CN105111634A - PVC insulation cable manufacturing formula - Google Patents
PVC insulation cable manufacturing formula Download PDFInfo
- Publication number
- CN105111634A CN105111634A CN201510643169.3A CN201510643169A CN105111634A CN 105111634 A CN105111634 A CN 105111634A CN 201510643169 A CN201510643169 A CN 201510643169A CN 105111634 A CN105111634 A CN 105111634A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc
- stearate
- calcium carbonate
- dioctyl phthalate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PVC insulation cable manufacturing formula. A manufacturing material comprises PVC, dibasic phosphate, dioctyl phthalate, lead stearate, petroleum ester, calcium carbonate, tribasic lead sulfate and calcined clay. The weight percent of the constitutional materials is as follows: 58 to 62 parts of PVC; 1.2 to 1.3 parts of dibasic phosphate; 1.1 to 1.3 parts of dioctyl phthalate; 0.4 to 0.6 parts of lead stearate; 10 to 12 parts of chlorinated paraffin; 2.2 to 2.5 parts of calcium stearate; 12 to 15 parts of petroleum easter; 3.5 to 4.5 parts of calcium carbonate; 1.5 to 2.0 parts of tribasic lead sulfate; 3.0 to 4.0 parts of calcined clay. The PVC insulation cable manufacturing formula adopts the dibasic phosphate, dioctyl phthalate, lead stearate, petroleum easter, calcium carbonate, tribasic lead sulfate and calcined clay as the auxiliary materials for manufacturing the PVC material, the manufactured PVC material is high in insulation performance, and the weaknesses of the prior art can be overcome.
Description
Technical field
The present invention relates to plastics Application and preparation technical field, be specially a kind of PVC insulated cable and make formula.
Background technology
PVC cable material is made up of polyvinyl chloride (PVC) RESINS, stablizer, softening agent, weighting agent, lubricant, oxidation inhibitor, tinting material etc.Proof voltage and the insulation resistance of PVC cable material are higher, but specific inductivity and dielectric loss larger.Therefore, the general main insulation layer being used as low pressure (≤1KV) and mesohigh (6 ~ 10KV) cable.PVC plastic, owing to having difficult combustion, oil resistant, Inverter fed motor, resistance to chemical attack and good water resistance, is therefore also widely used as the jacket material of electric wire.Utilize and add special property auxiliary agent or properties-correcting agent, the PVC cable material of heat resistant type (105 DEG C), cold resisting type, oil-resisting type, nonflammable, special soft-type and nontoxic type can be produced respectively, to meet the needs of special electric wire cable product.
But in prior art, do not have a kind of PVC cable material making formula that the insulativity of PVC insulated cable can be realized to strengthen, can not meet the needs of industrial production and people's life.
Summary of the invention
A kind of PVC insulated cable is the object of the present invention is to provide to make formula, to solve the problem proposed in above-mentioned background technology.
For achieving the above object, the invention provides following technical scheme: a kind of PVC insulated cable makes formula, make material and comprise PVC, two alkali formula phosphorous acid, dioctyl phthalate (DOP), lead stearate, phenyl alkylsulfonate, calcium carbonate, tribasic lead sulfate and calcinated argil; Described composition material accounts for percentage number: PVC58-62 part; Two alkali formula phosphorous acid 1.2-1.3 parts; Dioctyl phthalate (DOP) 1.1-1.3 part; Lead stearate 0.4-0.6; Clorafin 10-12 part; Calcium stearate 2.2-2.5 part; Phenyl alkylsulfonate 12-15 part; Calcium carbonate 3.5-4.5 part; Tribasic lead sulfate 1.5-2.0 part; Calcinated argil 3.0-4.0 part.
As further technical scheme of the present invention: described composition material accounts for percentage number and is: PVC59 part; Two 1.2 parts, alkali formula phosphorous acid; Dioctyl phthalate (DOP) 1.2 parts; Lead stearate 0.6; Clorafin 12 parts; Calcium stearate 2.4 parts; Phenyl alkylsulfonate 14 parts; 4.0 parts, calcium carbonate; Tribasic lead sulfate 1.9 parts; Calcinated argil 3.7 parts.
Compared with prior art, the invention has the beneficial effects as follows: this PVC insulated cable makes formula, adopt two alkali formula phosphorous acid, dioctyl phthalate (DOP), lead stearate, phenyl alkylsulfonate, calcium carbonate, tribasic lead sulfate and calcinated argil as the making subsidiary material of PVC material, obtained PVC material insulativity is strong, compensate for the deficiencies in the prior art.
