CN105131681A - High-voltage electrical apparatus insulating surface treating agent - Google Patents
High-voltage electrical apparatus insulating surface treating agent Download PDFInfo
- Publication number
- CN105131681A CN105131681A CN201510625818.7A CN201510625818A CN105131681A CN 105131681 A CN105131681 A CN 105131681A CN 201510625818 A CN201510625818 A CN 201510625818A CN 105131681 A CN105131681 A CN 105131681A
- Authority
- CN
- China
- Prior art keywords
- parts
- phenyl
- voltage electrical
- powder
- electrical appliances
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a high-voltage electrical apparatus insulating surface treating agent which is prepared from the following components in parts by mass: 54 to 58 parts of polyvinyl alcohol, 56 to 60 parts of polyurethane rubber, 52 to 56 parts of rosin modified phenolic resin, 56 to 60 parts of colophony powder, 52 to 56 parts of stearic acid, 56 to 60 parts of polyterpene resin, 52 to 56 parts of parachlorometaxylenol, 58 to 62 parts of hydroxypropyl starch ether, 52 to 56 parts of tert-butyl peroxybenzoate, 56 to 60 parts of acrylamide, 52 to 56 parts of acid graphite, 56 to 60 parts of N-phenyl-2-naphthylamine, 52 to 56 parts of zinc phosphate, 56 to 60 parts of phenyl trichlorosilane, 52 to 56 parts of lead sulfate tribasic, 56 to 60 parts of barium meta-sulfate, 52 to 56 parts of acrylic emulsion, 56 to 60 parts of antimonous oxide, 52 to 56 parts of spodumene powder, 56 to 60 parts of sodium alkyl benzene sulfonate, 52 to 56 parts of sodium pyrophosphate, 56 to 60 parts of glycidol phenyl ether and 1000 to 2000 parts of water. A product prepared by the agent has excellent corrosion resistance, flame retardancy, insulating property and mold resistance, and is suitable for being used in a high-voltage electrical apparatus.
Description
Technical field
The present invention relates to a kind of High-Voltage Electrical Appliances Surface Insulation treatment agent, belong to electrical facility technical field.
Background technology
Increasing along with socioeconomic develop rapidly and High-Voltage Electrical Appliances, High-Voltage Electrical Appliances Insulation Problems is more and more subject to people's attention, and electrical insulation system requires also more and more stricter.The development of Large Copacity generation technology impels the lifting of voltage of power, also constantly makes insulating material progress and optimization.Insulating material not only possesses in the process of application that cementability is good, the solidification process feature that comparatively science, thermotolerance and weather resistance are high, and its erosion resistance, resistance to mechanical intensity are also higher simultaneously, can meet the high-voltage wire construction requirement of various different requirement.
Summary of the invention
The object of the present invention is to provide a kind of High-Voltage Electrical Appliances Surface Insulation treatment agent, to realize the function of High-Voltage Electrical Appliances Surface Insulation treatment agent better.
To achieve these goals, technical scheme of the present invention is as follows.
A kind of High-Voltage Electrical Appliances Surface Insulation treatment agent, be made up of the component of following mass fraction: polyvinyl alcohol 54 ~ 58 parts, urethanes 56 ~ 60 parts, rosin modified phenolic resin 52 ~ 56 parts, colophonium powder 56 ~ 60 parts, stearic acid 52 ~ 56 parts, pinene resin 56 ~ 60 parts, parachlormetaxylenol 52 ~ 56 parts, hydroxypropyl starch ether 58 ~ 62 parts, peroxidized t-butyl perbenzoate 52 ~ 56 parts, acrylamide 56 ~ 60 parts, acidifying graphite 52 ~ 56 parts, N-phenyl-2-naphthylamine 56 ~ 60 parts, zinc phosphate 52 ~ 56 parts, phenyl-trichloro-silicane 56 ~ 60 parts, lead sulfate tribasic 52 ~ 56 parts, 56 ~ 60 parts, inclined barium sulfate, ACRYLIC EMULSION 52 ~ 56 parts, antimonous oxide 56 ~ 60 parts, 52 ~ 56 parts, triphane powder, sodium alkyl benzene sulfonate 56 ~ 60 parts, trisodium phosphate 52 ~ 56 parts, propylene oxide phenyl ether 56 ~ 60 parts, 1000 ~ 2000 parts, water.
