CN105143064A - Resin packaging bag for microwave oven, method for heating same, method for filling resin packaging bag for microwave oven, and package - Google Patents
Resin packaging bag for microwave oven, method for heating same, method for filling resin packaging bag for microwave oven, and package Download PDFInfo
- Publication number
- CN105143064A CN105143064A CN201480023089.1A CN201480023089A CN105143064A CN 105143064 A CN105143064 A CN 105143064A CN 201480023089 A CN201480023089 A CN 201480023089A CN 105143064 A CN105143064 A CN 105143064A
- Authority
- CN
- China
- Prior art keywords
- resin
- making
- packaging bag
- resin film
- mentioned
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The objective of the present invention is to provide a new resin packaging bag with which heat sterilization is possible after vacuum packaging, the contents of which can be cooked in a microwave oven without being transferred to a vessel, and with which the package itself can be used as a vessel. This resin packaging bag for microwave ovens is a packaging bag in which the peripheral part serves as a seal, and is characterized in that: the front side of the packaging bag comprises one resin film (2) and the reverse side comprises one resin sheet (1); and the resin film (2) and resin sheet (1) comprise materials that, when a package formed by sealing moisture-containing content between the resin film (2) and the resin sheet (1) is heated in a microwave with the reverse side resin sheet (1) serving as the bottom surface, are deformed by the heat and pressure of the steam generated from the content such that the reverse side resin sheet (1) forms a recessed shape, and said recessed shape is completely or partially maintained, even after heating has been completed.
Description
Technical field
The present invention relates to the packaging bag for packaged food etc.
Background technology
As heating, the mess kit of food, except the mess kit such as circular bottom pot, pan of type in the past, micro-wave oven is not only also becoming widely used fixed configurations in family as mess kit as heating apparatus.
Therefore, along with pasteurization, Refrigeration Technique universal, easily with the packaged pre-cooked or half pre-cooked retort pouch food of the heating such as micro-wave oven, frozen food, refrigeration (zero is fresh-keeping) food becoming general (with reference to patent documentation 1) so that this state is edible.
In addition, in recent years, there is the trend of increase in the family at less than two mouthfuls, a family, and the demand of the food of 1 ~ 2 people improves constantly.Particularly, the elderly increases, and Baby Boomer is retired gradually, and the family of dining constantly increases at home.And, in convenience store, reflect the change of such social condition, promptly enriched the product category of refrigeration (zero the is fresh-keeping) non-staple foodstuff of divided meal etc., particularly enriched packed product category.Except these refrigeration (zero is fresh-keeping) non-staple foodstuff, dumpling, pasta etc. water dip class and the product category implementing the frozen food freezing to process with this state also increases decocting.All food is all at StoreFront or at home implement furnace run with micro-wave oven and eat.
Incidentally, in general, retort pouch food, frozen food to save as prerequisite for a long time, not within the short time cook, sell for the purpose of.
The moisture processed food sold as these markets, in the circulation style of StoreFront, adopts three kinds of following methods.
(1) circulation under normal temperature state (after aseptic filling process or distillation (レ ト Le ト) sterilization processing, circulation sale at normal temperatures)
(2) circulation under frozen state (after aseptic filling process or pasteurization process, circulation sale at 3 ~ 10 DEG C)
(3) circulation (after freezing, circulation sale in a cold or frozen state) under freezing state
In the circulation style of above-mentioned (1) ~ (3), food is all packed by bag, plastic container, tank etc.Particularly as the packaged food of the situation of above-mentioned (1), (2), in order to extend the shelf life, usually after vacuum packaging, carry out pasteurization process, and carry out providing and delivering, displaying under normal temperature or zero fresh-keeping state.
The sterile package product obtained in sterilization container that are filled with a sealing in the environment of germ-free condition by the liquid that beverage etc. has carried out sterilization processing by board-like sterilizing unit in advance in large quantities circulate at normal temperature, but the moisture processed food containing solid matter is difficult to be processed by which.
In general non-staple foodstuff or the flesh of fish, poultry meat processed goods have employed following method: to be sealed in bag, plastic container and by retort sterilisation process, the bacterial destruction in food to be carried out sterilization, or implement pasteurization process and the bacterium in food remained on below certain bacterium number, take care of at low temperatures and circulation sale in order to the propagation after suppressing, or freezing immediately after cooking and circulation sale in a cold or frozen state.
When carrying out retort sterilisation, pasteurization process, if there is head room (space) in bag or container, then sterilizing time can be caused significantly to extend because of the effect of heat insulation of air, make the mouthfeel of content food (chewing strength, tongue sense, smooth feeling etc.), taste, color and luster, fragrance occurs rotten.In addition, if utilize steam, hot water to carry out pasteurization at ambient pressure, then bag, container can break because of the het expansion of air.
Put into the freezing pasta etc. of the container of being lived by chimeric cap seal, owing to not sealing completely, so be not suitable for long-term freezen protective.Frozen food is after freezing, and the face area of food increases, and therefore, although be in low temperature environment, oil is still easily oxidized by the oxygen in container.In order to enclose deoxidizer to keep nitrogen environment, need the flange portion by laminated thin membrane cover sealing packaging containers main body and completely isolated with extraneous gas.
In order to the pasta etc. with the ripe loading container of micro-wave oven system, need a part for strip off lid film in advance and the steam produced when heating that leaves.Make the ambient temperature in container remain on the rising of about 100 DEG C interior pressures when needing microwave-oven-heating, expect the cooking length of time that thaws shortening frozen food especially.
But make except heating effect is limited except originally just there is head room, as strip off lid film in advance a part of, cannot make to remain in container more than normal pressure, therefore, cooking length of time is understood elongated naturally.
In addition, if use, the packing container with head room that container molding and lid material combine is used as packing, then when vacuum packaging, the profile of container molding can be out of shape.
And, when using packing container, when carrying out retort sterilisation process, in order to suppress distortion of vessel, need the rising along with the product temperature of the food in container and the pressure come in regulable control distillation plant that declines, and also can be subject to the harmful effect of the effect of heat insulation of above-mentioned air.
As mentioned above, packing container carries out the situation of sterilization processing after not being adapted at vacuum packaging.
Therefore, as packing timber, have employed the packaging bag of the plastic sheeting containing resistance to effect of heat basically, non-staple foodstuff or the flesh of fish, poultry meat processed goods are contained in packaging bag usually, vacuum seal is also the state that entirely eliminated inner air, thus carries out retort sterilisation process or steam, hot-water sterilization function process.
And, in general when employing the packaged food of packaging bag, in order to carry out cooking in microwave oven, temporarily from bag, food being moved in vessel by customer and heating.
