CN105113707A - Light high-strength multilayer composite internal partition wall batten and preparation method thereof - Google Patents
Light high-strength multilayer composite internal partition wall batten and preparation method thereof Download PDFInfo
- Publication number
- CN105113707A CN105113707A CN201510600610.XA CN201510600610A CN105113707A CN 105113707 A CN105113707 A CN 105113707A CN 201510600610 A CN201510600610 A CN 201510600610A CN 105113707 A CN105113707 A CN 105113707A
- Authority
- CN
- China
- Prior art keywords
- plate
- internal partition
- strength
- multilayer composite
- warming plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a light high-strength multilayer composite internal partition wall batten and a preparation method thereof. The multilayer composite internal partition wall batten comprises a partition wall batten body, wherein insulation boards are arranged on the partition wall batten body; light mortar layers are laid on the upper surface and the lower surface of each insulation board; the light mortar layers are coated with high-strength anti-crack mortar outer layers; glass fiber grid reinforcing fabrics are laid at connecting parts of the light mortar layers and the high-strength anti-crack mortar outer layers. According to the invention, the light mortar layers are coated with the high-strength anti-crack mortar layers and the insulation boards are arranged in the light mortar layers, so that an insulation effect is realized, and meanwhile, the weight of the internal partition wall batten is reduced; each insulation board is composed of multiple polyphenyl boards or holes are formed in each insulation board, so that light mortar can flow into the insulation boards, the light mortar layers and the insulation boards are connected more tightly, and the strength of the internal partition wall batten is improved. In addition, the preparation method is simple and the internal partition wall batten can be prepared through one-time molding casting.
Description
Technical field
The present invention relates to a kind of inner separation wall body technology for building, particularly a kind of high-strength light MULTILAYER COMPOSITE batten of internal partition, also relates to the preparation method of above-mentioned batten of internal partition.
Background technology
In existing building engineering, normal several batten of internal partition that use are spliced to form inner wall panel, this mode convenience quick for installation.But existing inner wall panel sound insulation function is poor, also there is heat insulation effect bad, Heavy Weight, the problems such as intensity is not high, and flameproof effect is bad simultaneously.
Summary of the invention
Technical problem to be solved by this invention is for the deficiencies in the prior art, provides a kind of reasonable in design, easy for installation, the high-strength light MULTILAYER COMPOSITE batten of internal partition that soundproof effect is good.
Another technical problem to be solved by this invention there is provided the preparation method of above-mentioned high-strength light MULTILAYER COMPOSITE batten of internal partition.
Technical problem to be solved by this invention is realized by following technical scheme, the present invention is a kind of high-strength light MULTILAYER COMPOSITE batten of internal partition, is characterized in, is provided with partition wall plate body, be respectively equipped with tongue-and-groove and tenon block in the both sides of partition wall plate body, tongue-and-groove and tenon block mate mutually; Described partition wall plate body is provided with warming plate, and the upper and lower surface of warming plate is covered with lightweight screed layer, and it is outer that lightweight screed layer is coated with high-strength anticracking grout, is equipped with fiberglass mesh strengthens cloth at lightweight screed layer and the outer joint of high-strength anticracking grout.
Technical problem to be solved by this invention can also be realized further by following technical scheme, and described warming plate is made up of 3-4 block polyphenyl plate, is provided with the gap of 18-22cm between adjacent polyphenyl plate.
Technical problem to be solved by this invention can also be realized further by following technical scheme, described warming plate is made up of a whole plate polyphenyl plate, warming plate has several and the vertically disposed through hole of warming plate, be provided with intensive aspect in each through hole, intensive aspect and lightweight screed layer are connected as a single entity.
Technical problem to be solved by this invention can also be realized further by following technical scheme, and described through hole is that two row are arranged on warming plate, and often row are provided with 6-7 manhole, and the diameter of manhole is 50cm.
Technical problem to be solved by this invention can also be realized further by following technical scheme, and the width of described warming plate is 550cm.
Technical problem to be solved by this invention can also be realized further by following technical scheme, the length of described partition wall plate body is 2200-3000cm, width is 600cm, thickness is 100-200cm, the thickness of described warming plate is 20cm, the outer field thickness of high-strength anticracking grout of warming plate side is 15-55cm, and the thickness of lightweight screed layer is 20-35cm.
