CN105131788A - Supporting rod for outdoor tent and production process - Google Patents
Supporting rod for outdoor tent and production process Download PDFInfo
- Publication number
- CN105131788A CN105131788A CN201510602465.9A CN201510602465A CN105131788A CN 105131788 A CN105131788 A CN 105131788A CN 201510602465 A CN201510602465 A CN 201510602465A CN 105131788 A CN105131788 A CN 105131788A
- Authority
- CN
- China
- Prior art keywords
- agent
- parts
- support bar
- outdoor tent
- supporting rod
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a supporting rod for an outdoor tent and a production process. The supporting rod comprises a metal supporting rod body and a supporting rod coating arranged on the outer side of the metal supporting rod body, wherein the metal supporting rod body comprises the following components in parts by weight: 4-5 parts of C, 1-2.5 parts of Cu, 5-8 parts of Mn, 1-3 parts of Ti, 60-63 parts of Fe, 1-2.5 parts of Cr, 3-4 parts of Al, 3-5 parts of Co, 1.7-3.7 parts of Si, 1.5-2.5 parts of Sn, 1-3 parts of Ni and 1-2 parts of Pb; the supporting rod coating comprises the following components in parts by weight: 30-45 parts of epoxy resin, 1.5-3.5 parts of paint, 13-20 parts of a solvent, 0.15-1.3 parts of a defoaming agent, 0.2-0.5 part of a dispersing agent, 0.1-0.4 part of a curing agent, 0.14-0.33 part of a wetting agent, 0.12-0.5 part of an anti-settling agent, 0.13-0.2 part of a flatting agent, 0.1-0.3 part of an antirusting agent, 0.2-0.6 part of a drying agent, 0.3-0.5 part of a plasticizing agent, 0.1-0.4 part of a delustering agent, 0.2-0.5 part of a flame retardant, 0.13-0.17 part of an antifoulant, 0.2-0.5 part of an anti-skinning agent and 11-13 parts of a filling material. The supporting rod is high in toughness, light resistance and weatherability, and the service life of the supporting rod for the tent can be effectively prolonged.
Description
Technical field
The present invention relates to tent field, particularly relate to a kind of outdoor tent support bar and production technique.
Background technology
Open air goes camping, tent to equip, tent specifically must have sunshade, ventilation, the multiple outdoor function such as windproof, rainproof, warming, outdoor tent must adapt to various weather environment, as the support of tent, its support bar also needs to have certain function, more effectively could support tent to resist rugged environment.Directly metal material is processed in existing tent pole; and outside metal material, be provided with one deck coating be fixed; but metallic support rod is easily corroded and is also easily worn; be unfavorable for preservation and the use of support bar; so need to add suitable coating process outside to extend the work-ing life of support bar; also outside metallic support rod, some coatings are added in existing technology; but its coating added is fairly simple; function ratio is more single, effectively can not protect metallic support rod.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, provide a kind of outdoor tent support bar and production technique, to solve problems of the prior art.
For achieving the above object, the technical solution used in the present invention is as follows:
A kind of outdoor tent support bar, it is characterized in that: described outdoor tent support bar comprises metallic support rod and is arranged on the support bar coating outside metallic support rod, in described metallic support rod, the mass fraction of each component comprises 4-5 part C, 1-2.5 part Cu, 5-8 part Mn, 1-3 part Ti, 60-63 part Fe, 1-2.5 part Cr, 3-4 part Al, 3-5 part Co, 1.7-3.7 part Si, 1.5-2.5 part Sn, 1-3 part Ni, 1-2 part Pb, in described support bar coating, the mass fraction of each component comprises 30-45 part epoxy resin, 1.5-3.5 part pigment, 13-20 part solvent, 0.15-1.3 part defoamer, 0.2-0.5 part dispersion agent, 0.1-0.4 part solidifying agent, 0.14-0.33 part wetting agent, 0.12-0.5 part anti-settling agent, 0.13-0.2 part flow agent, 0.1-0.3 part rust-preventive agent, 0.2-0.6 part siccative, 0.3-0.5 part softening agent, 0.1-0.4 part matting agent, 0.2-0.5 part fire retardant, 0.13-0.17 part stain control agent, 0.2-0.5 part anti skinning agent, 11-13 part filler.