Incidentally, because bag expands because of the steam produced during heating, so usually a part can be broken a seal in advance before microwave-oven-heating, or steam is left while complete cooking as micro-wave oven reply function by the exhausr port be arranged on bag.
But, must be noted that to avoid scalding when micro-wave oven takes out, need to transfer to other containers in order to edible in this condition, also there is identical use inconvenience even if take home.
Food is moved in vessel very bothersome, and the vessel after needing cleaning to use, in addition, there is quantity of refuse when vessel are disposable tablewares increase such problem.
Prior art document
Patent documentation
Patent documentation 1: Japanese Unexamined Patent Publication 2008-290738 publication
Summary of the invention
The problem that invention will solve
The object of the present invention is to provide a kind of new resin-made packaging bag, it can carry out pasteurization after vacuum packaging, content need not be moved to vessel and just can carry out cooking in microwave oven in this condition, and packing itself can utilize as vessel.
For solving the means of problem
Present inventors etc. have found following packaging bag and have completed the present invention: a kind ofly circumference is sealed the packaging bag used, wherein, the face making packaging bag is resin film-making, another face is made to be resin-made membrane, thus collecting contains the content of moisture wherein, if make resin film-making side be bottom surface micro-wave oven microwave heating, then under the heat of the water vapour produced from content and the effect of pressure, the internal capacity of packaging bag increases, therewith concomitantly resin-made membrane expand and by the circumference pull-up of resin film-making, resin film-making is deformed into vessel-shaped, this state of being out of shape still is kept after heating terminates.
For solving the present invention of above-mentioned problem as following record.
(1) a kind of micro-wave oven resin-made packaging bag, it is that circumference is sealed the packaging bag used, it is characterized in that, the face side of packaging bag is made up of 1 resin-made membrane, rear side is made up of 1 resin film-making, above-mentioned resin-made membrane and resin film-making are made up of material as follows: during the packaging body formed making the resin film-making of above-mentioned rear side be bottom surface microwave-oven-heating between above-mentioned resin-made membrane and above-mentioned resin film-making to seal the content containing moisture, be out of shape under the heat of the water vapour produced from foregoing thing and the effect of pressure and make the resin film-making of above-mentioned rear side become concave shape, still all or locally this concave shape is maintained after heating terminates.
(2) the resin-made packaging bag of the micro-wave oven Gen Ju (1), is characterized in that, above-mentioned resin film-making is at the bonding resin-made laminates of resin-made membrane of its back side surface.
(3) a kind of micro-wave oven resin-made packaging bag, it is that circumference is sealed the packaging bag used, it is characterized in that, the face side of packaging bag is made up of 2 resin-made membranes, rear side is made up of 1 resin film-making, the resin-made membrane of the resin film-making side in above-mentioned 2 resin-made membranes bonds on the face of the face side of above-mentioned resin film-making, above-mentioned resin-made membrane and resin film-making are made up of material as follows: when the packaging body that the content of sealing containing moisture that make the resin film-making of above-mentioned rear side be bottom surface microwave-oven-heating between above-mentioned 2 resin-made membranes is formed, be out of shape under the heat of the water vapour produced from foregoing thing and the effect of pressure and make the resin film-making of above-mentioned rear side become concave shape, still all or locally this concave shape is maintained after heating terminates.
(4) the resin-made packaging bag of the micro-wave oven Gen Ju (3), it is characterized in that, the resin-made membrane of above-mentioned resin film-making and above-mentioned resin film-making side is by weak bonding, above-mentioned adhesive linkage is the adhesive linkage of weak gleyness, by the heating undertaken by micro-wave oven, the resin-made membrane of having accommodated content can be made to be separated with resin film-making.
(5) a kind of micro-wave oven resin-made packaging bag, it is that circumference is sealed the packaging bag used, it is characterized in that, form at the resin-made membrane of overlapped surfaces side, both sides of resin film-making and the resin-made membrane of rear side, above-mentioned resin-made membrane and resin film-making are made up of material as follows: during the packaging body formed making the resin-made membrane of above-mentioned rear side be bottom surface microwave-oven-heating between the resin-made membrane and above-mentioned resin film-making of above-mentioned face side to seal the content containing moisture, be out of shape under the heat of the water vapour produced from foregoing thing and the effect of pressure and make the resin film-making of above-mentioned rear side become concave shape, still all or locally this concave shape is maintained after heating terminates.
(6) the resin-made packaging bag of the micro-wave oven Gen Ju (5), is characterized in that, 1 resin-made membrane is carried on the back to be pasted sealing and defines the resin-made membrane of above-mentioned face side and the resin-made membrane of rear side.
(7) according to the micro-wave oven resin-made packaging bag according to any one of (1) ~ (4), it is characterized in that, formed in the following way: configure the content containing moisture in the resin film-making of strip or on the face of the inner side as packaging bag between the resin film-making of the strip of bonding resin-made membrane and the resin-made membrane of strip, then, at each unit area being configured with content, four limits are sealed, then by cutter, individuality is cut off one by one.
(8) according to the micro-wave oven resin-made packaging bag according to any one of (1) ~ (7), it is characterized in that, otch has been cut in above-mentioned resin film-making.
(9) according to the micro-wave oven resin-made packaging bag according to any one of (1) ~ (7), it is characterized in that, near the central portion of resin film-making, be pre-formed shallow recess.
(10) according to the micro-wave oven resin-made packaging bag according to any one of (1) ~ (7), it is characterized in that, in advance in concentrically alternately defining multiple annular recessed portion and annular convex respectively in resin film-making.
(11) according to the micro-wave oven resin-made packaging bag according to any one of (1) ~ (10), it is characterized in that, above-mentioned resin-made membrane is provided with triangle pad.
(12) according to micro-wave oven resin-made packaging bag according to any one of (1) ~ (11), it is characterized in that, be provided with the parts making steam hole automatically opening in microwave-oven-heating on resin-made membrane surface.
(13) according to the micro-wave oven resin-made packaging bag according to any one of (1) ~ (11), it is characterized in that, a part for the sealing of resin-made membrane and resin film-making is weak sealing, the part of above-mentioned weak sealing in microwave-oven-heating is peeled off, and as steam hole opening.
(14) a kind of according to the microwave-oven-heating method of the micro-wave oven according to any one of (1) ~ (13) with resin-made packaging bag, it is characterized in that, all or part of of the circumference of above-mentioned micro-wave oven resin-made packaging bag is clamped by framework, and when being out of shape with the heating plastic in micro-wave oven, the flange portion of resin film-making is that approximate horizontal mode carries out microwave-oven-heating.