The invention also discloses a kind of preparation method of the high-strength light MULTILAYER COMPOSITE batten of internal partition as described in above scheme, be characterized in, its step is as follows:
(1) warming plate process: when warming plate is made up of 3-4 block polyphenyl plate, be cut into corresponding size as requested, and by two external surface pluckings of every block polyphenyl plate; When warming plate is a monoblock polyphenyl plate, first in polyphenyl plate, open several through holes, then by two external surface pluckings of polyphenyl plate;
(2) mortar laying: according to the size molding of batten of internal partition, then the high-strength anticracking grout of one deck is laid at mold bottom, high-strength anticracking grout is laid fiberglass mesh and strengthens cloth, strengthen cloth is provided with lightweight screed layer baffle plate in fiberglass mesh, foamed light mortar in baffle plate, then the polyphenyl plate handled well in step (1) is placed on lightweight screed layer, after in polyphenyl plate foamed light mortar again, automatically, in the gap flowing into warming plate in lightweight screed layer formation process or through hole, the intensive aspect be connected as a single entity with lightweight screed layer is formed; Lightweight screed layer solidifies rear dismounting baffle plate, and on lightweight screed layer, then lay fiberglass mesh strengthen cloth, finally reinject high-strength anticracking grout, after mortar parches, namely obtain MULTILAYER COMPOSITE batten of internal partition.
Compared with prior art, the present invention, by coated lightweight screed layer in high-strength anticracking grout layer, is provided with warming plate, the effect of therefore existing insulation in lightweight screed layer, can alleviate again the weight of batten of internal partition simultaneously; And warming plate punches by polylith polyphenyl plate or on whole plate, therefore lightweight screed can flow into wherein, lightweight screed layer is connected with warming plate more tight, improves the intensity of inner partition plate.Preparation method is simple in addition, can one-shot forming build obtained.
Accompanying drawing explanation
Fig. 1 is a kind of cross section structure schematic diagram of the present invention;
Fig. 2 is another kind of cross section structure schematic diagram of the present invention.
Detailed description of the invention
Referring to accompanying drawing, further describe concrete technical scheme of the present invention, so that those skilled in the art understands the present invention further, and do not form the restriction to its right.
Embodiment 1, a kind of high-strength light MULTILAYER COMPOSITE batten of internal partition, with reference to Fig. 1, be provided with partition wall plate body, be respectively equipped with tongue-and-groove 1 and tenon block 4 in the both sides of partition wall plate body, tongue-and-groove 1 and tenon block 4 mate mutually, contribute to the splicing of polylith batten of internal partition and install.Described partition wall plate body is provided with warming plate 5, and the upper and lower surface of warming plate 5 is covered with lightweight screed layer 6, and lightweight screed layer 6 is coated with high-strength anticracking grout skin 2, is equipped with fiberglass mesh strengthens cloth 3 in outer 2 joints of lightweight screed layer 6 and high-strength anticracking grout.
Embodiment 2, in the high-strength light MULTILAYER COMPOSITE batten of internal partition described in embodiment 1, described warming plate 5 is made up of 3 pieces of polyphenyl plate, is provided with the gap of 20cm between adjacent polyphenyl plate.
Embodiment 3, in high-strength light MULTILAYER COMPOSITE batten of internal partition described in embodiment 1, with reference to figure 2, described warming plate 5 is made up of a whole plate polyphenyl plate, warming plate 5 has several and the vertically disposed through hole 7 of warming plate 5, be provided with intensive aspect in each through hole 7, intensive aspect and lightweight screed layer 6 are connected as a single entity, with reference to figure 2.
Embodiment 4, in the high-strength light MULTILAYER COMPOSITE batten of internal partition described in embodiment 3, described through hole 7 is arranged on warming plate 5 in two row, and often row are provided with 6 manholes, and the diameter of manhole is 50cm.
Embodiment 5, in the high-strength light MULTILAYER COMPOSITE batten of internal partition described in embodiment 1, the width of described warming plate 5 is 550cm.
Embodiment 6, in high-strength light MULTILAYER COMPOSITE batten of internal partition described in embodiment 1, the length of described partition wall plate body is 2200cm, width is 600cm, thickness is 100cm, the thickness of described warming plate 5 is 20cm, and the thickness of the high-strength anticracking grout skin 2 of warming plate 5 side is 15cm, and the thickness of lightweight screed layer 6 is 20cm.
Embodiment 7, in high-strength light MULTILAYER COMPOSITE batten of internal partition described in embodiment 1, the length of described partition wall plate body is 3000cm, width is 600cm, thickness is 200cm, the thickness of described warming plate 5 is 20cm, and the thickness of the high-strength anticracking grout skin 2 of warming plate 5 side is 55cm, and the thickness of lightweight screed layer 6 is 35cm.
