Summary of the invention
Main purpose of the present invention is to provide a kind of film intercepting blue light organic silica gel and make, and structure cannot be provided in the market to be simply easy to make, effectively can intercept again the technical problem of the film of blue light to solve.
In order to achieve the above object, technical scheme provided by the invention is:
A kind of obstruct blue light organic silica gel, adds the filter blue light dyestuff of some amount, filters the blue light of certain wavelength in organosilicon glue during making.
Preferably, described organosilicon glue is organic pressure-sensitive gel or organo-silicone rubber.
Preferably, described organic pressure-sensitive gel is one or more mixture in hydroxyl condensation type organic pressure-sensitive gel, peroxide cure condensed type organic silicon pressure sensitive adhesive, addition curable organic pressure-sensitive gel, room temperature vulcanized organic pressure-sensitive gel and organotin catalyzed type silicon pressure sensitive adhesive.
Preferably, described organo-silicone rubber is one or more mixture in liquid silastic, hydroxyl condensation type organo-silicone rubber, peroxide cure condensed type organic silicon rubber, addition curable organo-silicone rubber, room temperature vulcanized organo-silicone rubber and organotin catalyzed type silicon rubber.
Preferably, described organic pressure-sensitive gel is the solvent-laden organic pressure-sensitive gel of bag, and described solvent is toluene, dimethylbenzene or 100 ~ No. 120 solvent oils.
Preferably, described silicone pressure sensitive tackiness scope 0.1 ~ 5000gf/in.
Preferably, described filter blue light dyestuff is azo, methine class, azo-methine class, ketimide class, ketimide-methine class, azo metal complexing class, naphthalimide, nitrodiphenylamine class, aminoketones, nitro class, Anthraquinones, the mixture of one or more in quinoline, azines, cluck ton class, sulphur cluck ton class, benzothiazoles, benzimidazoles, benzanthrones, acenaphthene class, spirooxazine-spiro-pyrans class, lactone type, coumarins dyestuff.
Preferably, described organic silica gel component comprises organic silica gel water and filter blue light dyestuff, and wherein filter blue light dyestuff accounts for 0.0001 ~ 30% of gross weight.
A kind of obstruct blue light organic silica gel film, comprise stratum basale and organosilicon glue-line, and organic gel layer thickness is 0.01 ~ 2000 micron.
Intercept a preparation method for blue light organic silica gel film, mainly comprise the following steps:
Step one, filter blue light dyestuff to be added by approach such as stirring, kneading, Screw Extrusions at organic pressure-sensitive gel or organo-silicone rubber production process;
Step 2, the mixture even spread that step one obtained are on the base layer;
Obtain after step 3, dry solidification intercepting blue light organic silica gel film.
Preferably, above-mentioned azo is monoazo class or tetrazo class.
In sum, the present invention intercepts blue light organic silica gel and the film made has following beneficial effect:
(1) structure is simple, is easy to make;
(2) high energy shortwave blue light can effectively be intercepted.By improving the optical characteristics of organic silica gel, not only retaining the characteristic of organic silica gel water itself, can effectively intercept by the high strength blue light harmful to eyes simultaneously.This film can be used for the bonding of each membrane module of liquid-crystal display, also may be used for all kinds of protective membrane, rupture disk, without base material optical cement (OCA), LED display, relates to the production of the products such as LED light source.
embodiment
In order to make object of the present invention, technical scheme and advantage clearly, below in conjunction with embodiment, the present invention is described in detail.
Embodiment one
A kind of obstruct blue light organic silica gel, adds the filter blue light dyestuff of some amount, filters the blue light of certain wavelength in organosilicon glue during making.The blue light wavelength be filtered is between 380 nanometers to 500 nanometers.
In an embodiment, organosilicon glue is organic pressure-sensitive gel or organo-silicone rubber.Organic pressure-sensitive gel is one or more mixture in hydroxyl condensation type organic pressure-sensitive gel, peroxide cure condensed type organic silicon pressure sensitive adhesive, addition curable organic pressure-sensitive gel, room temperature vulcanized organic pressure-sensitive gel and organotin catalyzed type silicon pressure sensitive adhesive.Organic pressure-sensitive gel comprises solvent-borne type silicon pressure sensitive adhesive, and solvent is toluene or dimethylbenzene, and solvent oil is 100 ~ No. 120, silicone pressure sensitive tackiness scope 0.1 ~ 5000gf/in.
