CN105084824A - Novel water-resistant slurry - Google Patents
Novel water-resistant slurry Download PDFInfo
- Publication number
- CN105084824A CN105084824A CN201510501975.7A CN201510501975A CN105084824A CN 105084824 A CN105084824 A CN 105084824A CN 201510501975 A CN201510501975 A CN 201510501975A CN 105084824 A CN105084824 A CN 105084824A
- Authority
- CN
- China
- Prior art keywords
- new waterproof
- waterproof slurry
- slurry
- minute
- solid material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a novel water-resistant slurry which comprises a composite liquid material and a composite solid material in a weight ratio of 1:1. The composite liquid material comprises chlorinated rubber, liquid silica gel, polyvinyl chloride rubber powder, a vinyl acetate-ethylene copolymer (VAE) emulsion, an alkaliproof defoaming agent and a preservative. The composite solid material comprises white carbon black, light calcium carbonate, cement powder, polyvinyl alcohol dry glue powder and a pigment. The composite liquid material and composite solid material are combined to effectively solve the aging resistance of the emulsion and the toxicity resistance of the asphalt and obviously enhance the tensile strength, so that the novel water-resistant slurry has the advantages of high flexibility, high toughness, no pollution, no odor, high aging resistance, high binding force, flexible and variable usage modes and high practicality.
Description
Technical field
The present invention relates to waterproof paint technical field, particularly relate to a kind of new waterproof slurry, be particularly useful for the waterproofing slurry at the places such as metope, underground, tunnel.
Background technology
Waterproof paint is used for the waterproofing and leakage-stopping of construction work, is particularly useful for the WATER REPELLENT such as underground works, hydro project, tunnel, bridge, highway, harbour, body of wall, roof, flooring.
At present, most of waterproof paint is all adopt pitch series and acid propyl series two kinds of materials, and pitch material contaminate environment, distributes malicious taste, brings very big pollution to atmospheric layer; After acid propyl material meets water, fall apart and easy seepage through long period of soaking, wind, water water weak effect, anti-aging degree is low, and in addition, acid propyl material surface merges insecure with construction surface, not anti-aging under solar ultraviolet shines solarization.
Summary of the invention
Technical problem to be solved by this invention is, a kind of new waterproof slurry is provided, the carrying out of composite liquefied material and composite solid material is adopted to combine, effective resistance to deterioration of solution emulsion and the toxin immunity of pitch, and obviously increase tensile strength, have flexibility, toughness concurrently, pollution-free, odorlessness, anti-aging, cohesive force is strong, use-pattern is more flexible and changeable, practical.
For achieving the above object, the present invention adopts following technical proposals:
A kind of new waterproof slurry, is characterized in that, comprise composite liquefied material and composite solid material two kinds of components that weight ratio is 1:1;
In described composite liquefied material, the proportioning of each composition is:
Chlorinated rubber: 20-30 part
Liquid-state silicon gel: 5-15 part
Polyvinyl chloride rubber powder: 10-20 part
Vinyl acetate-ethylene copolymerization (VAE) emulsion: 20-40 part
Alkaline-resisting defoamer: 0.1-0.5 part
Sanitas: 0.3-0.8 part;
In described composite solid material, the proportioning of each composition is:
White carbon black: 10-20 part
Fine particle calcium carbonate: 15-35 part
Cement flour: 25-45 part
Polyvinyl alcohol dry glue powder: 5-10 part
Pigment: 0-0.2 part.
Especially, the blending process of described composite liquefied material: first add chlorinated rubber successively in electric stirring tank, liquid-state silicon gel, stir 20-25 minute, add polyvinyl chloride rubber powder, the mixing of vinyl acetate-ethylene copolymerization (VAE) emulsion is added after stirring 12-18 minute again, stir again and within 10-15 minute, reach evenly, add defoamer and sanitas, play froth breaking and stable effect, the described composite liquefied material prepared is packed for subsequent use, in addition, the proportioning of each material strictly must be controlled in above blending process, temperature condition, agitation condition, and the envrionment temperature used is higher than 0 DEG C.
Especially, the blending process of described composite solid material is: first white carbon black and cement flour are stirred, stir 10-15 minute, add fine particle calcium carbonate again, by three kinds of solid-state material mix and blends after 8-15 minute, then add polyvinyl alcohol (PVA) dry glue powder in this mixing solid phase material, stir 10-15 minute, according to working design require need color adjustment, can add pigment stir within 5-8 minute, namely make described composite solid material, sealed package is for subsequent use.
