CN105063458B - red copper soap - Google Patents
red copper soap Download PDFInfo
- Publication number
- CN105063458B CN105063458B CN201510496326.2A CN201510496326A CN105063458B CN 105063458 B CN105063458 B CN 105063458B CN 201510496326 A CN201510496326 A CN 201510496326A CN 105063458 B CN105063458 B CN 105063458B
- Authority
- CN
- China
- Prior art keywords
- parts
- soap
- red copper
- compound
- well mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses red copper soap. The red copper soap comprises, by weight, 30-40 parts of red copper, 6-9 parts of Al, 3-6 parts of B, 2-4 parts of K, 10-20 parts of Cr, 0.8-1.2 parts of Ni, 0.6-1.0 part of Mo, 1.2-2.2 parts of Si, 0.4-0.8 parts of Nb, 1.6-2.4 parts of Ti and 2-4 parts of N. The red copper soap has the beneficial effects that the red copper is adopted as the main component of alloy soap and is in cooperation with other metal elements, and the formed soap has the functions of peculiar smell removal and disinfection through anaerobic calcination and aerobic calcination. A user can use the soap without waiting and can use the soap immediately when needing the soap.
Description
Technical field
The present invention relates to metallic soaps, more particularly to alloy soap and preparation method thereof.
Background technology
Metal perfumed soap is the patented product of Germany's invention, is made up of stainless steel alloy, and profile and conventional toilet soaps are as good as, and is utilized
Physical method（Catalysis）Decompose macromolecular substances, mainly remove the strange taste such as fishlike smell and onion flavor, use
When both hands hold dispelling abnormal flavor by the appearance for washing half a minute by rubbing with the hands under water.Stainless steel perfumed soap generally will " half input water in,
Half is exposed in air ".When using for the first time, need to wait within -6 hours 5 hours ability normal work.Effective storage life can be tieed up
Hold 3 to 5 years.It is cover type that general tradition eliminates the mode of stink, such as aromatic, is that stink, nothing are covered with another kind of taste
Method really eliminates stink；Absorption type deodorant is reached after a while after degree of saturation, it is impossible to play effect again.And stainless steel is fertile
The deodorant principle of soap is substantially breakdown.When stainless steel alloy is contacted with air and hydrone simultaneously, catalyst work can be produced
With, the molecular structure of peculiar smell is decomposed, " reduction " is into tasteless state.It is main but stainless steel soap cannot replace traditional perfumed soap
Want function to be to eliminate the unusual smell, have no disinfective action.
The content of the invention
The technical problem to be solved in the present invention is that existing stainless steel soap use condition is harsh, and the stand-by period is oversize, and
Disinfective action cannot be played, for this provide it is a kind of by dispelling abnormal flavor again can disinfection red copper soap and preparation method thereof.
The technical scheme is that：Red copper soap, it is included by weight：The red copper of 30-40 parts, the Al of 6-9 parts,
Si, 0.4- of Mo, 1.2-2.2 part of Ni, 0.6-1.0 part of Cr, 0.8-1.2 part of K, 10-20 part of B, 2-4 part of 3-6 parts
The N of Ti and 2-4 parts of 0.8 part Nb, 1.6-2.4 part.
The preparation method of red copper soap, it is comprised the following steps：（1）, anaerobic calcining：By the B of Al, 3-6 part of 6-9 parts,
The Ni of Cr and 0.8-1.2 parts of K, 10-20 part of 2-4 parts is well mixed in nitrogen atmosphere and calcines 50- at 1500-1600 DEG C
60min, then calcining 30-40min forms compound A under 1600-1700 DEG C, 200-250Mpa in nitrogen atmosphere；（2）, have
Oxygen is calcined：The N of Ti and 2-4 parts of Nb, 1.6-2.4 part of Si, 0.4-0.8 part of Mo, 1.2-2.2 part of 0.6-1.0 parts is mixed
Conjunction is uniformly calcined 20-30min and forms compound B under oxygen-enriched environment at 1200-1300 DEG C；（3）, by compound A and mixing
Material B stands after being cooled to 500-600 DEG C and is well mixed, and the red copper for adding 30-40 parts calcines 30-40min at 1100-1200 DEG C
Slurries are formed, taking-up is poured mould into and mould plastic sheeting parcel is treated into slurries natural cooling is molded.
The invention has the beneficial effects as follows coordinating red copper as the main composition and other metallic elements of alloy soap, Jing
Cross anaerobic calcining and aerobic is calcined and causes the soap of shaping to have the effect for eliminating the unusual smell and sterilizing concurrently, use without waiting for needing
Use.
Specific embodiment
With reference to embodiment, the present invention will be further described.
Embodiment 1：Red copper soap, it is included by weight：30 parts of red copper, 6 parts of Al, 3 parts of B, 2 parts of K, 10
The Cr, 0.8 part of Ni, 0.6 part of Mo, 1.2 parts of Si, 0.4 part of Nb, Ti and 2 of 1.6 parts part of N of part.