(15) a kind of according to the microwave-oven-heating method of the micro-wave oven according to any one of (1) ~ (13) with resin-made packaging bag, it is characterized in that, all or part of framework having wall by the resin film-making side in the packaging bag of micro-wave oven resin-made of the circumference of above-mentioned micro-wave oven resin-made packaging bag carries out microwave-oven-heating clampingly, and above-mentioned wall controls plastic deformation during microwave-oven-heating.
(16) a kind of bag feeding type Research on Automatic Filling, it is characterized in that, after being filled with the content containing moisture by the peristome of the micro-wave oven resin-made packaging bag according to any one of (1) ~ (13) of three limit sealings in resin-made packaging bag, above-mentioned peristome sealing is carried out sealing resin packaging bag.
(17) a kind of bag feeding type Research on Automatic Filling, it is characterized in that, after the peristome of the micro-wave oven resin-made packaging bag Gen Ju (6) is filled with the content containing moisture, above-mentioned peristome sealing is carried out sealing resin packaging bag, above-mentioned micro-wave oven resin-made packaging bag according to claim (6) is by the resin-made membrane covering resin film-making of in a tubular form, the both ends of this resin-made membrane back of the body is pasted sealing, and circumference is sealed the packaging bag used, further, be carry out in the side of packaging bag holding sealing and being formed.
(18) a kind of roller supply type Research on Automatic Filling, it is the method for filling the content containing moisture in the micro-wave oven resin-made packaging bag Gen Ju (7), it is characterized in that, resin film-making is derived or the bonding resin film-making of resin-made membrane on the face of the inner side as packaging bag from roller, after the content put containing moisture is uploaded in above-mentioned resin film-making, the resin-made membrane of deriving from roller is overlapped into and covers foregoing thing, and side surface part is sealed, then, after peristome at two positions carries out end sealing and has carried out sealed package, by cutter, individuality is cut off one by one.
(19) packaging body, fills the content containing moisture and seals and formed in the micro-wave oven resin-made packaging bag according to any one of (1) ~ (13).
The effect of invention
Packaging bag of the present invention plays following effect: by with microwave-oven-heating, can carry out the cooking of content, and resin film-making can be deformed into vessel-shaped and use as tableware.
Accompanying drawing explanation
Fig. 1 is the figure representing the packaging bag filling content at the first embodiment of the present invention the state before the heating of hermetically sealed packaging body.
Fig. 2 represents with the packaging body shown in microwave-oven-heating Fig. 1 and makes resin film-making be deformed into the figure of the state of concavity.
Fig. 3 is the figure representing the packaging bag filling content at the second embodiment of the present invention the state before the heating of hermetically sealed packaging body.
Fig. 4 represents with the packaging body shown in microwave-oven-heating Fig. 3 and makes resin film-making be deformed into the figure of the state of concavity.
Fig. 5 is the figure representing the packaging bag filling content at the 3rd embodiment of the present invention the state before the heating of hermetically sealed packaging body.
Fig. 6 be represent to make with the packaging body shown in microwave-oven-heating Fig. 5 resin film-making be deformed into concavity after the figure of state that resin film-making has been separated with resin-made membrane.
Fig. 7 is the figure representing the packaging bag filling content at the 4th embodiment of the present invention the state before the heating of hermetically sealed packaging body.
Fig. 8 represents with the packaging body shown in microwave-oven-heating Fig. 7 and makes resin film-making be deformed into the figure of the state of concavity.
Fig. 9 is the figure of the structure of the resin film-making of the packaging bag representing the 5th embodiment of the present invention.
Figure 10 is the figure of an example of the framework representing the circumference for clamping packaging bag used in the 7th embodiment of the present invention.
Figure 11 is the figure of an example of the framework representing the circumference for clamping packaging bag used in the 8th embodiment of the present invention.
Figure 12 is the figure of other examples of the framework representing the circumference for clamping packaging bag used in the 7th embodiment of the present invention.
Figure 13 be represent for the manufacture of of the present invention first, second and third, the figure of the automatic filling device of the packaging bag of six embodiments.
Figure 14 is the figure in the cross section representing the a-a ' shown in Figure 13, b-b ', c-c '.
Figure 15 is the figure of the example representing the otch being arranged at resin film-making.
Detailed description of the invention
The heat of the steam that packaging bag of the present invention is produced when microwave-oven-heating by the thin resin film-making of the bottom side of bag becomes matrix with deform under pressure and plays the function of simple container, can as disposable container to economize on resources, the cheap and technology that convenience is high makes contributions for society.
In addition, the present invention is the breakthrough invention that can both be suitable for when taking any one circulation style in the circulation under the circulation under normal temperature state, the circulation under frozen state and freezing state.
The following describes the embodiment of packaging bag of the present invention.
Below, by micro-wave oven resin-made of the present invention packaging bag referred to as " packaging bag ".
(the first embodiment)
Fig. 1,2 represents present embodiment.
The packaging bag of present embodiment is that circumference is sealed the packaging bag used, and the face side of packaging bag is made up of 1 resin-made membrane, and rear side is made up of 1 resin film-making.Above-mentioned resin-made membrane and resin film-making are made up of material as follows: during the packaging body formed making the resin film-making of above-mentioned rear side be bottom surface microwave-oven-heating between resin-made membrane and resin film-making to seal the content containing moisture, be out of shape under the heat of the water vapour produced from foregoing thing and the effect of pressure and make the resin film-making of above-mentioned rear side become concave shape, after heating terminates, still all or locally maintaining this concave shape.
The resin-made laminates of above-mentioned resin film-making also can be that side surface is bonding at least overleaf resin-made membrane.As described later, sometimes in order to make resin film-making easily be out of shape, otch is set in resin film-making.Resin film-making is made up of barrier resin, and when whole packaging bag keeps barrier, otch may damage resin film-making and hinder its barrier.At the bonding barrier resin film of the rear side of resin film-making, thus can the barrier of maintenance package pack more reliably.
Fig. 1 shows an example of the packaging bag of present embodiment.
Fig. 1 (A) represents to fill content the figure of the packaging body of hermetically sealed state in the packaging bag of present embodiment, Fig. 1 (B) is a-a ' the line cutaway view of Fig. 1 (A), and Fig. 1 (C) is the enlarged drawing in the cross section of the side seals 11 of Fig. 1 (B).
Packaging body shown in Fig. 1 (A) can obtain in the following way: as Suo Shi Fig. 1 (B) and Fig. 1 (C) in resin film-making 1 overlapping resin-made membrane 2 and formed side seals 11,12 and end sealing 13 (underseal), thus define three limit sealing bags, then from after peristome is filled with the content 10 containing moisture, end sealing (closedtop) portion 14 is formed at peristome.
