CN105036590A - Modified polycarboxylate powder superplasticizer dedicated to flowable mortar - Google Patents
Modified polycarboxylate powder superplasticizer dedicated to flowable mortar Download PDFInfo
- Publication number
- CN105036590A CN105036590A CN201510425758.4A CN201510425758A CN105036590A CN 105036590 A CN105036590 A CN 105036590A CN 201510425758 A CN201510425758 A CN 201510425758A CN 105036590 A CN105036590 A CN 105036590A
- Authority
- CN
- China
- Prior art keywords
- superplasticizer
- polycarboxylic acid
- exclusively used
- polycarboxylate
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a modified polycarboxylate powder superplasticizer dedicated to flowable mortar. The superplasticizer comprises the following components by weight: 90.0-98.0% of a polycarboxylate original powder, 0.5-5.0% of superfine talc, 0.25-1.0% of an anti-adsorbent, 0.03-0.08% of high-viscosity biosynthesis collagen, 0.3-0.5% of fibril synthesized pulp, and 0.5-2.0% of retarder with high degree of polymerization. Through the above-described manner, the modified polycarboxylate powder superplasticizer dedicated to flowable mortar provided by the present invention with the help of physical complex and efficient, low-dosage additive improves the flowability of polycarboxylate superplasticizer, improves the spreading area of flowable mortar, extends the release time of the polycarboxylate force, maintains good degree of construction work, improves work efficiency, and improves the quality of construction.
Description
Technical field
The present invention relates to concrete field, particularly relate to a kind of modified polycarboxylic acid powder water reducer be exclusively used in mobility mortar.
Background technology
General polycarboxylate water-reducer is used in the mortar of mobility, and its time point played a role has difference because of the difference of material.In other words, the time that water reducer plays maximum utility is different, and what have can play a role completely at 15 seconds, and flowing property reaches best, and what have needs prolongation churning time to 1 minute, just can reach best flow effect.Although volume is identical, the field of application will be different.Particularly, along with social progress, the price of labour power is more and more higher, and simple dependence has manually removed a few thing, in efficiency with all can not well be ensured qualitatively.This just needs to use mechanized construction, and that just must supporting suitable material, and then requires that the additive of preparation performance excellence is to meet processing requirement.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of modified polycarboxylic acid powder water reducer be exclusively used in mobility mortar, pass through physical compounding, by effectively, the auxiliary agent that volume is low improves the flowing property of polycarboxylate water-reducer, improve the spreading area of flowing mortar, extend the time of releasing of polycarboxylate water-reducer reactive force, keep good construction working degree, improve working efficiency, perfect construction quality, pass through modified additive, poly carboxylic acid powder water reducer is made to increase water-keeping thickening effect, the tolerance of water reducer water can be improved, reduce bleeding, segregation, improve the self-healing performance of cement slurry.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of modified polycarboxylic acid powder water reducer be exclusively used in mobility mortar, it is characterized in that, comprise the component of following mass percent:
The former powder 90.0-98.0% of polycarboxylate water-reducer;
Superfine talcum powder 0.5-5.0%;
Anti-sorbent material 0.25-1.0%;
High viscosity biosynthesizing collagen 0.03-0.08%;
Protofibril synthetic paper-pulp 0.3-0.5%;
High-polymerization degree retardant 0.5-2.0%.
In a preferred embodiment of the present invention, the fineness of described superfine talcum powder is 600-1200 order.
In a preferred embodiment of the present invention, the component that described high viscosity biosynthesizing collagen comprises has: welan gum, high-viscosity cellulose ether and bone collagen.
In a preferred embodiment of the present invention, the low viscous fibrous material that described protofibril synthetic paper-pulp adopts high dispersive technology to obtain, its viscosity is between 5-300mPa.s.