Embodiment 8, a kind of preparation method of the high-strength light MULTILAYER COMPOSITE batten of internal partition as described in any one of embodiment 1-7, is characterized in that: its step is as follows:
(1) warming plate process: when warming plate is made up of 3-4 block polyphenyl plate, be cut into corresponding size as requested, and by two external surface pluckings of every block polyphenyl plate; When warming plate is a monoblock polyphenyl plate, first in polyphenyl plate, open several through holes, then by two external surface pluckings of polyphenyl plate;
(2) mortar laying: according to the size molding of batten of internal partition, then the high-strength anticracking grout of one deck is laid at mold bottom, high-strength anticracking grout is laid fiberglass mesh and strengthens cloth, strengthen cloth is provided with lightweight screed layer baffle plate in fiberglass mesh, foamed light mortar in baffle plate, then the polyphenyl plate handled well in step (1) is placed on lightweight screed layer, after in polyphenyl plate foamed light mortar again, automatically, in the gap flowing into warming plate in lightweight screed layer formation process or through hole, the intensive aspect be connected as a single entity with lightweight screed layer is formed; Lightweight screed layer solidifies rear dismounting baffle plate, and on lightweight screed layer, then lay fiberglass mesh strengthen cloth, finally reinject high-strength anticracking grout, after mortar parches, namely obtain MULTILAYER COMPOSITE batten of internal partition.
Claims (7)
1. a high-strength light MULTILAYER COMPOSITE batten of internal partition, is characterized in that: be provided with partition wall plate body, is respectively equipped with tongue-and-groove and tenon block in the both sides of partition wall plate body, and tongue-and-groove and tenon block mate mutually; Described partition wall plate body is provided with warming plate, and the upper and lower surface of warming plate is covered with lightweight screed layer, and it is outer that lightweight screed layer is coated with high-strength anticracking grout, is equipped with fiberglass mesh strengthens cloth at lightweight screed layer and the outer joint of high-strength anticracking grout.
2. high-strength light MULTILAYER COMPOSITE batten of internal partition according to claim 1, is characterized in that: described warming plate is made up of 3-4 block polyphenyl plate, is provided with the gap of 18-22cm between adjacent polyphenyl plate.
3. high-strength light MULTILAYER COMPOSITE batten of internal partition according to claim 1, it is characterized in that: described warming plate is made up of a whole plate polyphenyl plate, warming plate has several and the vertically disposed through hole of warming plate, be provided with intensive aspect in each through hole, intensive aspect and lightweight screed layer are connected as a single entity.
4. high-strength light MULTILAYER COMPOSITE batten of internal partition according to claim 3, is characterized in that: described through hole is that two row are arranged on warming plate, and often row are provided with 6-7 manhole, and the diameter of manhole is 50cm.
5. high-strength light MULTILAYER COMPOSITE batten of internal partition according to claim 1, is characterized in that: the width of described warming plate is 550cm.
6. high-strength light MULTILAYER COMPOSITE batten of internal partition according to claim 1, it is characterized in that: the length of described partition wall plate body is 2200-3000cm, width is 600cm, thickness is 100-200cm, the thickness of described warming plate is 20cm, the outer field thickness of high-strength anticracking grout of warming plate side is 15-55cm, and the thickness of lightweight screed layer is 20-35cm.
7. a preparation method for the high-strength light MULTILAYER COMPOSITE batten of internal partition as described in any one of claim 1-6, is characterized in that: its step is as follows:
Warming plate process: when warming plate is made up of 3-4 block polyphenyl plate, be cut into corresponding size as requested, and by two external surface pluckings of every block polyphenyl plate; When warming plate is a monoblock polyphenyl plate, first in polyphenyl plate, open several through holes, then by two external surface pluckings of polyphenyl plate;
Mortar laying: according to the size molding of batten of internal partition, then the high-strength anticracking grout of one deck is laid at mold bottom, high-strength anticracking grout is laid fiberglass mesh and strengthens cloth, strengthen cloth is provided with lightweight screed layer baffle plate in fiberglass mesh, foamed light mortar in baffle plate, then the polyphenyl plate handled well in step (1) is placed on lightweight screed layer, after in polyphenyl plate foamed light mortar again, automatically, in the gap flowing into warming plate in lightweight screed layer formation process or through hole, the intensive aspect be connected as a single entity with lightweight screed layer is formed; Lightweight screed layer solidifies rear dismounting baffle plate, and on lightweight screed layer, then lay fiberglass mesh strengthen cloth, finally reinject high-strength anticracking grout, after mortar parches, namely obtain MULTILAYER COMPOSITE batten of internal partition.