CN105113221A - Softener for tear-resisting chemical fiber fabric and preparation method thereof - Google Patents
Softener for tear-resisting chemical fiber fabric and preparation method thereof Download PDFInfo
- Publication number
- CN105113221A CN105113221A CN201510584115.4A CN201510584115A CN105113221A CN 105113221 A CN105113221 A CN 105113221A CN 201510584115 A CN201510584115 A CN 201510584115A CN 105113221 A CN105113221 A CN 105113221A
- Authority
- CN
- China
- Prior art keywords
- parts
- chemical
- softener
- tear
- blended fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a softener for a tear-resisting chemical fiber fabric. The softener is prepared from, by mass, 30-35 parts of stearic acid, 25-30 parts of N-Methyldioctylamine, 25-30 parts of acrylamide, 20-25 parts of alkylphenol ethoxylates and 40-45 parts of deionized water. The softener for the tear-resisting chemical fiber fabric is good in using effect, does not damage the surface of the fabric, is made of the raw materials easy to obtain, can be strongly bound with fibers, resists high temperature, washing and wear, can have an excellent softening effect and a smooth hand feeling, enables synthetic fibers to have a certain antistatic effect and can improve the wear resistance and tear strength of the fabric.
Description
Technical field
The present invention relates to a kind of anti tear chemical & blended fabric softener and preparation method thereof, belong to fabric arts.
Background technology
In the technical process such as usual fabric is weaved at chemical fibre, pre-treatment, it is coarse that several factors may make fabric become feel, all
Softener need be added and improve feel.Softener be one can give clothing and fabric feel, dress and use time have soft joyful
The daily chemical product of sensation.Level and smooth, the soft effect of softener is mainly due to after softener is adsorbed on fiber surface, prevent fiber from directly contacting with fiber, reduce the coefficient of kinetic friction between fiber and fiber and confficient of static friction, reduce the resistance between fabric component and the resistance between fabric and human body, to reach effect soft, smooth, comfortable and easy to wear.Particularly in recent years, softener becomes particularly important in textile processing, and almost each all have passed through soft finish from textile mills' textiles out.The main target of this arrangement be obtain a kind of softness feel to facilitate textile process and to improve wearability.Usually, the soft feel of comfortable is the decisive foundation of client when a purchase textiles, and therefore, soft feel is considered to the most important factor affecting textile sales.But the problems such as cost is high, performance is single, submissive less effective that current softener exists.
Summary of the invention
In order to solve the above-mentioned defect existed in prior art, the invention provides a kind of anti tear chemical & blended fabric softener and preparation method thereof.
For solving the problems of the technologies described above, the technical solution adopted in the present invention is as follows:
A kind of anti tear chemical & blended fabric softener, its raw material comprises following component: stearic acid 30-35 part, two octyl methyl tertiary amine 25-30 part, acrylamide 25-30 part, alkylphenol polyoxyethylene 20-25 part and deionized water 40-45 part, described number is mass fraction.
Above-mentioned softener has good submissive effect, and with low cost.
In order to strengthen the cooperative effect between each component further, strengthen submissive effect further, the raw material of above-mentioned anti tear chemical & blended fabric softener also comprises: lauryl sodium sulfate 25-30 part, and described number is mass fraction.
In order to strengthen the cooperative effect between each component further, strengthen submissive effect further, the raw material of above-mentioned anti tear chemical & blended fabric softener also comprises: triethanolamine 20-25 part, and described number is mass fraction.
In order to strengthen the cooperative effect between each component further, strengthen submissive effect further, the raw material of above-mentioned anti tear chemical & blended fabric softener also comprises: sodium carboxymethylcellulose 22-25 part, and described number is mass fraction.
In order to strengthen the cooperative effect between each component further, strengthen submissive effect further, the raw material of above-mentioned anti tear chemical & blended fabric softener also comprises: essential oil 15-20 part, and described number is mass fraction.
In order to strengthen the cooperative effect between each component further, strengthen submissive effect further, the raw material of above-mentioned anti tear chemical & blended fabric softener also comprises: epoxychloropropane 20-25 part, and described number is mass fraction.：
The preparation method of above-mentioned anti tear chemical & blended fabric softener, by stearic acid, two octyl methyl tertiary amine, acrylamide, alkylphenol polyoxyethylene and deionized water at 50 DEG C, stirs 6 hours, to obtain final product.
