CN105128551A - Preparation method for surface-printed button - Google Patents
Preparation method for surface-printed button Download PDFInfo
- Publication number
- CN105128551A CN105128551A CN201510553005.1A CN201510553005A CN105128551A CN 105128551 A CN105128551 A CN 105128551A CN 201510553005 A CN201510553005 A CN 201510553005A CN 105128551 A CN105128551 A CN 105128551A
- Authority
- CN
- China
- Prior art keywords
- button
- preparation
- paint
- present
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a preparation method for a surface-printed button. The preparation method is characterized by comprising the following steps: firstly, carrying out pre-treatment on button blank to obtain an original button of the button; and carrying out UV flat-plate printing on the surface of the original button, obtained in the last step, of the button to obtain the surface-printed button. The preparation method adopts a UV flat-plate printing mode, namely a color flat-plate printing process, also named as a color stacking process to replace a current process for printing UV printing ink onto the button, so that the surface-printed button is obtained by virtue of a special paint-spraying and pre-treatment and post-treatment mode. The surface-printed button prepared by the preparation method can be printed at the surface to have different colors which can be matched to to form different patterns, and therefore, the surface-printed button has obvious changeable color effect.
Description
Technical field
The invention belongs to garment production technical field, particularly relate to a kind of preparation method of printout surface button.
Background technology
Button is exactly fastener connected for the both sides hem on clothes, its initial effect is used to the left front of connecting clothing, now developing into gradually and have more artistry and ornamental except its original function of maintenance, is also the representative of the personalized and multifunction of dress ornament.Along with fashion elements constantly substitutes, the continuous change of fashion dress ornament, the manufacture craft of button is increasingly exquisite, and clothing button is also further exquisite,
Button, by the classification of its material, can be divided into natural class, chemical and other materials, this wherein chemical button be divided into again organicly to buckle, resin button, combination is buckled, urea is buckled, spray paint and buckle, electroplate and buckle, buckle by the emperor himself.Along with the fast development of button industry, require also day by day to improve to button, need to have that wearability is good, heat-resisting quantity is good, good corrosion resistance and kind miscellaneous, and the vivid feature such as beautiful of color of light, and sometimes also need reply clothes to produce a lot of different style, the button that shape is very strange.Thus, also go on the market one after another with the various button that various material makes, bucket victory is striven very, as gold-plated button, silver-plated button, screw buckle, engraving button, enameling button, material button etc., valuable also have white jade Buddha's hand button, pearl button covered with gold leaf, three inlaid with jade buttons, embedding golden agate button and coral button, beeswax button, amber button etc. are also had even to also have diamond button.The decorative pattern of button is also rich and varied, such as rolls over branch flowers, happiness,position and longevity auspiciousness etc., has everything, meet the different requirements of various fashion dress ornament.
At this wherein, the surface color button of various material is the button pattern that demand is larger, surface color button refers to paints on the surface of button, can be that planar monolayer colouring may also be multilayer colouring, thus form the effect with various colour image on button surface, and after multilayer colouring, similar color solid effect can also be formed.At present, along with the market competition of fierceness and the development in pluralism of dress ornament color day by day, surface color button has become one of element of a lot of trend dress ornament indispensability, multicolour effect is more easily arranged in pairs or groups clothes fashion, different pattern, can produce obvious flange, novel brilliant.
Existing all kinds of button surface wants to realize colour pattern on surface, general adopt retroussage or Laser Processing after the mode of putting the oil, realize the product of polychrome as needed, bat printing generally adopts lettering twice or mode repeatedly to solve, and laser is put the oil then more difficult realization again.But in recent years also occur that a kind of mode of numerial code spray drawing is to realize button colour pattern on surface, its design effect is put the oil than bat printing or Laser Processing again and is improved, but there is the defect of physicochemical property and effect realization.
Therefore, how can find a kind of processing method of button surface, can the modes such as above-mentioned retroussage be substituted, make button surface have the effect of various changeable color, the surface treatment of all kinds of button material can also be used for simultaneously, become one of manufacturer's problem demanding prompt solution in field.