As a modification of the present invention, described metallic support rod also comprises MgB
2, Mg
3n
2, Si
3b.
As a modification of the present invention, described filler comprises the mixture of any one or a few combination in titanium dioxide, barium metaborate, titanium dioxide, talcum powder, calcium carbonate, barium sulfate, silicon-dioxide.
As a modification of the present invention, described epoxy resin comprises propane type epoxy resin of di phenolic group and glycidyl amine epoxy resin.
As a modification of the present invention, described rust-preventive agent comprises zinc phosphate, iron powder, zinc powder and aluminium powder.
As a modification of the present invention, the production technique of described outdoor tent support bar is as follows:
1) first 4-5 part C, 60-63 part Fe, 1-2.5 part Cr is put into No. 1 smelting furnace, stir after heat fused, add 5-8 part Mn, 1-3 part Ti, 3-4 part Al, 1.7-3.7 part Si successively to smelting furnace again to stir, add after 3-5 part Co, 1-2 part Pb, 1.5-2.5 part Sn, 1-2.5 part Cu, 1-2 part Pb fusing stirs again in smelting furnace successively, pour inwall into and scribble in No. 2 smelting furnaces of MgB2, Mg3N2, Si3B and make melt;
2) melt is put into strainer after filtering, melt to be poured in mould and to anneal, and cooled mould is put into extrusion machine carries out cutting according to the size of regulation, chamfering, and the mould of well cutting is carried out grinding homogeneity, carry out quench treatment after grinding homogeneity and cool;
3) support bar coating is poured in spraying machine, to through step 2) metallic support rod produced sprays, and the metallic support rod sprayed cooled, and generate tent pole.
As a modification of the present invention, described support bar Coating process is as follows: get 30-45 part epoxy resin, 1.5-3.5 part pigment, 13-20 part solvent is placed in sand mill and once disperses, grinding, wait to disperse, 0.15-1.3 part defoamer is added again after grinding, 0.2-0.5 part dispersion agent, then mixture is put into three-roller and carry out twice dispersing, grinding, and will through twice dispersing, mixture after grinding puts into stirrer, get 0.1-0.4 part solidifying agent, 0.14-0.33 part wetting agent, 0.12-0.5 part anti-settling agent, 0.13-0.2 part flow agent, 0.1-0.3 part rust-preventive agent, 0.2-0.6 part siccative, 0.3-0.5 part softening agent, 0.1-0.4 part matting agent, 0.2-0.5 part fire retardant, 0.13-0.17 part stain control agent, 0.2-0.5 part anti skinning agent adds in stirrer successively, and stir, 11-13 part filler is added in stirrer and stirs, and after the mixture after stirring is filtered, filtrate is detected, detect qualified rear for subsequent use.
Owing to have employed above technology, the present invention comparatively prior art compares, and the beneficial effect had is as follows:
Be provided with Ti in the present invention, certain compound can be formed with other metallics, effectively can increase the toughness of metallic support rod; MgB is provided with in the present invention
2, Mg
3n
2, Si
3b, effectively can increase the toughness of support bar; In the present invention, twice dispersion, grinding are carried out to coating, can meticulousr by the raw mill of coating, coating is effectively mixed, makes the better effects if of coating; Be provided with rust-preventive agent, fire retardant and stain control agent in coating of the present invention, what can increase support bar puts corrodibility, flame retardant resistance, didirtresistance and anti-skinning; Be provided with titanium dioxide, barium metaborate, titanium dioxide in filler of the present invention, effectively can increase photostabilization and the weathering resistance of support bar, extend the work-ing life of tent pole; Be provided with anti skinning agent in the present invention, can effectively prevent support bar skinning.