In a preferred embodiment of the present invention, the component that described high-polymerization degree retardant comprises has: if organic synthesis has the polymkeric substance of water-reducing property, white sugar and Sunmorl N 60S
The invention has the beneficial effects as follows: the modified polycarboxylic acid powder water reducer be exclusively used in mobility mortar of the present invention, pass through physical compounding, by effectively, the auxiliary agent that volume is low improves the flowing property of polycarboxylate water-reducer, improve the spreading area of flowing mortar, extend the time of releasing of polycarboxylate water-reducer reactive force, keep good construction working degree, improve working efficiency, perfect construction quality, pass through modified additive, poly carboxylic acid powder water reducer is made to increase water-keeping thickening effect, the tolerance of water reducer water can be improved, reduce bleeding, segregation, improve the self-healing performance of cement slurry.
Embodiment
Be clearly and completely described to the technical scheme in the embodiment of the present invention below, obviously, described embodiment is only a part of embodiment of the present invention, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making other embodiments all obtained under creative work prerequisite, belong to the scope of protection of the invention.
The embodiment of the present invention comprises:
Be exclusively used in the modified polycarboxylic acid powder water reducer in mobility mortar, comprise the component of following mass percent:
The former powder 90.0-98.0% of polycarboxylate water-reducer;
Superfine talcum powder 0.5-5.0%;
Anti-sorbent material 0.25-1.0%;
High viscosity biosynthesizing collagen 0.03-0.08%;
Protofibril synthetic paper-pulp 0.3-0.5%;
High-polymerization degree retardant 0.5-2.0%.
In above-mentioned, the fineness of described superfine talcum powder is 600-1200 order.Superfine talcum powder is the ultra-fine natural talcum powder processed by high-purity talc ore deposit, strong acid, highly basic, in aqueous in alkalescence, pH value 8-9, oil absorbency and strong covering power, fusing point is high, specific heat is large, thermal conductivity and shrinking percentage low.
Further, the component that described high viscosity biosynthesizing collagen comprises has: welan gum, high-viscosity cellulose ether and bone collagen etc.; Described protofibril synthetic paper-pulp adopts a kind of low viscous fibrous material obtained by high dispersive technology abroad, and be similar to Mierocrystalline cellulose and be different from Mierocrystalline cellulose again, its viscosity is between 5-300mPa.s; The component that described high-polymerization degree retardant comprises has: if organic synthesis has polymkeric substance, the white sugar and Sunmorl N 60S etc. of water-reducing property.
In sum, the modified polycarboxylic acid powder water reducer be exclusively used in mobility mortar of the present invention, pass through physical compounding, by effectively, the auxiliary agent that volume is low improves the flowing property of polycarboxylate water-reducer, improve the spreading area of flowing mortar, extend the time of releasing of polycarboxylate water-reducer reactive force, keep good construction working degree, improve working efficiency, perfect construction quality, pass through modified additive, poly carboxylic acid powder water reducer is made to increase water-keeping thickening effect, the tolerance of water reducer water can be improved, reduce bleeding, segregation, improve the self-healing performance of cement slurry.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (5)
1. be exclusively used in the modified polycarboxylic acid powder water reducer in mobility mortar, it is characterized in that, comprise the component of following mass percent:
The former powder 90.0-98.0% of polycarboxylate water-reducer;
Superfine talcum powder 0.5-5.0%;
Anti-sorbent material 0.25-1.0%;
High viscosity biosynthesizing collagen 0.03-0.08%;
Protofibril synthetic paper-pulp 0.3-0.5%;
High-polymerization degree retardant 0.5-2.0%.
2. the modified polycarboxylic acid powder water reducer be exclusively used in mobility mortar according to claim 1, is characterized in that, the fineness of described superfine talcum powder is 600-1200 order.
3. the modified polycarboxylic acid powder water reducer be exclusively used in mobility mortar according to claim 1, is characterized in that, the component that described high viscosity biosynthesizing collagen comprises has: welan gum, high-viscosity cellulose ether and bone collagen.
4. the modified polycarboxylic acid powder water reducer be exclusively used in mobility mortar according to claim 1, is characterized in that, the low viscous fibrous material that described protofibril synthetic paper-pulp adopts high dispersive technology to obtain, and its viscosity is between 5-300mPa.s.
5. the modified polycarboxylic acid powder water reducer be exclusively used in mobility mortar according to claim 1, is characterized in that, the component that described high-polymerization degree retardant comprises has: if organic synthesis has the polymkeric substance of water-reducing property, white sugar and Sunmorl N 60S.