Summary of the invention
In view of this, the technical problem to be solved in the present invention is the preparation method providing a kind of printout surface button, method provided by the invention, can make at button printout surface multicolour pattern, make it have the effect of various changeable color, and the surface treatment of other button materials can also be used for, not by the restriction of button material, and meet corresponding professional standard.
The invention discloses a kind of preparation method of printout surface button, it is characterized in that, comprise the following steps:
A) by button blank after process in early stage, obtain that button is former to be buckled;
B) button obtained in above-mentioned steps is former buckles surface, carries out after UV flat board prints, obtaining printout surface button.
Preferably, described steps A) be specially:
A1) by button raw material through blanking, sorting and after polishing process, obtain button blank;
A2) button blank above-mentioned steps obtained, after system buckles moulding and polishing, obtains that button is former to be buckled.
Preferably, described process in early stage comprises surface coarsening process and/or spray-applied primer process.
Preferably, described process in early stage comprises additional process;
Described additional process comprises laser inscription, dye and spray paint in processing one or more.
Preferably, the printhead of described UV flat board printing and the distance on described button surface are 1 ~ 6mm.
Preferably, the UV lamp power that described UV flat board prints is 60 ~ 80W; The ink output pressure that described UV flat board prints is 4.5kg/cm
2~ 8.0kg/cm
2.
Preferably, described button is one or more in resin button, urea button, ox horn button, injection moulding button, true shellfish button and metal plating class button.
Preferably, described step B) also comprise afterwards,
C) after the surface spraying protective paint of above-mentioned printout surface button, dry and obtain finished surface printing button.
Preferably, described oven dry is that drying tunnel is dried or oven for drying, and the temperature of described oven dry is 60 ~ 90 DEG C, and the time of described oven dry is 50 ~ 60 minutes.
Preferably, described protective paint is mixed with resin paint, and described mixed with resin paint is made up of the main paint of resin, curing agent and diluent;
The mass percent of the main paint of described resin, curing agent and diluent is (90 ~ 110): (20 ~ 50): (50 ~ 600).
The invention discloses a kind of preparation method of printout surface button, comprise the following steps, first by button blank after process in early stage, obtain that button is former to be buckled; Then the button obtained in above-mentioned steps is former buckles surface, carries out after UV flat board prints, obtaining printout surface button.Present invention employs the mode that UV flat board prints, namely coloured plate prints, and is also called the color technique of heap, instead of existing technique, by UV ink print on button, and specifically sprays paint and pre-process and post-process mode, obtains printout surface button.Printout surface button prepared by the present invention can have different colors at button printout surface, and can match colors each other, forms different patterns, thus has obvious color variable color effect.Compared with prior art, instant invention overcomes the shortcoming that common mimeograph needs repeatedly overlapping colouring; Laser Processing cost is high, the shortcoming of marketability difference; And numerial code spray drawing to exist in part button material incompatible, the shortcomings such as finished product pattern poor stability, only lower powered ultraviolet lamp need be used to be cured simultaneously, high heat can not be produced in process, there is not button and burnt yellow phenomenon, also need not carry out later stage numerous and diverse cleaning treatment, simplify operating procedure; In addition the button material needed for preparation method provided by the invention, is not subject to the restriction of hardness and fusing point.Experimental result shows, printout surface button prepared by the present invention has obvious color variable color effect, and can also be used for the surface treatment of other button materials, not by the restriction of button material, and meets corresponding professional standard.
Accompanying drawing explanation
Fig. 1 is the outward appearance photo of printout surface shell button prepared by the embodiment of the present invention 1;
Fig. 2 is the outward appearance photo of printout surface plastic button prepared by the embodiment of the present invention 2;
Fig. 3 is the outward appearance photo of printout surface unsaturated polyester button prepared by the embodiment of the present invention 3.
Detailed description of the invention
In order to understand the present invention further, below in conjunction with embodiment, the preferred embodiments of the invention are described, but should be appreciated that these describe just as further illustrating the features and advantages of the present invention instead of the restriction to patent requirements of the present invention.