Embodiment
Below in conjunction with embodiment, illustrate the present invention further.
embodiment 1:
A kind of outdoor tent support bar, described outdoor tent support bar comprises metallic support rod and is arranged on the support bar coating outside metallic support rod, in described metallic support rod, the mass fraction of each component comprises 4 parts of C, 2.5 parts of Cu, 5 parts of Mn, 3 parts of Ti, 60 parts of Fe, 2.5 parts of Cr, 3 parts of Al, 5 parts of Co, 1.7 parts of Si, 2.5 parts of Sn, 1 part of Ni, 2 parts of Pb, in described support bar coating, the mass fraction of each component comprises 45 parts of epoxy resin, 1.5 parts of pigment, 20 parts of solvents, 0.15 part of defoamer, 0.5 part of dispersion agent, 0.1 part of solidifying agent, 0.33 part of wetting agent, 0.12 portion of anti-settling agent, 0.2 part of flow agent, 0.1 part of rust-preventive agent, 0.6 part of siccative, 0.3 part of softening agent, 0.4 part of matting agent, 0.2 part of fire retardant, 0.17 part of stain control agent, 0.2 part of anti skinning agent, 13 parts of fillers.
Described metallic support rod also comprises MgB
2, Mg
3n
2, Si
3b.
Described filler comprises the mixture of any one or a few combination in titanium dioxide, barium metaborate, titanium dioxide, talcum powder, calcium carbonate, barium sulfate, silicon-dioxide.
Described epoxy resin comprises propane type epoxy resin of di phenolic group and glycidyl amine epoxy resin.
Described rust-preventive agent comprises zinc phosphate, iron powder, zinc powder and aluminium powder.
The production technique of described outdoor tent support bar is as follows:
1) first 4 parts of C, 60 parts of Fe, 2.5 parts of Cr are put into No. 1 smelting furnace, stir after heat fused, add 5 parts of Mn successively to smelting furnace again, 3 parts of Ti, 3 parts of Al, 1.7 parts of Si stir, in smelting furnace, add 5 parts of Co, 2 parts of Pb more successively, after 2.5 parts of Sn, 2.5 parts of Cu, 2 parts of Pb fusings stir, pour inwall into and scribble in No. 2 smelting furnaces of MgB2, Mg3N2, Si3B and make melt;
2) melt is put into strainer after filtering, melt to be poured in mould and to anneal, and cooled mould is put into extrusion machine carries out cutting according to the size of regulation, chamfering, and the mould of well cutting is carried out grinding homogeneity, carry out quench treatment after grinding homogeneity and cool;
3) 45 parts of epoxy resin are got, 1.5 parts of pigment, 20 parts of solvents are placed in sand mill and once disperse, grinding, wait to disperse, 0.15 part of defoamer is added again after grinding, 0.5 part of dispersion agent, then mixture is put into three-roller and carry out twice dispersing, grinding, and will through twice dispersing, mixture after grinding puts into stirrer, get 0.1 part of solidifying agent, 0.33 part of wetting agent, 0.12 portion of anti-settling agent, 0.2 part of flow agent, 0.1 part of rust-preventive agent, 0.6 part of siccative, 0.3 part of softening agent, 0.4 part of matting agent, 0.2 part of fire retardant, 0.17 part of stain control agent, 0.2 part of anti skinning agent adds in stirrer successively, and stir, 13 parts of fillers are added in stirrer and stirs, and after the mixture after stirring is filtered, filtrate is detected, detect qualified rear for subsequent use,
4) the support bar coating produced in step 3) is poured in spraying machine, to through step 2) metallic support rod produced sprays, and the metallic support rod sprayed cooled, and generate tent pole.
Described defoamer is emulsifying agent; Described dispersion agent is phenylcarbinol; Described solidifying agent is ethylene glycol; Described wetting agent is sodium laurylsulfate; Described anti-settling agent is aerosil; Described flow agent is acrylic acid or the like flow agent; Described siccative is dibutyl tin laurate; Described softening agent is phthalic acid two (2-ethyl hexyl) ester; Described matting agent is poly-MU resin; Described fire retardant is Poly Brominated Diphenyl Ethers; Described stain control agent is Vanillyl pelargonic amide; Described anti skinning agent is hydroxyanisole.
