CN105088382A - Production technology for textile of sportive reed-free and trace-free shoulder girdle - Google Patents
Production technology for textile of sportive reed-free and trace-free shoulder girdle Download PDFInfo
- Publication number
- CN105088382A CN105088382A CN201510584119.2A CN201510584119A CN105088382A CN 105088382 A CN105088382 A CN 105088382A CN 201510584119 A CN201510584119 A CN 201510584119A CN 105088382 A CN105088382 A CN 105088382A
- Authority
- CN
- China
- Prior art keywords
- fabric
- reed
- production technology
- free
- nylon66 fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method for a textile of a sportive reed-free and trace-free shoulder girdle. The preparation method comprises the following steps: melt spinning, fabric blending, dyeing, washing, drying and after finishing. The preparation method is used for preparing the reed-free and trace-free shoulder girdle on sportive underwear. The produced shoulder girdle reaches an elastic ratio of 1 to 3 or even larger; the resilience force modulus of the reed-free shoulder girdle is always kept as a closer modulus from the start of stretching to the limit; the shoulder girdle always keeps comfortable openness and resilience force during wearing, use and sportive stretching and expansion, so that a tensioning trace can be avoided.
Description
Technical field
The present invention is specifically related to a kind of moving without the production technology of the fabric of the seamless shoulder belt of reed.
Background technology
Along with modern life level is more and more higher, underwear breaks up more and more thinner as body shaping underwear in life, pregnant woman's underwear, and athletic undergarment etc.Shoulder belt plays this very important function influence and the functional of underwear in various function underwear, comfortableness and wear result of use.The comfortable degree of tightness of common underwear shoulder belt regulates general dependence to regulate reed to regulate, reed is regulated to be substantially all metal, plastics hard object goods easily damage skin or occur strangling trace in friction of motion, and in underwear production process, reduce operation saving manpower and material cost.
Summary of the invention
Goal of the invention: the invention provides a kind of moving without the production technology of the fabric of the seamless shoulder belt of reed.
Technical scheme: a kind ofly to move without the production technology of the fabric of the seamless shoulder belt of reed, comprises the steps:
Step (1) melt spinning: nylon 66 resin is carried out melt spinning, wherein, in melt spinning process: the temperature of nylon66 fiber molten mass is between 180 DEG C ~ 320 DEG C; The hole count of spinnerets is 10 ~ 80, and aperture is 0.2 ~ 0.4mm, and spinnerets draw ratio is 3.0 ~ 3.5; The speed of winding is 3000 ~ 5000m/min;
Step (2) blended yarn woven fabric: the nylon66 fiber superfine Denier fibre prepared in step (1) and spandex blending are made fabric, it is 8-10 part that percentage by weight is wherein followed successively by described nylon66 fiber superfine Denier fibre, and described spandex is 12-16 part;
Step (3) dyes: by above-mentioned fabric, and immerse in dye liquor and dye, wherein, dyeing time is: 45-70min, and dyeing temperature is: 22 DEG C-28 DEG C; Dyestuff proportioning: fluorescent dye 3.0-4.5g/L, glacial acetic acid 2.5-5.6g/L, 4 bromide 3.6-6.2g/L, bleeding agent 2.4-7.3g/L, Sodium Polyacrylate 7.4-8.6g/L, glauber salt 2.9-3.7g/L;
Step (4) is washed: yarn is put into 13 DEG C of-18 DEG C of water and wash, and in water, add the Cationic fixing agents 17-24g/L exempting to adjust;
Step (5) is dried: fabric is put into drying baker and dries, the temperature of oven dry is 50 DEG C-68 DEG C, and drying time is 40-60min;
Step (6) Final finishing.
As optimization: in described step (1), melt spinning: the temperature of nylon66 fiber molten mass is at 220 DEG C; The hole count of spinnerets is 60, and aperture is 0.3mm, and spinnerets draw ratio is 3.3; The speed of winding is 4000m/min.
As optimization: in described step (2) blended yarn woven fabric, the nylon66 fiber superfine Denier fibre prepared and spandex blending are made fabric, it is 9 parts that percentage by weight is wherein followed successively by described nylon66 fiber superfine Denier fibre, and described spandex is 13 parts.