The all raw materials of the present invention, be not particularly limited its source, commercially buy or prepare according to conventional method well known to those skilled in the art.
The all raw materials of the present invention, are not particularly limited its purity, and the present invention preferably adopts analysis pure.
Printout surface button of the present invention, namely at the button of button printout surface pattern or font.
The invention discloses a kind of preparation method of printout surface button, it is characterized in that, comprise the following steps:
A) by button blank after process in early stage, obtain that button is former to be buckled;
B) button obtained in above-mentioned steps is former buckles surface, carries out after UV flat board prints, obtaining printout surface button.
The present invention first by button blank after process in early stage, obtain that button is former to be buckled; Described button be preferably in resin button, urea button, ox horn button, injection moulding button, true shellfish button and metal plating class button one or more, be more preferably resin button, urea button, ox horn button, injection moulding button, true shellfish button or metal plating class button, most preferably be resin button, ox horn button or true shellfish button.The preparation process of the present invention to described button blank is not particularly limited, with the method for button blank well known to those skilled in the art.
The present invention is not particularly limited described process in early stage, and with the processing mode in early stage of button blank well known to those skilled in the art, the present invention, for strengthening color effect or strengthening pattern performance tension force, preferably specifically adopts following steps:
First by button raw material through blanking, sorting and after polishing process, obtain button blank; Then button blank above-mentioned steps obtained, after system buckles moulding and polishing, obtains that button is former to be buckled.
The present invention is not particularly limited described blanking, sorting and the specific embodiment that polishes process, with above-mentioned technique well known to those skilled in the art, also according to the requirement of practical condition, specifically button material and product pattern and color, accommodation can be carried out.The present invention is for shell button raw material, first various shell will be contained, as the shell raw material of pearl shell, fine stern spiral shell, black lip shell etc., through raw material blanking, namely on overall shell, take off color, thickness, gloss etc. meet the stock producing button, be generally circle, but now uneven thickness etc. and positive and negative injustice; Secondly due to shell out-of-flatness, blanking can be oblique etc. phenomenon, blank sorting is carried out to the raw material after above-mentioned blanking, carries out grade separation by rough blanks such as different-thickness, color, gloss; Then sorted rough blank is carried out positive and negative polishing, carry out positive and negative by same grade button blank and polish, obtain the standard blank of same thickness, then carry out side dressing, namely grind side and namely grind diameter, make material circularity unified, finally obtain button blank.
The button blank that then above-mentioned steps obtains by the present invention, after system buckles moulding and polishing, obtains that button is former to be buckled.The specific embodiment of the present invention to described system button moulding and polishing is not particularly limited, with above-mentioned technique well known to those skilled in the art, also according to the requirement of practical condition, specifically button material and product pattern and color, accommodation can be carried out.Above-mentioned button blank, for shell button blank, is first carried out system and buckles moulding, be made into the moulding needed for various client by button, comprising operations such as eyelet processing by the present invention; And then carry out polishing blast, by processes such as button polished and cleaned, blasts, polishing can make pearly-lustre specific to shell blank or the natural characteristic as natural materials such as wooden, ox horns perform to ultimate attainment.
Simultaneously, the present invention is also preferred increases additional process after above-mentioned button moulding processed, the present invention is not particularly limited described additional process, those skilled in the art can according to the demand of practical condition, specifically button material and client, carry out adaptability selection and adjustment, the present invention be preferably laser inscription, Colour Difference and spray paint processing in one or more, be more preferably laser inscription, Colour Difference or processing of spraying paint; The concrete steps of the present invention to described laser inscription are not particularly limited, and those skilled in the art according to the demand of practical condition, specifically button material and client, can carry out accommodation; The concrete steps of the present invention to described Colour Difference are not particularly limited, and those skilled in the art according to the demand of practical condition, specifically button material and client, can carry out accommodation; The present invention is not particularly limited described concrete steps of spraying paint processing, and those skilled in the art according to the demand of practical condition, specifically button material and client, can carry out accommodation.