embodiment 2:
A kind of outdoor tent support bar, described outdoor tent support bar comprises metallic support rod and is arranged on the support bar coating outside metallic support rod, in described metallic support rod, the mass fraction of each component comprises 5 parts of C, 1 part of Cu, 8 parts of Mn, 1 part of Ti, 63 parts of Fe, 1 part of Cr, 4 parts of Al, 3 parts of Co, 3.7 parts of Si, 1.5 parts of Sn, 3 parts of Ni, 1 part of Pb, in described support bar coating, the mass fraction of each component comprises 30 parts of epoxy resin, 3.5 parts of pigment, 13 parts of solvents, 1.3 parts of defoamers, 0.2 part of dispersion agent, 0.4 part of solidifying agent, 0.14 part of wetting agent, 0.5 portion of anti-settling agent, 0.13 part of flow agent, 0.3 part of rust-preventive agent, 0.2 part of siccative, 0.5 part of softening agent, 0.1 part of matting agent, 0.5 part of fire retardant, 0.13 part of stain control agent, 0.5 part of anti skinning agent, 11 parts of fillers.
Described metallic support rod also comprises MgB
2, Mg
3n
2, Si
3b.
Described filler comprises the mixture of any one or a few combination in titanium dioxide, barium metaborate, titanium dioxide, talcum powder, calcium carbonate, barium sulfate, silicon-dioxide.
Described epoxy resin comprises propane type epoxy resin of di phenolic group and glycidyl amine epoxy resin.
Described rust-preventive agent comprises zinc phosphate, iron powder, zinc powder and aluminium powder.
The production technique of described outdoor tent support bar is as follows:
1) first 5 parts of C, 63 parts of Fe, 1 part of Cr are put into No. 1 smelting furnace, stir after heat fused, add 8 parts of Mn successively to smelting furnace again, 1 part of Ti, 4 parts of Al, 3.7 parts of Si stir, in smelting furnace, add 3 parts of Co, 1 part of Pb more successively, after 1.5 parts of Sn, 1 part of Cu, 1 part of Pb fusing stir, pour inwall into and scribble in No. 2 smelting furnaces of MgB2, Mg3N2, Si3B and make melt;
2) melt is put into strainer after filtering, melt to be poured in mould and to anneal, and cooled mould is put into extrusion machine carries out cutting according to the size of regulation, chamfering, and the mould of well cutting is carried out grinding homogeneity, carry out quench treatment after grinding homogeneity and cool;
3) 30 parts of epoxy resin are got, 3.5 parts of pigment, 13 parts of solvents are placed in sand mill and once disperse, grinding, wait to disperse, 1.3 parts of defoamers are added again after grinding, 0.2 part of dispersion agent, then mixture is put into three-roller and carry out twice dispersing, grinding, and will through twice dispersing, mixture after grinding puts into stirrer, get 0.4 part of solidifying agent, 0.14 part of wetting agent, 0.5 portion of anti-settling agent, 0.13 part of flow agent, 0.3 part of rust-preventive agent, 0.2 part of siccative, 0.5 part of softening agent, 0.1 part of matting agent, 0.5 part of fire retardant, 0.13 part of stain control agent, 0.5 part of anti skinning agent adds in stirrer successively, and stir, 11 parts of fillers are added in stirrer and stirs, and after the mixture after stirring is filtered, filtrate is detected, detect qualified rear for subsequent use,
4) the support bar coating produced in step 3) is poured in spraying machine, to through step 2) metallic support rod produced sprays, and the metallic support rod sprayed cooled, and generate tent pole.
Described defoamer is emulsifying agent; Described dispersion agent is phenylcarbinol; Described solidifying agent is ethylene glycol; Described wetting agent is sodium laurylsulfate; Described anti-settling agent is aerosil; Described flow agent is acrylic acid or the like flow agent; Described siccative is dibutyl tin laurate; Described softening agent is phthalic acid two (2-ethyl hexyl) ester; Described matting agent is poly-MU resin; Described fire retardant is Poly Brominated Diphenyl Ethers; Described stain control agent is Vanillyl pelargonic amide; Described anti skinning agent is hydroxyanisole.
