CN105131715A - 陶瓷喷墨打印用水性墨水及其制备方法 - Google Patents

陶瓷喷墨打印用水性墨水及其制备方法 Download PDF

Info

Publication number
CN105131715A
CN105131715A CN201510667026.6A CN201510667026A CN105131715A CN 105131715 A CN105131715 A CN 105131715A CN 201510667026 A CN201510667026 A CN 201510667026A CN 105131715 A CN105131715 A CN 105131715A
Authority
CN
China
Prior art keywords
ceramic
jet printing
ink jet
ink
printing use
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510667026.6A
Other languages
English (en)
Inventor
王护来
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510667026.6A priority Critical patent/CN105131715A/zh
Publication of CN105131715A publication Critical patent/CN105131715A/zh
Pending legal-status Critical Current

Abstract

本发明涉及水性墨水领域，特别涉及一种陶瓷喷墨打印用水性墨水。一种陶瓷喷墨打印用水性墨水，包括陶瓷色母、无机硼酸盐、固体悬浮剂和溶剂。与现有的水性油墨相比，本发明具有以下显著的特点：本发明的水性油墨配方中，巧妙的加入无机硼酸盐作为助色剂，使得所成的水性油墨发色能力更强，同时与釉面结合更牢固。另外在本发明中加入的固体悬浮剂有助于陶瓷色母的进一步分散，使得水性墨水的分散性更好，更不容易堵塞喷头。

Description

陶瓷喷墨打印用水性墨水及其制备方法
技术领域
本发明涉及水性墨水领域，特别涉及一种陶瓷喷墨打印用水性墨水。
背景技术
陶瓷喷墨技术的应用关键之一在于陶瓷墨水的研制，开发亮度强度高、彩色范围宽、打印流畅、稳定性好和安全环保的陶瓷墨水是未来的陶瓷喷墨打印的必然趋势。陶瓷墨水在喷墨时，陶瓷坯体温度较高，陶瓷墨水容易在喷头处凝固造成喷头的堵塞，如何开发出一种不易堵塞喷头的水性墨水是本技术领域的一个难题。
发明内容
本发明所要解决的技术问题是提供一种具有不易堵塞喷头，发色能力强的陶瓷喷墨打印用水性墨水。
本发明的另一个目的是提供上述水性墨水的制备方法。
一种陶瓷喷墨打印用水性墨水，包括陶瓷色母、无机硼酸盐、固体悬浮剂和溶剂。
进一步的，所酸述无机硼酸盐为硼酸钙和硼锌的至少一种。
进一步的，所述固体悬浮剂为亲水型气相二氧化硅。
进一步的，所述溶剂为1,2-丙二醇和二乙二醇单丁醚的混合溶剂。
进一步的，还包括功能助剂。
进一步的，所述功能助剂为消泡剂、防沉剂和流平剂中的至少一种。
进一步的，所述陶瓷喷墨打印用水性墨水的粘度为15～35mpa.s，表面张力为25～40mN/m。
进一步的，所述水性墨水由如下重量百分比的组分组成：
陶瓷色母20～40％；
无机硼酸盐8～12％；
固体悬浮剂2～5％；
溶剂25～40％；
功能助剂0.5～5％；
并用蒸馏水补充至100％。
上述陶瓷喷墨打印用水性墨水的制备方法，包括如下步骤：
将陶瓷色母、无机硼酸盐、固体悬浮剂和部分溶剂均匀混合后转入研磨机研磨，研磨后出浆再加入功能助剂、剩余溶剂和蒸馏水，最后过滤后可得本发明的陶瓷喷墨打印用水性墨水。
进一步的，所述研磨后的细度为D50＜250nm，D90＜800nm。
本发明具有如下有益效果：
与现有的水性油墨相比，本发明具有以下显著的特点：本发明的水性油墨配方中，巧妙的加入无机硼酸盐作为助色剂，使得所成的水性油墨发色能力更强，同时与釉面结合更牢固。另外在本发明中加入的固体悬浮剂有助于陶瓷色母的进一步分散，使得水性墨水的分散性更好，更不容易堵塞喷头。
具体实施方式
下面结合实施例对本发明进行详细的说明，实施例仅是本发明的优选实施方式，不是对本发明的限定。
本发明的制备工艺如无特别说明，均用以下制备方法所得。
将陶瓷色母、无机硼酸盐、固体悬浮剂和部分溶剂均匀混合后转入研磨机研磨，研磨后出浆再加入功能助剂、剩余溶剂和蒸馏水，最后过滤后可得本发明的陶瓷喷墨打印用水性墨水，其中，控制研磨后的细度为D50＜250nm，D90＜800nm。并且控制所得的陶瓷喷墨打印用水性墨水的粘度为15～35mpa.s，表面张力为25～40mN/m。
本发明所用消泡剂、防沉剂和流平剂均为市面常见产品均能实现本发明，按照所需功能添加，在实施例中不再详细描述。
实施例1
一种陶瓷喷墨打印用水性墨水，由如下重量百分比的组分组成：
陶瓷色母37％；硼酸钙8.5％；气相二氧化硅4.5％；1,2-丙二醇25％；二乙二醇单丁醚10％；消泡剂0.5％；防沉剂0.5％；流平剂0.5％；并用蒸馏水补充至100％。
实施例2
一种陶瓷喷墨打印用水性墨水，由如下重量百分比的组分组成：
陶瓷色母25％；硼酸锌11.5％；气相二氧化硅2.5％；1,2-丙二醇20％；二乙二醇单丁醚18％；消泡剂1.5％；防沉剂0.5％；流平剂1.5％；并用蒸馏水补充至100％。
实施例3
一种陶瓷喷墨打印用水性墨水，由如下重量百分比的组分组成：
陶瓷色母31％；硼酸锌10％；气相二氧化硅3.5％；1,2-丙二醇15％；二乙二醇单丁醚13％；消泡剂0.5％；防沉剂1.5％；流平剂1.5％；并用蒸馏水补充至100％。
实施例4
一种陶瓷喷墨打印用水性墨水，由如下重量百分比的组分组成：
陶瓷色母28％；硼酸钙9.5％；气相二氧化硅4％；1,2-丙二醇10％；二乙二醇单丁醚25％；消泡剂0.5％；防沉剂0.5％；流平剂1.5％；并用蒸馏水补充至100％。
上述实施例的水性油墨配方中，巧妙的加入无机硼酸盐作为助色剂，使得所成的水性油墨发色能力更强，同时与釉面结合更牢固。另外在上述实施例中加入的固体悬浮剂有助于陶瓷色母的进一步分散，使得水性墨水的分散性更好，更不容易堵塞喷头。
以上所述实施例仅表达了本发明的实施方式，其描述较为具体和详细，但并不能因此而理解为对本发明专利范围的限制，但凡采用等同替换或等效变换的形式所获得的技术方案，均应落在本发明的保护范围之内。