Especially, described alkaline-resisting defoamer is silicone antifoam agent, and wherein, silicone content is 30%.
Especially, described sanitas is isothiazolinone.
Especially, before construction, described composite liquefied material and described composite solid material are put in electric stirring tank successively according to the weight ratio of 1:1, stir and make for 5-10 minute, the necessary extemporaneous preparation of this waterproof paint, and environment for use temperature is higher than 0 DEG C.
A using method for new waterproof slurry, comprises the described new waterproof slurry of spraying, brushes described new waterproof slurry and scrape described new waterproof slurry.
Especially, spray described new waterproof slurry 2-3 time, thickness is 2-4mm, and brush described new waterproof slurry 2-3 time, thickness is 3-6mm, and scrape described new waterproof slurry 2-3 time, thickness is 3-6mm.
Especially, spray described new waterproof slurry, brush described new waterproof slurry or after scraping described new waterproof slurry, add glasscloth, be used for increasing tensile strength.
The invention has the beneficial effects as follows,
1, the fusion of liquid chlorine rubber, polyvinyl chloride rubber powder adds solid white carbon black, fine particle calcium carbonate, cement flour, polyvinyl alcohol, dye material, plays the resistance to deterioration of emulsion and the toxicity of anti-pitch.
2, the combination of composite liquefied material and composite solid material, obviously increases tensile strength, has flexibility, toughness concurrently, and pollution-free, odorlessness, anti-aging, cohesive force is strong.
3, use-pattern is more flexible, and traditional blade coating operates and brings a lot of convenience to highly difficult Construction Condition, and in the present invention, body of wall is rough and uneven in surface, can adopt jet printing type construction operation, and the little and complex region in limit can adopt painting way.
Embodiment
In order to the technical characterstic of this programme can be clearly described, below in conjunction with embodiment, the present invention is further illustrated.
Embodiment 1
A kind of new waterproof slurry, is characterized in that, comprise composite liquefied material and composite solid material two kinds of components that weight ratio is 1:1;
In described composite liquefied material, the proportioning of each composition is:
Chlorinated rubber: 20 parts
Liquid-state silicon gel: 5 parts
Polyvinyl chloride rubber powder: 10 parts
Vinyl acetate-ethylene copolymerization (VAE) emulsion: 20 parts
Alkaline-resisting defoamer: 0.1 part
Sanitas: 0.3 part;
In described composite solid material, the proportioning of each composition is:
White carbon black: 10 parts
Fine particle calcium carbonate: 15 parts
Cement flour: 25 parts
Polyvinyl alcohol dry glue powder: 5 parts
Pigment: 0 part.
The blending process of described composite liquefied material: first add chlorinated rubber, liquid-state silicon gel successively in electric stirring tank, stir 20 minutes, add polyvinyl chloride rubber powder, the mixing of vinyl acetate-ethylene copolymerization (VAE) emulsion is added after stirring 12 minutes again, stir again and within 10 minutes, reach evenly, add defoamer and sanitas, play froth breaking and stable effect, the described composite liquefied material prepared is packed for subsequent use, in addition, proportioning, temperature condition, the agitation condition of each material strictly must be controlled in above blending process, and the envrionment temperature 3 DEG C used.
The blending process of described composite solid material is: first white carbon black and cement flour are stirred, stir 10 minutes, add fine particle calcium carbonate again, by three kinds of solid-state material mix and blends after 8-minute, polyvinyl alcohol (PVA) dry glue powder is added again in this mixing solid phase material, stir 10 minutes, namely make described composite solid material, sealed package is for subsequent use.
Described alkaline-resisting defoamer is silicone antifoam agent, and wherein, silicone content is 30%.
Described sanitas is isothiazolinone.
Before construction, described composite liquefied material and described composite solid material are put in electric stirring tank successively according to the weight ratio of 1:1, stirs 5 clocks and make, the necessary extemporaneous preparation of this waterproof paint, and environment for use temperature 3 DEG C.
A using method for new waterproof slurry, comprises the described new waterproof slurry of spraying, brushes described new waterproof slurry and scrape described new waterproof slurry.
Spray described new waterproof slurry 2 times, thickness is 2mm, and brush described new waterproof slurry 2 times, thickness is 3mm, scrapes described new waterproof slurry 2 times, and thickness is 3mm.
