CN105082675A - Basalt fiber fireproof plate - Google Patents
Basalt fiber fireproof plate Download PDFInfo
- Publication number
- CN105082675A CN105082675A CN201510529332.3A CN201510529332A CN105082675A CN 105082675 A CN105082675 A CN 105082675A CN 201510529332 A CN201510529332 A CN 201510529332A CN 105082675 A CN105082675 A CN 105082675A
- Authority
- CN
- China
- Prior art keywords
- parts
- panel
- sandwich layer
- basalt fibre
- plastic laminated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a basalt fiber fireproof plate which comprises a bottom layer, a core layer and a faceplate. The core layer is positioned between the bottom layer and the faceplate. The basalt fiber fireproof plate is characterized in that the faceplate is made by, by weight, 23-42 parts of basalt fiber, 8-22 parts of glass fiber, 12-23 parts of aggregate and 6-12 parts of adhesive. The basalt fiber fireproof plate is good in fireproof effect and has a denoising function by changing materials without increasing thickness.
Description
Technical field
The present invention relates to the PLASTIC LAMINATED that building field is used, particularly relate to a kind of basalt fibre PLASTIC LAMINATED.
Background technology
Have another name called refractory slab, formal name used at school is thermosetting resin-impregnated paper high-pressure laminated board, english abbreviation is HPL (DecorativeHigh-pressureLaminate) is incrustation refractory building material, there is abundant surface color and polish, lines and special logistics performance, be widely used in the fields such as interior decoration, furniture, kitchen cabinet, laboratory table top, exterior wall.If Authorization Notice No. is CN203891389U, authorized announcement date is that the Chinese utility model patent on October 22nd, 2014 discloses a kind of absorbing sound and lowering noise PLASTIC LAMINATED, adopt glass magnesium fire prevention plate body and baking vanish aluminium perforated plate, built-in fire prevention expanding material, also comprise a compression glass centrifugal cotton fireprotection layer, so have splendid flameproof effect; Sound is inhaled in sound absorption cavity in the perforation of baking vanish aluminium perforated plate, greatly abates the noise; The bottom of sound absorption cavity is provided with several sound-absorption hole, and then there is sound absorbing layer the bottom of sound-absorption hole, and sound absorbing layer both can be located at separately the bottom position of sound-absorption hole, also all can cover one deck in the bottom surface of fire prevention plate body; Owing to can have sound absorption cavity, sound-absorption hole and sound absorbing layer simultaneously, the utility model is made to have good sound-absorbing effect.
Authorization Notice No. is CN203891236U, authorized announcement date is that the Chinese utility model patent on October 22nd, 2014 discloses a kind of shock-resistant composite fire-proof sheet material, described composite fire-proof sheet material comprises fixed bed, reinforcement, packing layer is connected end socket with port, described fixed bed is double-deck strap, vertically arranged reinforcement is provided with between double-deck strap, packing layer is provided with between described reinforcement and strap, elastic reactance impact tube is provided with in described packing layer, described elastic reactance impact tube comprises shock-resistant supervisor and looped pipeline, described shock-resistant supervisor is arranged in the middle part of packing layer, described shock-resistant looped pipeline is arranged on shock-resistant supervisor both sides, the utility model improves the impact resistance of PLASTIC LAMINATED own by the structure of the filler in packing layer and elastic reactance impact tube, simultaneously when suffering that weight clashes into, by expanded vermiculite and the buffering between shock-resistant supervisor and looped pipeline, decrease the impulsive force that double-deck strap surface is subject to, prevent double-deck strap surface fracture, substantially increase the service life of PLASTIC LAMINATED, save the maintenance cost of finishing and sheet material.
There is following defect in above-mentioned utility model: whole fire-proof board flameproof effect is not fine, reaches the object of noise reduction by arranging sound absorption cavity, sound-absorption hole and sound absorbing layer, adds the thickness of fire-proof board.
Summary of the invention
In order to overcome the above-mentioned defect that above-mentioned PLASTIC LAMINATED exists, the invention provides a kind of basalt fibre PLASTIC LAMINATED, this PLASTIC LAMINATED flameproof effect is better, and makes PLASTIC LAMINATED have the function of noise reduction by the change of material, can not increase the thickness of PLASTIC LAMINATED.
The present invention for solving the problems of the technologies described above adopted technical scheme is:
A kind of basalt fibre PLASTIC LAMINATED, comprise bottom, sandwich layer and panel, sandwich layer, between bottom and panel, is characterized in that: panel is with making with the composition of weight parts as follows:
Basalt fibre: 23 parts ~ 42 parts
Glass fibre: 8 parts ~ 22 parts
Aggregate: 12 parts ~ 23 parts
Binder: 6 parts ~ 12 parts.
