CN105111619A - Novel rubber-plastic material - Google Patents

Abstract

The invention relates to a novel-rubber plastic material which comprises the following components in parts by weight: 20 parts of styrene-butadiene rubber, 35 parts of paste resin, 60 parts of magnesium silicate, 25 parts of furnace black, 33 parts of illegal cooking oil, 0.5 part of liquid chlorine, 2.8 parts of stearate, 1 part of petrolatum, 2.2 parts of isopropanol, 2.5 parts of polyethyleneglycol, 2.5 parts of zinc oxide, 10 parts of AC (azodicarbonamide) foaming agent, 1.5 parts of antimony trioxide, 1.3 parts of magnesium oxide and 0.8 part of iron oxide. The preparation method comprises the following steps: oxidizing the illegal cooking oil, uniformly mixing with the other raw materials, banburying, plastifying, calendering, foaming, cutting, inspecting and packaging. By using the illegal cooking oil instead of other industrial greases, the novel-rubber plastic material can greatly save the cost, can effectively remove harmful components through dual oxidation, can be made into plastic products closely related to people, and can also be used as a food-grade plastic.

Description

A kind of Novel rubber plastic material

Technical field

The present invention relates to chemical rubber-plastics material, be specifically related to a kind of Novel rubber plastic material.

Background technology

Rubber and plastic is the general designation of rubber and Plastics Industry, they are all the auxiliary products of oil, they are all the same on source, but, in the process making product, physical property is different, purposes is different especially, the wide of rubber is exactly tire, and plastics, being more and more extensive along with the demand of technology and market and purposes, have be unable to do without inside daily life.

Along with updating and progress of rubber and plastic industry, security level required is more and more higher, people are using the awareness of safety of product of rubber and plastic also more and more higher, due to increasingly sternly completing of market competition, government department is also more and more tighter to the specification of rubber and plastic safety standards, and present Plastic Rubber Products can not reach use standard safely, containing benzene, toxic, and production cost is high.

Summary of the invention

Proposition technical scheme of the present invention is as follows:

A kind of Novel rubber plastic material, the weight part of its constitutive material is: 20 parts, styrene-butadiene rubber(SBR), paste resin 35 parts, Magnesium Silicate q-agent 60 parts, furnace black 25 parts, sewer oil 33 parts, liquid chlorine 0.5 part, stearate 2.8 parts, vaseline 1 part, Virahol 2.2 parts, polyoxyethylene glycol 2.5 parts, 2.5 parts, zinc oxide, AC whipping agent 10 parts, antimonous oxide 1.5 parts, 1.3 parts, magnesium oxide, ferric oxide 0.8 part.

Further, the weight part of its constitutive material is: styrene-butadiene rubber(SBR) 20g, paste resin 35g, Magnesium Silicate q-agent 60g, furnace black 25g, sewer oil 33g, liquid chlorine 0.5g, stearate 2.8g, vaseline 1g, Virahol 2.2g, polyoxyethylene glycol 2.5g, zinc oxide 2.5g, AC whipping agent 10g, antimonous oxide 1.5g, magnesium oxide 1.3g, ferric oxide 0.8g.

Further, a kind of Novel rubber plastic materials processing step, comprises the following steps:

(1) accurately take various raw material by the weight part of constitutive material, sewer oil is led to liquid chlorine again after vaporific oxidation, then with other raw material blendings, drop into Banbury mixer banburying 10min, make temperature reach 80-90 DEG C;

(2), after plastics good for Banbury mixer banburying being dropped into two roller machine 2min, slice cooling is for subsequent use;

(3) film that two roller machine melting is good is put into rolling press 15-20min calendering formation;

(4) shaping film drop into foaming furnace carry out foaming process 8-12min, control temperature at 150-170 DEG C, rotating speed 14-16m/min;

(5) cutting, inspection, packaging.

