CN105112012A - 一种物化交联反应高分子自粘防水卷材 - Google Patents
一种物化交联反应高分子自粘防水卷材 Download PDFInfo
- Publication number
- CN105112012A CN105112012A CN201510530847.5A CN201510530847A CN105112012A CN 105112012 A CN105112012 A CN 105112012A CN 201510530847 A CN201510530847 A CN 201510530847A CN 105112012 A CN105112012 A CN 105112012A
- Authority
- CN
- China
- Prior art keywords
- coiled material
- polymer
- materialization
- crosslinking reaction
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及防水卷材技术领域,具体涉及一种物化交联反应高分子自粘防水卷材,其包括:耐候保护砂层、耐候保护砂层上的高分子胶粘剂层以及高分子胶粘剂层上的高分子复合材料片材层。高分子复合材料片材为聚烯烃与纳米高岭土的复合材料,具有高强度高断裂伸长率;合成高分子胶粘剂是一个富电子体系,含有大π键,能与现浇混凝土实现永久粘接。
Description
技术领域
本发明涉及防水卷材技术领域,具体涉及一种物化交联反应高分子自粘防水卷材。
背景技术
防水卷材又称强力交叉膜,是一种由特制的交叉层压高密度聚乙烯(HDPE)强力薄膜与优质的高聚物自粘橡胶沥青经特殊工艺复合而成的高性能、冷施工的自粘复合膜防水卷材,主要是用于建筑墙体、屋面、以及隧道、公路、垃圾填埋场等处,起到抵御外界雨水、地下水渗漏的一种可卷曲成卷状的柔性建材产品,具有优异的尺寸稳定性,热稳定性,抗紫外线性能和双向耐撕裂性能。作为工程基础与建筑物之间无渗漏连接,是整个工程防水的第一道屏障,对整个工程起着至关重要的作用。目前,防水卷材产品的种类主要有沥青防水卷材和高分子防水卷材,例如沥青防水卷材、改性沥青防水卷材、SBS改性沥青防水卷材、自粘防水卷材、APP改性沥青防水卷材等。
但是现有技术中的自粘防水卷材如果处于一些特定的潮湿环境下,其防水性能还是无法满足实际的需求。
发明内容
本发明的目的是提供一种物化交联反应高分子自粘防水卷材,以解决现有技术的不足。
一种物化交联反应高分子自粘防水卷材,包括:耐候保护砂层、所述耐候保护砂层上的高分子胶粘剂层以及所述高分子胶粘剂层上的高分子复合材料片材层。
其中:
所述高分子胶粘剂层包括以下质量百分含量的各个组份:富电子体系软化油30~50%,热熔胶级弹性体4~6%,苯乙烯-丁二烯-苯乙烯嵌段共聚物5~10%,丁苯橡胶2~3%,废弃橡胶弹性体5~20%,防紫外剂0.1~0.5%,高温树脂3~6%,增粘树脂10~20%,界面剂0.05~0.15%,颜填料5~15%。
具体的,所述富电子体系软化油包括以下质量百分含量的各个组份:抽出油(石油馏分溶剂精制的抽出液经脱除溶剂后的油),重油,和轻油。其中,含抽出油10~20%,重油30~50%,轻油40~50%。富电子体系软化油中,抽出油主要成分为C6~C8的芳烃,轻油主要成分是含5到11个碳原子的链烷或环烷,重油主要成分为碳氢化合物。
热熔胶级弹性体可选自热熔级EVA,可通过购买得到,例如:美国杜邦公司的EVA250产品。
防紫外剂体可选自酚基取代的类紫外线吸收剂,可通过购买得到,例如:巴斯夫公司的UV328产品。