As optimization: in described step (3) dyeing, immersed in dye liquor by fabric and dye, wherein, dyeing time is: 60min, and dyeing temperature is: 26 DEG C; Dyestuff proportioning: fluorescent dye 3.8g/L, glacial acetic acid 4.6g/L, 4 bromide 5.7g/L, bleeding agent 5.3g/L, Sodium Polyacrylate 7.9g/L, glauber salt 3.3g/L.
As optimization: in described step (4) washing, yarn is put into 15 DEG C of water and wash, and in water, add the Cationic fixing agents 21g/L exempting to adjust.
Beneficial effect: the present invention be applied on athletic undergarment without the seamless shoulder belt of reed, the shoulder belt produced reaches the elastic proportional of 1:3 or more, resiliency modulus without reed fabric shoulder belt all remains modulus relatively to the limit from stretching, and shoulder belt uses motion to stretch all to remain all the time in expansion comfortable aperture and resiliency so there will not be and strangle trace in dress.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention will be described in detail.
Specific embodiment one:
Move without a production technology for the fabric of the seamless shoulder belt of reed, comprise the steps:
Step (1) melt spinning: nylon 66 resin is carried out melt spinning, wherein, in melt spinning process: the temperature of nylon66 fiber molten mass is between 180 DEG C; The hole count of spinnerets is 10, and aperture is 0.2mm, and spinnerets draw ratio is 3.0; The speed of winding is 3000m/min;
Step (2) blended yarn woven fabric: the nylon66 fiber superfine Denier fibre prepared in step (1) and spandex blending are made fabric, it is 8 parts that percentage by weight is wherein followed successively by described nylon66 fiber superfine Denier fibre, and described spandex is 12 parts;
Step (3) dyes: by above-mentioned fabric, and immerse in dye liquor and dye, wherein, dyeing time is: 45min, and dyeing temperature is: 22 DEG C; Dyestuff proportioning: fluorescent dye 3.0g/L, glacial acetic acid 2.5g/L, 4 bromide 3.6g/L, bleeding agent 2.4g/L, Sodium Polyacrylate 7.4g/L, glauber salt 2.9g/L;
Step (4) is washed: yarn is put into 13 DEG C of water and wash, and in water, add the Cationic fixing agents 17g/L exempting to adjust;
Step (5) is dried: fabric is put into drying baker and dries, the temperature of oven dry is 50 DEG C-68 DEG C, and drying time is 40min;
Step (6) Final finishing.
Specific embodiment two:
Move without a production technology for the fabric of the seamless shoulder belt of reed, comprise the steps:
Step (1) melt spinning: nylon 66 resin is carried out melt spinning, wherein, in melt spinning process: the temperature of nylon66 fiber molten mass is between 320 DEG C; The hole count of spinnerets is 80, and aperture is 0.4mm, and spinnerets draw ratio is 3.5; The speed of winding is 5000m/min;
Step (2) blended yarn woven fabric: the nylon66 fiber superfine Denier fibre prepared in step (1) and spandex blending are made fabric, it is 10 parts that percentage by weight is wherein followed successively by described nylon66 fiber superfine Denier fibre, and described spandex is 16 parts;
Step (3) dyes: by above-mentioned fabric, and immerse in dye liquor and dye, wherein, dyeing time is: 45-70min, and dyeing temperature is: 28 DEG C; Dyestuff proportioning: fluorescent dye 4.5g/L, glacial acetic acid 5.6g/L, 4 bromide 6.2g/L, bleeding agent 7.3g/L, Sodium Polyacrylate 8.6g/L, glauber salt 3.7g/L;
Step (4) is washed: yarn is put into 18 DEG C of water and wash, and in water, add the Cationic fixing agents 24g/L exempting to adjust;
Step (5) is dried: fabric is put into drying baker and dries, the temperature of oven dry is 68 DEG C, and drying time is 60min;
Step (6) Final finishing.
