CN105113226A - Softener for high-temperature-resistant chemical fiber fabric and preparation method thereof - Google Patents
Softener for high-temperature-resistant chemical fiber fabric and preparation method thereof Download PDFInfo
- Publication number
- CN105113226A CN105113226A CN201510584211.9A CN201510584211A CN105113226A CN 105113226 A CN105113226 A CN 105113226A CN 201510584211 A CN201510584211 A CN 201510584211A CN 105113226 A CN105113226 A CN 105113226A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistant chemical
- high temperature
- softener
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a softener for high-temperature-resistant chemical fiber fabric. The softener for the high-temperature-resistant chemical fiber fabric is prepared from, by mass, 15-25 parts of sorbitan fatty acid ester, 35-40 parts of polyoxyethylene ether, 25-30 parts of acrylamide, 20-25 parts of isopropanolamine and 35-40 parts of deionized water. The softener for the high-temperature-resistant chemical fiber fabric is good in use effect, does not damage the surface of the fabric, is prepared from the raw materials easy to obtain and can be strongly bonded with fiber, make the fabric resistant to high temperature, washing and wear, achieve an excellent softening effect and a smooth hand feeling, make synthetic fiber have a certain antistatic effect and improve the wear resistance and tear strength of the fabric.
Description
Technical field
The present invention relates to a kind of high temperature resistant chemical & blended fabric softener and preparation method thereof, belong to fabric arts.
Background technology
In the technical process such as usual fabric is weaved at chemical fibre, pre-treatment, it is coarse that several factors may make fabric become feel, all
Softener need be added and improve feel.Softener be one can give clothing and fabric feel, dress and use time have soft joyful
The daily chemical product of sensation.Level and smooth, the soft effect of softener is mainly due to after softener is adsorbed on fiber surface, prevent fiber from directly contacting with fiber, reduce the coefficient of kinetic friction between fiber and fiber and confficient of static friction, reduce the resistance between fabric component and the resistance between fabric and human body, to reach effect soft, smooth, comfortable and easy to wear.Particularly in recent years, softener becomes particularly important in textile processing, and almost each all have passed through soft finish from textile mills' textiles out.The main target of this arrangement be obtain a kind of softness feel to facilitate textile process and to improve wearability.Usually, the soft feel of comfortable is the decisive foundation of client when a purchase textiles, and therefore, soft feel is considered to the most important factor affecting textile sales.But the problems such as cost is high, performance is single, submissive less effective that current softener exists.
Summary of the invention
In order to solve the above-mentioned defect existed in prior art, the invention provides a kind of high temperature resistant chemical & blended fabric softener and preparation method thereof.
For solving the problems of the technologies described above, the technical solution adopted in the present invention is as follows:
A kind of high temperature resistant chemical & blended fabric softener, its raw material comprises following component: sorbitan fatty acid ester 15-25 part, polyoxyethylene ether 35-40 part, acrylamide 25-30 part, isopropanolamine 20-25 part and deionized water 35-40 part, described number is mass fraction.
Above-mentioned softener has good submissive effect, and with low cost.
In order to strengthen the cooperative effect between each component further, strengthen submissive effect further, the raw material of above-mentioned high temperature resistant chemical & blended fabric softener also comprises: essential oil 15-20 part, and described number is mass fraction.
In order to strengthen the cooperative effect between each component further, strengthen submissive effect further, the raw material of above-mentioned high temperature resistant chemical & blended fabric softener also comprises: octamethylcyclotetrasiloxane 20-25 part, and described number is mass fraction.
In order to strengthen the cooperative effect between each component further, strengthen submissive effect further, the raw material of above-mentioned high temperature resistant chemical & blended fabric softener also comprises: calcium chloride 12-15 part, and described number is mass fraction.
In order to strengthen the cooperative effect between each component further, strengthen submissive effect further, the raw material of above-mentioned high temperature resistant chemical & blended fabric softener also comprises: sodium nitrate 15-18 part, and described number is mass fraction.
In order to strengthen the cooperative effect between each component further, strengthen submissive effect further, the raw material of above-mentioned high temperature resistant chemical & blended fabric softener also comprises: stearic acid macrogol ester 15-20 part, described number is mass fraction.:
The preparation method of above-mentioned high temperature resistant chemical & blended fabric softener, by sorbitan fatty acid ester, polyoxyethylene ether, acrylamide, isopropanolamine and deionized water at 60 DEG C, stirs 5 hours, to obtain final product.
