CN105111766A - Production method of plastic bucket - Google Patents
Production method of plastic bucket Download PDFInfo
- Publication number
- CN105111766A CN105111766A CN201510529286.7A CN201510529286A CN105111766A CN 105111766 A CN105111766 A CN 105111766A CN 201510529286 A CN201510529286 A CN 201510529286A CN 105111766 A CN105111766 A CN 105111766A
- Authority
- CN
- China
- Prior art keywords
- parts
- production method
- plastic bucket
- present
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method of a plastic bucket, which comprises the following steps: proportionally putting the components into a stirrer, sufficiently stirring uniformly, and adding the mixture into a double screw extruder to perform extrusion and granulation, wherein the extrusion temperature is 165 DEG C. The production method overcome the defects of poor heat resistance, poor user experience, short service life and the like in the prior art, thereby implementing the advantages of favorable heat resistance, favorable user experience and long service life.
Description
Technical field
The present invention relates to plastic products technology field, particularly, relate to a kind of production method of plastic bucket.
Background technology
Raw material based on synthetic resins or natural resin, adds (or not adding) various additives for plastics, strongthener and filler, and under certain temperature, pressure, the type of making is moulded in processing or crosslinking curing is shaping, the solid material obtained or goods.Plastics refer to resin (or using monomer direct polymerization in the course of processing) as main component, with additives such as softening agent, weighting agent, lubricant, tinting materials for ancillary component, the material of energy flowing forming in the course of processing, be the macromolecular compound of synthesis, freely can change body styles.Utilize the material that raw material monomer is polymerized with synthesis or condensation reaction, be made up of additives such as synthetic resins and filler, softening agent, stablizer, lubricant, colorants, its main component is synthetic resins.
At present, the application of plastics is throughout the every field of industrial or agricultural, life, and plastics are also indispensable in daily life.Present handset shell major part be all adopt made of plastic, and the high temperature of the general not abilities more than 150 degree of current plastics, and color is more dull, cannot be transferred on goods by colour image by transfer machine.
Realizing in process of the present invention, contriver finds at least to exist in prior art the defect such as poor heat resistance, poor user experience and work-ing life is short.
Summary of the invention
The object of the invention is to, for the problems referred to above, propose a kind of production method of plastic bucket, to realize the advantage of the good and long service life of good heat resistance, Consumer's Experience.
For achieving the above object, the technical solution used in the present invention is: a kind of production method of plastic bucket, comprising:
(1) by each component of following parts by weight proportioning:
Elastomerics: 1 part;
Weighting agent: 2 parts;
Polyurethane Thermoplastic Elastomer rubber: 4 parts;
Softening agent: 2.1 parts;
Polypropylene: 3.5 parts;
Calcium carbonate: 2.6 parts;
Lubricant: 1.93 parts;
Polybutylene terephthalate: 3 parts;
Sanitas: 0.2 part;
Tinting material: 1.3 parts;
Stablizer: 2.15 parts;
Barium sulfate: 4.6 parts;
Synthetic resins: 8 parts;
(2) put into after stirrer stirs by each component by proportioning, compound is added twin screw extruder extruding pelletization, extrusion temperature is 165 DEG C.
The production method of the plastic bucket of various embodiments of the present invention, owing to comprising: put into after stirrer stirs by each component by proportioning, compound is added twin screw extruder extruding pelletization, extrusion temperature is 165 DEG C; Thus poor heat resistance in prior art, poor user experience and work-ing life short defect can be overcome, to realize the advantage of the good and long service life of good heat resistance, Consumer's Experience.
Other features and advantages of the present invention will be set forth in the following description, and, partly become apparent from specification sheets, or understand by implementing the present invention.
Below by embodiment, technical scheme of the present invention is described in further detail.
Embodiment
Below the preferred embodiments of the present invention are described, should be appreciated that preferred embodiment described herein is only for instruction and explanation of the present invention, is not intended to limit the present invention.
According to the embodiment of the present invention, provide a kind of production method of plastic bucket, comprising:
(1) by each component of following parts by weight proportioning:
Elastomerics: 1 part;
Weighting agent: 2 parts;
Polyurethane Thermoplastic Elastomer rubber: 4 parts;
Softening agent: 2.1 parts;
Polypropylene: 3.5 parts;
Calcium carbonate: 2.6 parts;
Lubricant: 1.93 parts;
Polybutylene terephthalate: 3 parts;
Sanitas: 0.2 part;
Tinting material: 1.3 parts;
Stablizer: 2.15 parts;
Barium sulfate: 4.6 parts;
Synthetic resins: 8 parts;
(2) put into after stirrer stirs by each component by proportioning, compound is added twin screw extruder extruding pelletization, extrusion temperature is 165 DEG C.
Technical scheme products obtained therefrom of the present invention, empirical tests, thermotolerance is high; Surface can effectively absorb heat sublimation ink ink, and by heat sublimation ink print image out through the mode of heating, image user liked is attached on product surface, promotes the personalised effects used; There is fire-retardant and resistant to elevated temperatures performance.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (1)
1. a production method for plastic bucket, is characterized in that, comprising:
(1) by each component of following parts by weight proportioning:
Elastomerics: 1 part;
Weighting agent: 2 parts;
Polyurethane Thermoplastic Elastomer rubber: 4 parts;
Softening agent: 2.1 parts;
Polypropylene: 3.5 parts;
Calcium carbonate: 2.6 parts;
Lubricant: 1.93 parts;
Polybutylene terephthalate: 3 parts;
Sanitas: 0.2 part;
Tinting material: 1.3 parts;
Stablizer: 2.15 parts;
Barium sulfate: 4.6 parts;
Synthetic resins: 8 parts;
(2) put into after stirrer stirs by each component by proportioning, compound is added twin screw extruder extruding pelletization, extrusion temperature is 165 DEG C.