Spray described new waterproof slurry, brush described new waterproof slurry or after scraping described new waterproof slurry, add glasscloth, be used for increasing tensile strength, 6 hours of constructing winter can reach surface cure.。
Embodiment 2
A kind of new waterproof slurry, is characterized in that, comprise composite liquefied material and composite solid material two kinds of components that weight ratio is 1:1;
In described composite liquefied material, the proportioning of each composition is:
Chlorinated rubber: 30 parts
Liquid-state silicon gel: 15 parts
Polyvinyl chloride rubber powder: 20 parts
Vinyl acetate-ethylene copolymerization (VAE) emulsion: 40 parts
Alkaline-resisting defoamer: 0.5 part
Sanitas: 0.8 part;
In described composite solid material, the proportioning of each composition is:
White carbon black: 20 parts
Fine particle calcium carbonate: 35 parts
Cement flour: 45 parts
Polyvinyl alcohol dry glue powder: 10 parts
Pigment: 0.2 part.
The blending process of described composite liquefied material: first add chlorinated rubber, liquid-state silicon gel successively in electric stirring tank, stir 25 minutes, add polyvinyl chloride rubber powder, the mixing of vinyl acetate-ethylene copolymerization (VAE) emulsion is added after stirring 18 minutes again, stir again and within 15 minutes, reach evenly, add defoamer and sanitas, play froth breaking and stable effect, the described composite liquefied material prepared is packed for subsequent use, in addition, proportioning, temperature condition, the agitation condition of each material strictly must be controlled in above blending process, and the envrionment temperature 30 DEG C used.
The blending process of described composite solid material is: first white carbon black and cement flour are stirred, stir 15 minutes, add fine particle calcium carbonate again, by three kinds of solid-state material mix and blends after 15 minutes, polyvinyl alcohol (PVA) dry glue powder is added again in this mixing solid phase material, stir 15 minutes, add pigment and stir and within 8 minutes, namely make described composite solid material, sealed package is for subsequent use.
Described alkaline-resisting defoamer is silicone antifoam agent, and wherein, silicone content is 30%.
Described sanitas is isothiazolinone.
Before construction, described composite liquefied material and described composite solid material are put in electric stirring tank successively according to the weight ratio of 1:1, stir and make for 10 minutes, the necessary extemporaneous preparation of this waterproof paint, and environment for use temperature 30 DEG C.
A using method for new waterproof slurry, comprises the described new waterproof slurry of spraying, brushes described new waterproof slurry and scrape described new waterproof slurry.
Spray described new waterproof slurry 3 times, thickness is 4mm, and brush described new waterproof slurry 3 times, thickness is 6mm, scrapes described new waterproof slurry 3 times, and thickness is 6mm.
Spray described new waterproof slurry, brush described new waterproof slurry or after scraping described new waterproof slurry, add glasscloth, be used for increasing tensile strength, summer 3, hours can reach surface cure.
Embodiment 3
A kind of new waterproof slurry, is characterized in that, comprise composite liquefied material and composite solid material two kinds of components that weight ratio is 1:1;
In described composite liquefied material, the proportioning of each composition is:
Chlorinated rubber: 25 parts
Liquid-state silicon gel: 10 parts
Polyvinyl chloride rubber powder: 15 parts
Vinyl acetate-ethylene copolymerization (VAE) emulsion: 30 parts
Alkaline-resisting defoamer: 0.3 part
Sanitas: 0.5 part;
In described composite solid material, the proportioning of each composition is:
White carbon black: 15 parts
Fine particle calcium carbonate: 25 parts
Cement flour: 33 parts
Polyvinyl alcohol dry glue powder: 8 parts
Pigment: 0.1 part.
The blending process of described composite liquefied material: first add chlorinated rubber, liquid-state silicon gel successively in electric stirring tank, stir 22 minutes, add polyvinyl chloride rubber powder, the mixing of vinyl acetate-ethylene copolymerization (VAE) emulsion is added after stirring 15 minutes again, stir again and within 13 minutes, reach evenly, add defoamer and sanitas, play froth breaking and stable effect, the described composite liquefied material prepared is packed for subsequent use, in addition, proportioning, temperature condition, the agitation condition of each material strictly must be controlled in above blending process, and the envrionment temperature 20 DEG C used.
The blending process of described composite solid material is: first white carbon black and cement flour are stirred, stir 13 minutes, add fine particle calcium carbonate again, by three kinds of solid-state material mix and blends after 13 minutes, polyvinyl alcohol (PVA) dry glue powder is added again in this mixing solid phase material, stir 13 minutes, add pigment and stir and within 7 minutes, namely make described composite solid material, sealed package is for subsequent use.
Described alkaline-resisting defoamer is silicone antifoam agent, and wherein, silicone content is 30%.
Described sanitas is isothiazolinone.
