CN105086122B - 一种狼牙瑜伽柱的制备方法 - Google Patents

一种狼牙瑜伽柱的制备方法 Download PDF

Info

Publication number
CN105086122B
CN105086122B CN201510432661.6A CN201510432661A CN105086122B CN 105086122 B CN105086122 B CN 105086122B CN 201510432661 A CN201510432661 A CN 201510432661A CN 105086122 B CN105086122 B CN 105086122B
Authority
CN
China
Prior art keywords
wolf
fang
yoga post
preparation
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510432661.6A
Other languages
English (en)
Other versions
CN105086122A (zh
Inventor
章炳芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHANGJIAGANG HONGLI RUBBER & PLASTIC PRODUCTS Co Ltd
Original Assignee
ZHANGJIAGANG HONGLI RUBBER & PLASTIC PRODUCTS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHANGJIAGANG HONGLI RUBBER & PLASTIC PRODUCTS Co Ltd filed Critical ZHANGJIAGANG HONGLI RUBBER & PLASTIC PRODUCTS Co Ltd
Priority to CN201510432661.6A priority Critical patent/CN105086122B/zh
Publication of CN105086122A publication Critical patent/CN105086122A/zh
Application granted granted Critical
Publication of CN105086122B publication Critical patent/CN105086122B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种狼牙瑜伽柱的制备方法，包括准备原料、密炼机中密炼、在螺杆挤出机中塑化、挤出、经模口风冷切粒得到混合料颗粒，将混合料颗粒保温通过注射发泡机注射到带有狼牙花纹的成型模具中，高温高压后得到外包层，将塑料管快速装入的外包层的凹槽内；空冷，使外包层收缩，包裹在塑料管外围形成狼牙瑜伽柱；本发明成本低，工序少，制作周期短，不使用胶水，高环保，生产出来的瑜伽柱表面材料无拼接，硬度均匀，花纹表皮强度高，产品外观光亮，色彩鲜艳，变形量小，回弹率高，经久耐用。