Further, above-mentioned High-Voltage Electrical Appliances Surface Insulation treatment agent, be made up of the component of following mass fraction: polyvinyl alcohol 54 parts, urethanes 56 parts, rosin modified phenolic resin 52 parts, colophonium powder 56 parts, stearic acid 52 parts, pinene resin 56 parts, parachlormetaxylenol 52 parts, hydroxypropyl starch ether 58 parts, peroxidized t-butyl perbenzoate 52 parts, acrylamide 56 parts, acidifying graphite 52 parts, N-phenyl-2-naphthylamine 56 parts, zinc phosphate 52 parts, phenyl-trichloro-silicane 56 parts, lead sulfate tribasic 52 parts, 56 parts, inclined barium sulfate, ACRYLIC EMULSION 52 parts, antimonous oxide 56 parts, 52 parts, triphane powder, sodium alkyl benzene sulfonate 56 parts, trisodium phosphate 52 parts, propylene oxide phenyl ether 56 parts, 1000 parts, water.
Further, above-mentioned High-Voltage Electrical Appliances Surface Insulation treatment agent, be made up of the component of following mass fraction: polyvinyl alcohol 56 parts, urethanes 58 parts, rosin modified phenolic resin 54 parts, colophonium powder 58 parts, stearic acid 54 parts, pinene resin 58 parts, parachlormetaxylenol 54 parts, hydroxypropyl starch ether 60 parts, peroxidized t-butyl perbenzoate 54 parts, acrylamide 58 parts, acidifying graphite 54 parts, N-phenyl-2-naphthylamine 58 parts, zinc phosphate 54 parts, phenyl-trichloro-silicane 58 parts, lead sulfate tribasic 54 parts, 58 parts, inclined barium sulfate, ACRYLIC EMULSION 54 parts, antimonous oxide 58 parts, 54 parts, triphane powder, sodium alkyl benzene sulfonate 58 parts, trisodium phosphate 54 parts, propylene oxide phenyl ether 58 parts, 1500 parts, water.
Further, above-mentioned High-Voltage Electrical Appliances Surface Insulation treatment agent, be made up of the component of following mass fraction: polyvinyl alcohol 58 parts, urethanes 60 parts, rosin modified phenolic resin 56 parts, colophonium powder 60 parts, stearic acid 56 parts, pinene resin 60 parts, parachlormetaxylenol 56 parts, hydroxypropyl starch ether 62 parts, peroxidized t-butyl perbenzoate 56 parts, acrylamide 60 parts, acidifying graphite 56 parts, N-phenyl-2-naphthylamine 60 parts, zinc phosphate 56 parts, phenyl-trichloro-silicane 60 parts, lead sulfate tribasic 56 parts, 60 parts, inclined barium sulfate, ACRYLIC EMULSION 56 parts, antimonous oxide 60 parts, 56 parts, triphane powder, sodium alkyl benzene sulfonate 60 parts, trisodium phosphate 56 parts, propylene oxide phenyl ether 60 parts, 2000 parts, water.
Further, above-mentioned High-Voltage Electrical Appliances Surface Insulation treatment agent preparation method step is as follows:
(1) by the polyvinyl alcohol of described mass fraction, urethanes, rosin modified phenolic resin, stearic acid, pinene resin, parachlormetaxylenol, hydroxypropyl starch ether, peroxidized t-butyl perbenzoate, acrylamide, acidifying graphite, N-phenyl-2-naphthylamine, zinc phosphate, phenyl-trichloro-silicane, lead sulfate tribasic, inclined barium sulfate, ACRYLIC EMULSION, antimonous oxide, sodium alkyl benzene sulfonate, trisodium phosphate, propylene oxide phenyl ether adds in the water of above-mentioned mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion about 5000 ~ 5400r/min, jitter time is 30 ~ 60min,
(2) add the triphane powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion about 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the colophonium powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion about 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix rear obtained this product.