苯乙烯-丁二烯-苯乙烯嵌段共聚物可选自星型SBS,可通过购买得到,例如,韩国LG公司的SBS411产品。
丁苯橡胶可选自粉末类丁苯橡胶PSBR,可通过购买得到,例如,山东桥隆化工科技有限责任公司的PSBR产品。
废弃橡胶弹性体可选自天然精细橡胶粉三元乙丙类胶粉,可通过购买得到,例如,江阴市众晨橡塑有限公司的三元乙丙胶粉产品。
增粘树脂可选自C9石油树脂,萜烯树脂,可通过购买得到,例如:濮阳市恒丰石油化工有限公司公司的C9石油树脂产品,淄博齐哲化工有限公司的萜烯树脂产品。
高温树脂可选自古马隆树脂类树脂,可通过购买得到,例如:濮阳市瑞科化工有限公司的古马隆树脂产品
界面剂可选自高分子改性水泥类材料,可通过购买得到,例如:武汉众鑫久久新型建材有限公司公司的ZX-901产品。
颜填料可选自铁红类颜料,滑石粉类填料,可通过购买得到,例如:石家庄市讯达化工有限责任公司的氧化铁红130产品,凉山州锡成新材料股份有限公司的工业级滑石粉HSH-600产品。
高分子胶粘剂层可与现浇混凝土产生物理渗透及化学交联反应实现永久性粘接。其机理为:非沥青基体系物化交联反应自粘防水卷材中的界面剂通过渗透到未干的水泥砂浆中去(物理过程),由于非沥青基体系物化交联反应自粘防水卷材是一个富电子体系,含有大π键,而未干的水泥砂浆中的金属离子是缺电子体系,所以富电子体系和缺电子体系通过配位反应生产配合物,使得非沥青基体系物化交联反应自粘防水卷材与混凝土形成一个致密并且有一定强度的整体。
所述高分子复合材料片材层为聚烯烃与表面改性纳米高岭土的复合层,其制备方法如下:将纳米高岭土(一维尺寸为纳米级的片状粉体)经改性剂进行表面改性,得到表面改性高岭土,再将所述表面改性高岭土与聚烯烃经过混合后密炼造粒干燥,然后通过挤出成型,得到高分子复合材料片材层的材料。密炼的温度为175~185℃,密炼时间为12~18min。
具体的,所述聚烯烃选自高密度聚乙烯、低密度聚乙烯、线性低密度聚乙烯、共聚聚丙烯、均聚丙烯或POE中的任意一种或多种的混合。
具体的,所述改性剂选自丙烯酸丁酯、甲基丙烯酸甲酯、硅烷偶联剂或钛酸酯偶联剂中的任意一种或多种的混合。
所述耐候保护砂层为石英砂层,优选的,石英砂粒径为0.5~1mm。石英砂层在卷材铺设后,保护胶料不受太阳直接照射。
有益效果:
1)物化交联反应高分子自粘防水卷材的高分子复合材料片材具有高强度高断裂伸长率。
2)物化交联反应高分子自粘防水卷材的合成高分子胶粘剂能与现浇混凝土实现永久粘接。
具体实施方式
以下对本发明的原理和特征进行描述,所举实例只用于解释本发明,并非用于限定本发明的范围。
实施例1
1)高分子胶粘剂层,具体的,将:富电子体系软化油40%,热熔胶级弹性体4%,苯乙烯-丁二烯-苯乙烯嵌段共聚物7.5%,丁苯橡胶2.5%,废弃橡胶弹性体17%,防紫外剂0.3%,高温树脂4%,增粘树脂12%,界面剂0.1%,铁红3%,滑石粉9.4%混合后,得到。
2)高分子复合材料片材层由聚烯烃与表面改性纳米高岭土的复合层,具体的,将纳米高岭土经改性剂进行表面改性,得到表面改性高岭土,在将表面改性高岭土与聚烯烃经过混合后密炼造粒干燥,然后通过单螺杆挤出三辊压光挤出成型,得到高分子复合材料片材层的材料,片材厚度为0.67-0.73mm。
3)将高分子复合材料片材层、高分子胶粘剂层和石英砂层进行复合,得到物化交联反应高分子自粘防水卷材,其中片材层厚度为0.67-0.73mm,高分子胶粘剂层厚度为0.47-0.53mm,石英砂完全覆盖胶料。
实施例1得到的防水卷材测试数据如下表:
测试标准为GB/T23457-2009
实施例2