The preparation method of red copper soap, it is comprised the following steps：（1）, anaerobic calcining：By 6 parts of Al, 3 parts of B, 2 parts
K, Cr and 0.8 of 10 parts part of Ni are well mixed in nitrogen atmosphere and 50min are calcined at 1500 DEG C, then in nitrogen atmosphere in
1600 DEG C, calcine 30min under 200Mpa and form compound A；（2）, aerobic calcining：By 0.6 part of Mo, 1.2 parts of Si, 0.4 part
Nb, Ti and 2 of 1.6 parts part of N be well mixed under oxygen-enriched environment at 1200 DEG C calcine 20min formed compound B；（3）、
Compound A and compound B is stood and be well mixed after being cooled to 500 DEG C, the red copper for adding 30 parts calcines 30min at 1100 DEG C
Slurries are formed, taking-up is poured mould into and mould plastic sheeting parcel is treated into slurries natural cooling is molded.
Embodiment 2：Red copper soap, it is included by weight：35 parts of red copper, 7 parts of Al, 5 parts of B, 3 parts of K, 15
The Cr, 1.0 parts of Ni, 0.8 part of Mo, 1.6 parts of Si, 0.6 part of Nb, Ti and 3 of 2.0 parts part of N of part.
The preparation method of red copper soap, it is comprised the following steps：（1）, anaerobic calcining：By 7 parts of Al, 5 parts of B, 3 parts
K, Cr and 1.0 of 15 parts part of Ni are well mixed in nitrogen atmosphere and 55min are calcined at 1550 DEG C, then in nitrogen atmosphere in
1650 DEG C, calcine 35min under 225Mpa and form compound A；（2）, aerobic calcining：By 0.8 part of Mo, 1.6 parts of Si, 0.6 part
Nb, Ti and 3 of 2.0 parts part of N be well mixed under oxygen-enriched environment at 1250 DEG C calcine 25min formed compound B；（3）、
Compound A and compound B is stood and be well mixed after being cooled to 550 DEG C, the red copper for adding 35 parts calcines 35min at 1150 DEG C
Slurries are formed, taking-up is poured mould into and mould plastic sheeting parcel is treated into slurries natural cooling is molded.
Embodiment 3：Red copper soap, it is included by weight：40 parts of red copper, 9 parts of Al, 6 parts of B, 4 parts of K,
20 parts of Cr, 1.2 parts of Ni, 1.0 parts of Mo, 2.2 parts of Si, 0.8 part of Nb, Ti and 4 of 2.4 parts part of N.
The preparation method of red copper soap, it is comprised the following steps：（1）, anaerobic calcining：By 9 parts of Al, 6 parts of B, 4 parts
K, Cr and 1.2 of 20 parts part of Ni are well mixed in nitrogen atmosphere and 60min are calcined at 1600 DEG C, then in nitrogen atmosphere in
1700 DEG C, calcine 40min under 250Mpa and form compound A；（2）, aerobic calcining：By 1.0 parts of Mo, 2.2 parts of Si, 0.8 part
Nb, Ti and 4 of 2.4 parts part of N be well mixed under oxygen-enriched environment at 1300 DEG C calcine 30min formed compound B；（3）、
Compound A and compound B is stood and be well mixed after being cooled to 600 DEG C, the red copper for adding 40 parts calcines 40min at 1200 DEG C
Slurries are formed, taking-up is poured mould into and mould plastic sheeting parcel is treated into slurries natural cooling is molded.
Soap of the invention obtained through anaerobic calcining and aerobic due to calcining the compound A to be formed and compound B is caused
The soap of shaping has natural texture and layering, and surface is up to several hours when using without the need for polishing without the need under water.It is purple
Copper is in the final step in 300-400 DEG C of addition, it is ensured that red copper does not occur chemical reaction with compound A and compound B, makes copper
Ion can easily discharge, and play dispelling abnormal flavor, sterilized effect.Plastic sheeting is most important to the dispelling abnormal flavor of soap,
Can ensure that alloying component does not contact generation oxidation reaction with oxygen during shaping.Mould can as needed be selected with moulding
Select, such as ellipse, rectangle, triangle etc..
Claims (1)
1. red copper soap, is characterized in that it is included by weight：The red copper of 30-40 parts, B, 2-4 of Al, 3-6 part of 6-9 parts
The Nb of Si, 0.4-0.8 part of Mo, 1.2-2.2 part of Ni, 0.6-1.0 part of Cr, 0.8-1.2 part of K, 10-20 part of part,
The N of Ti and 2-4 parts of 1.6-2.4 parts, its preparation method is comprised the following steps：（1）, anaerobic calcining：By Al, 3-6 part of 6-9 parts
The Ni of Cr and 0.8-1.2 parts of K, 10-20 part of B, 2-4 part be well mixed in nitrogen atmosphere and forged at 1500-1600 DEG C
50-60min is burnt, then 30-40min is calcined under 1600-1700 DEG C, 200-250MPa in nitrogen atmosphere and form compound A；
（2）, aerobic calcining：By Ti and 2-4 parts of Nb, 1.6-2.4 part of Si, 0.4-0.8 part of Mo, 1.2-2.2 part of 0.6-1.0 parts
N be well mixed under oxygen-enriched environment at 1200-1300 DEG C calcine 20-30min formed compound B；（3）, by compound A and
Compound B stands after being cooled to 500-600 DEG C and is well mixed, and the red copper for adding 30-40 parts calcines 30- at 1100-1200 DEG C
40min forms slurries, and taking-up is poured mould into and mould plastic sheeting parcel is treated into slurries natural cooling is molded.