CN105133809B - A kind of paper walltile and preparation method thereof - Google Patents
A kind of paper walltile and preparation method thereof Download PDFInfo
- Publication number
- CN105133809B CN105133809B CN201510575623.6A CN201510575623A CN105133809B CN 105133809 B CN105133809 B CN 105133809B CN 201510575623 A CN201510575623 A CN 201510575623A CN 105133809 B CN105133809 B CN 105133809B
- Authority
- CN
- China
- Prior art keywords
- paper
- walltile
- base sheet
- resin base
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a kind of paper walltile and preparation method thereof.A kind of paper walltile, including resin base sheet and the paper layer for the upper surface for being laid on the resin base sheet；The paper layer is mainly made up of following component：By weight, paper, water, adhesive, acrylic paints.Its preparation method comprises the following steps：According to the formula of the paper layer, all raw materials are mixed, sized mixing, paper pulp is obtained；The paper pulp is layered on to the surface of the resin base sheet, re-dry obtains product.Paper is dexterously combined together by the paper walltile of the present invention with resin base sheet, possesses advantages below：Light specific gravity, radiationless element, without formaldehyde components, non-volatility peculiar smell, sound-absorbing effect is good, plasticity is strong, easy to clean, service life length, sound construction, ventilative and compatibility is good, sense of touch is soft, euphorosia etc..
Description
Technical field
The present invention relates to building material field, in particular to a kind of paper walltile and preparation method thereof.
Background technology
The walltile of broad sense includes mosaic (i.e. the wall brick of small size) and large-sized face brick.
Using ceramics, marble, glass, metal or tapestry etc. more than traditional metope brick.These materials are in use
There is its limitation.For example：Ceramics are a kind of most traditional mosaics, relatively more dull, with waterproof, protection against the tide, wear-resisting and easy
The features such as cleaning, but its plasticity is not strong, and surface is chilly；Marble lithotome contains radiation element, and material valency is high, and surface is hard
Cold, not sound-absorbing, compatibility is weak, than great, is mainly used in exterior wall, uses high intensity viscose containing formaldehyde or cement；Glass Mosaic：
Relatively common and monochromatic system, it is more transparent sparkling and crystal-clear, can be reflective, surface is chilly, and compatibility is weak, is mainly used in exterior wall, using high-strength
Spend viscose containing formaldehyde；Metal mosaic：Monochrome, glossy and metal-like, fashionable individual character, surface is hale and hearty chilly, and compatibility is weak,
Use high intensity viscose containing formaldehyde；Tapestry：Sound-absorbing, easily makes and is stained with dust and difficult cleaning dirty, the time, long color and luster moved back old, affine
Property is strong.Use high intensity viscose containing formaldehyde.
In view of this, it is special to propose the present invention.
The content of the invention
The first object of the present invention is to provide a kind of paper walltile, and described paper walltile has light specific gravity, radiationless
The advantages of element, sound-absorbing effect are good, plasticity is strong.
The second object of the present invention is a kind of preparation method of described paper walltile of offer, and this method has simple easy
Operate, manufacturing process is pollution-free, the non-toxic volatile ingredient of finished product, the advantages of making material is cheap.
In order to realize the above-mentioned purpose of the present invention, spy uses following technical scheme：
A kind of paper walltile, including resin base sheet and the paper layer for the upper surface for being laid on the resin base sheet；The paper
Matter layer is mainly made up of following component：By weight, 1.5 parts of paper, 1.8-2.2 parts of water, 0.8-1.2 parts of adhesive, acrylic paints
0.8-1 parts.
Paper is dexterously combined together by above-mentioned paper walltile with resin base sheet, possesses advantages below：It is light specific gravity, radiationless
Element, sound-absorbing effect are good, plasticity is strong, easy to clean, service life length, sound construction, ventilative and compatibility is good, sense of touch is soft,
Euphorosia etc..