1)高分子胶粘剂层,具体的,将:富电子体系软化油42%,热熔胶级弹性体5%,苯乙烯-丁二烯-苯乙烯嵌段共聚物9%,丁苯橡胶1%,废弃橡胶弹性体12%,防紫外剂0.3%,高温树脂4%,增粘树脂13%,界面剂0.1%,铁红4%,滑石粉9.6%混合后,得到。
2)高分子复合材料片材层由聚烯烃与表面改性纳米高岭土的复合层,具体的,将纳米高岭土经改性剂进行表面改性,得到表面改性高岭土,在将表面改性高岭土与聚烯烃经过混合后密炼造粒干燥,然后通过单螺杆挤出三辊压光挤出成型,得到高分子复合材料片材层的材料,片材厚度为1.16-1.24mm。
3)将高分子复合材料片材层、高分子胶粘剂层和石英砂层进行复合,得到物化交联反应高分子自粘防水卷材,其中片材层厚度为1.16-1.24mm,高分子胶粘剂层厚度为0.47-0.53mm,石英砂完全覆盖胶料。
实施例2得到的防水卷材测试数据如下表:
测试标准为GB/T23457-2009
实施例3
1)高分子胶粘剂层,具体的,将:富电子体系软化油48%,热熔胶级弹性体6%,丁苯橡胶5%,废弃橡胶弹性体8%,防紫外剂0.3%,增粘树脂17%,界面剂0.1%,铁红4%,滑石粉11.6%混合后,得到。
2)高分子复合材料片材层由聚烯烃与表面改性纳米高岭土的复合层,具体的,将纳米高岭土经改性剂进行表面改性,得到表面改性高岭土,在将表面改性高岭土与聚烯烃经过混合后密炼造粒干燥,然后通过单螺杆挤出三辊压光挤出成型,得到高分子复合材料片材层的材料,片材厚度为1.45-1.55mm。
3)将高分子复合材料片材层、高分子胶粘剂层和石英砂层进行复合,得到物化交联反应高分子自粘防水卷材,其中片材层厚度为1.45-1.55mm,高分子胶粘剂层厚度为0.47-0.53mm,石英砂完全覆盖胶料。
实施例3得到的防水卷材测试数据如下表:
测试标准为GB/T23457-2009
以上所述仅为本发明的较佳实施方式,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (7)
1.一种物化交联反应高分子自粘防水卷材,其特征在于,包括:耐候保护砂层、所述耐候保护砂层上的高分子胶粘剂层以及所述高分子胶粘剂层上的高分子复合材料片材层。
2.根据权利要求1所述的物化交联反应高分子自粘防水卷材,其特征在于,所述高分子胶粘剂层包括以下质量百分含量的各个组份:富电子体系软化油30~50%,热熔胶级弹性体4~6%,苯乙烯-丁二烯-苯乙烯嵌段共聚物5~10%,丁苯橡胶2~3%,废弃橡胶弹性体10~20%,防紫外剂0.1~0.5%,高温树脂5~6%,增粘树脂15~20%,界面剂0.05~0.15%,颜填料10~20%。
3.根据权利要求2所述的物化交联反应高分子自粘防水卷材,其特征在于,所述富电子体系软化油包括以下质量百分含量的各个组份:抽出油10~20%,重油30~50%,轻油40~50%。
4.根据权利要求1所述的物化交联反应高分子自粘防水卷材,其特征在于,所述高分子复合材料片材层为聚烯烃与表面改性纳米高岭土的复合层,其制备方法如下:将纳米高岭土经改性剂进行表面改性,得到表面改性高岭土,再将所述表面改性高岭土与聚烯烃经过混合后密炼造粒干燥,然后通过挤出成型,得到高分子复合材料片材层的材料。
5.根据权利要求4所述的物化交联反应高分子自粘防水卷材,其特征在于:所述聚烯烃选自高密度聚乙烯、低密度聚乙烯、线性低密度聚乙烯、共聚聚丙烯、均聚丙烯或POE中的任意一种或多种的混合。
6.根据权利要求4所述的物化交联反应高分子自粘防水卷材,其特征在于:所述改性剂选自丙烯酸丁酯、甲基丙烯酸甲酯、硅烷偶联剂或钛酸酯偶联剂中的任意一种或多种的混合。
7.根据权利要求1至6任一所述的物化交联反应高分子自粘防水卷材,其特征在于:所述耐候保护砂层为石英砂层,石英砂粒径为0.5~1mm。