CN105088590A - Mould-proof blanket production process - Google Patents
Mould-proof blanket production process Download PDFInfo
- Publication number
- CN105088590A CN105088590A CN201510530420.5A CN201510530420A CN105088590A CN 105088590 A CN105088590 A CN 105088590A CN 201510530420 A CN201510530420 A CN 201510530420A CN 105088590 A CN105088590 A CN 105088590A
- Authority
- CN
- China
- Prior art keywords
- soaping
- mildew
- woollen blanket
- manufacture craft
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a mould-proof blanket production process. The mould-proof blanket production process comprises the following steps of: printing, roll compacting, drying, ageing, soaping, washing, softening, drying, carding, polishing, cropping and sewing; and soaping agent is adopted in the soaping process to complete soaping, and the formula of the soaping agent comprises: maleic-methyl acrylate copolymer, surfactant, antifoaming agent, Ethy Diaminedhephen Acetic-Na, dodecyl dimethyl benzyl ammonium chloride, isothiazolinone, polyoxyethylene sorbitan fatty acid ester (T-60), methylparaben and deionized water. According to the special soaping agent, the blanket can be effectively prevented from being eroded by mould.
Description
technical field
The present invention relates to a kind of mildew-resistant woollen blanket manufacture craft.
Background technology
China's most area is in subtropical zone, have a moderate climate humidity, particularly In Middle And Lower Reaches of Changjiang River, because of its distinctive intermittent drizzles in the rainy season seasons, the Growth and Reproduction of very suitable mould, and therefore mold species is numerous and diverse very easily there is going rotten of textile product, causes appreciable economic loss and mould very easily contaminated environment, causes certain threat to the healthy of consumer.
Mould is a kind of microorganism, and mould is biological the same with other, in order to survive, need draw certain energy from the external world, to maintain himself existence and procreation.Mould discharges harmful substance while absorption " nutriment ", going mouldy, along with the breeding of mould gains interest, making to go mouldy and developing both in depth and in breadth, thus making object that serious mildew and rot phenomenon occur to making the object of its parasitism be corroded.Woollen blanket is long-time very easily mouldy in a humid environment.
Summary of the invention
For above-mentioned prior art Problems existing, the invention provides a kind of mildew-resistant woollen blanket manufacture craft, produce quick, the woollen blanket anti-mold effect produced is good.
To achieve these goals, the technical solution used in the present invention is: a kind of mildew-resistant woollen blanket manufacture craft, comprises the following steps: stamp, roll compacting, dry, evaporate, soap, wash, softness, oven dry, carding, polishing, cropping, to make,
Adopt soaping agent in technique of wherein soaping to soap,
Soaping agent formula is: be made up of following each component by weight percentage:
Horse propylene copolymer 50 ~ 75%
Surfactant 5 ~ 15%
Defoamer 0.1 ~ 0.5%
The large sodium acetate 1 ~ 5% of ethylenediamine two salicyl
Dodecyl benzyl dimethyl ammonium chloride 0.1 ~ 5%,
Isothiazolinone 0.1 ~ 5%,
Polyoxyethylene sorbitan fatty acid ester (T-60) 0.1 ~ 5%,
Methyl hydroxybenzoate 0.1 ~ 5%
Deionized water surplus.
Washing adopts open soaper.
Dry and select hot-air oven, temperature controls 135-150.Between C.
Evaporating employing high temperature steaming, is at ambient pressure 170.The superheated steam decatize of C 7 minutes.
Steam temperature: 102 ~ 105 DEG C, saturated vapor steaming time: 20min.
Soft prescription is:
Leavening agent: 5.1kg
Softener: 6.2kg
Antistatic additive: 14kg
Water: 500L.
The present invention is by special soaping agent, its Formulations Formula is: horse propylene copolymer, surfactant, defoamer, the large sodium acetate of ethylenediamine two salicyl, dodecyl benzyl dimethyl ammonium chloride, isothiazolinone, polyoxyethylene sorbitan fatty acid ester (T-60), methyl hydroxybenzoate and deionized water, effective prevention mould is to the erosion of woollen blanket
Permeated after being affixed to fibrous inside or surface mould contact mould inhibitor, medicament is adsorbed in fungal cell adventitia, then through epicyte, enter in people's plasm, final to mould in fatal position, its mechanism is: destroying eucaryotic cell structure one affects metabolic capability *, and destroying nucleic acid structure affects mould breeding thus the growth that effectively inhibit mould.