Above-mentioned each component function is as follows:
(1) polyvinyl alcohol: organic compound, white plates, cotton-shaped or pulverulent solids, tasteless.Water-soluble, be insoluble to gasoline, kerosene, vegetables oil, benzene, toluene, ethylene dichloride, tetracol phenixin, acetone, vinyl acetic monomer, methyl alcohol, ethylene glycol etc.Be slightly soluble in dimethyl sulfoxide (DMSO).Polyvinyl alcohol is important industrial chemicals, for the manufacture of polyvinyl acetal, resistance to gasoline pipeline and vinylon synthon, fabric-treating agent, emulsifying agent, paper coating, tackiness agent, glue etc.
(2) urethanes: the advantage such as have that hardness is high, intensity good, snappiness, high-wearing feature, tear-resistant, ageing-resistant, resistance to ozone, radiation hardness and good electroconductibility, adhesiveproperties are excellent, is widely used in stamping-out, bending, shallow recessing, shallow drawing and molding procedure.
(3) rosin modified phenolic resin: the macromolecule product carrying out chemical reaction generation with alkylphenol, formaldehyde, polyvalent alcohol and rosin.Due to the polynuclear plane feature of its uniqueness, there is good pigment wetting performance, react with suitable gelifying agent simultaneously and can obtain certain viscoelastic binder and be thus widely used in offset litho printing ink, the direct gloss affecting printing-ink, dryness, water resisting property, viscosity, rheological, printing performance etc., at present for flexographic ink.
(4) colophonium powder: to tap from pine trunk and the resin obtained is made through pulverizing, main component is sylvic acid.Viscosifying power is very strong, under the condition of heating and pressurizing, and this product fusing and by thermoprint material binding by boiling hot body surface.
(5) stearic acid: sterling is the wax-like small pieces xln of white slightly gloss.Be slightly soluble in cold water, be dissolved in alcohol, acetone, be soluble in benzene, chloroform, ether, tetracol phenixin, dithiocarbonic anhydride, amyl acetate-n and toluene etc.Nontoxic.Be widely used in inhibition and generation cosmetic, plastics cold resistant plasticizer, releasing agent, stablizer, tensio-active agent, thiofide, water-resisting agent, rumbling compound, metallic soap, metalliferous mineral flotation agent, tenderizer, pharmaceuticals and other organic chemicals.
(6) pinene resin: transparent brittle solid resin, nontoxic, odorless, anti-olefin(e) acid, anti-diluted alkaline, have good thermostability and electrical insulating property.
(7) parachlormetaxylenol: a kind of antimildew and antibacterial agent of wide spectrum, to most Gram-positive, negative bacterium, fungi, mould kills effect, it can be used as antimildew and antibacterial agent and is widely used in sterilization or personal-care supplies, as anti-dandruff shampoo, in the antibacterial detergents such as Liquid soap, soap and other sanitary product.Also the industrial circles such as glue, product, paint, weaving, leather, papermaking can be used for as sanitas and mould inhibitor.
(8) hydroxypropyl starch ether: a kind of is raw material with natural phant, the white fine powder obtained through modification, highly etherification reaction, then spraying dry, not plasticizer-containing.Good fast thickening ability; Medium-viscosity, has certain water-retentivity; Consumption is little, and extremely low addition can reach very high effect; As tackiness agent, suspension agent and thickening material.
(9) peroxidized t-butyl perbenzoate: colourless to micro-yellow liquid.Slightly aromatic odour.Water insoluble, can organic solvent be dissolved in.Be widely used in such as ethene, vinylbenzene, in the polymerization processes such as propylene, vinyl acetate between to for plastic, Phthalic acid, diallyl ester and iso-butylene, be used as initiator.In curable unsaturated polyester process, be widely used in and draw in the moulding processs such as agent as SMC, BMC, DMC, also can apply with the composition curing systems as two in compositions such as MEPK, BPO or TBPO that some activity are higher meanwhile.
