CN105057913A - 硬面耐磨开弧焊丝 - Google Patents

硬面耐磨开弧焊丝 Download PDF

Info

Publication number
CN105057913A
CN105057913A CN201510398554.6A CN201510398554A CN105057913A CN 105057913 A CN105057913 A CN 105057913A CN 201510398554 A CN201510398554 A CN 201510398554A CN 105057913 A CN105057913 A CN 105057913A
Authority
CN
China
Prior art keywords
welding wire
open arc
arc welding
wear
hard
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510398554.6A
Other languages
English (en)
Inventor
施志儒
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Up Wear Resistance Compound Materials Co Ltd
Original Assignee
Suzhou Up Wear Resistance Compound Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Up Wear Resistance Compound Materials Co Ltd filed Critical Suzhou Up Wear Resistance Compound Materials Co Ltd
Priority to CN201510398554.6A priority Critical patent/CN105057913A/zh
Publication of CN105057913A publication Critical patent/CN105057913A/zh
Pending legal-status Critical Current

Abstract

本发明一种硬面耐磨开弧焊丝，所述焊丝组分的重量百分比为：碳5.1-5.5％、锰1.2-1.4％、硅0.8-1.2％、铬21-23％、铌6.3-6.7％、钼6.3-6.7％、钒0.9-1.1％、钨1.9-2.1％、余量为铁。本发明使熔敷金属具备非常好的抗中度冲击、抗严重磨损、抗腐蚀性能，具备良好的耐高温特性，适用于650℃以上的高温条件下的磨耗。

Description

硬面耐磨开弧焊丝
技术领域
本发明涉及堆焊领域，具体涉及一种硬面耐磨开弧焊丝。
背景技术
烧结机适用于大型黑色冶金烧结厂的烧结作业，它是抽风烧结过程中的主体设备，可将不同成份，不同粒度的精矿粉，富矿粉烧结成块，并部分消除矿石中所含的硫，磷等有害杂质。单齿辊，主要用于烧结机尾部，破碎650℃-800℃的热烧结矿，由于烧结生产工艺连续性的要求，单齿辊必须使用寿命在一年以上，但是单齿辊破碎的物料是650℃以上的大块热烧结矿，大大降低了单齿辊的使用寿命，为了延长单齿辊的使用寿命，人们选择了在单齿辊磨损的部位通过堆焊工艺改造金属成分的办法。
因此，就需要一种硬面耐磨开弧焊丝解决上述堆焊的问题。
发明内容
本发明的目的是提供一种抗冲击、耐磨损、耐腐蚀、耐高温的硬面耐磨开弧焊丝。
本发明通过如下技术方案实现上述目的：一种硬面耐磨开弧焊丝，所述焊丝组分的重量百分比为：碳5.1-5.5％、锰1.2-1.4％、硅0.8-1.2％、铬21-23％、铌6.3-6.7％、钼6.3-6.7％、钒0.9-1.1％、钨1.9-2.1％、余量为铁。
进一步的，所述焊丝堆焊出的熔敷金属硬度为63-67HRC。
进一步的，所述焊丝的直径为2.4mm或2.8mm。
进一步的，所述焊丝的延伸长度为30-35mm。
进一步的，所述焊丝组分的重量百分比为：碳5.1％、锰1.2％、硅0.8％、铬21％、铌6.7％、钼6.7％、钒1.1％、钨2.1％、铁55.3％。
进一步的，所述焊丝组分的重量百分比为：碳5.5％、锰1.4％、硅1.2％、铬23％、铌6.3％、钼6.3％、钒0.9％、钨1.9％、铁53.5％。
进一步的，所述焊丝组分的重量百分比为：碳5.3％、锰1.3％、硅1％、铬22％、铌6.5％、钼6.5％、钒1％、钨2％、铁54.4％。
与现有技术相比，本发明硬面耐磨开弧焊丝的有益效果是：使熔敷金属具备非常好的抗中度冲击、抗严重磨损、抗腐蚀性能，具备良好的耐高温特性，适用于650℃以上的高温条件下的磨耗。
具体实施方式
下面结合具体实施例对本发明进一步进行描述。
实施例1
一种硬面耐磨开弧焊丝，所述焊丝组分的重量百分比为：碳5.1％、锰1.2％、硅0.8％、铬21％、铌6.7％、钼6.7％、钒1.1％、钨2.1％、铁55.3％。焊丝的直径为2.4mm，焊丝的延展长度为35mm，使用所述焊丝的焊接电流为280A、焊接电压为29V，使用所述焊丝堆焊出的熔敷金属硬度为63HRC。
实施例2
一种硬面耐磨开弧焊丝，所述焊丝组分的重量百分比为：碳5.5％、锰1.4％、硅1.2％、铬23％、铌6.3％、钼6.3％、钒0.9％、钨1.9％、铁53.5％。焊丝的直径为2.8mm，焊丝的延展长度为30mm，使用所述焊丝的焊接电流为400A、焊接电压为30V，使用所述焊丝堆焊出的熔敷金属硬度为67HRC。
实施例3
一种硬面耐磨开弧焊丝，所述焊丝组分的重量百分比为：碳5.3％、锰1.3％、硅1％、铬22％、铌6.5％、钼6.5％、钒1％、钨2％、铁54.4％。焊丝的直径为2.4mm，焊丝的延展长度为32.5mm，使用所述焊丝的焊接电流为350A、焊接电压为28V，使用所述焊丝堆焊出的熔敷金属硬度为65HRC。
本发明使熔敷金属具备非常好的抗中度冲击、抗严重磨损、抗腐蚀性能，具备良好的耐高温特性，适用于650℃以上的高温条件下的磨耗。

Claims (7)

1.一种硬面耐磨开弧焊丝，其特征在于，所述焊丝组分的重量百分比为：碳5.1-5.5％、锰1.2-1.4％、硅0.8-1.2％、铬21-23％、铌6.3-6.7％、钼6.3-6.7％、钒0.9-1.1％、钨1.9-2.1％、余量为铁。
2.根据权利要求1所述的硬面耐磨开弧焊丝，其特征在于：所述焊丝堆焊出的熔敷金属硬度为63-67HRC。
3.根据权利要求1所述的硬面耐磨开弧焊丝，其特征在于：所述焊丝的直径为2.4mm或2.8mm。
4.根据权利要求1所述的硬面耐磨开弧焊丝，其特征在于：所述焊丝的延伸长度为30-35mm。
5.根据权利要求1所述的硬面耐磨开弧焊丝，其特征在于：所述焊丝组分的重量百分比为：碳5.1％、锰1.2％、硅0.8％、铬21％、铌6.7％、钼6.7％、钒1.1％、钨2.1％、铁55.3％。
6.根据权利要求1述的硬面耐磨开弧焊丝，其特征在于：所述焊丝组分的重量百分比为：碳5.5％、锰1.4％、硅1.2％、铬23％、铌6.3％、钼6.3％、钒0.9％、钨1.9％、铁53.5％。
7.根据权利要求1述的硬面耐磨开弧焊丝，其特征在于：所述焊丝组分的重量百分比为：碳5.3％、锰1.3％、硅1％、铬22％、铌6.5％、钼6.5％、钒1％、钨2％、铁54.4％。
CN201510398554.6A 2015-07-09 2015-07-09 硬面耐磨开弧焊丝 Pending CN105057913A (zh)