Wherein, preferably, difference in appearance is smaller for the stickiness of resin base sheet and paper material, therefore both are combined together both
Easy processing, and attractive in appearance, and both combine the surface of rear paper layers and be presented small cellular, therefore sound-absorbing effect has and protrudes
Advantage, it is adaptable to the inner wall of building such as music hall, cinema, workshop.And paper stock can be both bonded in by the adhesive in paper layer
Together, it is to avoid being scattered after paper water suction to shape, and again can be bonded in paper layer on resin base sheet securely, acrylic paints can
To change the color of paper layer, make walltile variation, the cohesive force between paper stock bonding, paper and bottom plate can also be strengthened, and
Play waterproof effect.
In addition, above-mentioned paper walltile both includes larger-size walltile, also the mosaic including small size, i.e., of the invention
Paper walltile be applied to arbitrary dimension, while the moulding of paper walltile is not also restricted, any color pattern can be processed into
Or the moulding of shape.
Preferably, the resin base sheet is PVC bottom plates or PC bottom plates or plexiglass base plate.
These three bottom plates respectively have its advantage.PVC bottom plate toughness is strong, lightweight, and service life can be increased for walltile；
PC bottom plates are spumescence material, and quality is lighter, but because of easy brittle failure, takes down surface plastic materials film while retaining bottom plastic film；Have
The machine glass film plates transparency, chemical stability, mechanical property and good endurance, attractive appearance.
Preferably, the thickness of the paper layer is 3-5mm.
The paper walltile of this thickness can meet daily sound-absorption requirement completely.
Preferably, the paper is soft paper, soft paper easy processing.Cardboard or linen-cotton, bagasse, wood can certainly be used
The natural fibers such as broken, hay, the harder material of these quality is that can be used by mechanical crushing.In addition, the paper used in the present invention
Can be the waste paper recycled.
Preferably, the adhesive is polyvinyl acetate, and compared to other adhesives, polyvinyl acetate has water
The advantages of dissolubility is good, nontoxic, dryness is strong.
The preparation method of paper walltile described above, comprises the following steps：
According to the formula of the paper layer, all raw materials are mixed, sized mixing, paper pulp is obtained；
The paper pulp is layered on to the rough surface of the resin base sheet, re-dry obtains product.
Above-mentioned preparation method separates the processing of paper layer and the processing of bottom plate, thus is more easy to implementation process control.Separately
Outside, the step of whole preparation process is not related to complex process, thus have the advantages that simple to operation.
Preferably, also include before the paper layer is layered on after the surface of the resin base sheet and dry：
Carry out embossed.
Preferably, the method sized mixing is：Add water, be stirred for, it is simple to operation.
Embossed can both optimize the moulding of walltile, make it have the texture appearance of grace, can increase papery again
Cohesive between layer and bottom plate.
Preferably, the method for the drying is：2-3min, then natural drying 5-6min are first dried at 40-50 DEG C.
By above drying means, the honeycomb structure of papery layer surface is more small, is more evenly distributed, thus the wall prepared
Face brick sound-absorption coefficient is higher, and sound-absorption coefficient difference everywhere is smaller.
Preferably, before the paper pulp is layered on into the surface of the resin base sheet：First by the surface of the resin base sheet
Mill is coarse.
When backplate surface is coarse and paper layer adhesion it is stronger, frictional force is big, and paper layer is difficult full wafer and dropped.
Compared with prior art, beneficial effects of the present invention are：
(1) paper walltile of the invention overcomes most of shortcoming of conventional wall face brick, proportion, environmental protection, sound-absorbing effect,
There is outstanding advantage in terms of plasticity, cleaning difficulty or ease, service life, sound construction degree, ventilative and compatibility, outward appearance, cost.
(2) one of uniqueness of paper walltile of the invention is " paper " applying wall brick, has both taken full advantage of the advantage of paper,
The shortcoming that resin base sheet compensate for paper is borrowed again.
(3) one of uniqueness of paper walltile of the invention also resides in the surface of paper layer and is presented cellular, with stronger
Sound-absorbing effect, is that the vocal music inner wall of building such as music hall, cinema and house ornamentation wall decoration provide a kind of new material.
(4) present invention expands the species of walltile using the acrylic paints for being difficult to decolourize, and more multiselect is provided for consumer
Select.
(5) present invention makes walltile have certain water-proof function using the acrylic paints for being difficult to decolourize.
(6) making material of paper walltile of the invention is environment-friendly materials.
