CN105038340A - Oil and corrosion resistance composite coating on ceiling surface - Google Patents
Oil and corrosion resistance composite coating on ceiling surface Download PDFInfo
- Publication number
- CN105038340A CN105038340A CN201510545702.2A CN201510545702A CN105038340A CN 105038340 A CN105038340 A CN 105038340A CN 201510545702 A CN201510545702 A CN 201510545702A CN 105038340 A CN105038340 A CN 105038340A
- Authority
- CN
- China
- Prior art keywords
- coating
- corrosion resistance
- parts
- oil
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an oil and corrosion resistance composite coating on a ceiling surface. The coating comprises, by weight, nanometer aluminium oxide, saligenin, pentadecanolide, titanium carbide, zirconium silicate, sodium silicate, glass fiber, 2,6-dimethyl-2,6-octadiene-8-alcohol, montmorillonoid, sorbic acid, an organo-siloxane coupling agent, a phosphate binder, polyoxyethylene lauryl ether, isolicoflavone and deionized water. The oil and corrosion resistance composite coating on the ceiling surface has the advantages that the obtained coating material has the good mechanical property and high strength, and also has the effects of abrasion resistance, high temperature resistance and corrosion resistance.
Description
Technical field
The invention belongs to paint field, relate to the corrosion-resistant compound coating of a kind of ceiling face oil resistant.
Background technology
In current building decoration field, ceiling has been the material of construction that a class extensively adopts.For different places, varying environment, different needs, there is the ceiling material of multiple unlike material, as plaster tablet suspended ceiling, aluminum-pinch, plastic plate etc.
Kitchen, due to its special Working environment, can produce a large amount of oil smoke, high-temperature volatile gas, acid and alkali substance, therefore propose special requirement to ceiling for kitchen use, as oil resistant ability, resistance to elevated temperatures, corrosion resistance nature.But existing top ceiling material does not generally have above-mentioned performance.
Summary of the invention
For deficiency of the prior art, the invention provides the corrosion-resistant compound coating of a kind of ceiling face oil resistant, described coating material comprises following component by weight:
Nano aluminium oxide 30-40 part,
Saligenin 50-60 part,
Thibetolide 10-15 part,
Titanium carbide 4-8 part,
Zirconium silicate 1-5 part,
Water glass 1-5 part,
Glass fibre 8-15 part,
2,6-dimethyl-2,6-octadiene-8-alcohol 4-12 part,
Polynite 1-10 part,
Sorbic Acid 3-10 part,
Organo-siloxane coupling agent 5-8 part,
Phosphoric acid salt binding agent 15-18 part,
Ethoxylated dodecyl alcohol 30-45 part,
Isoliquiritigenin 1-2 part,
Deionized water 5-15 part;
Wherein, described glass fibre adopts pH value to be the treatment solution process of 4-5 in advance, and prescription for the treatment of liquid is calculated as follows by mass percentage:
Silicon-dioxide 5-6%,
Ferrous sulfate 1.5-3%,
Glacial acetic acid 0.3-0.8%,
Water surplus.
Further, the particle diameter of described nano aluminium oxide is below 50nm.
The present invention by introducing 2,6-dimethyl-2,6-octadiene-8-alcohol, titanium carbide, zirconium silicate and aluminum oxide in coating, produces the wear resistance that synergy improves coating with coated coating; By introducing ethoxylated dodecyl alcohol, phosphoric acid salt binding agent and isoliquiritigenin in coating, produce the sticking power that synergy improves priming paint and base material; Non-corrosibility and the vapor-proof seepage force of coating is improved by introducing glass fibre in coating.By adding polynite, Sorbic Acid, thibetolide in coating, producing synergy and making coating volatilization when sintering film forming produced capillary effect of leaving away can strain the gap of molten particles.
The invention has the advantages that this preparation method is scientific and reasonable, simple, be convenient to implement, the coating obtained is attached at existing aluminum top ceiling substrate surface, not only increase the mechanical property of top ceiling, intensity, also significantly improves wear-resisting, the heat resistanceheat resistant of top ceiling, corrosion-resistant, oil-resistant characteristic, more meets the requirement of the complicated harsh environments such as kitchen, laboratory.
Embodiment
Below by embodiment, technical scheme of the present invention is described in further detail.