In addition, packaging body shown in Fig. 1 (A) also can obtain in the following way: the content 10 of mounting containing moisture in resin film-making 1 overlapping resin-made membrane 2 and after defining side seals 11,12, will hold sealing 13,14 vacuum seal thereon.
As shown in Fig. 1 (C), the base material 21 of resin-made membrane has to carry out sealing the thermal adhesive layer 22 be made up of thermal adhesive resin at a mask.
If with the packaging body shown in microwave-oven-heating Fig. 1, then from the content 10 containing moisture, produce water vapour and pressure in packaging body is increased, as illustrated in fig. 2, the internal volume of packaging bag increases.Along with the increase of internal volume, the stress of the circumference of resin film-making 1 pull-up is upward had an effect by the circumference of resin-made membrane 2, and resin film-making 1 plastic deformation becomes concavity and forms vessel.The heating undertaken by micro-wave oven if terminate, then the resin film-making 1 of this packaging body is owing to no longer meeting the Plastic Deformation Conditions of the temperature and pressure of heating steam, so form trait is in concavity (vessel-shaped).
Fig. 2 represents with the packaging body shown in microwave-oven-heating Fig. 1 and makes resin film-making be deformed into the figure of the state of concavity.
Afterwards, by removing resin-made membrane all or part of, the resin film-making of concavity can use using this state as vessel.
As the material of resin film-making 1, the material of application of stress when can pass through heating and plastic deformation can be adopted, but as preferred material, can exemplify out and add Packed polypropylene foil.In the case, the thickness of resin film-making is namely enough at about 200 ~ 300 μm.
In addition, the resin film-making 2 that the present invention uses comprises resin-made foam piece.
On the other hand, as the material of resin-made membrane, preferably namely use microwave-oven-heating that the film of the resistance to effect of heat of thermal contraction does not occur yet, such as pet film can have been exemplified.In addition, in order to make resin-made membrane, there is Thermoadhesive and thermal adhesive resin layer is set on the heat bonding face of resin-made membrane, and as this thermal adhesive resin, preferred LLDPE (LinearLowDensityPolyethylene: linear low density polyethylene), CPP (CastPolypropylene: cast polypropylene).
(the second embodiment)
Fig. 3,4 represents present embodiment.Fig. 3 represents the example being filled with the packaging body of content in the packaging bag of present embodiment.
The packaging bag of present embodiment is that circumference is sealed the packaging bag used, and the face side of packaging bag is made up of 2 resin-made membranes 2,3 as Suo Shi Fig. 3 (C), and rear side is made up of 1 resin film-making 1.The resin-made membrane 3 of the inner side in above-mentioned 2 resin-made membranes bonds in resin film-making 1, above-mentioned resin-made membrane 2,3 and resin film-making 1 are made up of material as follows: during the packaging body formed at content containing moisture of the sealing that makes the resin film-making 1 of above-mentioned rear side be bottom surface microwave-oven-heating between above-mentioned 2 resin-made membranes, be out of shape under the heat of the water vapour produced from foregoing thing and the effect of pressure and make the resin film-making 1 of above-mentioned rear side become concave shape, after heating terminates, still all or locally maintaining this concave shape.
Fig. 3 (A) represents to fill content the figure of the packaging body of hermetically sealed state in the packaging bag of present embodiment, Fig. 3 (B) is b-b ' the line cutaway view of Fig. 3 (A), and Fig. 3 (C) is the enlarged drawing in the cross section of the side seals 11 of Fig. 3 (B).
Packaging body shown in Fig. 3 (A) is made up of resin-made membrane 2, resin-made membrane 3 and resin film-making 1, such as obtain by such as under type: form three limit sealing bags by resin-made membrane 2 and resin-made membrane 3, resin-made membrane 3 is bonding with resin film-making 1, then, after be filled with the content 10 containing moisture from peristome, form end sealing 14 at peristome.
As shown in Fig. 3 (C), the base material 21,31 of resin-made membrane has to carry out sealing the thermal adhesive layer 22,32 be made up of thermal adhesive resin at a mask.
In this case, be that the face not forming thermal adhesive layer of the face of resin film-making 1 and resin-made membrane 3 is superimposed.And, when have employed as resin film-making 1 add Packed polypropylene foil, have employed pet film as resin-made membrane 3, because both are not undertaken bonding by heat-sealing, so need to arrange adhesive linkage between resin film-making 1 and resin-made membrane 3.
Fig. 4 represents with the packaging body shown in microwave-oven-heating Fig. 3 and makes resin film-making 1 be deformed into the figure of the state of concavity.
(the 3rd embodiment)
Fig. 5,6 represents present embodiment.Fig. 5 represents the example being filled with the packaging body of content in the packaging bag of present embodiment.
Present embodiment is the application of the second embodiment.
In the present embodiment, the adhesive linkage between the resin film-making 1 of the second embodiment and resin-made membrane 3 is made to be the adhesive linkage of weak gleyness.Like this, after finishing the heating undertaken by micro-wave oven, resin film-making 1 can be separated with the resin-made membrane 2,3 of having accommodated content 10.And, the content 10 being contained in resin-made membrane 2,3 can be taken out and moves in the vessel of resin film-making 1 and eat.
The packaging bag of present embodiment in resin-made membrane 2,3, has accommodated the form of content in the same manner as the packaging bag of the second embodiment, therefore, even if having aperture in resin film-making 1, also can keep the sealing state of packaging bag.
Fig. 5 (A) represents to fill content the figure of the packaging body of hermetically sealed state in the packaging bag of present embodiment, Fig. 5 (B) is c-c ' the line cutaway view of Fig. 5 (A), and Fig. 5 (C) is the enlarged drawing in the cross section of the side seals 11 of Fig. 5 (B).
Packaging body shown in Fig. 5 (A) is made up of resin-made membrane 2, resin-made membrane 3 and resin film-making 1.This packaging body such as obtains by such as under type: form three limit sealing bags by resin-made membrane 2 and resin-made membrane 3, and resin-made membrane 3 is bonding with resin film-making 1, then, after be filled with the content 10 containing moisture from peristome, form end sealing 14 at peristome.
As shown in Fig. 5 (C), a face of the base material 21,31 of resin-made membrane has to carry out sealing the thermal adhesive layer 22,32 be made up of thermal adhesive resin.
And, adhesive linkage between resin film-making 1 and resin film 3 is weak gleyness, by the heating undertaken by micro-wave oven, can hanker being separated with the bonding portion S of resin-made membrane 3 in resin film-making 1 adding, or by finger force, resin film-making 1 can be separated with resin-made membrane 3 after heating terminates.