Embodiment
Embodiment of the present invention is described in detail below in conjunction with embodiment, but those skilled in the art will
Understand, the following example is merely to illustrate the present invention, and is not construed as limiting the scope of the present invention.It is unreceipted specific in embodiment
Condition person, the condition advised according to normal condition or manufacturer is carried out.Agents useful for same or the unreceipted production firm person of instrument, be
The conventional products that can be obtained by commercially available purchase.
Embodiment 1
A kind of paper walltile：
By weight, soft 1.5 parts of paper, 0.8 part of polyvinyl acetate, 1.8 parts of water, green 0.8 part of acrylic paints are taken, are mixed
Close, size mixing, obtain paper pulp；
The surface mill of PVC bottom plates is coarse；
The paper pulp is layered on to the surface of PVC bottom plates, 2min, then natural drying 5min are first dried at 40 DEG C, production is produced
Product.
Embodiment 2
A kind of paper walltile：
By weight, soft 1.5 parts of paper, 1.2 parts of polyvinyl acetate, 2.2 parts of water, red 0.8 part of acrylic paints are taken, are mixed
Close, size mixing, obtain paper pulp；
The surface mill of PVC bottom plates is coarse；
The paper pulp is layered on to the surface of PVC bottom plates, 3min, then natural drying 6min are first dried at 50 DEG C, production is produced
Product.
Embodiment 3
A kind of paper walltile：
By weight, soft 1.5 parts of paper, 1 part of polyvinyl acetate, 2 parts of water, 0.8 part of yellow acrylic paints are taken, mix,
Size mixing, obtain paper pulp；
The surface mill of PVC bottom plates is coarse；
The paper pulp is layered on to the surface of PVC bottom plates, 2.5min, then natural drying 5.5min are first dried at 45 DEG C, i.e.,
Obtain product.
Embodiment 4
A kind of paper walltile：
By weight, soft 1.5 parts of paper, 1 part of polyvinyl acetate, 2 parts of water, green 1 part of acrylic paints, mixing, tune are taken
Slurry, obtains paper pulp；
The rough surface of PC bottom plates is handled；
The paper pulp is layered on to the surface of PC bottom plates, 2.5min, then natural drying 5.5min are first dried at 45 DEG C, is produced
Product.
Embodiment 5
A kind of paper walltile：
By weight, soft 1.5 parts of paper, 1 part of polyvinyl acetate, 2 parts of water, green 1 part of acrylic paints, mixing, tune are taken
Slurry, obtains paper pulp；
Lucite surface is ground coarse；
The paper pulp is layered on to the surface of plexiglass base plate, 2.5min, then natural drying are first dried at 45 DEG C
5.5min, produces product.
Embodiment 6
A kind of paper walltile：
By weight, soft 1.5 parts of paper, 1 part of polyvinyl acetate, 1.5 parts of water, green 1 part of acrylic paints are taken, mix,
Size mixing, obtain paper pulp；
Lucite surface is ground coarse；
The paper pulp is layered on to the surface of plexiglass base plate, embossed is carried out；
After embossing, 2.5min, then natural drying 5.5min are first dried at 45 DEG C, product is produced.
Embodiment 7
A kind of paper walltile：
By weight, soft 1.5 parts of paper, 1 part of polyvinyl acetate, 2 parts of water, green 0.8 part of acrylic paints are taken, mix,
Size mixing, obtain paper pulp；
Lucite surface is ground coarse；
The paper pulp is layered on to the rough surface of plexiglass base plate, 2.5min, then natural drying are first dried at 45 DEG C
5.5min, produces product.
Embodiment 8
A kind of mosaic：
By weight, soft 1.5 parts of paper, 1 part of polyvinyl acetate, 2 parts of water, red 1 part of acrylic paints, mixing, tune are taken
Slurry, obtains paper pulp；
Lucite surface is ground coarse；
The paper pulp is layered on to the rough surface of plexiglass base plate, 2.5min, then natural drying are first dried at 45 DEG C
5.5min, produces product.