Description

一种狼牙瑜伽柱的制备方法
技术领域
本发明属于橡塑制品技术领域，具体涉及一种狼牙瑜伽柱的制备方法。
背景技术
现在人们生活水平的不断提高，就更加注重身体健康，瑜伽运动是强身健体的优选项目，而瑜伽柱就是瑜伽练习者较为常用的理想辅助用具，目前市场上销售的瑜伽柱绝大部分采用表层为带有花纹的EVA材料、内心为塑料硬管通过裁切、胶粘、模压成型的产品，简称模压成型瑜伽柱，这种加工方法有几个缺陷：1、要经过12道工序，从备料到产品需要15天的生产周期，工序多，制作周期长，2、原材料利用率低：EVA原板加工时通过去皮、去边、倒角，原板的利用率只能达到70%左右；3、虽然采用的是能达到环保要求的胶水，也只是能说明胶水的毒性目前在可以接受的范围内，并非100%的环保；4、EVA材料的胶水拼接缝处的强度会低于其他部位，会缩短瑜伽柱的使用寿命；5、采用模压成型的成品表面花纹硬度差异大；由于瑜伽柱表面坯料是用厚度相同的EVA泡沫材制作的，在装入带有花纹的定型模具中加工过程中受花纹的深浅不同所受的压力也不同，因而导致产品表面硬也就不同（外硬内软，差别在8-10度），因此需要一种质量更好，更环保耐用的瑜伽柱。
发明内容
为解决上述问题，本发明公开了一种狼牙瑜伽柱的制备方法，成本低，工序少，制作周期短，不使用胶水，环保，生产出来的瑜伽柱表面材料无拼接，硬度均匀，花纹表皮强度高，产品外观光亮，色彩鲜艳，变形量小，经久耐用。
为达到上述目的，本发明的技术方案如下：
一种狼牙瑜伽柱的制备方法，其特征在于：包括以下步骤：
（1）准备原料：其质量组分为：乙烯-醋酸乙烯共聚物：80-95份、发泡剂：8-15份、补强填充剂：10-15份、促进剂：2-5份、活性剂：5-10份、硫化剂：1-2份、防老剂：1-2份、颜料：3-5份；
（2）密炼机预热温度为70-80℃，将原料放入密炼机中密炼15-30分钟，密炼温度110-120℃、压力5-8KG/M2的条件下使原料搅拌均匀、熔化出料，密炼机转速为50-60rpm；
（3）将步骤（2）后的原料放入温度为110-115℃的螺杆挤出机中塑化、挤出、经模口风冷切粒得到混合料颗粒，颗粒尺寸为3-8mm；
（4）将混合料颗粒保温通过注射发泡机在注射压力为600-900KG/CM2的条件下注射到带有狼牙花纹的成型模具中，模具内温度为180±10℃，压力为135-150 KG/M2，保压5-10分钟，开模得到外包层；
（5）将塑料管快速装入步骤（4）的外包层的凹槽内；
（6）在10-20℃空冷，使外包层收缩，包裹在塑料管外围形成狼牙瑜伽柱；
（7）修理废边、检验、包装、入库。
作为本发明的一种改进，所述的发泡剂为碳酸氢钠、碳酸氢铵、偶氮二甲酰胺、4，4′- 氧代双苯磺酰肼、N，N′- 二亚硝基五亚甲基四胺其中的一种或者两种以上的组合物。
作为本发明的一种改进，所述补强填充剂为改性海泡石、纳米结构白炭黑、改性高岭土。
作为本发明的一种改进，所述的活性剂为硼砂、硬脂酸、氧化锌、氧化镁其中的至少一种。
作为本发明的一种改进，所述促进剂为 2- 硫醇基苯并噻唑、二硫化二苯并噻唑、N- 环已基-2- 苯并噻唑次磺酰胺、四甲基二硫化秋兰姆、二丁基二硫代氨基甲酸锌中的至少一种。
作为本发明的一种改进，所述硫化剂为硫磺、一氯化硫、硒、氨基甲酸乙酯其中的一种或者两种以上的组合物。
作为本发明的一种改进，所述防老剂为N-异丙基-N'-苯基对苯二胺、四[β-（3，5-二叔丁基-4-羟基苯基）丙酸]季戊四醇酯中的至少一种。
按照上述制备方法制造出来的一种狼牙瑜伽柱，其特征在于：包括外包层和塑料管，所述外包层为空心圆柱体，外包层内侧设有凹槽，所述塑料管设置在凹槽内，所述外包层表面交错分布的按摩凸点。
作为本发明的一种改进，所述按摩凸点为狼牙形或者半圆形或者圆台形。
作为本发明的一种改进，所述硬塑料管为ABS管或者EVA管。
本发明的有益效果是：
（1）材料简单，采用乙烯-醋酸乙烯共聚物（EVA）为主料，生产出来的瑜伽柱成本低，竞争力强，工艺科学，密炼机温度控制在125℃以下，交联剂不会在密炼机内交联，确保产品质量。
（2) 工艺流程少，制作周期短：本发明所述的注射发泡工艺只经过配料、造粒、注射发泡、修边包装等流程，而且经过造粒，原料无需时效处理，从备料到产品完工只需要5天时间，工作效率提高2倍；
（3）原材料利用率高：注射发泡工艺是将混合料直接注射到带有花纹的成型模具内，最后收缩成型，因此省去了模压成型生产工艺中的去皮、去边、排料损耗环节的原材料损耗，使原材料的利用率达到90%以上；
（4）不使用胶水，确保产品绝对环保； 塑料管是利用塑料制品热胀冷缩的原理将刚从注射发泡机中出模的产品表层温度较高，内孔尺寸较大的时段快速装入，随着温度逐步降低，表面层将塑料管紧紧包柱，因此不用胶水，没有脱胶的顾虑（以前的瑜伽柱生产工艺为模压成型：将原料制成泡沫板，摆放10-15天，在泡沫板和塑料管表面均匀地涂上专用胶水，将泡沫板卷在塑料管表面，再放在模具内加压成型，这种瑜伽柱时间长了以后，会脱胶开裂，而且有接缝）；
（5）瑜伽柱表面材料无拼接缝：是因为带有花纹的成型模具在闭合的状态下，混合料通过注射的方式进入模具的，所以材料就是没有接缝，使产品使用寿命比模压成型瑜伽柱延长一倍以上；
（6）表面花纹硬度均匀：混合料在注射时呈快速流动状，会迅速到达模具的各个部位，并通过一段时间的保压，使表面花纹硬度均匀；