Fig. 6 represents with the packaging body shown in microwave-oven-heating Fig. 5 and makes resin film-making 1 be deformed into the figure of the state of concavity.
(the 4th embodiment)
Fig. 7,8 represents present embodiment.
The packaging bag of present embodiment is that circumference is sealed the packaging bag used, and the face side of packaging bag and rear side are made up of resin-made membrane 2 respectively, and cover resin film-making 1 by the resin-made membrane 2 of face side and the resin-made membrane 2 of rear side.Above-mentioned resin-made membrane 2 and resin film-making 1 are made up of material as follows: during the packaging body formed at the content 10 making the resin-made membrane 2 of above-mentioned rear side be bottom surface microwave-oven-heating between the resin-made membrane 2 and resin film-making 1 of above-mentioned face side to seal containing moisture, be out of shape under the heat of water vapour produced from foregoing thing 10 and the effect of pressure and make the resin film-making 1 of above-mentioned rear side become concave shape, after heating terminates, still all or locally maintaining this concave shape.
In addition, in the present embodiment, resin film-making 1 can be clamped between 2 resin-made membranes 2 and form three limit sealings, 1 resin-made membrane 2 also can be made for tubulose and configure resin film-making 1 wherein and resin-made membrane 2 carried out back of the body subsides sealing at both ends.
Fig. 7 shows an example of the packaging bag of present embodiment.
Fig. 7 (A) represents to fill content the figure of the packaging body of hermetically sealed state in the packaging bag of present embodiment, Fig. 7 (B) is d-d ' the line cutaway view of Fig. 7 (A), and Fig. 7 (C) is the enlarged drawing in the cross section of the side seals 11 of Fig. 7 (B).
Packaging body shown in Fig. 7 (A), covers resin film-making 1 by 1 resin-made membrane 2, and the both ends of resin film 2 are carried on the back pastes sealing and defines back of the body subsides sealing 15.In addition, the resin-made membrane 2 of face side is sealed at circumference with resin film-making 1.
The packaging bag of present embodiment has the simply such advantage of the manufacture of packaging bag.
Fig. 8 represents with the packaging body shown in microwave-oven-heating Fig. 7 and makes resin film-making 1 be deformed into the figure of the state of concavity.
(the 5th embodiment)
Fig. 9 represents present embodiment.
In the packaging bag of present embodiment, in advance in concentrically alternately defining multiple annular convex 33 and annular recessed portion 34 respectively in resin film-making 1.
As the shape of ring-type, the various shapes such as rectangular ring, circular annular form, elliptical annular can be selected.
Example shown in Fig. 9 has protuberance, the recess of rectangular ring.
Fig. 9 (A) is the figure observing packaging bag from resin film-making 1 side.Fig. 9 (B) is the X-X line cross section of Fig. 9 (A).As shown in Fig. 9 (B), the cross section of resin film-making 1 becomes bending rugose shape.
Made by microwave-oven-heating the resin film-making of rear side be deformed into concave shape and be shaped packaging bag of the present invention in, in the resin film-making of the general plane shape occurred when the matrix reservation shape after having pressed this shaping, in concentrically alternately forming multiple annular convex and annular recessed portion respectively.
The packaging bag formed in the following way becomes the packaging bag of present embodiment: in resin film-making, make this in advance with heart shaped concaveconvex shape by employing the sheet-like formed of mould, circumference is sealed against one another at its face side overlapping resin-made membrane.
If make the resin film-making 1 of above-mentioned rear side for bottom surface microwave-oven-heating at the content of this packaging bag sealing containing moisture the packaging body that formed, then under the heat of the water vapour produced from foregoing thing and the effect of pressure, resin film-making 1 is softened, due to the rising of interior pressure, annular convex 33 and annular recessed portion 34 as extending surplus formation is made to extend and form the shape of container.
According to the present embodiment, and smooth resin film-making 1 is used in compared with the situation of the bottom surface side of packaging bag, the matrix container shapes formed by microwave-oven-heating can be made to be formed closer to reservation shape.
Figure 9 illustrates the example concentric annular convex 33 and annular recessed portion 34 not being arranged on the periphery of resin film-making 1.But the formation annular convex 33 in resin film-making 1 and the region of annular recessed portion 34 can set as one sees fit.Annular convex 33 and annular recessed portion 34 also can be arranged on whole of resin film-making 1.
(the 6th embodiment)
In above-mentioned, illustrate and make three limit sealing bags in advance and be used as packaging bag and the situation of filling content is wherein illustrated.
But, also can be as illustrated in fig. 13, the resin film-making 1 of strip or the bonding resin film-making 1 of resin-made membrane and the resin-made membrane 2 of strip are derived from stock roll respectively, deploy content thing 10 between resin film-making 1 and resin-made membrane 2, then, at each unit area being configured with content 10, four limits are sealed, then by individuality being cut off one by one with cutter 36 and forming each packaging bag.Under these circumstances, although form packaging body while formation packaging bag, such embodiment is also contained in the embodiment of packaging bag of the present invention.
Usually, this term of packaging bag refers to the component with opening of filling before content.But, when utilizing method as above to form packaging body while forming packaging bag, there is not this mode of packaging bag with opening.But the packaging body obtained with above-mentioned method, to be filled in packaging bag and by hermetically sealed state this point at content, with fill content in the packaging bag with opening and the packaging body carrying out sealing and obtain without any difference.
Therefore, the portions of packaging material while formation packaging bag as above when formation packaging body is in the present invention also referred to as " packaging bag ".
Present embodiment can be applied to the packaging bag of above-mentioned first, second, and third embodiment.
In addition, also after be derived resin film-making from raw material, resin film-making can be formed the annular convex 33 as shown in above-mentioned 5th embodiment and annular recessed portion 34, and is transported to Contents Fill operation.
As mentioned above, if export to the filling of content from raw material, singualtion all undertaken by an equipment, then do not need to store packaging bag, therefore, joint space-efficient is effective.
(other embodiments of packaging bag)
As other embodiments about packaging bag, embodiment below can be exemplified out.
(1) also otch can be cut out in resin film-making.By having otch like this, the distortion of resin film-making becomes easy.In addition, this otch needs to be formed in the mode maintaining sealing state certainly.
As otch, in order to enable amount, the shape of resin film-making and content be out of shape accordingly, the shape of such as otch 39 as shown in figure 15 can be considered.
(2) resin film-making can be plane basically, but also must be not necessarily plane.
Such as, heating can also to be utilized in resin film-making and the methods such as pressing mold form recess in advance simplely.