Described panel comprises following with the composition of weight parts:
Basalt fibre: 30 parts ~ 38 parts
Glass fibre: 12 parts ~ 16 parts
Aggregate: 14 parts ~ 18 parts
Binder: 8 parts ~ 10 parts.
Described sandwich layer be halogen-free flameproof mineral-modified fill out core material.
Compared with prior art, the present invention has following beneficial effect:
The present invention is owing to adding basalt fibre in the panel, and acid-fast alkali-proof strengthens, and fire line strengthens, but also has the function of noise reduction.The present invention adds the function of noise reduction by the change of material, does not need the thickness increasing PLASTIC LAMINATED.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described, and described embodiment is only the present invention's part embodiment, is not whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making other embodiments used obtained under creative work prerequisite, belongs to protection scope of the present invention.
Embodiment 1
A kind of basalt fibre PLASTIC LAMINATED, comprise bottom, sandwich layer and panel, sandwich layer, between bottom and panel, is characterized in that: panel is with making with the composition of weight parts as follows:
Basalt fibre: 23 parts
Glass fibre: 8 parts
Aggregate: 12 parts
Binder: 6 parts.
Described sandwich layer be halogen-free flameproof mineral-modified fill out core material.
Embodiment 2
A kind of basalt fibre PLASTIC LAMINATED, comprise bottom, sandwich layer and panel, sandwich layer, between bottom and panel, is characterized in that: panel is with making with the composition of weight parts as follows:
Basalt fibre: 42 parts
Glass fibre: 22 parts
Aggregate: 23 parts
Binder: 12 parts.
Described sandwich layer be halogen-free flameproof mineral-modified fill out core material.
Embodiment 3
A kind of basalt fibre PLASTIC LAMINATED, comprise bottom, sandwich layer and panel, sandwich layer, between bottom and panel, is characterized in that: panel is with making with the composition of weight parts as follows:
Basalt fibre: 25 parts
Glass fibre: 12 parts
Aggregate: 20 parts
Binder: 10 parts.
Described sandwich layer be halogen-free flameproof mineral-modified fill out core material.
Embodiment 4
A kind of basalt fibre PLASTIC LAMINATED, comprise bottom, sandwich layer and panel, sandwich layer, between bottom and panel, is characterized in that: panel is with making with the composition of weight parts as follows:
Basalt fibre: 30 parts
Glass fibre: 18 parts
Aggregate: 16 parts
Binder: 11 parts.
Described sandwich layer be halogen-free flameproof mineral-modified fill out core material.
Embodiment 5
A kind of basalt fibre PLASTIC LAMINATED, comprise bottom, sandwich layer and panel, sandwich layer, between bottom and panel, is characterized in that: panel is with making with the composition of weight parts as follows:
Basalt fibre: 35 parts
Glass fibre:: 15 parts
Aggregate: 16 parts
Binder: 9 parts.
Described sandwich layer be halogen-free flameproof mineral-modified fill out core material.
Embodiment 6
A kind of basalt fibre PLASTIC LAMINATED, comprise bottom, sandwich layer and panel, sandwich layer, between bottom and panel, is characterized in that: panel is with making with the composition of weight parts as follows:
Basalt fibre: 30 parts
Glass fibre: 12 parts
Aggregate: 14 parts
Binder: 10 parts.
Described sandwich layer be halogen-free flameproof mineral-modified fill out core material.
Embodiment 7
A kind of basalt fibre PLASTIC LAMINATED, comprise bottom, sandwich layer and panel, sandwich layer, between bottom and panel, is characterized in that: panel is with making with the composition of weight parts as follows:
Basalt fibre: 38 parts
Glass fibre: 16 parts
Aggregate: 18 parts
Binder: 8 parts.
Described sandwich layer be halogen-free flameproof mineral-modified fill out core material.
Claims (2)
1. a basalt fibre PLASTIC LAMINATED, comprises bottom, sandwich layer and panel, and sandwich layer, between bottom and panel, is characterized in that: panel is with making with the composition of weight parts as follows:
Basalt fibre: 23 parts ~ 42 parts
Glass fibre: 8 parts ~ 22 parts
Aggregate: 12 parts ~ 23 parts
Binder: 6 parts ~ 12 parts.
2. a kind of basalt fibre PLASTIC LAMINATED according to claim 1, is characterized in that: described panel comprises following with the composition of weight parts:
Basalt fibre: 30 parts ~ 38 parts
Glass fibre: 12 parts ~ 16 parts
Aggregate: 14 parts ~ 18 parts
Binder: 8 parts ~ 10 parts.