The present invention, for strengthening color effect or strengthening pattern performance tension force, promotes the physicochemical property that button shows, preferably also comprises surface coarsening process and/or spray-applied primer process, more preferably comprise surface coarsening process and spray-applied primer process to described process in early stage; The specific embodiment of the present invention to described surface coarsening process and spray-applied primer process is not particularly limited, with above-mentioned technical process well known to those skilled in the art, also according to the requirement of practical condition, specifically button material and product pattern and color, accommodation can be carried out.The button that above-mentioned steps obtains by the present invention is former to be buckled through surface coarsening process, namely adopts chemical medicinal liquid to carry out wharf's pavement quality, increases surface roughness, then carry out spray-applied primer process.The present invention is not particularly limited described chemical medicinal liquid and priming paint, with well known to those skilled in the art for the chemical medicinal liquid in button production process and priming paint.
The present invention obtains through above-mentioned steps that button is former to be buckled, and then carries out on its surface after UV flat board prints, obtaining printout surface button.
The present invention is not particularly limited the equipment that described UV flat board prints, and with the dull and stereotyped printing device of UV well known to those skilled in the art, the present invention is preferably UV flat-panel printer.The present invention is the stability ensureing to print, preferably by former for above-mentioned button buckle to come on fixture fixing after, then carry out UV flat board and print; The present invention is not particularly limited described fixture, with button fixture well known to those skilled in the art.The present invention is for strengthening color effect or strengthening pattern performance tension force, improve printing effect and strengthen layout reduction degree, preferably the dull and stereotyped print parameters of UV is specifically arranged, the distance on the printhead that described UV flat board prints and described button surface is preferably 1 ~ 6mm, be more preferably 2 ~ 5mm, most preferably be 3 ~ 4mm; The UV lamp power that described UV flat board prints is preferably 60 ~ 80W, is more preferably 62 ~ 78W, is more preferably 65 ~ 75W, most preferably be 70W; The ink output pressure that described UV flat board prints is preferably 4.5kg/cm
2~ 8.0kg/cm
2, be more preferably 5.0kg/cm
2~ 7.5kg/cm
2, be more preferably 5.5kg/cm
2~ 7.0kg/cm
2, most preferably be 6.0kg/cm
2~ 6.5kg/cm
2; The present invention is not particularly limited other parameters that described UV flat board prints, and those skilled in the art according to the demand of practical condition, specifically button material and client, can carry out accommodation.
The present invention obtains after printout surface button through above-mentioned steps, for improving product appearance and wearability, preferably after the surface spraying protective paint of described surface engraving button, drying and obtaining finished surface printing button.The present invention is not particularly limited above-mentioned steps, with button post-processing step well known to those skilled in the art; The equipment of spraying of the present invention is not particularly limited, and with spraying equipment well known to those skilled in the art, the present invention is preferably spray gun spraying; The described bore sprayed paint is preferably 1.1 ~ 1.3mm, is more preferably 1.15 ~ 1.25mm; The present invention's other conditions to described spraying are not particularly limited, with spraying conditions well known to those skilled in the art.
The present invention is not particularly limited described protective paint, with the varnish for spraying button well known to those skilled in the art, varnish of the present invention is preferably mixed with resin paint, described mixed with resin paint is made up of the main paint of resin, curing agent and diluent, the addition of described epoxy resin is preferably 90 ~ 110 weight portions, be more preferably 95 ~ 105 weight portions, be more preferably 98 ~ 102 weight portions; The addition of described illusion-colour mica sheet is preferably 0.1 ~ 1.0 weight portion, is more preferably 0.3 ~ 0.8 weight portion, most preferably is 0.4 ~ 0.7 weight portion; The addition of described amine curing agent is preferably 20 ~ 50 weight portions, is more preferably 25 ~ 45 weight portions, most preferably is 30 ~ 40 weight portions; The addition of described diluent is preferably 50 ~ 600 weight portions, is more preferably 100 ~ 500 weight portions, is more preferably 200 ~ 400 weight portions, most preferably is 250 ~ 350 weight portions.