embodiment 3:
A kind of outdoor tent support bar, described outdoor tent support bar comprises metallic support rod and is arranged on the support bar coating outside metallic support rod, in described metallic support rod, the mass fraction of each component comprises 4 parts of C, 2 parts of Cu, 7 parts of Mn, 2 parts of Ti, 60 parts of Fe, 2.5 parts of Cr, 4 parts of Al, 4 parts of Co, 2 parts of Si, 2 parts of Sn, 1 part of Ni, 2 parts of Pb, in described support bar coating, the mass fraction of each component comprises 40 parts of epoxy resin, 3.5 parts of pigment, 13 parts of solvents, 1.3 parts of defoamers, 0.4 part of dispersion agent, 0.2 part of solidifying agent, 0.14 part of wetting agent, 0.5 portion of anti-settling agent, 0.13 part of flow agent, 0.2 part of rust-preventive agent, 0.4 part of siccative, 0.4 part of softening agent, 0.1 part of matting agent, 0.5 part of fire retardant, 0.13 part of stain control agent, 0.2 part of anti skinning agent, 11 parts of fillers.
Described metallic support rod also comprises MgB
2, Mg
3n
2, Si
3b.
Described filler comprises the mixture of any one or a few combination in titanium dioxide, barium metaborate, titanium dioxide, talcum powder, calcium carbonate, barium sulfate, silicon-dioxide.
Described epoxy resin comprises propane type epoxy resin of di phenolic group and glycidyl amine epoxy resin.
Described rust-preventive agent comprises zinc phosphate, iron powder, zinc powder and aluminium powder.
The production technique of described outdoor tent support bar is as follows:
1) first 4 parts of C, 60 parts of Fe, 2.5 parts of Cr are put into No. 1 smelting furnace, stir after heat fused, add 7 parts of Mn successively to smelting furnace again, 2 parts of Ti, 4 parts of Al, 2 parts of Si stir, in smelting furnace, add 4 parts of Co, 2 parts of Pb more successively, after 2 parts of Sn, 2 parts of Cu, 2 parts of Pb fusings stir, pour inwall into and scribble in No. 2 smelting furnaces of MgB2, Mg3N2, Si3B and make melt;
2) melt is put into strainer after filtering, melt to be poured in mould and to anneal, and cooled mould is put into extrusion machine carries out cutting according to the size of regulation, chamfering, and the mould of well cutting is carried out grinding homogeneity, carry out quench treatment after grinding homogeneity and cool;
3) 40 parts of epoxy resin are got, 3.5 parts of pigment, 13 parts of solvents are placed in sand mill and once disperse, grinding, wait to disperse, 1.3 parts of defoamers are added again after grinding, 0.4 part of dispersion agent, then mixture is put into three-roller and carry out twice dispersing, grinding, and will through twice dispersing, mixture after grinding puts into stirrer, get 0.2 part of solidifying agent, 0.14 part of wetting agent, 0.5 portion of anti-settling agent, 0.13 part of flow agent, 0.2 part of rust-preventive agent, 0.4 part of siccative, 0.4 part of softening agent, 0.1 part of matting agent, 0.5 part of fire retardant, 0.13 part of stain control agent, 0.2 part of anti skinning agent adds in stirrer successively, and stir, 11 parts of fillers are added in stirrer and stirs, and after the mixture after stirring is filtered, filtrate is detected, detect qualified rear for subsequent use,
4) the support bar coating produced in step 3) is poured in spraying machine, to through step 2) metallic support rod produced sprays, and the metallic support rod sprayed cooled, and generate tent pole.
Described defoamer is emulsifying agent; Described dispersion agent is phenylcarbinol; Described solidifying agent is ethylene glycol; Described wetting agent is sodium laurylsulfate; Described anti-settling agent is aerosil; Described flow agent is acrylic acid or the like flow agent; Described siccative is dibutyl tin laurate; Described softening agent is phthalic acid two (2-ethyl hexyl) ester; Described matting agent is poly-MU resin; Described fire retardant is Poly Brominated Diphenyl Ethers; Described stain control agent is Vanillyl pelargonic amide; Described anti skinning agent is hydroxyanisole.
The enforcement the performance test results of table 1 tent pole
Test result duration of service of table 2 tent pole
Above-described embodiment is only the preferred technical solution of the present invention; and should not be considered as restriction of the present invention; the technical scheme that protection scope of the present invention should be recorded with claim; the equivalents comprising technical characteristic in the technical scheme of claim record is protection domain; namely the equivalent replacement within the scope of this improves, also within protection scope of the present invention.