In an embodiment, organo-silicone rubber is one or more mixture in liquid silastic, hydroxyl condensation type organo-silicone rubber, peroxide cure condensed type organic silicon rubber, addition curable organo-silicone rubber, room temperature vulcanized organo-silicone rubber and organotin catalyzed type silicon rubber.
In an embodiment, filter blue light dyestuff is azo, methine class, azo-methine class, ketimide class, ketimide-methine class, azo metal complexing class, naphthalimide, nitrodiphenylamine class, aminoketones, nitro class, Anthraquinones, the mixture of one or more in quinoline, azines, cluck ton class, sulphur cluck ton class, benzothiazoles, benzimidazoles, benzanthrones, acenaphthene class, spirooxazine-spiro-pyrans class, lactone type, coumarins dyestuff.Azo is monoazo class or tetrazo class.
In the present embodiment, selected materials comprises the organic pressure-sensitive gel 610 of 100g, and producer is momentive; The BPO(dibenzoyl peroxide of 5g), producer is Akzo Nobel; The azo complex dyestuff 1 of 1g, producer is BASF; Also has the toluene (technical grade) of 50g.
After being mixed by above-mentioned materials, be uniformly coated on 50 microns of clear PET film surfaces, obtain after dry solidification intercepting blue light organic silica gel film, this film comprises organic layer of silica gel and stratum basale, described stratum basale and PET film layer.Then its 430 ~ 500 nano blue light rejection rate is detected.
In an embodiment, filter blue light dyestuff is added by approach such as stirring, kneading, Screw Extrusions at organic pressure-sensitive gel or organo-silicone rubber production process, also directly can be added by filter blue light dyestuff after organic pressure-sensitive gel or organo-silicone rubber production process.
Embodiment two
A kind of obstruct blue light organic silica gel, adds the filter blue light dyestuff of some amount, filters the blue light of certain wavelength in organosilicon glue during making.The blue light wavelength be filtered is between 380 nanometers to 500 nanometers.
In an embodiment, organosilicon glue is organic pressure-sensitive gel or organo-silicone rubber.Organic pressure-sensitive gel is one or more mixture in hydroxyl condensation type organic pressure-sensitive gel, peroxide cure condensed type organic silicon pressure sensitive adhesive, addition curable organic pressure-sensitive gel, room temperature vulcanized organic pressure-sensitive gel and organotin catalyzed type silicon pressure sensitive adhesive.Organic pressure-sensitive gel comprises solvent-borne type silicon pressure sensitive adhesive, and solvent is toluene or dimethylbenzene, and solvent oil is 100 ~ No. 120, silicone pressure sensitive tackiness scope 0.1 ~ 5000gf/in.
In an embodiment, organo-silicone rubber is one or more mixture in liquid silastic, hydroxyl condensation type organo-silicone rubber, peroxide cure condensed type organic silicon rubber, addition curable organo-silicone rubber, room temperature vulcanized organo-silicone rubber and organotin catalyzed type silicon rubber.
In an embodiment, filter blue light dyestuff is azo, methine class, azo-methine class, ketimide class, ketimide-methine class, azo metal complexing class, naphthalimide, nitrodiphenylamine class, aminoketones, nitro class, Anthraquinones, the mixture of one or more in quinoline, azines, cluck ton class, sulphur cluck ton class, benzothiazoles, benzimidazoles, benzanthrones, acenaphthene class, spirooxazine-spiro-pyrans class, lactone type, coumarins dyestuff.Azo is monoazo class or tetrazo class.
In the present embodiment, selected materials comprises the silicon rubber of 100g, and producer is Jiangxi spark; The BPO(dibenzoyl peroxide of 5g), producer is Akzo Nobel; The azo complex dyestuff 1 of 1g, producer is BASF; Also has the toluene (technical grade) of 50g.
After being mixed by above-mentioned materials, be uniformly coated on glass surface, obtain after dry solidification intercepting blue light organic silica gel film, this film comprises organic layer of silica gel and stratum basale, described stratum basale and glass.Then its 430 ~ 500 nano blue light rejection rate is detected.
In an embodiment, filter blue light dyestuff is added by approach such as stirring, kneading, Screw Extrusions at organic pressure-sensitive gel or organo-silicone rubber production process, also directly can be added by filter blue light dyestuff after organic pressure-sensitive gel or organo-silicone rubber production process.
Embodiment three
A kind of obstruct blue light organic silica gel, adds the filter blue light dyestuff of some amount, filters the blue light of certain wavelength in organosilicon glue during making.The blue light wavelength be filtered is between 380 nanometers to 500 nanometers.