The present invention is the effect after improving sprayed protection paint, and described mixed with resin paint preferably includes epoxy resin and/or acrylic resin, more preferably comprises epoxy resin and acrylic resin, most preferably is 618 epoxy resin and PJ23-65 acrylic resin; The present invention is the paint film property improving mixed with resin paint, preferably also comprise dispersant and diluent, the present invention is not particularly limited described dispersant and diluent, with the dispersant for lacquer type organic coating well known to those skilled in the art and diluent, the preferred described diluent of the present invention is cyclohexanone, dimethylbenzene and DAA; Described dispersant is BYK141 and/or BYK358.The optimal component of described mixed with resin paint, for making button Realization of Product effect optimization, is preferably 618 epoxy resin by the present invention, PJ23-65 acrylic resin, cyclohexanone, dimethylbenzene, DAA, BYK141 and BYK358, the mass fraction of the present invention to above-mentioned optimal component is not particularly limited, and with the programs of lacquer type organic coating well known to those skilled in the art, the present invention is preferably 618 epoxy resin of 20 ~ 40 weight portions, the PJ23-65 acrylic resin of 22 ~ 26 weight portions, the cyclohexanone of 10 ~ 20 weight portions, the dimethylbenzene of 10 ~ 20 weight portions, the DAA of 10 ~ 20 weight portions, the BYK141 of 0.1 ~ 0.5 weight portion and the BYK358 of 0.1 ~ 0.5 weight portion, is more preferably 618 epoxy resin of 25 ~ 35 weight portions, the PJ23-65 acrylic resin of 23 ~ 25 weight portions, the cyclohexanone of 13 ~ 17 weight portions, the dimethylbenzene of 14 ~ 16 weight portions, the DAA of 13 ~ 17 weight portions, the BYK141 of 0.2 ~ 0.4 weight portion and the BYK358 of 0.2 ~ 0.4 weight portion, most preferably is 618 epoxy resin of 30 weight portions, 24.5 the PJ23-65 acrylic resin of weight portion, the cyclohexanone of 13 ~ 17 weight portions, the dimethylbenzene of 15 weight portions, the DAA of 15 weight portions, the BYK141 of 0.3 weight portion and the BYK358 of 0.2 weight portion.
Described curing agent is preferably diethylaminopropylamine, one or more in ethylenediamine, hexamethylene diamine, diethylenetriamine and triethylene tetramine, be more preferably diethylaminopropylamine, ethylenediamine, hexamethylene diamine, diethylenetriamine or triethylene tetramine, be more preferably diethylaminopropylamine, hexamethylene diamine or triethylene tetramine, most preferably be diethylaminopropylamine; Described diluent is preferably dimethylbenzene, cyclohexanone and butanols; The ratio of the present invention to described diluent is not particularly limited, and with the diluent for lacquer type organic coating mixing well known to those skilled in the art, the mass ratio of dimethylbenzene, cyclohexanone and butanols in described diluent is preferably 16:1:3 by the present invention; The model of the present invention to above-mentioned concrete model raw material is not particularly limited, with universal models raw material in industry well known to those skilled in the art; The source of the present invention to above-mentioned concrete model raw material is not particularly limited, with method well known to those skilled in the art preparation or commercially.
The method of the present invention to described oven dry is not particularly limited, and with button furnace drying method well known to those skilled in the art, oven dry of the present invention is preferably drying tunnel and dries or oven for drying; The temperature of described oven dry is preferably 60 ~ 90 DEG C, is more preferably 65 ~ 85 DEG C, most preferably is 70 ~ 80 DEG C; The time of described oven dry is preferably 50 ~ 60 minutes, is more preferably 53 ~ 58 minutes, most preferably is 55 minutes; The present invention's other conditions to described oven dry are not particularly limited, with button drying condition well known to those skilled in the art; The equipment of the present invention to described oven dry is not particularly limited, with button drying plant well known to those skilled in the art.