Specific embodiment three:
Move without a production technology for the fabric of the seamless shoulder belt of reed, comprise the steps:
Step (1) melt spinning: nylon 66 resin is carried out melt spinning, wherein, in melt spinning process: the temperature of nylon66 fiber molten mass is between 220 DEG C; The hole count of spinnerets is 60, and aperture is 0.3mm, and spinnerets draw ratio is 3.3; The speed of winding is 4000m/min;
Step (2) blended yarn woven fabric: the nylon66 fiber superfine Denier fibre prepared in step (1) and spandex blending are made fabric, it is 9 parts that percentage by weight is wherein followed successively by described nylon66 fiber superfine Denier fibre, and described spandex is 13 parts;
Step (3) dyes: by above-mentioned fabric, and immerse in dye liquor and dye, wherein, dyeing time is: 60min, and dyeing temperature is: 26 DEG C; Dyestuff proportioning: fluorescent dye 3.8g/L, glacial acetic acid 4.6g/L, 4 bromide 5.7g/L, bleeding agent 5.3g/L, Sodium Polyacrylate 7.9g/L, glauber salt 3.3g/L;
Step (4) is washed: yarn is put into 15 DEG C of water and wash, and in water, add the Cationic fixing agents 21g/L exempting to adjust;
Step (5) is dried: fabric is put into drying baker and dries, the temperature of oven dry is 57 DEG C, and drying time is 50min;
Step (6) Final finishing.
The present invention is not limited to above-mentioned preferred forms; anyone can draw other various forms of products under enlightenment of the present invention; no matter but any change is done in its shape or structure; every have identical with the application or akin technical scheme, all drops within protection scope of the present invention.
Claims (5)
1. move without a production technology for the fabric of the seamless shoulder belt of reed, it is characterized in that: comprise the steps:
Step (1) melt spinning: nylon 66 resin is carried out melt spinning, wherein, in melt spinning process: the temperature of nylon66 fiber molten mass is between 180 DEG C ~ 320 DEG C; The hole count of spinnerets is 10 ~ 80, and aperture is 0.2 ~ 0.4mm, and spinnerets draw ratio is 3.0 ~ 3.5; The speed of winding is 3000 ~ 5000m/min;
Step (2) blended yarn woven fabric: the nylon66 fiber superfine Denier fibre prepared in step (1) and spandex blending are made fabric, it is 8-10 part that percentage by weight is wherein followed successively by described nylon66 fiber superfine Denier fibre, and described spandex is 12-16 part;
Step (3) dyes: by above-mentioned fabric, and immerse in dye liquor and dye, wherein, dyeing time is: 45-70min, and dyeing temperature is: 22 DEG C-28 DEG C; Dyestuff proportioning: fluorescent dye 3.0-4.5g/L, glacial acetic acid 2.5-5.6g/L, 4 bromide 3.6-6.2g/L, bleeding agent 2.4-7.3g/L, Sodium Polyacrylate 7.4-8.6g/L, glauber salt 2.9-3.7g/L;
Step (4) is washed: yarn is put into 13 DEG C of-18 DEG C of water and wash, and in water, add the Cationic fixing agents 17-24g/L exempting to adjust;
Step (5) is dried: fabric is put into drying baker and dries, the temperature of oven dry is 50 DEG C-68 DEG C, and drying time is 40-60min;
Step (6) Final finishing.
2. motion according to claim 1 is without the production technology of the fabric of the seamless shoulder belt of reed, it is characterized in that: in described step (1), melt spinning: the temperature of nylon66 fiber molten mass is at 220 DEG C; The hole count of spinnerets is 60, and aperture is 0.3mm, and spinnerets draw ratio is 3.3; The speed of winding is 4000m/min.
3. motion according to claim 1 is without the production technology of the fabric of the seamless shoulder belt of reed, it is characterized in that: in described step (2) blended yarn woven fabric, the nylon66 fiber superfine Denier fibre prepared and spandex blending are made fabric, it is 9 parts that percentage by weight is wherein followed successively by described nylon66 fiber superfine Denier fibre, and described spandex is 13 parts.
4. motion according to claim 1 is without the production technology of the fabric of the seamless shoulder belt of reed, it is characterized in that: in described step (3) dyeing, immersed in dye liquor by fabric and dye, wherein, dyeing time is: 60min, and dyeing temperature is: 26 DEG C; Dyestuff proportioning: fluorescent dye 3.8g/L, glacial acetic acid 4.6g/L, 4 bromide 5.7g/L, bleeding agent 5.3g/L, Sodium Polyacrylate 7.9g/L, glauber salt 3.3g/L.
5. motion according to claim 1 is without the production technology of the fabric of the seamless shoulder belt of reed, it is characterized in that: in described step (4) washing, yarn is put into 15 DEG C of water and wash, and in water, add the Cationic fixing agents 21g/L exempting to adjust.