Like this, when microwave-oven-heating, resin film-making easily can be deformed into concave shape.In addition, if form dark recess, then packaging bag volume makes circulation cost raise greatly, in addition, because head room is large, so packaging bag can be out of shape when vacuum seal, therefore not preferred.
(3) the triangle pad (Crotch) as triangle contact pin so also can be set on resin-made membrane.If make the amount of content increase by arranging triangle pad, then the internal volume of bag also can increase, therefore, even if change the kind of content and measure the kind also not needing to change resin bag.
(4) in microwave-oven-heating, steam hole automatically opening in a part for resin-made membrane.
According to time of heat, the wattage of micro-wave oven, hanker packaging bag and likely break adding.In order to guard against this situation, also can be arranged in microwave-oven-heating on resin-made membrane surface the parts making steam hole automatically opening in a part for resin-made membrane.As the structure for this object, can exemplify out such as the structure of patent No. 4817583 publications records.
(5) be sealed at resin-made membrane in the packaging bag of circumference of resin film-making, weak seal section is set in a part for sealing.Thus, in microwave-oven-heating, above-mentioned weak seal section is peeled off and as steam hole opening, therefore, even if superheated, packaging body also can not break.
Below, the embodiment of the microwave-oven-heating method of packaging bag of the present invention is described.
(the 7th embodiment)
According to Figure 10, present embodiment is described.
Figure 10 (A) be the figure representing the framework 40 that heating uses when being filled with the packaging body of content in packaging bag of the present invention, Figure 10 (B) ~ Figure 10 (D) show the circumference of clamping packaging bag in this framework and state with microwave-oven-heating during packaging body over time.
First, the framework 40 having been linked two frame components 41,42 by articulation piece 43 as shown in Figure 10 (A) is prepared.Then, as shown in Figure 10 (B), clamp the flange part (circumference) 46 of packaging bag with frame component 41,42, flange part 46 is fixed by stationary member 44,45, to prevent from coming off from framework 40.
If use microwave-oven-heating packaging body in this condition, then as shown in Figure 10 (C), packaging bag is expanded, and resin film-making plastic deformation becomes vessel-shaped.Then, if terminate microwave-oven-heating, then as shown in Figure 10 (D), the shape invariance of resin film-making retainer ware.
By using framework 40 like this, the flange part 46 of resin film-making is constrained to maintenance flat state by framework, and therefore, flange part can not fold, obtains the vessel of good looking appearance.
(the 8th embodiment)
According to Figure 11, present embodiment is described.
Figure 11 (A) be the figure representing the framework 50 with wall that heating uses when being filled with the packaging body of content in packaging bag of the present invention, Figure 11 (B) ~ Figure 11 (D) show the circumference of clamping packaging bag in this framework and state with microwave-oven-heating during packaging body over time.
First, prepare having been linked by articulation piece 53 as shown in Figure 11 (A) to there is the frame component 51 of wall and the framework 50 of frame component 52.Then, as shown in Figure 11 (B), clamped the flange part (circumference) 46 of packaging bag by frame component 51,52, flange part 46 is fixed by stationary member 54,55, to prevent from coming off from framework.
If use microwave-oven-heating packaging body in this condition, then as shown in Figure 11 (C), packaging bag is expanded, and resin film-making plastic deformation becomes vessel-shaped.Then, if terminate microwave-oven-heating, then as shown in Figure 11 (D), the shape invariance of resin film-making retainer ware.
In addition, wall 51 does not need whole face to be all made up of wall material, as shown in figure 12, can arrange space part 56 at wall yet.
By using framework 50 like this, can control the plastic deformation of the resin film-making part forming vessel, resin film-making becomes by the state of die forming in micro-wave oven, therefore, resin film-making can be made to be shaped as the vessel of the shape of expection, to possess more as the outward appearance of vessel.
The following describes the embodiment of the fill method of filling to packaging bag of the present invention.
(the 9th embodiment)
When the packaging bag of above-mentioned embodiment is the resin-made packaging bag circumference of three sealing formed, the content containing moisture is filled from the unencapsulated peristome of the packaging bag being transported to automatic filling device, then by sealing arrangement, this peristome is sealed, carry out automatic filling (bag feeding type Research on Automatic Filling) thus.
(the tenth embodiment)
When packaging bag is the resin-made packaging bag of above-mentioned 4th embodiment, by resin-made membrane covering resin film-making in a tubular form, the resin-made membrane back of the body is pasted sealing and carries out end sealing in the side of packaging bag, after peristome is filled with the content containing moisture, by sealing arrangement, this peristome is sealed, carry out automatic filling (bag feeding type Research on Automatic Filling) thus.
(the 11 embodiment)
When packaging bag is the resin-made packaging bag of above-mentioned first embodiment, resin film-making is derived from roller, after the content put containing moisture is uploaded in this resin film-making, the resin-made membrane of deriving from roller is overlapped into and covers this content, side surface part is sealed, then, after the peristome at two positions carries out end sealing to have carried out sealed package, by cutter, individuality is cut off one by one, carry out automatic filling (roller supply type Research on Automatic Filling) thus.
Figure 13 is the figure of the roller supply type Research on Automatic Filling that present embodiment is described.
The resin film-making 1 of deriving from stock roll is transported by towards vacuum seal 35.
In conveyance way, in resin film-making 1, mounting contains the content of moisture.Figure 14 (A) is a-a ' the line cutaway view of Figure 13.
Then, the resin-made membrane 2 of deriving from stock roll is overlaid on the content 10 containing moisture.Figure 14 (B) is b-b ' the line cutaway view of Figure 13.
Overlap has the resin film-making 1 of resin-made membrane 2 and enters vacuum seal containing the content 10 of moisture, is sealed to form as packaging body in vacuum seal by vacuum degassing.Figure 14 (C) is c-c ' the line cutaway view of Figure 13.As shown in Figure 14 (C), resin film-making 1, resin-made membrane 2 and the content 10 containing moisture become the state be close to.
Then, individuality is cut off by cutter 36 and becomes packaging body 37 by the continuum of the packaging bag be vacuum sealed one by one.
In fig. 13, the dash area of the surrounding of packaging body 37 represents sealing 38.
(the 12 embodiment)
As embodiments of the present invention, be included in the micro-wave oven resin-made packaging bag of above-mentioned each embodiment the content hermetically sealed packaging body of accommodating containing moisture.
Embodiment
According to embodiment, the present invention is described.In addition, so-called those skilled in the art easily carry out taking the circumstances into consideration change to embodiments of the invention shown below, correction forms other embodiments, these change, correction is contained in the present invention, and the following description is the example in the preferred embodiment of the present invention, does not limit the present invention.