The present invention obtains finished surface through above-mentioned steps and prints button, adopts method of the present invention not to be subject to the restriction of hardness and fusing point, goes for multiple button material; The material of button of the present invention be preferably in resin, urea, ox horn, injection moulding, Zhen Bei and metal plating class button one or more, be more preferably resin, urea, ox horn, injection moulding, Zhen Bei or metal plating class button, be more preferably resin, ox horn, Zhen Bei or metal plating class button, most preferably be and elect resin, ox horn or true shellfish button as.
The present invention obtains finished surface through above-mentioned steps and prints button, preparation method provided by the invention can have different colors at button printout surface, and can match colors each other, form different patterns, thus there is obvious color variable color effect.Instant invention overcomes the shortcoming that common mimeograph needs repeatedly overlapping colouring; Laser Processing cost is high, the shortcoming of marketability difference; And numerial code spray drawing to exist in part button material incompatible, the shortcomings such as finished product pattern poor stability, only lower powered ultraviolet lamp need be used to be cured simultaneously, high heat can not be produced in process, there is not button and burnt yellow phenomenon, also need not carry out later stage numerous and diverse cleaning treatment, simplify operating procedure; In addition the button material needed for preparation method provided by the invention, is not subject to the restriction of hardness and fusing point.Experimental result shows, printout surface button prepared by the present invention has obvious color variable color effect, and can also be used for the surface treatment of other button materials, not by the restriction of button material, and meets corresponding professional standard.
In order to understand the present invention further, below in conjunction with embodiment, the preparation method to printout surface button provided by the invention is described, and protection scope of the present invention is not limited by the following examples.
Embodiment 1
UV flat board prints colored shell button
Shell button blank: take off color, thickness, gloss etc. and meet the stock producing button on overall fine stern spiral shell shell, the blanks such as different-thickness, color, gloss are carried out grade separation, same grade button blank is carried out positive and negative polish, obtain the standard rough blank of same thickness, again rough blank side is repaired, make rough blank diameter unified, finally obtain the shell button blank that diameter is 11.43mm.
System button moulding: button is carried out positive and negative moulding scraper on the deduction processed scraping moulding, the perforating of four eyelets, namely from front-back two-sided flat unperforated product, is spread to by deduction processed and positive and negatively has surface modeling, and perforated product.
Additional process: select CO
2laser inscription, by the anaglyph needed for radium-shine for product surface one-tenth, its radium-shine way selection automation equipment, and it is uneven to realize product internal circular surfaces by the radium-shine mode of bitmap.
Polishing: the former button of shell button through moulding and additional process prepared by above-mentioned steps, pour in polishing machine, carry out water roll cast light by rotten-stone, the burr stayed when removing system button and cutter pin unequal phenomenon, then put into dry milling polishing machine, carry out further polishing, to reach required luminosity, then by Ultrasonic Cleaning, remove the dust on button surface and unnecessary burnishing oil, to increase paint fastness, finally obtain that the button after polishing is former to be buckled.
Surface coarsening process and priming paint spray paint: chemical surface roughening treatment, and the transparent AC of certain proportioning is painted primer spray, finally obtain that button is former to be buckled.
Surface UV flat board prints operation: to be that the button of 11.43mm is former buckle diameter above-mentioned steps obtained, on the intensive regular fixture being arranged in breadth 280mm*360mm, according to design drawing pattern, input effectively prints drawing, and reset CMYK value, printhead height is in 2.0mm, and UV lamp power 70W, ink pressure are about 5.2kg/cm
2and amount 40% out of ink, start to carry out UV flat board and print, after solidification, obtain printout surface button.
Surface spraying protective paint process: the printout surface button after printing is carried out epoxy-based lacquers spray coating, then carry out baking process, baking temperature is 60 DEG C, and the time is 60 minutes, obtains finished surface and print button after lower button.
The finished surface prepared embodiment 1 prints colored shell button and carries out outward appearance detection, experimental result shows, see Fig. 1, Fig. 1 is the outward appearance photo of printout surface shell button prepared by the embodiment of the present invention 1, as shown in Figure 1, finished product shell surface prepared by the present invention prints button, has different colors, color matching is good each other, can form truly lively pattern.
