CN105036652A - 新型沙漠砂混凝土 - Google Patents

新型沙漠砂混凝土 Download PDF

Info

Publication number
CN105036652A
CN105036652A CN201510446050.7A CN201510446050A CN105036652A CN 105036652 A CN105036652 A CN 105036652A CN 201510446050 A CN201510446050 A CN 201510446050A CN 105036652 A CN105036652 A CN 105036652A
Authority
CN
China
Prior art keywords
sand
desert sand
cement
water
novel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510446050.7A
Other languages
English (en)
Inventor
李志强
何明胜
金瑾
唐艳娟
曾晓云
陈俊杰
朱后刚
王高鹏
罗梦生
侯玮瑶
翟伟
郭龙龙
曹冲
林增锦
杨华
靳阿强
彭安程
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shihezi University
Original Assignee
Shihezi University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shihezi University filed Critical Shihezi University
Priority to CN201510446050.7A priority Critical patent/CN105036652A/zh
Publication of CN105036652A publication Critical patent/CN105036652A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种新型沙漠砂混凝土，由以下配合比的原料制备而成：水胶比为0.4，灰砂比为1/2.5-1/1.5，沙漠砂替代率为30％-40％，减水剂为1.0％-1.5％。本发明在混凝土的原材料中，将部分沙漠砂代替建筑用砂，可减少建筑能耗，并遵循因地制宜、就地取材和合理开发利用自然资源的原则，不仅有效地缓解建筑用砂的供需矛盾，而且充分利用了新疆沙漠砂的丰富资源。

Description

新型沙漠砂混凝土
技术领域
本发明涉及混凝土制备领域，具体涉及一种新型沙漠砂混凝土。
背景技术
随着社会的飞速发展，以及城镇化建设的快速推进，建筑能耗在社会总能耗中所占比例越来越大。由于混凝土价格低廉、制备简单等不可取代的优点，仍是当今世界上用量最大的人造材料。随着工程量急剧增加，以及国家对砂石采集的相关管理规定，使得建筑用砂供需矛盾日益突出。
发明内容
为解决上述问题，本发明提供了一种新型沙漠砂混凝土，在混凝土的原材料中，将部分沙漠砂代替建筑用砂，可减少建筑能耗，并遵循因地制宜、就地取材和合理开发利用自然资源的原则，不仅有效地缓解建筑用砂的供需矛盾，而且充分利用了新疆沙漠砂的丰富资源。
为实现上述目的，本发明采取的技术方案为：
新型沙漠砂混凝土，由以下配合比的原料制备而成：水胶比为0.4，灰砂比为1/2.5-1/1.5，沙漠砂替代率为30％-40％，减水剂为1.0％-1.5％。
其中，所述水泥采用硅酸盐水泥。
其中，所述砂采用新疆玛纳斯河水洗河砂，中砂，细度模数MX＝2.93，堆积密度为1560kg/m3。
其中，所述石子采用卵石，最大粒径Dmax＝25mm，体积密度为2650kg/m3。
其中，所述沙漠砂采用古尔班通古特沙漠砂，为新疆准格尔盆地150团场表面浮砂，平均粒径为0.183mm，MX＝0.334。
其中，所述减水剂采用HSC聚羧酸高性能减水剂，减水率20％。
其中，水胶比为0.4，灰砂比为1/2，沙漠砂替代率为40％，减水剂为0.5％。
本发明具有以下有益效果：
在混凝土的原材料中，将部分沙漠砂代替建筑用砂，可减少建筑能耗，并遵循因地制宜、就地取材和合理开发利用自然资源的原则，不仅有效地缓解建筑用砂的供需矛盾，而且充分利用了新疆沙漠砂的丰富资源。
具体实施方式
为了使本发明的目的及优点更加清楚明白，以下结合实施例对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
以下实施例中水泥采用硅酸盐水泥；砂采用新疆玛纳斯河水洗河砂，中砂，细度模数MX＝2.93，堆积密度为1560kg/m3；石子采用卵石，最大粒径max＝25mm，体积密度为2650kg/m3；沙漠砂采用古尔班通古特沙漠砂，为新疆准格尔盆地150团场表面浮砂，平均粒径为0.183mm，MX＝0.334，其化学成分如表1所示。
表1古尔班通古特沙漠砂化学成分％
减水剂采用青岛虹厦外加剂厂生产的HSC聚羧酸高性能减水剂，减水率20％。拌合水、养护水均用自来水。
实施例
按表2所示的数据进行混凝土的制备，试块尺寸为150mm×150mm×150mm，试块制作1d后拆模，分别养护7d和28d后，依据GB/T50081-2002《普通混凝土力学性能试验方法标准》进行抗压强度试验
表2混凝土材料配合比
沙漠砂混凝土7d和28d的抗压强度试验结果见表3。
表3试验结果
由表3可知，沙漠砂混凝土28d抗压强度的平均值为49.76MPa，且其和易性良好，可广泛用于实际建筑工程之中。
经试验，当沙漠砂混凝土的配合比：水胶比为0.4，灰砂比为1/2，沙漠砂替代率为40％，减水剂为0.5％，此时的混凝土性能最佳，此时的混凝土性能最佳。(水胶比为水/水泥之比；灰砂比为水泥/(砂+沙漠砂)之比；沙漠砂替代率为沙漠砂/(砂+沙漠砂)；减水剂参量为减水剂/(水泥+水+砂+沙漠砂)之比)
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以作出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (7)

1.新型沙漠砂混凝土，其特征在于，由以下配合比的原料制备而成：水胶比为0.4，灰砂比为1/2.5-1/1.5，沙漠砂替代率为30％-40％，减水剂为1.0％-1.5％。
2.根据权利要求1所述的新型沙漠砂混凝土，其特征在于，所述水泥采用硅酸盐水泥。
3.根据权利要求1所述的新型沙漠砂混凝土，其特征在于，所述砂采用新疆玛纳斯河水洗河砂，中砂，细度模数MX＝2.93，堆积密度为1560kg/m3。
4.根据权利要求1所述的新型沙漠砂混凝土，其特征在于，所述石子采用卵石，最大粒径Dmax＝25mm，体积密度为2650kg/m3。
5.根据权利要求1所述的新型沙漠砂混凝土，其特征在于，所述沙漠砂采用古尔班通古特沙漠砂，为新疆准格尔盆地150团场表面浮砂，平均粒径为0.183mm，MX＝0.334。
6.根据权利要求1所述的新型沙漠砂混凝土，其特征在于，所述减水剂采用HSC聚羧酸高性能减水剂，减水率20％。
7.根据权利要求1所述的新型沙漠砂混凝土，其特征在于，水胶比为0.4，灰砂比为1/2，沙漠砂替代率为40％，减水剂为0.5％。
CN201510446050.7A 2015-07-24 2015-07-24 新型沙漠砂混凝土 Pending CN105036652A (zh)