In addition, in following record, pet sheet shows polyethylene terephthalate, and LLDPE represents linear low density polyethylene, and PP represents polypropylene.
In addition, the resin-made membrane used in an embodiment and resin film-making use material shown below respectively.
(resin-made membrane)
PET (12 μm thick): Dongli Ltd. P60
LLDPE (50 μm thick): Futamura Kagaku Kabushiki Kais XHT
(resin film-making)
Be added with the PP sheet (250 μm thick) of filler (french talc, calcium carbonate)
[embodiment 1]
(test condition)
Make the packaging bag shown in Fig. 1 as follows.
The size of sample (packaging bag): 128mm × 175mm
Resin-made membrane: PET (12 μm thick)/LLDPE (50 μm thick)
Resin film-making: add Packed PP sheet (250 μm thick)
The mode of bag: directly seal resin-made membrane at the periphery of resin film-making.
Content: containing the paper of 10cc water
Microwave-oven-heating sets: 500W, 1 minute
Sample number: 5
(test results)
It is after microwave-oven-heating as a result, the aviation value of height on 4 limits from the bottom surface of resin film-making to sealing is 31.75mm.
[embodiment 2]
(test condition)
Make the packaging bag shown in Fig. 3 as follows.
The size of sample (packaging bag): 128mm × 175mm
Resin-made membrane: PET (12 μm thick)/LLDPE (50 μm thick)
Resin film-making: add Packed PP sheet (250 μm thick)
The mode of bag: the directly bonding three limit sealing bags be made up of resin-made membrane in resin film-making.
Content: containing the paper of 10cc water
Microwave-oven-heating sets: 500W, 1 minute
Sample number: 5
(test results)
It is after microwave-oven-heating as a result, the aviation value of height on 4 limits from the bottom surface of resin film-making to sealing is 29.25mm.
[embodiment 3]
(test condition)
Make the packaging bag shown in Fig. 5 as follows.
The size of sample (packaging bag): 128mm × 175mm
Resin-made membrane: PET (12 μm thick)/LLDPE (50 μm thick)
Resin film-making: add Packed PP sheet (250 μm thick)
The mode of bag: in resin film-making only on four limits with the weak bonding three limit sealing bags be made up of resin-made membrane of arbitrary width.
Content: containing the paper of 10cc water
Microwave-oven-heating sets: 500W, 1 minute
Sample number: 5
(test results)
It is after microwave-oven-heating as a result, the aviation value of height on 4 limits from the bottom surface of resin film-making to sealing is 29.75mm.
In addition, resin film-making and resin-made membrane can easily be separated after microwave-oven-heating.
[embodiment 4]
(test condition)
Make the packaging bag shown in Fig. 7 as follows.
The size of sample (packaging bag): 128mm × 175mm
Resin-made membrane: PET (12 μm thick)/LLDPE (50 μm thick)
Resin film-making: add Packed PP sheet (250 μm thick)
The mode of bag: upper surface 4 limits sealing resin film-making on the bag of putting the palms together before one be made up of resin-made membrane with arbitrary width.
Content: containing the paper of 10cc water
Microwave-oven-heating sets: 500W, 1 minute
Sample number: 5
(test results)
It is after microwave-oven-heating as a result, the aviation value of height on 4 limits from the bottom surface of resin film-making to sealing is 27.75mm.
[embodiment 5]
(test condition)
Packaging bag has been made in the same manner as in Example 4 as except resin film-making in example 4 except have employed the resin film-making shown in Fig. 9.
The size of sample (packaging bag): 128mm × 175mm
Resin-made membrane: PET (12 μm thick)/LLDPE (50 μm thick)
Resin film-making: add Packed PP sheet (200 μm thick)
Annular convex: 3 (H=3mm, L=4mm)
The mode of bag: upper surface 4 limits sealing resin film-making on the bag of putting the palms together before one be made up of resin-made membrane with arbitrary width.
Content: containing the paper of 10cc water
Microwave-oven-heating sets: 500W, 1 minute
Sample number: 5
(test results)
For embodiment 1 ~ 4, after microwave-oven-heating as a result, the aviation value of height on 4 limits from the bottom surface of resin film-making to sealing is 27.75mm.
For embodiment 5, after microwave-oven-heating as a result, the aviation value of height on 4 limits from the bottom surface of resin film-making to sealing is 42.50mm.
Resin film-making after the heating obtained by above-described embodiment all becomes the vessel shape of height about 30mm, has the degree of depth enough used as tableware.
The effect enumerating packaging bag of the present invention as follows.
(1) packaging bag of the present invention is by with microwave-oven-heating, can carry out the cooking of content and resin film-making can be made to be deformed into vessel-shaped and to use as tableware.
(2) when employing the packing container of pallet, if there is head room, then when carrying out pasteurization after vacuum packaging, pallet can deform, therefore, packaging bag of the present invention is not suitable for this packaging, sterilization mode, if but then can carry out vacreation packaging.
(3) when packing container owing to there is head room and volume is large, so the problem that Existential Space efficiency (material stock space efficiency, conveying efficiency, display efficiency) difference is such in packaging for foodstuff workshop and circulation process, but packaging bag of the present invention in packaging for foodstuff workshop and circulation process can not as packing container volume large, therefore space efficiency is good.
(4) as the resin film-making being used in invention, the resin film-making thinner than the resin film-making of packing container can be used, therefore, there is the advantage that use amount, the environmental protection that can reduce resin material is such.
(5) packaging bag of the present invention is aspect and bag face (Off ェ イ ス face) is resin-made membrane basically, and therefore, compared with the packing container of pallet+lid material, the degree of freedom of design is high, and highlighting is excellent.
Description of reference numerals
1 resin film-making
2 resin-made membranes
3 resin-made membranes
10 containing the content of moisture
11,12 side seals
13,14 end sealings
15 back ofs the body paste sealing
21 resin-made membrane base materials
22 thermal adhesive layer
31 resin-made membrane base materials
32 thermal adhesive layer
33 protuberances
34 recesses
35 vacuum seals
36 cutters
37 packaging bodies
38 sealings
39 otch
40 frameworks
41,42 frame components
43 articulation pieces
44,45 stationary members
46 flange parts
50 frameworks
51,52 frame components
53 articulation pieces
54,55 stationary members
56 space parts
S bonding portion.
Claims (19)
1. a micro-wave oven resin-made packaging bag, it is that circumference is sealed the packaging bag used, and it is characterized in that,
The face side of packaging bag is made up of 1 resin-made membrane, rear side is made up of 1 resin film-making, above-mentioned resin-made membrane and resin film-making are made up of material as follows: during the packaging body formed making the resin film-making of above-mentioned rear side be bottom surface microwave-oven-heating between above-mentioned resin-made membrane and above-mentioned resin film-making to seal the content containing moisture, be out of shape under the heat of the water vapour produced from foregoing thing and the effect of pressure and make the resin film-making of above-mentioned rear side become concave shape, after heating terminates, still all or locally maintaining this concave shape.