Claims (10)

1.陶瓷喷墨打印用水性墨水，其特征在于，包括陶瓷色母、无机硼酸盐、固体悬浮剂和溶剂。
2.根据权利要求1所述的陶瓷喷墨打印用水性墨水，其特征在于，所述无机硼酸盐为硼酸钙和硼酸锌的至少一种。
3.根据权利要求2所述的陶瓷喷墨打印用水性墨水，其特征在于，所述固体悬浮剂为亲水型气相二氧化硅。
4.根据权利要求2所述的陶瓷喷墨打印用水性墨水，其特征在于，所述溶剂为1,2-丙二醇和二乙二醇单丁醚的混合溶剂。
5.根据权利要求2所述的陶瓷喷墨打印用水性墨水，其特征在于，还包括功能助剂。
6.根据权利要求5所述的陶瓷喷墨打印用水性墨水，其特征在于，所述功能助剂为消泡剂、防沉剂和流平剂中的至少一种。
7.根据权利要求6所述的陶瓷喷墨打印用水性墨水，其特征在于，所述陶瓷喷墨打印用水性墨水的粘度为15～35mpa.s，表面张力为25～40mN/m。
8.根据权利要求7所述的陶瓷喷墨打印用水性墨水，其特征在于，由如下重量百分比的组分组成：
陶瓷色母20～40％；
无机硼酸盐8～12％；
固体悬浮剂2～5％；
溶剂25～40％；
功能助剂0.5～5％；
并用蒸馏水补充至100％。
9.权利要求8所述的陶瓷喷墨打印用水性墨水的制备方法，其特征在于包括如下步骤：将陶瓷色母、无机硼酸盐、固体悬浮剂和部分溶剂均匀混合后转入研磨机研磨，研磨后出浆再加入功能助剂、剩余溶剂和蒸馏水，最后过滤后可得本发明的陶瓷喷墨打印用水性墨水。
10.根据权利要求9所述的陶瓷喷墨打印用水性墨水的制备方法，其特征在于，所述研磨后的细度为D50＜250nm，D90＜800nm。
CN201510667026.6A 2015-10-15 2015-10-15 陶瓷喷墨打印用水性墨水及其制备方法 Pending CN105131715A (zh)