(10) acrylamide: a kind of white crystal chemical substance is the raw material producing polyacrylamide.By machinery, physics, chemistry effect, rise adhesive effect.
(11) acidifying graphite: there are flexibility, spreadability, heat retaining property, compression resilience, autohension etc.Its purposes widely, is do the indispensable raw material of graphite series refractory materials, also can be used as graphite paper, weaving graphite line, various graphite gasket and the sealing material for the run, drip, leak of high pressure position.
(12) N-phenyl-2-naphthylamine: light grey needle crystal or powder, has ammonia taste, water insoluble, is dissolved in ethanol, acetone, benzene.As natural rubber, elastomeric anti-aging agent, to oxygen, heat seal deflects cause aging protective benefits, has certain restraining effect to poisonous metal.
(13) zinc phosphate: colourless oblique square crystal or white micro-crystals powder, be corrosive and deliquescence.Be dissolved in mineral acid, ammoniacal liquor, ammonium salt solution; Be insoluble to ethanol; Almost insoluble in water.As the base-material of the various products such as alcohol aldehyde, phenolic aldehyde, epoxy resin, the fire retardant of chlorinated rubber, synthesized polymer material, also for the production of water-soluble products and non-poisonous antirust pigment.
(14) phenyl-trichloro-silicane: colourless liquid, is dissolved in benzene, ether treats most organic solvent, for the manufacture of silicone intermediate and produce phenyl polysiloxane.
(15) lead sulfate tribasic: white or micro-yellow powder.Water insoluble and organic solvent, dissolves in hot ammonium acetate and bases, and nitric acid, Thickish hot hydrochloric acid.Without flammable and corrodibility, easy moisture absorption, decomposes by solar radiation variable color under dampness.This product has stabilization to polyvinyl chloride, and has excellent thermotolerance and electrical insulating property, and its light fastness, is particularly suitable for high temperature process.Due to its excellent property, be widely used in vinyl electrical material, and be specially adapted to make electric wire, cable etc.
(16) inclined barium sulfate: colourless orthorhombic system crystals or white amorphous powder.Water-soluble, ethanol and acid hardly.Be dissolved in hot concentrated sulfuric acid.For industry such as powder-product, paint, ink, pigment, rubber, store battery, plastics and art papers.
(17) ACRYLIC EMULSION: shallow white translucent emulsion, nontoxic, non-stimulated, harmless, meet environmental requirement, non-film height photopolymer resin, have excellent gloss and the transparency, antiblocking performance is good.Galvanic deposit product, for the binding agent of metal water-miscible paint, plastics water-miscible paint.
(18) antimonous oxide: white powder, water insoluble, be dissolved in sodium hydroxide solution and acid.For white pigment, paint and plastics, play pigment and fire-retardant.
(19) triphane powder: have stable, resistance to thermal property, as lithium chemical preparations raw material, is widely used in lithiumation work, glass, ceramic industry.
(20) sodium alkyl benzene sulfonate: aniorfic surfactant.Because production cost is low, performance is good, thus of many uses, be the maximum synthetic surfactant of household detergent consumption, also produce the organic amine salts such as inorganic salt and trolamine such as a part of magnesium, calcium.
(21) trisodium phosphate: water white transparency crystallization or white crystalline powder.Soluble in water, its aqueous solution is in alkalescence; Be insoluble to alcohol.It has the phosphatic general character of General polymeric, and the being knotted property of the protein that namely has emulsifying property, dispersiveness, prevents fats oxidn, improves, also has and suppress the oxidation of food and the effect of fermentation at a high ph.Dispersion agent and emulsifying agent is used as in Chemical Manufacture.Also can be used for the aspect such as water conditioner, oil drilling, in the food industry as quality improver, emulsifying agent, buffer reagent, sequestrant etc.