（7）花纹表皮强度高，外观更加光亮，经久耐用，其中缓冲区可以对身体的各个部位进行舒展运动，按摩区内设有多个交错的按摩凸点，可以对人体的关键部位、穴道进行强力按摩，减轻和防止肌肉肿胀，达到缓解压力、放松身心、健身塑形的效果；颜料的颜色为红色、蓝色、橙色、紫色等，产品色彩鲜艳，不褪色。
（8）整体不变形，如果塑料管采用EVA管，可以为空心的，也可以为实心的，塑料管为实心，缓冲性能好，时间长也不会变形，使用时能够很好的防松筋膜，减小肌肉的收缩程度，使肌肉获得放松，塑料管为空心，回弹率好，能够纠正肌肉不平衡，改善关节活动幅度，减轻关节压力，塑料管为ABS管，增强神经肌肉有效性，维持良好的肌肉长度，达到自我防松的效果。
附图说明
图1为本发明所述的狼牙瑜伽柱结构示意图。
图2为本发明所述的狼牙瑜伽柱的剖面图。
附图标记列表：
1、外包层，2、塑料管，3、凹槽，4、按摩凸点。
具体实施方式
下面结合附图和具体实施方式，进一步阐明本发明，应理解下述具体实施方式仅用于说明本发明而不用于限制本发明的范围。
实施例1
本实施例所述的一种狼牙瑜伽柱的制备方法，包括以下步骤：
（1）准备原料：其质量组分为：乙烯-醋酸乙烯共聚物：85份、碳酸氢钠：12份、改性海泡石：13份、2- 硫醇基苯并噻唑：4份、硼砂：7份、硫磺：1份、N-异丙基-N'-苯基对苯二胺：2份、颜料：4份；
（2）密炼机预热温度为75℃，将原料放入密炼机中密炼22分钟，密炼温度115℃、压力7KG/M2的条件下使原料搅拌均匀、熔化出料，密炼机转速为55rpm；
（3）将步骤（2）后的原料放入温度为112℃的螺杆挤出机中塑化、挤出、经模口风冷切粒得到混合料颗粒，颗粒尺寸为6mm；
（4）将混合料颗粒保温通过注射发泡机在注射压力为800KG/CM2的条件下注射到带有狼牙花纹的成型模具中，模具内温度为180℃，压力为140KG/M2，保压8分钟，开模得到外包层；
（5）将塑料管快速装入步骤（4）的外包层的凹槽内；
（6）在15℃空冷，使外包层收缩，包裹在塑料管外围形成狼牙瑜伽柱；
（7）修理废边、检验、包装、入库。
按照上述制备方法制造出来的一种狼牙瑜伽柱，包括外包层1和塑料管2，所述外包层1为空心圆柱体，外包层1内侧设有凹槽3，所述塑料管2设置在凹槽3内，所述外包层1表面交错分布的按摩凸点4。
本实施例所述按摩凸点4为狼牙形。
本实施例所述塑料管为ABS管。
实施例2
本实施例所述的一种狼牙瑜伽柱的制备方法，包括以下步骤：
（1）准备原料：其质量组分为：乙烯-醋酸乙烯共聚物：80份、偶氮二甲酰胺：15份、纳米结构白炭黑：10份、四甲基二硫化秋兰姆：5份、硬脂酸：5份、一氯化硫：2份、四[β-（3，5-二叔丁基-4-羟基苯基）丙酸]季戊四醇酯：1份、颜料：5份；
（2）密炼机预热温度为70℃，将原料放入密炼机中密炼30分钟，密炼温度110℃、压力8KG/M2的条件下使原料搅拌均匀、熔化出料，密炼机转速为50rpm；
（3）将步骤（2）后的原料放入温度为115℃的螺杆挤出机中塑化、挤出、经模口风冷切粒得到混合料颗粒，颗粒尺寸为3mm；
（4）将混合料颗粒保温通过注射发泡机在注射压力为900KG/CM2的条件下注射到带有狼牙花纹的成型模具中，模具内温度为170℃，压力为150 KG/M2，保压5分钟，开模得到外包层；
（5）将塑料管快速装入步骤（4）的外包层的凹槽内；
（6）在20℃空冷，使外包层收缩，包裹在塑料管外围形成狼牙瑜伽柱；
（7）修理废边、检验、包装、入库。
按照上述制备方法制造出来的一种狼牙瑜伽柱，包括外包层和塑料管，所述外包层为空心圆柱体，外包层内侧设有凹槽，所述塑料管设置在凹槽内，所述外包层表面交错分布的按摩凸点。
本实施例所述按摩凸点为半圆形。
本实施例所述塑料管为EVA空心管。
实施例3
本实施例所述的一种狼牙瑜伽柱的制备方法，包括以下步骤：
（1）准备原料：其质量组分为：乙烯-醋酸乙烯共聚物：95份、N，N′- 二亚硝基五亚甲基四胺：8份、改性高岭土：15份、二丁基二硫代氨基甲酸锌：2份、氧化镁：10份、氨基甲酸乙酯：1份、N-异丙基-N'-苯基对苯二胺：2份、颜料：3份；
（2）密炼机预热温度为80℃，将原料放入密炼机中密炼15分钟，密炼温度120℃、压力5KG/M2的条件下使原料搅拌均匀、熔化出料，密炼机转速为60rpm；
（3）将步骤（2）后的原料放入温度为110℃的螺杆挤出机中塑化、挤出、经模口风冷切粒得到混合料颗粒，颗粒尺寸为8mm；
（4）将混合料颗粒保温通过注射发泡机在注射压力为600KG/CM2的条件下注射到带有狼牙花纹的成型模具中，模具内温度为190℃，压力为135 KG/M2，保压10分钟，开模得到外包层；
（5）将塑料管快速装入步骤（4）的外包层的凹槽内；
（6）在10℃空冷，使外包层收缩，包裹在塑料管外围形成狼牙瑜伽柱；
（7）修理废边、检验、包装、入库。
按照上述制备方法制造出来的一种狼牙瑜伽柱，包括外包层和塑料管，所述外包层为空心圆柱体，外包层内侧设有凹槽，所述塑料管设置在凹槽内，所述外包层表面交错分布的按摩凸点。
本实施例所述按摩凸点为圆台形。
本实施例所述塑料管为EVA空心管。
检测结果如下：
本发明方案所公开的技术手段不仅限于上述实施方式所公开的技术手段，还包括由以上技术特征任意组合所组成的技术方案。