The NM technology of the present invention is all with reference to prior art.
It is of the present invention that anti tear chemical & blended fabric softener result of use well, does not damage fabric face, raw material is easy to get, strong with the adhesion of fiber, high temperature resistant, water-fastness, wear-resisting, excellent soft effect and smooth feel can be obtained, and synthetic fiber can be made to have certain antistatic effect, ABRASION RESISTANCE and the tearing brute force of fabric can also be improved.
Detailed description of the invention
In order to understand the present invention better, illustrate content of the present invention further below in conjunction with embodiment, but content of the present invention is not only confined to the following examples.
Embodiment 1
A kind of raw material of anti tear chemical & blended fabric softener comprises following component: stearic acid 32 parts, two octyl methyl tertiary amine 28 parts, acrylamide 28 parts, alkylphenol polyoxyethylene (TX-4, Jiangsu Hai'an Petrochemical Plant) 22 parts, lauryl sodium sulfate 28 parts, triethanolamine 23 parts, sodium carboxymethylcellulose 24 parts, essential oil 18 parts, epoxychloropropane 23 parts and deionized water 43 parts, described number is mass fraction.
The preparation method of above-mentioned anti tear chemical & blended fabric softener, mixes each raw material components, at 50 DEG C, stirs 6 hours, to obtain final product.
Embodiment 2
Substantially the same manner as Example 1, difference is: the raw material of anti tear chemical & blended fabric softener comprises following component: stearic acid 35 parts, two octyl methyl tertiary amine 30 parts, acrylamide 30 parts, alkylphenol polyoxyethylene 25 parts, lauryl sodium sulfate 30 parts, triethanolamine 25 parts, sodium carboxymethylcellulose 25 parts, essential oil 20 parts, epoxychloropropane 25 parts and deionized water 45 parts, described number is mass fraction.
Embodiment 3
Substantially the same manner as Example 1, difference is: the raw material of anti tear chemical & blended fabric softener comprises following component: stearic acid 30 parts, two octyl methyl tertiary amine 25 parts, acrylamide 25 parts, alkylphenol polyoxyethylene 20 parts, lauryl sodium sulfate 25 parts, triethanolamine 20 parts, sodium carboxymethylcellulose 22 parts, essential oil 15 parts, epoxychloropropane 20 parts and deionized water 40 parts, described number is mass fraction.
Application Example: by after chemical & blended fabric the various embodiments described above gained softener infiltration 10min, (use amount is 5g/m
2), the performance such as high temperature resistant, water-fastness, wear-resisting, anti-tear broken, antistatic of fabric all promotes more than 46%, and obtains excellent soft effect and smooth feel, and after washing 10 times, performance degradation is less than 1%.
Claims (7)
1. an anti tear chemical & blended fabric softener, it is characterized in that: its raw material comprises following component: stearic acid 30-35 part, two octyl methyl tertiary amine 25-30 part, acrylamide 25-30 part, alkylphenol polyoxyethylene 20-25 part and deionized water 40-45 part, described number is mass fraction.
2. anti tear chemical & blended fabric softener as claimed in claim 1, it is characterized in that: its raw material also comprises: lauryl sodium sulfate 25-30 part, described number is mass fraction.
3. anti tear chemical & blended fabric softener as claimed in claim 1 or 2, it is characterized in that: its raw material also comprises: triethanolamine 20-25 part, described number is mass fraction.
4. anti tear chemical & blended fabric softener as claimed in claim 1 or 2, it is characterized in that: its raw material also comprises: sodium carboxymethylcellulose 22-25 part, described number is mass fraction.
5. anti tear chemical & blended fabric softener as claimed in claim 1 or 2, it is characterized in that: its raw material also comprises: essential oil 15-20 part, described number is mass fraction.
6. anti tear chemical & blended fabric softener as claimed in claim 1 or 2, it is characterized in that: its raw material also comprises: epoxychloropropane 20-25 part, described number is mass fraction.
7. the preparation method of the anti tear chemical & blended fabric softener described in claim 1-6 any one, it is characterized in that: by stearic acid, two octyl methyl tertiary amine, acrylamide, alkylphenol polyoxyethylene and deionized water at 50 DEG C, stir 6 hours, to obtain final product.