CN105088399A - Composite feather textile material with fresh scent - Google Patents
Composite feather textile material with fresh scent Download PDFInfo
- Publication number
- CN105088399A CN105088399A CN201510460101.1A CN201510460101A CN105088399A CN 105088399 A CN105088399 A CN 105088399A CN 201510460101 A CN201510460101 A CN 201510460101A CN 105088399 A CN105088399 A CN 105088399A
- Authority
- CN
- China
- Prior art keywords
- feather
- parts
- subsequent use
- textile material
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a composite feather textile material with fresh scent. The material is characterized by comprising, by weight, 40-60 parts of poultry feathers, 14-17 parts of down feathers, 1-3 parts of silane coupling agents KH550, 1-2 parts of nano silicon dioxide, 1-2 parts of nano silver, 14-20 parts of chitosan, 30-50 parts of polypropylene, 1-3 parts of rosemary powder, 1-2 parts of gastrodia elata, 0.4-1 part of glycerol monolaurate and a proper amount of water. The added rosemary powder, the added gastrodia elata and the added glycerol monolaurate enhance sterilizing performance, the fresh scent, health-care functions and other performance beneficial to human body health of the feather textile material . The prepared composite feather textile material is simple and novel in structure, the preparing method is simple, material sources are simple, performance is excellent, and the material has high practicality and popularization value.
Description
Technical field
The present invention relates to textile material technical field, be specifically related to a kind of compound feather textile material with pure and fresh fragrance and preparation method thereof.
Background technology
In textile industry, only have Isotactic polypropylene can be used to produce textile fabric, this is because Isotactic polypropylene fiber has higher degree of crystallinity and the degree of orientation, regularity is better.Therefore Isotactic polypropylene fiber is widely used as sewing thread, bandage, textile bags and bio-medical material.But because Isotactic polypropylene fiber lacks dyeability, limit its application in textile garment field.Eider down is a kind of natural protein fibre material, except a small amount of for making warming packing material in clothes and bedding and in the composite as except reinforcing material, major part just simple processing process is used as feed or adopts the methods such as fermentation to degrade, and causes a large amount of wastes.When fiber made separately by eider down, fragility is large, tensile strength is low, is not suitable for making coat, is only suitable for being filled in inside clothes obtaining very strong warmth retention property, because eider down content in feather is very few, usually only account for 20 ~ 25%, use cost is too high, feather fiber is not utilized very well, very unfortunately.The present invention utilizes discarded feather to be degraded into keratin solution, then with the chitosan solution blend spinning of modification, compatibility is good, recycling Isotactic polypropylene fills feather fiber, reduce the consumption of feather, gain in weight, and improve the performance of the aspects such as the intensity of fiber, modulus, heat resistance, chemical resistance and anti-corrosive properties, develop novel weaving face fabric, facilitate society and expanding economy.
Summary of the invention
The object of this invention is to provide a kind of compound feather textile material with pure and fresh fragrance and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the invention is to be realized by following technological means:
A kind of compound feather textile material with pure and fresh fragrance, it is characterized in that, be made up of the raw material of following weight portion: poultry feather 40-60, eider down 14-17, Silane coupling agent KH550 1-3, nano silicon 1-2, Nano Silver 1-2, shitosan 14-20, polypropylene 30-50, rosemary, Xue MingRosma rinus officinalis powder 1-3, rhizoma Gastrodiae 1-2, lauric monoglyceride 0.4-1, water are appropriate;
A kind of compound feather textile material with pure and fresh fragrance of the present invention, be made up of following concrete steps:
(1) poultry feather and feather stem are separated, use clear water rinsed clean respectively, dry, carry out processed, feather extruding is separated, and feather stem carries out torsion extruding, sterilizing and deodorization under 100-200 ° of C in high-pressure sterilizing pot is added to eider down mixing after again feather and feather stem being cut into mean size, after spontaneous combustion cooling, mixing feather material is placed in alcohol and soaks 4-6 hour, then be neutral post-drying with clear water washing surface, be ground into powder for subsequent use;
(2) Silane coupling agent KH550 appropriate isopropyl alcohol dissolving is placed in reaction vessel, add nano silicon, Nano Silver again, stirring and refluxing 1-3h under 70-90 ° of C, cooling, for subsequent use after suction filtration, washing, drying, again shitosan glacial acetic acid solution is dissolved and make the chitosan-acetic acid solution that content is 3%, then with after NaOH alkalization 2-3h, add above-mentioned mixture for subsequent use, 2-3h is reacted under 40-60 ° of C, cooling, filters, washs, for subsequent use after drying;
(3) material prepared by step (1) and step (2) is used equivalent dissolution with solvents respectively, makes keratin content in feather within the scope of 8-13%, then be mixed and made into composite spinning stoste, carry out after spinning short cut for subsequent use;
(4) polypropylene and all the other remaining material mixing are added to main feeding trough in double screw extruder, the short collodion silk of cutting step (3) obtained again adds at natural exhaust outlet, blending extrusion temperature section is 195 ° of C, 190 ° of C, 190 ° of C, 185 ° of C, 180 ° of C, 165 ° of C, 110 ° of C, obtain composite master batch, composite master batch is carried out spinning.