Before construction, described composite liquefied material and described composite solid material are put in electric stirring tank successively according to the weight ratio of 1:1, stir and make for 8 minutes, the necessary extemporaneous preparation of this waterproof paint, and environment for use temperature 20 DEG C.
A using method for new waterproof slurry, comprises the described new waterproof slurry of spraying, brushes described new waterproof slurry and scrape described new waterproof slurry.
Spray described new waterproof slurry 2 times, thickness is 3mm, and brush described new waterproof slurry 3 times, thickness is 5mm, scrapes described new waterproof slurry 2 times, and thickness is 5mm.
Spray described new waterproof slurry, brush described new waterproof slurry or after scraping described new waterproof slurry, add glasscloth, be used for increasing tensile strength, spring, construction in summer 4 hours can reach surface cure.
The present invention can pass through existing techniques in realizing without the technical characteristic described, and does not repeat them here.Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited only to above-mentioned citing, and the change of the art those of ordinary skill done by essential scope of the present invention, remodeling, interpolation or replacing, also should belong to protection scope of the present invention.
Claims (9)
1. a new waterproof slurry, is characterized in that, comprises composite liquefied material and composite solid material two kinds of components that weight ratio is 1:1;
In described composite liquefied material, the proportioning of each composition is:
Chlorinated rubber: 20-30 part
Liquid-state silicon gel: 5-15 part
Polyvinyl chloride rubber powder: 10-20 part
Vinyl acetate-ethylene copolymerization (VAE) emulsion: 20-40 part
Alkaline-resisting defoamer: 0.1-0.5 part
Sanitas: 0.3-0.8 part;
In described composite solid material, the proportioning of each composition is:
White carbon black: 10-20 part
Fine particle calcium carbonate: 15-35 part
Cement flour: 25-45 part
Polyvinyl alcohol dry glue powder: 5-10 part
Pigment: 0-0.2 part.
2. a kind of new waterproof slurry as claimed in claim 1, it is characterized in that, the blending process of described composite liquefied material: first add chlorinated rubber successively in electric stirring tank, liquid-state silicon gel, stir 20-25 minute, add polyvinyl chloride rubber powder, the mixing of vinyl acetate-ethylene copolymerization (VAE) emulsion is added after stirring 12-18 minute again, stir again and within 10-15 minute, reach evenly, add defoamer and sanitas, play froth breaking and stable effect, the described composite liquefied material prepared is packed for subsequent use, in addition, the proportioning of each material strictly must be controlled in above blending process, temperature condition, agitation condition, and the envrionment temperature used is higher than 0 DEG C.
3. a kind of new waterproof slurry as claimed in claim 1, it is characterized in that, the blending process of described composite solid material is: first white carbon black and cement flour are stirred, stir 10-15 minute, add fine particle calcium carbonate again, by three kinds of solid-state material mix and blends after 8-15 minute, polyvinyl alcohol (PVA) dry glue powder is added again in this mixing solid phase material, stir 10-15 minute, according to working design require need color adjustment, can add pigment stirring and within 5-8 minute, namely make described composite solid material, sealed package is for subsequent use.
4. a kind of new waterproof slurry as claimed in claim 1 or 2, is characterized in that, described alkaline-resisting defoamer is silicone antifoam agent, and wherein, silicone content is 30%.
5. a kind of new waterproof slurry as described in claim 1 or 3, is characterized in that, described sanitas is isothiazolinone.
6. as a kind of new waterproof slurry as described in arbitrary in claim 1 to 5, it is characterized in that, before construction, described composite liquefied material and described composite solid material are put in electric stirring tank successively according to the weight ratio of 1:1, stir and make for 5-10 minute, the necessary extemporaneous preparation of this waterproof paint, and environment for use temperature is higher than 0 DEG C.
7. the using method of a kind of new waterproof slurry as claimed in claim 6, is characterized in that, comprises the described new waterproof slurry of spraying, brushes described new waterproof slurry and scrape described new waterproof slurry.
8. the using method of a kind of new waterproof slurry as claimed in claim 7, is characterized in that, sprays described new waterproof slurry 2-3 time, thickness is 2-4mm, brushes described new waterproof slurry 2-3 time, and thickness is 3-6mm, scrape described new waterproof slurry 2-3 time, thickness is 3-6mm.
9. the using method of a kind of new waterproof slurry as claimed in claim 7 or 8, is characterized in that, sprays described new waterproof slurry, brushes described new waterproof slurry or after scraping described new waterproof slurry, adds glasscloth, is used for increasing tensile strength.