(22) propylene oxide phenyl ether: colourless transparent liquid, is soluble in ether, benzene, water insoluble.As the reactive thinner of epoxy resin adhesive, the intermediate of organic synthesis.
This beneficial effect of the invention is: these High-Voltage Electrical Appliances Surface Insulation treatment agent process of preparing is simple, and the product prepared by the present invention has good corrosion-resistant fire retardant insulating anti-microbial property, is adapted at using in High-Voltage Electrical Appliances.。
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is described, better to understand the present invention.
embodiment 1
High-Voltage Electrical Appliances Surface Insulation treatment agent in the present embodiment, be made up of the component of following mass fraction: polyvinyl alcohol 54 parts, urethanes 56 parts, rosin modified phenolic resin 52 parts, colophonium powder 56 parts, stearic acid 52 parts, pinene resin 56 parts, parachlormetaxylenol 52 parts, hydroxypropyl starch ether 58 parts, peroxidized t-butyl perbenzoate 52 parts, acrylamide 56 parts, acidifying graphite 52 parts, N-phenyl-2-naphthylamine 56 parts, zinc phosphate 52 parts, phenyl-trichloro-silicane 56 parts, lead sulfate tribasic 52 parts, 56 parts, inclined barium sulfate, ACRYLIC EMULSION 52 parts, antimonous oxide 56 parts, 52 parts, triphane powder, sodium alkyl benzene sulfonate 56 parts, trisodium phosphate 52 parts, propylene oxide phenyl ether 56 parts, 1000 parts, water.
Above-mentioned High-Voltage Electrical Appliances Surface Insulation treatment agent preparation method step is as follows:
(1) by the polyvinyl alcohol of described mass fraction, urethanes, rosin modified phenolic resin, stearic acid, pinene resin, parachlormetaxylenol, hydroxypropyl starch ether, peroxidized t-butyl perbenzoate, acrylamide, acidifying graphite, N-phenyl-2-naphthylamine, zinc phosphate, phenyl-trichloro-silicane, lead sulfate tribasic, inclined barium sulfate, ACRYLIC EMULSION, antimonous oxide, sodium alkyl benzene sulfonate, trisodium phosphate, propylene oxide phenyl ether adds in the water of above-mentioned mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5400r/min, jitter time is 60min,
(2) add the triphane powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min;
(3) add the colophonium powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min; Mix rear obtained this product.
embodiment 2
High-Voltage Electrical Appliances Surface Insulation treatment agent in the present embodiment, be made up of the component of following mass fraction: polyvinyl alcohol 56 parts, urethanes 58 parts, rosin modified phenolic resin 54 parts, colophonium powder 58 parts, stearic acid 54 parts, pinene resin 58 parts, parachlormetaxylenol 54 parts, hydroxypropyl starch ether 60 parts, peroxidized t-butyl perbenzoate 54 parts, acrylamide 58 parts, acidifying graphite 54 parts, N-phenyl-2-naphthylamine 58 parts, zinc phosphate 54 parts, phenyl-trichloro-silicane 58 parts, lead sulfate tribasic 54 parts, 58 parts, inclined barium sulfate, ACRYLIC EMULSION 54 parts, antimonous oxide 58 parts, 54 parts, triphane powder, sodium alkyl benzene sulfonate 58 parts, trisodium phosphate 54 parts, propylene oxide phenyl ether 58 parts, 1500 parts, water.
Above-mentioned High-Voltage Electrical Appliances Surface Insulation treatment agent preparation method step is as follows:
(1) by the polyvinyl alcohol of described mass fraction, urethanes, rosin modified phenolic resin, stearic acid, pinene resin, parachlormetaxylenol, hydroxypropyl starch ether, peroxidized t-butyl perbenzoate, acrylamide, acidifying graphite, N-phenyl-2-naphthylamine, zinc phosphate, phenyl-trichloro-silicane, lead sulfate tribasic, inclined barium sulfate, ACRYLIC EMULSION, antimonous oxide, sodium alkyl benzene sulfonate, trisodium phosphate, propylene oxide phenyl ether adds in the water of above-mentioned mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 5200r/min, jitter time is 45min,
(2) add the triphane powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min;
(3) add the colophonium powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min; Mix rear obtained this product.