The NM technology of the present invention is all with reference to prior art.
The present invention is high temperature resistant, and chemical & blended fabric softener result of use well, does not damage fabric face, raw material is easy to get, strong with the adhesion of fiber, high temperature resistant, water-fastness, wear-resisting, excellent soft effect and smooth feel can be obtained, and synthetic fiber can be made to have certain antistatic effect, ABRASION RESISTANCE and the tearing brute force of fabric can also be improved.
Detailed description of the invention
In order to understand the present invention better, illustrate content of the present invention further below in conjunction with embodiment, but content of the present invention is not only confined to the following examples.
Embodiment 1
A kind of raw material of high temperature resistant chemical & blended fabric softener comprises following component: sorbitan fatty acid ester 19 parts, polyoxyethylene ether (building the fatty alcohol-polyoxyethylene ether of chemical industry purchased from Suzhou section) 38 parts, acrylamide 28 parts, isopropanolamine 23 parts, essential oil 18 parts, octamethylcyclotetrasiloxane 23 parts, 14 parts, calcium chloride, 17 parts, sodium nitrate, stearic acid macrogol ester 18 parts and deionized water 32 parts, described number is mass fraction.
The preparation method of above-mentioned high temperature resistant chemical & blended fabric softener, mixes each raw material components, at 60 DEG C, stirs 5 hours, to obtain final product.
Embodiment 2
Substantially the same manner as Example 1, difference is: the raw material of high temperature resistant chemical & blended fabric softener comprises following component: sorbitan fatty acid ester 15 parts, polyoxyethylene ether 35 parts, acrylamide 25 parts, isopropanolamine 20 parts, essential oil 15 parts, octamethylcyclotetrasiloxane 20 parts, 12 parts, calcium chloride, 15 parts, sodium nitrate, stearic acid macrogol ester 15 parts and deionized water 35 parts, described number is mass fraction.
Embodiment 3
Substantially the same manner as Example 1, difference is: the raw material of high temperature resistant chemical & blended fabric softener comprises following component: sorbitan fatty acid ester 25 parts, polyoxyethylene ether 40 parts, acrylamide 30 parts, isopropanolamine 25 parts, essential oil 20 parts, octamethylcyclotetrasiloxane 25 parts, 15 parts, calcium chloride, 18 parts, sodium nitrate, stearic acid macrogol ester 20 parts and deionized water 40 parts, described number is mass fraction.
Application Example: by after chemical & blended fabric the various embodiments described above gained softener infiltration 10min, (use amount is 5g/m
2), the performance such as high temperature resistant, water-fastness, wear-resisting, anti-tear broken, antistatic of fabric all promotes more than 45%, and obtains excellent soft effect and smooth feel, and after washing 10 times, performance degradation is less than 1%.
Claims (7)
1. a high temperature resistant chemical & blended fabric softener, it is characterized in that: its raw material comprises following component: sorbitan fatty acid ester 15-25 part, polyoxyethylene ether 35-40 part, acrylamide 25-30 part, isopropanolamine 20-25 part and deionized water 35-40 part, described number is mass fraction.
2. high temperature resistant chemical & blended fabric softener as claimed in claim 1, it is characterized in that: its raw material also comprises: essential oil 15-20 part, described number is mass fraction.
3. high temperature resistant chemical & blended fabric softener as claimed in claim 1 or 2, it is characterized in that: its raw material also comprises: octamethylcyclotetrasiloxane 20-25 part, described number is mass fraction.
4. high temperature resistant chemical & blended fabric softener as claimed in claim 1 or 2, it is characterized in that: its raw material also comprises: calcium chloride 12-15 part, described number is mass fraction.
5. high temperature resistant chemical & blended fabric softener as claimed in claim 1 or 2, it is characterized in that: its raw material also comprises: sodium nitrate 15-18 part, described number is mass fraction.
6. high temperature resistant chemical & blended fabric softener as claimed in claim 1 or 2, is characterized in that: its raw material also comprises: stearic acid macrogol ester 15-20 part, described number is mass fraction.
7. the preparation method of the high temperature resistant chemical & blended fabric softener described in claim 1-6 any one, is characterized in that: by sorbitan fatty acid ester, polyoxyethylene ether, acrylamide, isopropanolamine and deionized water at 60 DEG C, stirs 5 hours, to obtain final product.