2. micro-wave oven resin-made according to claim 1 packaging bag, is characterized in that,
Above-mentioned resin film-making is at the bonding resin-made laminates of resin-made membrane of its back side surface.
3. a micro-wave oven resin-made packaging bag, it is that circumference is sealed the packaging bag used, and it is characterized in that,
The face side of packaging bag is made up of 2 resin-made membranes, rear side is made up of 1 resin film-making, the resin-made membrane of the resin film-making side in above-mentioned 2 resin-made membranes bonds on the face of the face side of above-mentioned resin film-making, above-mentioned resin-made membrane and resin film-making are made up of material as follows: when the packaging body that the content of sealing containing moisture that make the resin film-making of above-mentioned rear side be bottom surface microwave-oven-heating between above-mentioned 2 resin-made membranes is formed, be out of shape under the heat of the water vapour produced from foregoing thing and the effect of pressure and make the resin film-making of above-mentioned rear side become concave shape, still all or locally this concave shape is maintained after heating terminates.
4. micro-wave oven resin-made according to claim 3 packaging bag, is characterized in that,
The resin-made membrane of above-mentioned resin film-making and above-mentioned resin film-making side is by weak bonding, and above-mentioned adhesive linkage is the adhesive linkage of weak gleyness, by the heating undertaken by micro-wave oven, the resin-made membrane of having accommodated content can be made to be separated with resin film-making.
5. a micro-wave oven resin-made packaging bag, it is that circumference is sealed the packaging bag used, and it is characterized in that,
Form at the resin-made membrane of overlapped surfaces side, both sides of resin film-making and the resin-made membrane of rear side, above-mentioned resin-made membrane and resin film-making are made up of material as follows: during the packaging body formed making the resin-made membrane of above-mentioned rear side be bottom surface microwave-oven-heating between the resin-made membrane and above-mentioned resin film-making of above-mentioned face side to seal the content containing moisture, be out of shape under the heat of the water vapour produced from foregoing thing and the effect of pressure and make the resin film-making of above-mentioned rear side become concave shape, still all or locally this concave shape is maintained after heating terminates.
6. micro-wave oven resin-made according to claim 5 packaging bag, is characterized in that,
1 resin-made membrane is carried on the back to be pasted sealing and defines the resin-made membrane of above-mentioned face side and the resin-made membrane of rear side.
7. micro-wave oven resin-made according to any one of claim 1 to 4 packaging bag, is characterized in that,
Formed in the following way: configure the content containing moisture in the resin film-making of strip or on the face of the inner side as packaging bag between the resin film-making of the strip of bonding resin-made membrane and the resin-made membrane of strip, then, at each unit area being configured with content, four limits are sealed, then by cutter, individuality is cut off one by one.
8. micro-wave oven resin-made according to any one of claim 1 to 7 packaging bag, is characterized in that,
Otch in above-mentioned resin film-making.
9. micro-wave oven resin-made according to any one of claim 1 to 7 packaging bag, is characterized in that,
Shallow recess has been pre-formed near the central portion of resin film-making.
10. micro-wave oven resin-made according to any one of claim 1 to 7 packaging bag, is characterized in that,
In advance in concentrically alternately defining multiple annular recessed portion and annular convex respectively in resin film-making.
11. micro-wave oven resin-made according to any one of claim 1 to 10 packaging bags, is characterized in that,
Above-mentioned resin-made membrane is provided with triangle pad.
12. micro-wave oven resin-made packaging bags according to any one of claim 1 to 11, is characterized in that,
The parts making steam hole automatically opening in microwave-oven-heating are provided with on resin-made membrane surface.
13. micro-wave oven resin-made packaging bags according to any one of claim 1 to 11, is characterized in that,
A part for the sealing of resin-made membrane and resin film-making is weak sealing, and the part of above-mentioned weak sealing in microwave-oven-heating is peeled off, and as steam hole opening.
14. 1 kinds of microwave-oven-heating methods of resin-made packaging bag of the micro-wave oven according to any one of claim 1 ~ 13, is characterized in that,
All or part of of the circumference of above-mentioned micro-wave oven resin-made packaging bag is clamped by framework, and when being out of shape with the heating plastic in micro-wave oven, the flange portion of resin film-making is that approximate horizontal mode carries out microwave-oven-heating.
15. 1 kinds of microwave-oven-heating methods of resin-made packaging bag of the micro-wave oven according to any one of claim 1 ~ 13, is characterized in that,
All or part of framework having wall by the resin film-making side in the packaging bag of micro-wave oven resin-made of the circumference of above-mentioned micro-wave oven resin-made packaging bag carries out microwave-oven-heating clampingly, and above-mentioned wall controls plastic deformation during microwave-oven-heating.
16. 1 kinds of bag feeding type Research on Automatic Filling, is characterized in that,
After being filled with the content containing moisture by the peristome of the micro-wave oven resin-made packaging bag according to any one of claim 1 ~ 13 of three limit sealings in resin-made packaging bag, above-mentioned peristome sealing is carried out sealing resin packaging bag.
17. 1 kinds of bag feeding type Research on Automatic Filling, is characterized in that,
After the peristome of micro-wave oven resin-made according to claim 6 packaging bag is filled with the content containing moisture, above-mentioned peristome sealing is carried out sealing resin packaging bag, the packaging bag of above-mentioned micro-wave oven resin-made according to claim 6 is by the resin-made membrane covering resin film-making of in a tubular form, the both ends of this resin-made membrane back of the body is pasted sealing, and circumference is sealed the packaging bag used, further, be carry out in the side of packaging bag holding sealing and being formed.
18. 1 kinds of roller supply type Research on Automatic Filling, it is the method for filling the content containing moisture to micro-wave oven resin-made packaging bag according to claim 7, it is characterized in that,
Resin film-making is derived or the bonding resin film-making of resin-made membrane on the face of the inner side as packaging bag from roller, after the content put containing moisture is uploaded in above-mentioned resin film-making, the resin-made membrane of deriving from roller is overlapped into and covers foregoing thing, and side surface part is sealed, then, individuality is cut off by cutter after carrying out end sealing and having carried out sealed package by peristome at two positions one by one.
19. 1 kinds of packaging bodies, fill the content containing moisture and seal and formed in the micro-wave oven resin-made packaging bag according to any one of claim 1 ~ 13.