Claims (7)
1. an outdoor tent support bar, it is characterized in that: described outdoor tent support bar comprises metallic support rod and is arranged on the support bar coating outside metallic support rod, in described metallic support rod, the mass fraction of each component comprises 4-5 part C, 1-2.5 part Cu, 5-8 part Mn, 1-3 part Ti, 60-63 part Fe, 1-2.5 part Cr, 3-4 part Al, 3-5 part Co, 1.7-3.7 part Si, 1.5-2.5 part Sn, 1-3 part Ni, 1-2 part Pb, in described support bar coating, the mass fraction of each component comprises 30-45 part epoxy resin, 1.5-3.5 part pigment, 13-20 part solvent, 0.15-1.3 part defoamer, 0.2-0.5 part dispersion agent, 0.1-0.4 part solidifying agent, 0.14-0.33 part wetting agent, 0.12-0.5 part anti-settling agent, 0.13-0.2 part flow agent, 0.1-0.3 part rust-preventive agent, 0.2-0.6 part siccative, 0.3-0.5 part softening agent, 0.1-0.4 part matting agent, 0.2-0.5 part fire retardant, 0.13-0.17 part stain control agent, 0.2-0.5 part anti skinning agent, 11-13 part filler.
2. a kind of outdoor tent support bar according to claim 1, is characterized in that: described metallic support rod also comprises MgB
2, Mg
3n
2, Si
3b.
3. a kind of outdoor tent support bar according to claim 1, is characterized in that: described filler comprises the mixture of any one or a few combination in titanium dioxide, barium metaborate, titanium dioxide, talcum powder, calcium carbonate, barium sulfate, silicon-dioxide.
4. a kind of outdoor tent support bar according to claim 1, is characterized in that: described epoxy resin comprises propane type epoxy resin of di phenolic group and glycidyl amine epoxy resin.
5. a kind of outdoor tent support bar according to claim 1, is characterized in that: described rust-preventive agent comprises zinc phosphate, iron powder, zinc powder and aluminium powder.
6. a kind of outdoor tent support bar according to claim 1, is characterized in that, the production technique of described outdoor tent support bar is as follows:
1) first 4-5 part C, 60-63 part Fe, 1-2.5 part Cr is put into No. 1 smelting furnace, stir after heat fused, add 5-8 part Mn, 1-3 part Ti, 3-4 part Al, 1.7-3.7 part Si successively to smelting furnace again to stir, add after 3-5 part Co, 1-2 part Pb, 1.5-2.5 part Sn, 1-2.5 part Cu, 1-2 part Pb fusing stirs again in smelting furnace successively, pour inwall into and scribble in No. 2 smelting furnaces of MgB2, Mg3N2, Si3B and make melt;
2) melt is put into strainer after filtering, melt to be poured in mould and to anneal, and cooled mould is put into extrusion machine carries out cutting according to the size of regulation, chamfering, and the mould of well cutting is carried out grinding homogeneity, carry out quench treatment after grinding homogeneity and cool;
3) support bar coating is poured in spraying machine, to through step 2) metallic support rod produced sprays, and the metallic support rod sprayed cooled, and generate tent pole.
7. a kind of outdoor tent support bar according to claim 6, is characterized in that, described support bar Coating process is as follows: get 30-45 part epoxy resin, 1.5-3.5 part pigment, 13-20 part solvent is placed in sand mill and once disperses, grinding, waits to disperse, 0.15-1.3 part defoamer is added again after grinding, 0.2-0.5 part dispersion agent, then puts into three-roller by mixture and carries out twice dispersing, grinding, and will through twice dispersing, mixture after grinding puts into stirrer, gets 0.1-0.4 part solidifying agent, 0.14-0.33 part wetting agent, 0.12-0.5 part anti-settling agent, 0.13-0.2 part flow agent, 0.1-0.3 part rust-preventive agent, 0.2-0.6 part siccative, 0.3-0.5 part softening agent, 0.1-0.4 part matting agent, 0.2-0.5 part fire retardant, 0.13-0.17 part stain control agent, 0.2-0.5 part anti skinning agent adds in stirrer successively, and stirs, and is added in stirrer by 11-13 part filler and stirs, and after being filtered by the mixture after stirring, detects, detect qualified rear for subsequent use to filtrate.