In an embodiment, organosilicon glue is organic pressure-sensitive gel or organo-silicone rubber.Organic pressure-sensitive gel is one or more mixture in hydroxyl condensation type organic pressure-sensitive gel, peroxide cure condensed type organic silicon pressure sensitive adhesive, addition curable organic pressure-sensitive gel, room temperature vulcanized organic pressure-sensitive gel and organotin catalyzed type silicon pressure sensitive adhesive.Organic pressure-sensitive gel comprises solvent-borne type silicon pressure sensitive adhesive, and solvent is toluene or dimethylbenzene, and solvent oil is 100 ~ No. 120, silicone pressure sensitive tackiness scope 0.1 ~ 5000gf/in.
In an embodiment, organo-silicone rubber is one or more mixture in liquid silastic, hydroxyl condensation type organo-silicone rubber, peroxide cure condensed type organic silicon rubber, addition curable organo-silicone rubber, room temperature vulcanized organo-silicone rubber and organotin catalyzed type silicon rubber.
In an embodiment, filter blue light dyestuff is azo, methine class, azo-methine class, ketimide class, ketimide-methine class, azo metal complexing class, naphthalimide, nitrodiphenylamine class, aminoketones, nitro class, Anthraquinones, the mixture of one or more in quinoline, azines, cluck ton class, sulphur cluck ton class, benzothiazoles, benzimidazoles, benzanthrones, acenaphthene class, spirooxazine-spiro-pyrans class, lactone type, coumarins dyestuff.Azo is monoazo class or tetrazo class.
In the present embodiment, selected materials comprises 107 silicon rubber of 100g, and producer is Jiangxi spark; The dibutyl tin laurate of 8g, producer is blue sky, Hubei; The methyl silicate of 10g, producer is blue sky, Hubei; The azo complex dyestuff 1 of 1g, producer is BASF; Also has the toluene (technical grade) of 50g.
After being mixed by above-mentioned materials, be uniformly coated on glass surface, obtain after dry solidification intercepting blue light organic silica gel film, this film comprises organic layer of silica gel and stratum basale, described stratum basale and glass.Then its 430 ~ 500 nano blue light rejection rate is detected.
In an embodiment, filter blue light dyestuff is added by approach such as stirring, kneading, Screw Extrusions at organic pressure-sensitive gel or organo-silicone rubber production process, also directly can be added by filter blue light dyestuff after organic pressure-sensitive gel or organo-silicone rubber production process.
Embodiment four
A kind of obstruct blue light organic silica gel, adds the filter blue light dyestuff of some amount, filters the blue light of certain wavelength in organosilicon glue during making.The blue light wavelength be filtered is between 380 nanometers to 500 nanometers.
In an embodiment, organosilicon glue is organic pressure-sensitive gel or organo-silicone rubber.Organic pressure-sensitive gel is one or more mixture in hydroxyl condensation type organic pressure-sensitive gel, peroxide cure condensed type organic silicon pressure sensitive adhesive, addition curable organic pressure-sensitive gel, room temperature vulcanized organic pressure-sensitive gel and organotin catalyzed type silicon pressure sensitive adhesive.Organic pressure-sensitive gel comprises solvent-borne type silicon pressure sensitive adhesive, and solvent is toluene or dimethylbenzene, and solvent oil is 100 ~ No. 120, silicone pressure sensitive tackiness scope 0.1 ~ 5000gf/in.
In an embodiment, organo-silicone rubber is one or more mixture in liquid silastic, hydroxyl condensation type organo-silicone rubber, peroxide cure condensed type organic silicon rubber, addition curable organo-silicone rubber, room temperature vulcanized organo-silicone rubber and organotin catalyzed type silicon rubber.
In an embodiment, filter blue light dyestuff is azo, methine class, azo-methine class, ketimide class, ketimide-methine class, azo metal complexing class, naphthalimide, nitrodiphenylamine class, aminoketones, nitro class, Anthraquinones, the mixture of one or more in quinoline, azines, cluck ton class, sulphur cluck ton class, benzothiazoles, benzimidazoles, benzanthrones, acenaphthene class, spirooxazine-spiro-pyrans class, lactone type, coumarins dyestuff.Azo is monoazo class or tetrazo class.
In the present embodiment, selected materials comprises the vinylsiloxane rubber of 110g, and producer is Chengdu, Sichuan morning twilight chemical research institute; The containing hydrogen silicone oil of 100g, producer is Chengdu, Sichuan morning twilight chemical research institute; The azo complex dyestuff 2 of 3g, producer is BASF; A small amount of catalyst platinum complex compound, producer is Chengdu, Sichuan morning twilight chemical research institute; Finally also have a small amount of inhibitor alkynol, producer is Chengdu, Sichuan morning twilight chemical research institute.