Claims (9)

1.一种狼牙瑜伽柱的制备方法，其特征在于：包括以下步骤：
（1）准备原料：其质量组分为：乙烯-醋酸乙烯共聚物：80-95份、发泡剂：8-15份、补强填充剂：10-15份、促进剂：2-5份、活性剂：5-10份、硫化剂：1-2份、防老剂：1-2份、颜料：3-5份；
（2）密炼机预热温度为70-80℃，将原料放入密炼机中密炼15-30分钟，密炼温度110-120℃、压力5-8KG/CM2的条件下使原料搅拌均匀、熔化出料，密炼机转速为50-60rpm；
（3）将步骤（2）后的原料放入温度为110-115℃的螺杆挤出机中塑化、挤出、经模口风冷切粒得到混合料颗粒，颗粒尺寸为3-8mm；
（4）将混合料颗粒保温通过注射发泡机在注射压力为600-900KG/CM2的条件下注射到带有狼牙花纹的成型模具中，模具内温度为180±10℃，压力为135-150 KG/CM2，保压5-10分钟，开模得到外包层；
（5）将塑料管快速装入步骤（4）的外包层的凹槽内；
（6）在10-20℃空冷，使外包层收缩，包裹在塑料管外围形成狼牙瑜伽柱；
（7）修理废边、检验、包装、入库；
所述的狼牙瑜伽柱，包括外包层和塑料管，所述外包层为空心圆柱体，外包层内侧设有凹槽，所述塑料管设置在凹槽内，所述外包层表面交错分布有按摩凸点。
2.根据权利要求1所述的一种狼牙瑜伽柱的制备方法，其特征在于：所述的发泡剂为碳酸氢钠、碳酸氢铵、偶氮二甲酰胺、4，4′- 氧代双苯磺酰肼、N，N′- 二亚硝基五亚甲基四胺其中的一种或者两种以上的组合物。
3.根据权利要求1所述的一种狼牙瑜伽柱的制备方法，其特征在于：所述补强填充剂为改性海泡石或纳米结构白炭黑或改性高岭土。
4.根据权利要求1所述的一种狼牙瑜伽柱的制备方法，其特征在于：所述的活性剂为硼砂、硬脂酸、氧化锌、氧化镁其中的至少一种。
5.根据权利要求1所述的一种狼牙瑜伽柱的制备方法，其特征在于：所述促进剂为 2-硫醇基苯并噻唑、二硫化二苯并噻唑、N- 环已基-2- 苯并噻唑次磺酰胺、四甲基二硫化秋兰姆、二丁基二硫代氨基甲酸锌中的至少一种。
6.根据权利要求1所述的一种狼牙瑜伽柱的制备方法，其特征在于：所述硫化剂为硫磺、一氯化硫、硒、氨基甲酸乙酯其中的一种或者两种以上的组合物。
7.根据权利要求1所述的一种狼牙瑜伽柱的制备方法，其特征在于：所述防老剂为N-异丙基-N'-苯基对苯二胺、四[β-（3，5-二叔丁基-4-羟基苯基）丙酸]季戊四醇酯中的至少一种。
8.根据权利要求1所述的一种狼牙瑜伽柱的制备方法，其特征在于：所述按摩凸点为狼牙形或者半圆形或者圆台形。
9.根据权利要求1所述的一种狼牙瑜伽柱的制备方法，其特征在于：所述塑料管为ABS管或者EVA管。
CN201510432661.6A 2015-07-22 2015-07-22 一种狼牙瑜伽柱的制备方法 Active CN105086122B (zh)