Embodiment one:
The corrosion-resistant compound coating of a kind of ceiling face oil resistant, described coating material comprises following component by weight:
Nano aluminium oxide 30 parts,
Saligenin 50 parts,
Thibetolide 10 parts
Titanium carbide 4 parts,
Zirconium silicate 1 part,
Water glass 1 part,
8 parts, glass fibre,
2,6-dimethyl-2,6-octadiene-8-alcohol 4 parts,
Polynite 1 part,
Sorbic Acid 3 parts,
Organo-siloxane coupling agent 5 parts,
Phosphoric acid salt binding agent 15 parts,
Ethoxylated dodecyl alcohol 30 parts,
Isoliquiritigenin 1 part,
Deionized water 5 parts;
Wherein, described glass fibre adopts pH value to be the following treatment solution process of 4-5 in advance, and prescription for the treatment of liquid is calculated as follows by mass percentage:
Silicon-dioxide 5%,
Ferrous sulfate 1.5%,
Glacial acetic acid 0.3%,
Water surplus.
Embodiment two:
The corrosion-resistant compound coating of a kind of ceiling face oil resistant, described coating material comprises following component by weight:
Nano aluminium oxide 40 parts,
Saligenin 60 parts,
Thibetolide 15 parts
Titanium carbide 8 parts,
Zirconium silicate 5 parts,
Water glass 5 parts,
15 parts, glass fibre,
2,6-dimethyl-2,6-octadiene-8-alcohol 12 parts,
Polynite 10 parts,
Sorbic Acid 10 parts,
Organo-siloxane coupling agent 8 parts,
Phosphoric acid salt binding agent 18 parts,
Ethoxylated dodecyl alcohol 45 parts,
Isoliquiritigenin 2 parts,
Deionized water 15 parts;
Wherein, described glass fibre adopts pH value to be the following treatment solution process of 4-5 in advance, and prescription for the treatment of liquid is calculated as follows by mass percentage:
Silicon-dioxide 6%,
Ferrous sulfate 3%,
Glacial acetic acid 0.8%,
Water surplus.
The above-mentioned composite coating that the present invention prepares is coated in aluminum top ceiling matrix surface, and solidification obtains coating, and it still has higher wear-resistant, thermotolerance and corrosion resistance nature under the high temperature conditions.Experimental result shows, take aluminium sheet as metallic matrix, and the coating obtained tests its high temperature resistant test under the furnace temperature of 200 DEG C, and its resistance toheat is more than 5 times of ordinary aluminum plate, and the corrosion resistance nature under high temperature is more than 15 times of ordinary aluminum plate.
The above; be only the specific embodiment of the present invention; but protection scope of the present invention is not limited thereto; any those of ordinary skill in the art are in the technical scope disclosed by the present invention; the change can expected without creative work or replacement, all should be encompassed within protection scope of the present invention.Therefore, the protection domain that protection scope of the present invention should limit with claims is as the criterion.
Claims (2)
1. the corrosion-resistant compound coating of ceiling face oil resistant, is characterized in that: described coating material comprises following component by weight:
Nano aluminium oxide 30-40 part,
Saligenin 50-60 part,
Thibetolide 10-15 part
Titanium carbide 4-8 part,
Zirconium silicate 1-5 part,
Water glass 1-5 part,
Glass fibre 8-15 part,
2,6-dimethyl-2,6-octadiene-8-alcohol 4-12 part,
Polynite 1-10 part,
Sorbic Acid 3-10 part,
Organo-siloxane coupling agent 5-8 part,
Phosphoric acid salt binding agent 15-18 part,
Ethoxylated dodecyl alcohol 30-45 part,
Isoliquiritigenin 1-2 part,
Deionized water is about 5-15 part;
Wherein, described glass fibre adopts pH value to be the treatment solution process of 4-5 in advance, and prescription for the treatment of liquid is calculated as follows by mass percentage:
Silicon-dioxide 5-6%,
Ferrous sulfate 1.5-3%,
Glacial acetic acid 0.3-0.8%,
Water surplus.
2. the corrosion-resistant compound coating of ceiling face oil resistant according to claim 1, is characterized in that: the particle diameter of described nano aluminium oxide is below 50nm.