Beneficial effect of the present invention: utilize sewer oil to replace other commercial grease, can be more cost-saving, and after atomization preliminary oxidation, reusable liquid chlorine carries out the mode of Strong oxdiative, carry out dual oxidation, effectively remove oxious component, reduce distributing of oxious component, the closely-related plastics with people can be made as, also can be used as food grade plastic and use.

Embodiment

A kind of Novel rubber plastic material, by its parts by weight, comprising: 20 parts, styrene-butadiene rubber(SBR), paste resin 35 parts, Magnesium Silicate q-agent 60 parts, furnace black 25 parts, sewer oil 33 parts, liquid chlorine 0.5 part, stearate 2.8 parts, vaseline 1 part, Virahol 2.2 parts, polyoxyethylene glycol 2.5 parts, 2.5 parts, zinc oxide, AC whipping agent 10 parts, antimonous oxide 1.5 parts, 1.3 parts, magnesium oxide, ferric oxide 0.8 part.

Further, the weight part of its constitutive material is: styrene-butadiene rubber(SBR) 20g, paste resin 35g, Magnesium Silicate q-agent 60g, furnace black 25g, sewer oil 33g, liquid chlorine 0.5g, stearate 2.8g, vaseline 1g, Virahol 2.2g, polyoxyethylene glycol 2.5g, zinc oxide 2.5g, AC whipping agent 10g, antimonous oxide 1.5g, magnesium oxide 1.3g, ferric oxide 0.8g.

Further, a kind of Novel rubber plastic materials processing step, comprises the following steps:

(1) accurately take various raw material by the weight part of constitutive material, sewer oil is led to liquid chlorine again after vaporific oxidation, then with other raw material blendings, drop into Banbury mixer banburying 10min, make temperature reach 80-90 DEG C;

(2), after plastics good for Banbury mixer banburying being dropped into two roller machine 2min, slice cooling is for subsequent use;

(3) film that two roller machine melting is good is put into rolling press 15-20min calendering formation;

(4) shaping film drop into foaming furnace carry out foaming process 8-12min, control temperature at 150-170 DEG C, rotating speed 14-16m/min;

(5) cutting, inspection, packaging.

Claims (3)

1. a Novel rubber plastic material, it is characterized in that, the weight part of its constitutive material is: 20 parts, styrene-butadiene rubber(SBR), paste resin 35 parts, Magnesium Silicate q-agent 60 parts, furnace black 25 parts, sewer oil 33 parts, liquid chlorine 0.5 part, stearate 2.8 parts, vaseline 1 part, Virahol 2.2 parts, polyoxyethylene glycol 2.5 parts, 2.5 parts, zinc oxide, AC whipping agent 10 parts, antimonous oxide 1.5 parts, 1.3 parts, magnesium oxide, ferric oxide 0.8 part.

2. a kind of Novel rubber plastic material according to claim 1, it is characterized in that, the weight part of its constitutive material is: styrene-butadiene rubber(SBR) 20g, paste resin 35g, Magnesium Silicate q-agent 60g, furnace black 25g, sewer oil 33g, liquid chlorine 0.5g, stearate 2.8g, vaseline 1g, Virahol 2.2g, polyoxyethylene glycol 2.5g, zinc oxide 2.5g, AC whipping agent 10g, antimonous oxide 1.5g, magnesium oxide 1.3g, ferric oxide 0.8g.

3. a kind of Novel rubber plastic material according to claim 1, is characterized in that, comprise the following steps:

(1) accurately take various raw material by the weight part of constitutive material, sewer oil is led to liquid chlorine again after vaporific oxidation, then with other raw material blendings, drop into Banbury mixer banburying 10min, make temperature reach 80-90 DEG C;

(2), after plastics good for Banbury mixer banburying being dropped into two roller machine 2min, slice cooling is for subsequent use;

(3) film that two roller machine melting is good is put into rolling press 15-20min calendering formation;

(4) shaping film drop into foaming furnace carry out foaming process 8-12min, control temperature at 150-170 DEG C, rotating speed 14-16m/min;

(5) cutting, inspection, packaging.