Advantage of the present invention is: the present invention utilizes discarded feather to carry out dehydration taste removal deodorizing degreasing, makes the keratin solution of suitable solubility, and utilize nano silicon and Nano Silver modification of chitosan by dissolution with solvents, shitosan is had excellent antibacterial, sterilization, the performance that antibacterial and uvioresistant etc. are excellent, the fabric that the present invention utilizes chitosan solution and keratin solution co-blended spinning to obtain has good hygroscopicity, antibiotic property, the features such as biodegradability, and the ABRASION RESISTANCE enhancing material again by adding polypropylene, tensile strength, the characteristic of the aspects such as weight, decreases the consumption of feather fiber, adds the novelty teabag of feather, the rosemary, Xue MingRosma rinus officinalis powder of interpolation, rhizoma Gastrodiae and lauric monoglyceride enhance the bactericidal properties of feather textile material, pure and fresh fragrance, the performance that health care etc. are useful to health, compound feather textile material structure prepared by the present invention is simply novel, and preparation method is simple, material source is simple, and excellent performance, has very strong practicality and promotional value.
Detailed description of the invention
A kind of compound feather textile material with pure and fresh fragrance, it is characterized in that, be made up of the raw material of following weight portion (kilogram): poultry feather 57, eider down 16, Silane coupling agent KH550 3, nano silicon 2, Nano Silver 1, shitosan 17, polypropylene 46, rosemary, Xue MingRosma rinus officinalis powder 2, rhizoma Gastrodiae 1, lauric monoglyceride 0.6, water are appropriate;
A kind of compound feather textile material with pure and fresh fragrance of the present invention, be made up of following concrete steps:
(1) poultry feather and feather stem are separated, use clear water rinsed clean respectively, dry, carry out processed, feather extruding is separated, and feather stem carries out torsion extruding, sterilizing and deodorization under 150 ° of C in high-pressure sterilizing pot is added to eider down mixing after again feather and feather stem being cut into mean size, after spontaneous combustion cooling, mixing feather material is placed in alcohol to soak 6 hours, then is neutral post-drying with clear water washing surface, be ground into powder for subsequent use;
(2) Silane coupling agent KH550 appropriate isopropyl alcohol dissolving is placed in reaction vessel, add nano silicon, Nano Silver again, stirring and refluxing 3h under 80 ° of C, cooling, for subsequent use after suction filtration, washing, drying, again shitosan glacial acetic acid solution is dissolved and make the chitosan-acetic acid solution that content is 3%, then with after NaOH alkalization 3h, add above-mentioned mixture for subsequent use, 2h is reacted under 50 ° of C, cooling, filters, washs, for subsequent use after drying;
(3) material prepared by step (1) and step (2) is used equivalent dissolution with solvents respectively, makes keratin content in feather in 11% scope, then be mixed and made into composite spinning stoste, carry out after spinning short cut for subsequent use;
(4) polypropylene and all the other remaining material mixing are added to main feeding trough in double screw extruder, the short collodion silk of cutting step (3) obtained again adds at natural exhaust outlet, blending extrusion temperature section is 195 ° of C, 190 ° of C, 190 ° of C, 185 ° of C, 180 ° of C, 165 ° of C, 110 ° of C, obtain composite master batch, composite master batch is carried out spinning.
The eider down composite fibre performance indications parameter using the present invention to prepare is as follows:
Hydroscopicity (%): 12.6;
Regain (%): 5.3;
Extensibility (%): 32.1;
Tensile break strength (N): 6.2.
Claims (2)
1. the compound feather textile material with pure and fresh fragrance, it is characterized in that, be made up of the raw material of following weight portion: poultry feather 40-60, eider down 14-17, Silane coupling agent KH550 1-3, nano silicon 1-2, Nano Silver 1-2, shitosan 14-20, polypropylene 30-50, rosemary, Xue MingRosma rinus officinalis powder 1-3, rhizoma Gastrodiae 1-2, lauric monoglyceride 0.4-1, water are appropriate.
2. a kind of compound feather textile material with pure and fresh fragrance according to claim 1, is characterized in that, be made up of following concrete steps:
(1) poultry feather and feather stem are separated, use clear water rinsed clean respectively, dry, carry out processed, feather extruding is separated, and feather stem carries out torsion extruding, sterilizing and deodorization under 100-200 ° of C in high-pressure sterilizing pot is added to eider down mixing after again feather and feather stem being cut into mean size, after spontaneous combustion cooling, mixing feather material is placed in alcohol and soaks 4-6 hour, then be neutral post-drying with clear water washing surface, be ground into powder for subsequent use;
(2) Silane coupling agent KH550 appropriate isopropyl alcohol dissolving is placed in reaction vessel, add nano silicon, Nano Silver again, stirring and refluxing 1-3h under 70-90 ° of C, cooling, for subsequent use after suction filtration, washing, drying, again shitosan glacial acetic acid solution is dissolved and make the chitosan-acetic acid solution that content is 3%, then with after NaOH alkalization 2-3h, add above-mentioned mixture for subsequent use, 2-3h is reacted under 40-60 ° of C, cooling, filters, washs, for subsequent use after drying;
(3) material prepared by step (1) and step (2) is used equivalent dissolution with solvents respectively, makes keratin content in feather within the scope of 8-13%, then be mixed and made into composite spinning stoste, carry out after spinning short cut for subsequent use;
(4) polypropylene and all the other remaining material mixing are added to main feeding trough in double screw extruder, the short collodion silk of cutting step (3) obtained again adds at natural exhaust outlet, blending extrusion temperature section is 195 ° of C, 190 ° of C, 190 ° of C, 185 ° of C, 180 ° of C, 165 ° of C, 110 ° of C, obtain composite master batch, composite master batch is carried out spinning.