CN105041927A - High-temperature-resisting automobile disc type brake block - Google Patents
High-temperature-resisting automobile disc type brake block Download PDFInfo
- Publication number
- CN105041927A CN105041927A CN201510343726.XA CN201510343726A CN105041927A CN 105041927 A CN105041927 A CN 105041927A CN 201510343726 A CN201510343726 A CN 201510343726A CN 105041927 A CN105041927 A CN 105041927A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- brake block
- automobile disc
- disc type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A high-temperature-resisting automobile disc type brake block is made of raw materials including, by weight, 9 parts to 16 parts of attapulgite, 5 parts to 8 parts of rutile titanium dioxide, 1 part to 5 parts of a crosslinking modifier, 6 parts to 11 parts of methyl phenyl siloxane branched chain type prepolymer, 4 parts to 8 parts of barite, 2 parts to 6 parts of steel wool fibers, 3 parts to 9 parts of butadiene-acrylonitrile rubber phenol, 6 parts to 10 parts of thermosetting resin, 2 parts to 6 parts of carbon fibers, 5 parts to 10 parts of barium sulfate, 7 parts to 10 parts of potassium titanate fibers, 1 part to 4 parts of mica, 4 parts to 6 parts of copper powder, 1 part to 4 parts of resin and 6 parts to 14 parts of cashew nut shell oil friction powder. The high-temperature-resisting automobile disc type brake block has the beneficial effects of having the good high-temperature-resisting performance, and meanwhile being rapid in cooling, better in wear resistance and long in service life.
Description
Technical field
The present invention relates to a kind of resistant to elevated temperatures automobile disc brake pad.
Background technique
Disk type brake has one to fix with tire and synchronizedly rotates to obtain circular disc, uses oil pressure to promote brake block clamping roudnel, produce frictional force is braked by contact during brake.Disc brake pad (dish) is divided into ordinary disc-type and ventilated disc.At present, automobile brake friction plate uses antimonous sulfide in a large number, also exists containing heavy metal, to environment; Simultaneously common brake block, when high temperature friction, there will be slight ruckbildung, sometimes because friction is comparatively frequent, occurs the taste burnt, well can not play braking action.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of automobile disc brake pad, has good resistance to high temperature, and heat radiation is very fast simultaneously, and wear resistance is better, long service life.
For solving prior art problem, technological scheme provided by the invention is, a kind of resistant to elevated temperatures automobile disc brake pad, and it is made up of the raw material of following parts by weight:
Attapulgite 9-16 part, rutile type titanium white 5-8 part, cross-linked modifier 1-5 part, methyl phenyl siloxane branched chain type prepolymer 6-11 part, barite 4-8 part, steel wool fiber 2-6 part, Nitrile Rubber phenol 3-9 part, thermosetting resin 6-10 part, carbon fiber 2-6 part, barium sulphate 5-10 part, potassium titanate fibre 7-10 part, mica 1-4 part, copper powder 4-6 part, resin 1-4 part, cashew nut shell oil Frication powder 6-14 part.
The invention has the beneficial effects as follows: automobile disc brake pad of the present invention, have good resistance to high temperature, heat radiation is very fast simultaneously, and wear resistance is better, long service life.
Embodiment
embodiment 1
A kind of resistant to elevated temperatures automobile disc brake pad, it is made up of the raw material of following parts by weight:
Attapulgite 9 parts, rutile type titanium white 5 parts, cross-linked modifier 1 part, methyl phenyl siloxane branched chain type prepolymer 6 parts, 4 parts, barite, steel wool fiber 2 parts, 3 parts, Nitrile Rubber phenol, thermosetting resin 6 parts, carbon fiber 2 parts, 5 parts, barium sulphate, potassium titanate fibre 7 parts, 1 part, mica, copper powder 4 parts, resin 1 part, cashew nut shell oil Frication powder 6 parts.
embodiment 2
A kind of resistant to elevated temperatures automobile disc brake pad, it is made up of the raw material of following parts by weight:
Attapulgite 16 parts, rutile type titanium white 8 parts, cross-linked modifier 5 parts, methyl phenyl siloxane branched chain type prepolymer 11 parts, 8 parts, barite, steel wool fiber 6 parts, 9 parts, Nitrile Rubber phenol, thermosetting resin 10 parts, carbon fiber 6 parts, 10 parts, barium sulphate, potassium titanate fibre 10 parts, 4 parts, mica, copper powder 6 parts, resin 4 parts, cashew nut shell oil Frication powder 14 parts.
Claims (1)
1. a resistant to elevated temperatures automobile disc brake pad, is characterized in that: it is made up of the raw material of following parts by weight:
Attapulgite 9-16 part, rutile type titanium white 5-8 part, cross-linked modifier 1-5 part, methyl phenyl siloxane branched chain type prepolymer 6-11 part, barite 4-8 part, steel wool fiber 2-6 part, Nitrile Rubber phenol 3-9 part, thermosetting resin 6-10 part, carbon fiber 2-6 part, barium sulphate 5-10 part, potassium titanate fibre 7-10 part, mica 1-4 part, copper powder 4-6 part, resin 1-4 part, cashew nut shell oil Frication powder 6-14 part.