Be laid in glass surface after being mixed by above-mentioned materials, make certain thickness organic silica gel film, this film comprises organic layer of silica gel and stratum basale, described stratum basale and glass.Organosilicon glue-line can be stripped out by this film after sulfidizing, then detects its 430 ~ 500 nano blue light rejection rate.
In an embodiment, filter blue light dyestuff is added by approach such as stirring, kneading, Screw Extrusions at organic pressure-sensitive gel or organo-silicone rubber production process, also directly can be added by filter blue light dyestuff after organic pressure-sensitive gel or organo-silicone rubber production process.
Embodiment five
A kind of obstruct blue light organic silica gel, adds the filter blue light dyestuff of some amount, filters the blue light of certain wavelength in organosilicon glue during making.The blue light wavelength be filtered is between 380 nanometers to 500 nanometers.
In an embodiment, organosilicon glue is organic pressure-sensitive gel or organo-silicone rubber.Organic pressure-sensitive gel is one or more mixture in hydroxyl condensation type organic pressure-sensitive gel, peroxide cure condensed type organic silicon pressure sensitive adhesive, addition curable organic pressure-sensitive gel, room temperature vulcanized organic pressure-sensitive gel and organotin catalyzed type silicon pressure sensitive adhesive.Organic pressure-sensitive gel comprises solvent-borne type silicon pressure sensitive adhesive, and solvent is toluene or dimethylbenzene, and solvent oil is 100 ~ No. 120, silicone pressure sensitive tackiness scope 0.1 ~ 5000gf/in.
In an embodiment, organo-silicone rubber is one or more mixture in liquid silastic, hydroxyl condensation type organo-silicone rubber, peroxide cure condensed type organic silicon rubber, addition curable organo-silicone rubber, room temperature vulcanized organo-silicone rubber and organotin catalyzed type silicon rubber.
In an embodiment, filter blue light dyestuff is azo, methine class, azo-methine class, ketimide class, ketimide-methine class, azo metal complexing class, naphthalimide, nitrodiphenylamine class, aminoketones, nitro class, Anthraquinones, the mixture of one or more in quinoline, azines, cluck ton class, sulphur cluck ton class, benzothiazoles, benzimidazoles, benzanthrones, acenaphthene class, spirooxazine-spiro-pyrans class, lactone type, coumarins dyestuff.Azo is monoazo class or tetrazo class.
In the present embodiment, selected materials comprises the Polymethyl methacrylate of 100g, and producer is Chengdu, Sichuan morning twilight chemical research institute; The containing hydrogen silicone oil of 10g, producer is Chengdu, Sichuan morning twilight chemical research institute; The azo complex dyestuff 3 of 5g, producer is BASF; A small amount of catalyst platinum complex compound, producer is Chengdu, Sichuan morning twilight chemical research institute; Finally also have a small amount of inhibitor alkynol, producer is Chengdu, Sichuan morning twilight chemical research institute.
Be laid in glass surface after being mixed by above-mentioned materials, make certain thickness organic silica gel film, this film comprises organic layer of silica gel and stratum basale, described stratum basale and glass.Organosilicon glue-line can be stripped out by this film after sulfidizing, then detects its 430 ~ 500 nano blue light rejection rate.
In an embodiment, filter blue light dyestuff is added by approach such as stirring, kneading, Screw Extrusions at organic pressure-sensitive gel or organo-silicone rubber production process, also directly can be added by filter blue light dyestuff after organic pressure-sensitive gel or organo-silicone rubber production process.
In an embodiment, make organic layer of silica gel thickness and can be 0.01 ~ 2000 micron.Preferably, organic gel layer thickness is 0.01 micron, 1 micron, 5 microns, 10 microns.Preferred scope is 50 ~ 200 microns.
The performance testing index of the obstruct blue light organic silica gel film that embodiment 1 ~ embodiment 5 is obtained is as follows:
Last it is noted that above embodiment is only in order to illustrate technical scheme of the present invention, be not intended to limit; Although with reference to previous embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that: it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature; And these amendments or replacement, do not make the essence of appropriate technical solution depart from the scope of various embodiments of the present invention technical scheme.
In a word, the foregoing is only preferred embodiment of the present invention, all equalizations done according to the present patent application the scope of the claims change and modify, and all should belong to the covering scope of patent of the present invention.