制备方法：
(1)将聚四氟乙烯、铜粉、石墨球磨至800目，加入高速混料机中混合均匀；
(2)将混匀的原料于20℃下加入到压模机中加压成型；
(3)烧结：将步骤(2)得到的成型后原料进行烧结，8小时升温至380℃，保温12小时，再降温至327℃，保温3小时，自然降温，得所述机轧辊滑板。
实施例2
原料配比：聚四氟乙烯50kg，铜粉40kg，石墨10kg。
制备方法：
(1)将聚四氟乙烯、铜粉、石墨球磨至900目，加入高速混料机中混合均匀；
(2)将混匀的原料于22℃下加入到压模机中加压成型；
(3)烧结：将步骤(2)得到的成型后原料进行烧结，6小时升温至375℃，保温15小时，再降温至330℃，保温2小时，自然降温，得所述机轧辊滑板。
实施例3
原料配比：聚四氟乙烯45kg，铜粉45kg，石墨10kg。
制备方法：
(1)将聚四氟乙烯、铜粉、石墨球磨至1000目，加入高速混料机中混合均匀；
(2)将混匀的原料于25℃下加入到压模机中加压成型；
(3)烧结：将步骤(2)得到的成型后原料进行烧结，10小时升温至385℃，保温10小时，再降温至320℃，保温4小时，自然降温，得所述机轧辊滑板。
分别对实施例1-3制备得到的滑板进行性能测试，性能测试结果见表1。
表1实施例1-3制备得到的滑板的性能测试结果
Claims (3)
1.一种无缝钢管定径机轧辊滑板，其特征在于：由如下重量百分数的原料制成：
聚四氟乙烯40-55％；
铜粉35-50％；
石墨10-15％。
2.根据权利要求1所述的无缝钢管定径机轧辊滑板，其特征在于：由如下重量百分数的原料制成：
聚四氟乙烯45％；
铜粉40％；
石墨15％。
3.一种权利要求1或2所述的无缝钢管定径机轧辊滑板的制备方法，其特征在于：包括如下步骤：
(1)将聚四氟乙烯、铜粉、石墨球磨至800-1000目，加入高速混料机中混合均匀；
(2)将混匀的原料于20-25℃下加入到压模机中加压成型；
(3)烧结：将步骤(2)得到的成型后原料进行烧结，6-10小时升温至375-385℃，保温10-15小时，再降温至320-330℃，保温2-4小时，自然降温，得所述机轧辊滑板。