Embodiment
Be clearly and completely described to the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
The invention provides a kind of technical scheme: a kind of PVC insulated cable makes formula, make material and comprise PVC, two alkali formula phosphorous acid, dioctyl phthalate (DOP), lead stearate, phenyl alkylsulfonate, calcium carbonate, tribasic lead sulfate and calcinated argil; Described composition material accounts for percentage number: PVC58-62 part; Two alkali formula phosphorous acid 1.2-1.3 parts; Dioctyl phthalate (DOP) 1.1-1.3 part; Lead stearate 0.4-0.6; Clorafin 10-12 part; Calcium stearate 2.2-2.5 part; Phenyl alkylsulfonate 12-15 part; Calcium carbonate 3.5-4.5 part; Tribasic lead sulfate 1.5-2.0 part; Calcinated argil 3.0-4.0 part.
As further technical scheme of the present invention: described composition material accounts for percentage number and is: PVC59 part; Two 1.2 parts, alkali formula phosphorous acid; Dioctyl phthalate (DOP) 1.2 parts; Lead stearate 0.6; Clorafin 12 parts; Calcium stearate 2.4 parts; Phenyl alkylsulfonate 14 parts; 4.0 parts, calcium carbonate; Tribasic lead sulfate 1.9 parts; Calcinated argil 3.7 parts.
embodiment one:
Select the PVC insulated cable of making 100 parts; Employing proportioning is:
PVC60 part; Two 1.2 parts, alkali formula phosphorous acid; Dioctyl phthalate (DOP) 1.3 parts; Lead stearate 0.6; Clorafin 11 parts; Calcium stearate 2.4 parts; Phenyl alkylsulfonate 13 parts; 4.5 parts, calcium carbonate; Tribasic lead sulfate 2.0 parts; Calcinated argil 4.0 parts.
embodiment two:
Select the PVC insulated cable of making 100 parts; Employing proportioning is:
PVC59 part; Two 1.3 parts, alkali formula phosphorous acid; Dioctyl phthalate (DOP) 1.2 parts; Lead stearate 0.6; Clorafin 11 parts; Calcium stearate 2.4 parts; Phenyl alkylsulfonate 15 parts; 4.5 parts, calcium carbonate; Tribasic lead sulfate 2.0 parts; Calcinated argil 4.0 parts.
embodiment three:
Select the PVC insulated cable of making 100 parts; Employing proportioning is:
PVC62 part; Two 1.2 parts, alkali formula phosphorous acid; Dioctyl phthalate (DOP) 1.2 parts; Lead stearate 0.6; Clorafin 11 parts; Calcium stearate 2.5 parts; Phenyl alkylsulfonate 13 parts; 4.0 parts, calcium carbonate; Tribasic lead sulfate 1.50 parts; Calcinated argil 3.0 parts.
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and when not deviating from spirit of the present invention or essential characteristic, the present invention can be realized in other specific forms.Therefore, no matter from which point, all should embodiment be regarded as exemplary, and be nonrestrictive, scope of the present invention is limited by claims instead of above-mentioned explanation, and all changes be therefore intended in the implication of the equivalency by dropping on claim and scope are included in the present invention.Any Reference numeral in claim should be considered as the claim involved by limiting.
In addition, be to be understood that, although this specification sheets is described according to embodiment, but not each embodiment only comprises an independently technical scheme, this narrating mode of specification sheets is only for clarity sake, those skilled in the art should by specification sheets integrally, and the technical scheme in each embodiment also through appropriately combined, can form other embodiments that it will be appreciated by those skilled in the art that.
Claims (2)
1. a PVC insulated cable makes formula, makes material and comprises PVC, two alkali formula phosphorous acid, dioctyl phthalate (DOP), lead stearate, phenyl alkylsulfonate, calcium carbonate, tribasic lead sulfate and calcinated argil; It is characterized in that: described composition material accounts for percentage number and is: PVC58-62 part; Two alkali formula phosphorous acid 1.2-1.3 parts; Dioctyl phthalate (DOP) 1.1-1.3 part; Lead stearate 0.4-0.6; Clorafin 10-12 part; Calcium stearate 2.2-2.5 part; Phenyl alkylsulfonate 12-15 part; Calcium carbonate 3.5-4.5 part; Tribasic lead sulfate 1.5-2.0 part; Calcinated argil 3.0-4.0 part.
2. make formula according to a kind of PVC insulated cable according to claim 1, it is characterized in that: described composition material accounts for percentage number and is: PVC59 part; Two 1.2 parts, alkali formula phosphorous acid; Dioctyl phthalate (DOP) 1.2 parts; Lead stearate 0.6; Clorafin 12 parts; Calcium stearate 2.4 parts; Phenyl alkylsulfonate 14 parts; 4.0 parts, calcium carbonate; Tribasic lead sulfate 1.9 parts; Calcinated argil 3.7 parts.