Carry out physicochemical property detection to the shell surface printing button that embodiment 1 prepares, experimental result shows, according to standard GB/T/T28491-2012, after dry-cleaning, color and luster is without significant change, concrete staining class 4 .5 level; According to standard GB/T/T28491-2012, press color and luster without significant change, concrete staining class 4 .5 level; According to standard GB/T/T28491-2012,5 color and lusters of machine-washing are without significant change.Above-mentioned physicochemical property testing result shows, shell surface prepared by the present invention prints the test of its physicochemical property of button and meets professional standard completely.
Embodiment 2
UV flat board prints colored plastic (ABS) button
Plastic button blank: by making mould, then injection machine die cast obtains the plastic button blank that diameter is 25.40mm, has now completed button appearance and modeling.
Additional process: by lacquer spraying technique, by product front and reverse side coated white magnetic colored paint simultaneously.
Surface UV flat board prints operation: to be that the button of 25.40mm is former buckle diameter above-mentioned steps obtained, on the intensive regular fixture being arranged in breadth 280mm*360mm, according to design drawing pattern, input effectively prints drawing, and be necessary to reset CMYK value, printhead height is in 1.8mm, and UV lamp power 75W, ink pressure are about 4.7kg/cm
2and amount 40% out of ink etc., starting to carry out UV flat board prints, and obtains printout surface button after solidification.
Surface spraying protective paint process: the printout surface button after printing is carried out epoxy-based lacquers spray coating, then carry out baking process, baking temperature is about 70 DEG C, and the time is 50 minutes, obtains finished surface and print button after lower button.
Outward appearance detection is carried out to finished surface printing colored plastic (ABS) button that embodiment 2 prepares, experimental result shows, see Fig. 2, Fig. 2 is the outward appearance photo of printout surface plastic button prepared by the embodiment of the present invention 2, as shown in Figure 2, finished plastic (ABS) printout surface button prepared by the present invention, has different colors, color matching is good each other, can form truly lively pattern.
Carry out physicochemical property detection to the frosting printing button that embodiment 2 prepares, experimental result shows, according to standard GB/T/T29290-2012, after dry-cleaning, color and luster is without significant change, concrete staining class 4 .5 level; According to standard GB/T/T29290-2012, press color and luster without significant change, concrete staining class 4 .5 level; According to standard GB/T/T29290-2012,5 color and lusters of machine-washing are without significant change.Above-mentioned physicochemical property testing result shows, frosting prepared by the present invention prints the test of its physicochemical property of button and meets professional standard completely.
Embodiment 3
UV flat board prints colored unsaturated polyester (UP) (resin) button
Unsaturated polyester (UP) blank: by the mode of centrifuge making sheet or aluminum round rod rod, obtain blank raw material, again by different cutting modes, finally obtain the unsaturated polyester button blank that diameter is 12.70mm, it is characterized in that the circular blanks having certain thickness (general 3.0 ~ 8.0mm).
System button moulding: button is carried out positive and negative moulding scraper on the deduction processed scraping moulding, the perforating of four or 2 two eyelets, namely from front-back two-sided flat unperforated product, is spread to by deduction processed and positive and negatively has surface modeling, and perforated product.
Polishing: the former button of unsaturated polyester button through moulding and additional process prepared by above-mentioned steps, pour in polishing machine, carry out water roll cast light by rotten-stone, the burr stayed when removing system button and cutter pin unequal phenomenon, then put into dry milling polishing machine, carry out further polishing, to reach required luminosity, then by Ultrasonic Cleaning, remove the dust on button surface and unnecessary burnishing oil, to increase paint fastness, finally obtain that the button after polishing is former to be buckled.
Surface UV flat board prints operation: to be that the button of 12.70mm is former buckle diameter above-mentioned steps obtained, on the intensive regular fixture being arranged in breadth 280mm*360mm, according to design drawing pattern, input effectively prints drawing, and be necessary to reset CMYK value, printhead height is in 3.0mm, and UV lamp power 65W, ink pressure are about 7.0kg/cm
2and amount 40% out of ink etc., starting to carry out UV flat board prints, and obtains printout surface button after solidification.
