CN105128579A - Processing technology of heavy bamboo paper weights - Google Patents
Processing technology of heavy bamboo paper weights Download PDFInfo
- Publication number
- CN105128579A CN105128579A CN201510536337.9A CN201510536337A CN105128579A CN 105128579 A CN105128579 A CN 105128579A CN 201510536337 A CN201510536337 A CN 201510536337A CN 105128579 A CN105128579 A CN 105128579A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- heavy
- paperweight
- processing technology
- heavy bamboo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a processing technology of heavy bamboo paper weights. The processing technology comprises the following steps: washing, air-drying, cutting, carbonizing and crushing a bamboo raw material so as to obtain bamboo particles; crushing cinnamomum camphora presl into cinnamomum camphora presl particles; mixing the cinnamomum camphora presl particles into the bamboo particles according to a ratio of 1-2: 10, uniformly mixing, spreading the mixed particles, spraying an adhesive, and drying so as to obtain a plywood; cutting the plywood, stacking the cut plywood according to the thickness requirement, putting the plywood into a die, and molding through hot-press so as to obtain a heavy bamboo board; sawing the heavy bamboo board into heavy bamboo paper weight blanks according to the size of the paper weights, drying, putting the heavy bamboo paper weight blanks into a mixed wax solution consisting of liquid wax, palm oil and glycerinum to be soaked, taking out and drying; and grinding, polishing and engraving by laser the bamboo paper weight paper blanks having been soaked in the wax so as to obtain the heavy bamboo paper weights. The production technology is simple to operate, the raw materials are easy to obtain, and the produced heavy bamboo paper weights have high density and high hardness, can prevent worms and repel water, are attractive, elegant and bright, and feel great.
Description
Technical field
The present invention relates to bamboo product manufacture field, be specially a kind of processing technology of heavy bamboo paperweight.
Background technology
Bamboo, has another name called bamboo, originates in from China.Various in style, perennial gramineous bamboo department linoleic plant, stem is wooden, is a branch gramineous, is distributed in tropical and subtropical region, and East Asia, Southeast Asia and the Indian Ocean and Pacific Islands distribute the most concentrated, kind is a lot.Bamboo branch bar is tall and straight, slender, and the four seasons are verdant, the proud rain of Ling Shuan, and extremely Chinese like, with plum, orchid, chrysanthemum be called four gentleman, with plum, pine be called three durable plants of winter: pine, bamboo and plum blossom, the men of literature and writing at all times, likes that bamboo chants bamboo person numerous.
Paperweight is ancient Chinese Han nationality traditional arts and crafts.Refer to write in order to the thing of platen when drawing a picture, common mostly is rectangular bar shaped, for some reason also referred to as paperweight, nose bar.Initial paperweight is not solid shape.The origin of paperweight is because scholar in ancient times often can be placed on small-sized bronze ware, jadeware on desk and play appreciation; because they have certain component, people are while enjoying, also can be used for smoothly platen or pressure book; in the course of time, a kind of study articles-paperweight is developed into.Because bamboo has unique cultural connotation, Chinese have again special liking to bamboo, and bamboo has again convenience of drawing materials, cheap feature simultaneously, so bamboo paperweight is very by the welcome of Chinese scholar.
Having special requirement as paperweight, first must have certain weight, is secondly certain color and cultural connotation, and therefore bamboo paperweight also must have above attribute just can be accepted.
Summary of the invention
The object of this invention is to provide a kind of processing technology of heavy bamboo paperweight, the processing technology of the heavy bamboo paperweight of this invention, method is simple, is applicable to mechanically actuated, and it is high that the heavy bamboo paperweight of processing has density, and hardness is strong, the effect of waterproof insectproof, while elegance attractive in appearance.
The object of the invention is to be achieved through the following technical solutions:
The processing technology of a kind of heavy bamboo paperweight of the present invention, comprises the following steps:
(1) rinsed well by raw material bamboo water, dry, block, carbonization in carbide furnace, the bamboo after carbonization is crushed to particle diameter within 2mm, obtained bamboo particle;
(2) lignum cinnamomi camphorae water is rinsed well, dry, block, be crushed to particle diameter within 2mm, obtained lignum cinnamomi camphorae particle;
(3) be incorporated in bamboo particle in the ratio of 1 ~ 2:10 by lignum cinnamomi camphorae particle, mix, spread out by hybrid particles, thickness is at 1.0 ~ 1.5mm, and glue spraying, dries 1 ~ 2 hour, obtain glued board at 45 ~ 50 DEG C of temperature;
(4) size of glued board according to mould is cut, according to thickness requirement, the glued board after cutting is stacked die-filling, hot-forming, obtained heavy bamboo clappers;
(5) heavy bamboo clappers is pressed the size sawing Cheng Chongzhu paperweight base of paperweight, dry, put into blended wax liquid and soak 10 ~ 12 hours, take out, dry;
Described blended wax liquid, comprises following component and forms by weight: atoleine 85 ~ 90 parts, palm oil 5 ~ 10 parts, glycerine 3 ~ 5 parts;
(6) by bamboo paperweight base sanding and polishing heavy after waxdip, laser engraving, to obtain final product.
Preferably, raw material bamboo described in described step (1) can be the bamboo of various quality or the leftover bits and pieces of bamboo.
Preferably, carbonization described in described step (1) is specially and is blocked by raw material bamboo, puts into carbide furnace, by the steam treated 40 ~ 60 minutes of about 0.5Mpa pressure.
Preferably, phenolic resin glue is used in glue spraying step described in described step (3).
Preferably, described in described step (4), the hot-forming hot pressing temperature that is specially is 180 ~ 200 DEG C, and pressure is hot pressing under the condition of 80 ~ 100Mpa.