Embodiment 9
A kind of mosaic：
By weight, soft 1.5 parts of paper, 1 part of polyvinyl acetate, 2 parts of water, green 1 part of acrylic paints, mixing, tune are taken
Slurry, obtains paper pulp；
Lucite surface is ground coarse；
The paper pulp is layered on to the rough surface of plexiglass base plate, 2.5min, then natural drying are first dried at 45 DEG C
5.5min, produces product.
Embodiment 10
A kind of paper walltile：
By weight, soft 1.5 parts of paper, 1 part of polyvinyl acetate, 2 parts of water, green 1 part of acrylic paints, mixing, tune are taken
Slurry, obtains paper pulp；
PVC backplate surfaces are ground coarse；
The paper pulp is layered on to the surface of PVC bottom plates, thickness is about 3mm, first dries 2.5min at 45 DEG C afterwards, then certainly
5.5min is so dried, product is produced.
Embodiment 11
A kind of paper walltile：
By weight, soft 1.5 parts of paper, 1 part of polyvinyl acetate, 2 parts of water, green 0.8 part of acrylic paints are taken, mix,
Size mixing, obtain paper pulp；
PVC backplate surfaces are ground coarse；
The paper pulp is layered on to the surface of PVC bottom plates, thickness is about 5mm, first dries 2.5min at 45 DEG C afterwards, then certainly
5.5min is so dried, product is produced.
Embodiment 12
A kind of paper walltile：
By weight, soft 1.5 parts of paper, 1 part of polyvinyl acetate, 2 parts of water, green 0.8 part of acrylic paints are taken, mix,
Size mixing, obtain paper pulp；
PVC backplate surfaces are ground coarse；
The paper pulp is layered on to the surface of PVC bottom plates, thickness is about 4mm, first dries 2.5min at 45 DEG C afterwards, then certainly
5.5min is so dried, product is produced.
Embodiment 13
A kind of paper walltile：
By weight, 1 part of cardboard, 0.8 part of polyvinyl acetate, 1.8 parts of water, green 0.8 part of acrylic paints are taken, are mixed
Close, size mixing, obtain paper pulp；
PVC backplate surfaces are ground coarse；
The paper pulp is layered on to the surface of PVC bottom plates, 2-3min, then natural drying 5-6min are first dried at 40-50 DEG C,
Produce product.
Embodiment 14
A kind of mosaic：
By weight, 1 part of cardboard, 1 part of polyvinyl acetate, 2 parts of water, green 1 part of acrylic paints are taken, mixes, size mixing,
Obtain paper pulp；
Lucite surface is ground coarse；
The paper pulp is layered on to the rough surface of plexiglass base plate, 2.5min, then natural drying are first dried at 45 DEG C
5.5min, produces product.
Although illustrate and describing the present invention with specific embodiment, but it will be appreciated that without departing substantially from the present invention's
Many other changes and modification can be made in the case of spirit and scope.It is, therefore, intended that in the following claims
Including belonging to all such changes and modifications in the scope of the invention.
Claims (5)
1. a kind of paper walltile, it is characterised in that the papery including resin base sheet He the upper surface for being laid on the resin base sheet
Layer；The paper layer is mainly made up of following component：By weight, 1.5 parts of paper, 1.8-2.2 parts of water, 0.8-1.2 parts of adhesive,
0.8-1 parts of acrylic paints；
The paper walltile is mainly prepared from by following methods：
According to the formula of the paper layer, all raw materials are mixed, sized mixing, being added water when sizing mixing is stirred for, and obtains paper pulp；
It is first that the surface mill of the resin base sheet, PVC bottom plates, PC bottom plates or plexiglass base plate is coarse, then again by the paper
Slurry is layered on the surface of the resin base sheet, PVC bottom plates, PC bottom plates or plexiglass base plate, then carries out embossed, re-dry
Obtain product；
Wherein, dry method is：2-3min, then natural drying 5-6min are first dried at 40-50 DEG C.
2. paper walltile according to claim 1, it is characterised in that the adhesive is polyvinyl acetate.
3. paper walltile according to claim 1, it is characterised in that the resin base sheet be PVC bottom plates or PC bottom plates or
Plexiglass base plate.
4. paper walltile according to claim 1, it is characterised in that the thickness of the paper layer is 3-5mm.
5. paper walltile according to claim 1, it is characterised in that the paper is soft paper.