CN105113319A - Impact-resisting packaging paper box and preparation method thereof - Google Patents
Impact-resisting packaging paper box and preparation method thereof Download PDFInfo
- Publication number
- CN105113319A CN105113319A CN201510578167.0A CN201510578167A CN105113319A CN 105113319 A CN105113319 A CN 105113319A CN 201510578167 A CN201510578167 A CN 201510578167A CN 105113319 A CN105113319 A CN 105113319A
- Authority
- CN
- China
- Prior art keywords
- shock resistance
- parts
- packaging box
- pulp
- box according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an impact-resisting packaging paper box. The impact-resisting packaging paper box is characterized by being prepared from, by weight, 80-100 parts of raw paper pulp, 1-3 parts of moisture-proof agents, 1-3 parts of fire retardants and 5-8 parts of reinforcing agents. The invention further discloses a preparation method of the impact-resisting packaging paper box. The reinforcing agents are added in the paper pulp, effective constituents in the reinforcing agents coat fibers, and therefore the finally-obtained packaging paper box has the good strength, toughness and impact resistance and is not prone to damage.
Description
Technical field
The present invention relates to a kind of shock resistance Packaging Box and preparation method thereof, belong to pulp technology for making paper.
Background technology
For paper products, it is in the application of packaging field, more and more extensively.But it is along with the popularity of packaging product, more and more higher to the requirement of packaging material, more especially higher to requirement of strength, Packaging Box is needed to have stronger impact resistance, and at present, hot due in carton material, cause its shock resistance more weak, packaging demand cannot be met.
Summary of the invention
The object of the present invention is to provide that a kind of intensity is high, the shock resistance Packaging Box of good toughness and preparation method thereof.
In order to reach the object of foregoing invention, the present invention realizes by the following technical solutions:
A kind of shock resistance Packaging Box, is characterized in that, comprises following component and the parts by weight of each component are:
Body paper paper pulp: 80-100 part;
Anti-blushing agent: 1-3 part;
Fire retardant: 1-3 part;
Reinforcing agent: 5-8 part.
Further, above-mentioned shock resistance Packaging Box, preferably, comprises following component and the parts by weight of each component are:
Body paper paper pulp: 90 parts;
Anti-blushing agent: 2 parts;
Fire retardant: 2 parts;
Reinforcing agent: 6 parts.
And described reinforcing agent is modified carbon black.And described modified carbon black carries out surface treatment modification by rare-earth coupling agent.
Described anti-blushing agent is silica gel.
Described fire retardant is halogen-free inorganic flame retardant or phosphorus flame retardant.
Described body paper paper pulp is at least one in wood pulp, bamboo pulp, reed pulp, straw pulp.
In addition, the preparation method of above-mentioned shock resistance Packaging Box, is characterized in that, comprise the following steps: according to ratio of weight and number, in body paper paper pulp, add fire retardant, carry out copy paper after mixing and obtain shock resistance wrapping paper, be then prepared into shock resistance Packaging Box according to carton specification.
Beneficial effect of the present invention is: the present invention by adding reinforcing agent in paper pulp, and in the process that paper is shaping, the active ingredient in reinforcing agent is in the fibre coated, final Packaging Box is made to have good intensity, toughness, and shock resistance, not fragile.
detailed description of the invention:
Below in conjunction with specific embodiment, concrete introduction is done to the present invention.
embodiment 1
In 90 parts of wood pulps, add silica gel anti-blushing agent 2 parts, halogen-free inorganic flame retardant 2 parts and modified carbon black 6 parts, mix and obtain shock resistance wrapping paper according to routine paper technique copy paper afterwards, be then prepared into shock resistance Packaging Box according to carton specification.
embodiment 2
In 80 parts of bamboo pulps and reed pulp, add silica gel anti-blushing agent 1 part, phosphorus flame retardant 1 part and modified carbon black 8 parts, mix and obtain shock resistance wrapping paper according to routine paper technique copy paper afterwards, be then prepared into shock resistance Packaging Box according to carton specification.
embodiment 3
In 100 parts of straw pulps, add silica gel anti-blushing agent 3 parts, halogen-free inorganic flame retardant 3 parts and modified carbon black 5 parts, mix and obtain shock resistance wrapping paper according to routine paper technique copy paper afterwards, be then prepared into shock resistance Packaging Box according to carton specification.
Modified carbon black in above-described embodiment 1-3 all carries out surface treatment modification by rare-earth coupling agent.
The performance test of the packing board of above-described embodiment 1-3 is as shown in table 1:
The performance of the packing board of table 1: embodiment 1-3
| Performance | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Unnotched impact strength (kJ/m 2) | 18 | 16 | 16 |
| Notch impact strength (kJ/m 2) | 1.9 | 2.0 | 1.6 |
| TENSILE STRENGTH (MPa) | 26 | 22 | 25 |
| Elongation at break (%) | 2.3 | 2.2 | 2.0 |
| Bending strength (MPa) | 20 | 20 | 18 |
| Bending modulus (MPa) | 2160 | 2020 | 2010 |
As shown in Table 1: the present invention by adding reinforcing agent in paper pulp, and in the process that paper is shaping, the active ingredient in reinforcing agent is in the fibre coated, makes final Packaging Box have good intensity, toughness, and shock resistance, not fragile.
The above is only the preferred embodiment of patent of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from patent principle of the present invention; can also make some improvements and modifications, these improvements and modifications also should be considered as the protection domain of patent of the present invention.
Claims (8)
1. a shock resistance Packaging Box, is characterized in that, comprises following component and the parts by weight of each component are:
Body paper paper pulp: 80-100 part;
Anti-blushing agent: 1-3 part;
Fire retardant: 1-3 part;
Reinforcing agent: 5-8 part.
2. a kind of shock resistance Packaging Box according to claim 1, is characterized in that, comprises following component and the parts by weight of each component are:
Body paper paper pulp: 90 parts;
Anti-blushing agent: 2 parts;
Fire retardant: 2 parts;
Reinforcing agent: 6 parts.
3. a kind of shock resistance Packaging Box according to claim 1 and 2, is characterized in that, described reinforcing agent is modified carbon black.
4. a kind of shock resistance Packaging Box according to claim 3, it is characterized in that, described modified carbon black carries out surface treatment modification by rare-earth coupling agent.
5. a kind of shock resistance Packaging Box according to claim 1, is characterized in that, described anti-blushing agent is silica gel.
6. a kind of shock resistance Packaging Box according to claim 3, is characterized in that, described fire retardant is halogen-free inorganic flame retardant or phosphorus flame retardant.
7. a kind of shock resistance Packaging Box according to claim 1, is characterized in that, described body paper paper pulp is at least one in wood pulp, bamboo pulp, reed pulp, straw pulp.
8. the preparation method of a shock resistance Packaging Box according to claim 1, it is characterized in that, comprise the following steps: according to ratio of weight and number, anti-blushing agent, fire retardant and reinforcing agent is added in body paper paper pulp, carry out copy paper after mixing and obtain shock resistance wrapping paper, be then prepared into shock resistance Packaging Box according to carton specification.