Preferably, oven dry described in described step (5) is specially and dries 1 ~ 2 hour at 70 ~ 80 DEG C of temperature.
Advantage of the present invention:
1. this processing technology is simple to operate, is applicable to mechanically actuated, and be beneficial to factory normalization and produce, obtained heavy bamboo paperweight density is large, hardness is high, has texture, elegant in appearance, and platen is effective.
2. this processing technology, can use various bamboo or bamboo leftover bits and pieces as raw material, and the utilization rate improving bamboo is high.
3. this processing technology, by carbonization, makes starch in bamboo wood, breaks down proteins, makes moth and mould lose source of nutrition, kills worm's ovum and fungi simultaneously, and after process, bamboo wood is bronze-colored or coffee-like.
4. this processing technology, by adding a certain amount of lignum cinnamomi camphorae particle as raw material, can insect protected, there is the fragrance of fragrant camphor tree simultaneously.
5. this processing technology, heavy bamboo paperweight base, by waxdip, can play good waterproof effect, and simultaneously obtained after waxdip sanding and polishing heavy bamboo paperweight, feel is lubricated, and has good brightness.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment
Collect the leftover bits and pieces of various bamboo or bamboo as raw material bamboo, produce according to the following steps:
(1) raw material bamboo water is rinsed well, dry, block, carbonization in carbide furnace, by carbonization, makes starch in bamboo wood, breaks down proteins, make moth and mould lose source of nutrition, kill worm's ovum and fungi simultaneously, after process, bamboo wood is bronze-colored or coffee-like.
Bamboo after carbonization is crushed to particle diameter within 2mm, obtained bamboo particle;
(2) lignum cinnamomi camphorae water is rinsed well, dry, block, be crushed to particle diameter within 2mm, obtained lignum cinnamomi camphorae particle;
(3) be incorporated in bamboo particle in the ratio of 1 ~ 2:10 by lignum cinnamomi camphorae particle, mix, spread out by hybrid particles, thickness is at 1.0 ~ 1.5mm, and glue spraying, dries 1 ~ 2 hour, obtain glued board at 45 ~ 50 DEG C of temperature; By adding a certain amount of lignum cinnamomi camphorae particle as raw material, can insect protected, there is the fragrance of fragrant camphor tree simultaneously.
(4) size of glued board according to mould cut, according to thickness requirement, stack die-filling by the glued board after cutting, hot-forming, hot pressing temperature is 180 ~ 200 DEG C, and pressure is 80 ~ 100Mpa, obtained heavy bamboo clappers;
(5) heavy bamboo clappers is pressed the size sawing Cheng Chongzhu paperweight base of paperweight, dry, dry 1 ~ 2 hour at 70 ~ 80 DEG C of temperature, put in the blended wax liquid prepared and soak 10 ~ 12 hours, take out, dry;
Preparation blended wax liquid, get following composition by weight: atoleine 85 ~ 90 parts, palm oil 5 ~ 10 parts, glycerine 3 ~ 5 parts, heating and melting, is fully uniformly mixed;
Heavy bamboo paperweight base, by waxdip, can play good waterproof effect, and simultaneously obtained after waxdip sanding and polishing heavy bamboo paperweight, feel is lubricated, and has good brightness.
(6) by bamboo paperweight base sanding and polishing heavy after waxdip, laser engraving, to obtain final product.
Claims (6)
1. a processing technology for heavy bamboo paperweight, is characterized in that: comprise the following steps:
(1) rinsed well by raw material bamboo water, dry, block, carbonization in carbide furnace, the bamboo after carbonization is crushed to particle diameter within 2mm, obtained bamboo particle;
(2) lignum cinnamomi camphorae water is rinsed well, dry, block, be crushed to particle diameter within 2mm, obtained lignum cinnamomi camphorae particle;
(3) be incorporated in bamboo particle in the ratio of 1 ~ 2:10 by lignum cinnamomi camphorae particle, mix, spread out by hybrid particles, thickness is at 1.0 ~ 1.5mm, and glue spraying, dries 1 ~ 2 hour, obtain glued board at 45 ~ 50 DEG C of temperature;
(4) size of glued board according to mould is cut, according to thickness requirement, the glued board after cutting is stacked die-filling, hot-forming, obtained heavy bamboo clappers;
(5) heavy bamboo clappers is pressed the size sawing Cheng Chongzhu paperweight base of paperweight, dry, put into blended wax liquid and soak 10 ~ 12 hours, take out, dry;
Described blended wax liquid, comprises following component and forms by weight: atoleine 85 ~ 90 parts, palm oil 5 ~ 10 parts, glycerine 3 ~ 5 parts;
(6) by bamboo paperweight base sanding and polishing heavy after waxdip, laser engraving, to obtain final product.
2. the processing technology of heavy bamboo paperweight according to claim 1, is characterized in that: raw material bamboo described in described step (1) can be the bamboo of various quality or the leftover bits and pieces of bamboo.
3. the processing technology of heavy bamboo paperweight according to claim 1, is characterized in that: carbonization described in described step (1) is specially and is blocked by bamboo, puts into carbide furnace, by the steam treated 40 ~ 60 minutes of about 0.5Mpa pressure.
4. the processing technology of heavy bamboo paperweight according to claim 1, is characterized in that: use phenolic resin glue in glue spraying step described in described step (3).
5. the processing technology of heavy bamboo paperweight according to claim 1, is characterized in that: described in described step (4), the hot-forming hot pressing temperature that is specially is 180 ~ 200 DEG C, and pressure is hot pressing under the condition of 80 ~ 100Mpa.
6. the processing technology of heavy bamboo paperweight according to claim 1, is characterized in that: dry described in described step (5) to be specially and dry 1 ~ 2 hour at 70 ~ 80 DEG C of temperature.