embodiment 3
High-Voltage Electrical Appliances Surface Insulation treatment agent in the present embodiment, be made up of the component of following mass fraction: polyvinyl alcohol 58 parts, urethanes 60 parts, rosin modified phenolic resin 56 parts, colophonium powder 60 parts, stearic acid 56 parts, pinene resin 60 parts, parachlormetaxylenol 56 parts, hydroxypropyl starch ether 62 parts, peroxidized t-butyl perbenzoate 56 parts, acrylamide 60 parts, acidifying graphite 56 parts, N-phenyl-2-naphthylamine 60 parts, zinc phosphate 56 parts, phenyl-trichloro-silicane 60 parts, lead sulfate tribasic 56 parts, 60 parts, inclined barium sulfate, ACRYLIC EMULSION 56 parts, antimonous oxide 60 parts, 56 parts, triphane powder, sodium alkyl benzene sulfonate 60 parts, trisodium phosphate 56 parts, propylene oxide phenyl ether 60 parts, 2000 parts, water.
Above-mentioned High-Voltage Electrical Appliances Surface Insulation treatment agent preparation method step is as follows:
(1) by the polyvinyl alcohol of described mass fraction, urethanes, rosin modified phenolic resin, stearic acid, pinene resin, parachlormetaxylenol, hydroxypropyl starch ether, peroxidized t-butyl perbenzoate, acrylamide, acidifying graphite, N-phenyl-2-naphthylamine, zinc phosphate, phenyl-trichloro-silicane, lead sulfate tribasic, inclined barium sulfate, ACRYLIC EMULSION, antimonous oxide, sodium alkyl benzene sulfonate, trisodium phosphate, propylene oxide phenyl ether adds in the water of above-mentioned mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, jitter time is 30min,
(2) add the triphane powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min;
(3) add the colophonium powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is 20min; Mix rear obtained this product.
Carry out performance measurement for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, measured data are as shown in table 1.Fire protection flame retarding level estimate adopts UL94 standard.
Table 1 the performance test results
Visible, product of the present invention have preferably corrosion-resistant, fire-retardant, insulation, anti-microbial property.
The above is the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.
Claims (5)
1. a High-Voltage Electrical Appliances Surface Insulation treatment agent, it is characterized in that: be made up of the component of following mass fraction: polyvinyl alcohol 54 ~ 58 parts, urethanes 56 ~ 60 parts, rosin modified phenolic resin 52 ~ 56 parts, colophonium powder 56 ~ 60 parts, stearic acid 52 ~ 56 parts, pinene resin 56 ~ 60 parts, parachlormetaxylenol 52 ~ 56 parts, hydroxypropyl starch ether 58 ~ 62 parts, peroxidized t-butyl perbenzoate 52 ~ 56 parts, acrylamide 56 ~ 60 parts, acidifying graphite 52 ~ 56 parts, N-phenyl-2-naphthylamine 56 ~ 60 parts, zinc phosphate 52 ~ 56 parts, phenyl-trichloro-silicane 56 ~ 60 parts, lead sulfate tribasic 52 ~ 56 parts, 56 ~ 60 parts, inclined barium sulfate, ACRYLIC EMULSION 52 ~ 56 parts, antimonous oxide 56 ~ 60 parts, 52 ~ 56 parts, triphane powder, sodium alkyl benzene sulfonate 56 ~ 60 parts, trisodium phosphate 52 ~ 56 parts, propylene oxide phenyl ether 56 ~ 60 parts, 1000 ~ 2000 parts, water.