Detailed description of the invention
Example of the present invention can not limit the present invention to explanation of the present invention, and any change in the implication suitable with the present invention and scope and adjustment, all should think within the scope of the invention.
Embodiment 1: a kind of mildew-resistant woollen blanket manufacture craft, comprises the following steps: stamp, roll compacting, dry, evaporate, soap, wash, softness, oven dry, carding, polishing, cropping, to make,
Adopt soaping agent in technique of wherein soaping to soap,
Soaping agent formula is: be made up of following each component by weight percentage:
Horse propylene copolymer 50%
Surfactant 5%
Defoamer 0.5%
The large sodium acetate 5% of ethylenediamine two salicyl
Dodecyl benzyl dimethyl ammonium chloride 2%,
Isothiazolinone 2%,
Polyoxyethylene sorbitan fatty acid ester (T-60) 4%,
Methyl hydroxybenzoate 3%
Deionized water surplus.
Washing adopts open soaper.
Dry and select hot-air oven, temperature controls 135-150.Between C.
Evaporating employing high temperature steaming, is the superheated steam decatize 7 minutes of 170 DEG C at ambient pressure.
Steam temperature: 102 ~ 105 DEG C, saturated vapor steaming time: 20min.
Soft prescription is:
Leavening agent: 5.1kg
Softener: 6.2kg
Antistatic additive: 14kg
Water: 500L.
Embodiment 2:
Method be that embodiment 1 is identical, difference is that soaping agent formula is: be made up of following each component by weight percentage:
Horse propylene copolymer 65%
Surfactant 11%
Defoamer 0.3%
The large sodium acetate 1% of ethylenediamine two salicyl
Dodecyl benzyl dimethyl ammonium chloride 1%,
Isothiazolinone 1%,
Polyoxyethylene sorbitan fatty acid ester (T-60) 2%,
Methyl hydroxybenzoate 2%
Deionized water surplus.
Embodiment 3:
Method be that embodiment 1 is identical, difference is that soaping agent formula is: be made up of following each component by weight percentage:
Horse propylene copolymer 75%
Surfactant 12%
Defoamer 0.4%
The large sodium acetate 2% of ethylenediamine two salicyl
Dodecyl benzyl dimethyl ammonium chloride 3%,
Isothiazolinone 4%,
Polyoxyethylene sorbitan fatty acid ester (T-60) 2%,
Methyl hydroxybenzoate 1%
Deionized water surplus.
Above-described specific embodiment, further describes object of the present invention, technical scheme and beneficial effect, and institute it should be understood that and the foregoing is only specific embodiments of the invention, is not limited to the present invention.The present invention expands to any new feature of disclosing in this manual or any combination newly, and the step of the arbitrary new method disclosed or process or any combination newly.
Claims (6)
1. a mildew-resistant woollen blanket manufacture craft, comprises the following steps: stamp, roll compacting, dry, evaporate, soap, wash, softness, oven dry, carding, polishing, cropping, to make;
Adopt soaping agent in technique of wherein soaping to soap,
Soaping agent formula is: be made up of following each component by weight percentage:
Horse propylene copolymer 50 ~ 75%
Surfactant 5 ~ 15%
Defoamer 0.1 ~ 0.5%
The large sodium acetate 1 ~ 5% of ethylenediamine two salicyl
Dodecyl benzyl dimethyl ammonium chloride 0.1 ~ 5%,
Isothiazolinone 0.1 ~ 5%,
Polyoxyethylene sorbitan fatty acid ester (T-60) 0.1 ~ 5%,
Methyl hydroxybenzoate 0.1 ~ 5%
Deionized water surplus.
2. a kind of mildew-resistant woollen blanket manufacture craft according to claim 1, is characterized in that, washing adopts open soaper.
3. a kind of mildew-resistant woollen blanket manufacture craft according to claim 1, is characterized in that, dry and select hot-air oven, temperature controls between 135-150 DEG C.
4. a kind of mildew-resistant woollen blanket manufacture craft according to claim 1, is characterized in that, evaporate employing high temperature steaming, is the superheated steam decatize 7 minutes of 170 DEG C at ambient pressure.
5. a kind of mildew-resistant woollen blanket manufacture craft according to claim 1, is characterized in that, steam temperature: 102 ~ 105 DEG C, saturated vapor steaming time: 20min.
6. a kind of mildew-resistant woollen blanket manufacture craft according to claim 1, it is characterized in that, soft prescription is:
Leavening agent: 5.1kg;
Softener: 6.2kg;
Antistatic additive: 14kg;
Water: 500L.