Additional process: after obtaining printout surface button, again by the mode of vacuum coating, button surface and side are all plated the coating of bright silver, after coating again with optical-fiber laser by radium-shine for the local color of printing portion stripping, namely expose the feature of printing portion, finally form finished product.
Surface spraying protective paint process: the printout surface button after additional process is carried out epoxy-based lacquers spray coating, then carry out baking process, baking temperature is about 80 DEG C, and the time is 55 minutes, obtains finished surface and print button after lower button.
Outward appearance detection is carried out to finished surface printing unsaturated polyester (UP) (resin) button that embodiment 3 prepares, experimental result shows, see Fig. 3, Fig. 3 is the outward appearance photo of printout surface unsaturated polyester button prepared by the embodiment of the present invention 3, as shown in Figure 3, finished product unsaturated polyester (UP) printout surface button prepared by the present invention, has different colors, color matching is good each other, can form truly lively pattern.
Carry out physicochemical property detection to the unsaturated polyester (UP) printout surface button that embodiment 3 prepares, experimental result shows, according to standard GB/T/T29290-2012, after dry-cleaning, color and luster is without significant change, concrete staining class 4 .5 level; According to standard GB/T/T29290-2012, press color and luster without significant change, concrete staining class 4 .5 level; According to standard GB/T/T29290-2012,5 color and lusters of machine-washing are without significant change.Above-mentioned physicochemical property testing result shows, its physicochemical property of unsaturated polyester (UP) printout surface button test prepared by the present invention meets professional standard completely.
Above the preparation method of a kind of printout surface button provided by the present invention is described in detail.Apply a concrete example herein to set forth principle of the present invention and embodiment, the explanation of above embodiment just understands method of the present invention and core concept thereof for helping.It should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention, can also carry out some improvement and modification to the present invention, these improve and modify and also fall in the protection domain of the claims in the present invention.
Claims (10)
1. a preparation method for printout surface button, is characterized in that, comprises the following steps:
A) by button blank after process in early stage, obtain that button is former to be buckled;
B) button obtained in above-mentioned steps is former buckles surface, carries out after UV flat board prints, obtaining printout surface button.
2. preparation method according to claim 1, is characterized in that, described steps A) be specially:
A1) by button raw material through blanking, sorting and after polishing process, obtain button blank;
A2) button blank above-mentioned steps obtained, after system buckles moulding and polishing, obtains that button is former to be buckled.
3. preparation method according to claim 1, is characterized in that, described process in early stage comprises surface coarsening process and/or spray-applied primer process.
4. preparation method according to claim 1, is characterized in that, described process in early stage comprises additional process;
Described additional process comprises laser inscription, dye and spray paint in processing one or more.
5. preparation method according to claim 1, is characterized in that, the distance on the printhead that described UV flat board prints and described button surface is 1 ~ 6mm.
6. preparation method according to claim 1, is characterized in that, the UV lamp power that described UV flat board prints is 60 ~ 80W; The ink output pressure that described UV flat board prints is 4.5kg/cm
2~ 8.0kg/cm
2.
7. preparation method according to claim 1, is characterized in that, described button is one or more in resin button, urea button, ox horn button, injection moulding button, true shellfish button and metal plating class button.
8. preparation method according to claim 1, is characterized in that, described step B) also comprise afterwards,
C) after the surface spraying protective paint of above-mentioned printout surface button, dry and obtain finished surface printing button.
9. preparation method according to claim 8, is characterized in that, described oven dry is that drying tunnel is dried or oven for drying, and the temperature of described oven dry is 60 ~ 90 DEG C, and the time of described oven dry is 50 ~ 60 minutes.
10. preparation method according to claim 8, is characterized in that, described protective paint is mixed with resin paint, and described mixed with resin paint is made up of the main paint of resin, curing agent and diluent;
The mass percent of the main paint of described resin, curing agent and diluent is (90 ~ 110): (20 ~ 50): (50 ~ 600).