2. High-Voltage Electrical Appliances Surface Insulation treatment agent according to claim 1, it is characterized in that: described High-Voltage Electrical Appliances Surface Insulation treatment agent is made up of the component of following mass fraction: polyvinyl alcohol 54 parts, urethanes 56 parts, rosin modified phenolic resin 52 parts, colophonium powder 56 parts, stearic acid 52 parts, pinene resin 56 parts, parachlormetaxylenol 52 parts, hydroxypropyl starch ether 58 parts, peroxidized t-butyl perbenzoate 52 parts, acrylamide 56 parts, acidifying graphite 52 parts, N-phenyl-2-naphthylamine 56 parts, zinc phosphate 52 parts, phenyl-trichloro-silicane 56 parts, lead sulfate tribasic 52 parts, 56 parts, inclined barium sulfate, ACRYLIC EMULSION 52 parts, antimonous oxide 56 parts, 52 parts, triphane powder, sodium alkyl benzene sulfonate 56 parts, trisodium phosphate 52 parts, propylene oxide phenyl ether 56 parts, 1000 parts, water.
3. according to the High-Voltage Electrical Appliances Surface Insulation treatment agent described in claim 1 to 2, it is characterized in that: described High-Voltage Electrical Appliances Surface Insulation treatment agent is made up of the component of following mass fraction: polyvinyl alcohol 56 parts, urethanes 58 parts, rosin modified phenolic resin 54 parts, colophonium powder 58 parts, stearic acid 54 parts, pinene resin 58 parts, parachlormetaxylenol 54 parts, hydroxypropyl starch ether 60 parts, peroxidized t-butyl perbenzoate 54 parts, acrylamide 58 parts, acidifying graphite 54 parts, N-phenyl-2-naphthylamine 58 parts, zinc phosphate 54 parts, phenyl-trichloro-silicane 58 parts, lead sulfate tribasic 54 parts, 58 parts, inclined barium sulfate, ACRYLIC EMULSION 54 parts, antimonous oxide 58 parts, 54 parts, triphane powder, sodium alkyl benzene sulfonate 58 parts, trisodium phosphate 54 parts, propylene oxide phenyl ether 58 parts, 1500 parts, water.
4. the High-Voltage Electrical Appliances Surface Insulation treatment agent according to claims 1 to 3, it is characterized in that: described High-Voltage Electrical Appliances Surface Insulation treatment agent is made up of the component of following mass fraction: polyvinyl alcohol 58 parts, urethanes 60 parts, rosin modified phenolic resin 56 parts, colophonium powder 60 parts, stearic acid 56 parts, pinene resin 60 parts, parachlormetaxylenol 56 parts, hydroxypropyl starch ether 62 parts, peroxidized t-butyl perbenzoate 56 parts, acrylamide 60 parts, acidifying graphite 56 parts, N-phenyl-2-naphthylamine 60 parts, zinc phosphate 56 parts, phenyl-trichloro-silicane 60 parts, lead sulfate tribasic 56 parts, 60 parts, inclined barium sulfate, ACRYLIC EMULSION 56 parts, antimonous oxide 60 parts, 56 parts, triphane powder, sodium alkyl benzene sulfonate 60 parts, trisodium phosphate 56 parts, propylene oxide phenyl ether 60 parts, 2000 parts, water.
5. the High-Voltage Electrical Appliances Surface Insulation treatment agent according to claim 1 or 4, is characterized in that: described High-Voltage Electrical Appliances Surface Insulation treatment agent preparation method step is as follows:
(1) by the polyvinyl alcohol of described mass fraction, urethanes, rosin modified phenolic resin, stearic acid, pinene resin, parachlormetaxylenol, hydroxypropyl starch ether, peroxidized t-butyl perbenzoate, acrylamide, acidifying graphite, N-phenyl-2-naphthylamine, zinc phosphate, phenyl-trichloro-silicane, lead sulfate tribasic, inclined barium sulfate, ACRYLIC EMULSION, antimonous oxide, sodium alkyl benzene sulfonate, trisodium phosphate, propylene oxide phenyl ether adds in the water of above-mentioned mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion about 5000 ~ 5400r/min, jitter time is 30 ~ 60min,
(2) add the triphane powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion about 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the colophonium powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion about 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix rear obtained this product.