CN106747026A - A kind of strong concrete and preparation method thereof - Google Patents
A kind of strong concrete and preparation method thereof Download PDFInfo
- Publication number
- CN106747026A CN106747026A CN201710113565.4A CN201710113565A CN106747026A CN 106747026 A CN106747026 A CN 106747026A CN 201710113565 A CN201710113565 A CN 201710113565A CN 106747026 A CN106747026 A CN 106747026A
- Authority
- CN
- China
- Prior art keywords
- prepared
- stone
- cement
- sand
- concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of strong concrete and preparation method thereof, according to mass percent, it is prepared from the following components：Cement 4% 12%, flyash 1% 5%, miberal powder 1% 5%, sand 2% 8%, stone 35% 45%, haydite 15% 25%, carbon fiber 2% 8%, iron powder 4% 12%, water 4% 12%, preparation method is：Cement, flyash, miberal powder, sand, stone, haydite, iron powder are added in mixer, compound is prepared after stirring, to water is added in compound, strong concrete is prepared after stirring.The present invention has the advantages that the concrete strength for preparing is high, quality is good.
Description
Technical field
The present invention relates to road construction field, a kind of specifically strong concrete and preparation method thereof.
Background technology
With the continuous progressive and development in epoch, the quantity of building, mileage of highway etc. are continuously increased, and concrete is made
It is important construction material, has been widely used.
Concrete, referred to as " concrete ", refer to by Binder Materials by the general designation of the cementing integral engineered composite material that gathers materials,
The word of concrete one generally said refers to make Binder Materials with cement, and sand, masonry gather materials, coordinate by a certain percentage with water, agitated
Obtained by cement concrete, also referred to as normal concrete, it is widely used in road construction.
The intensity of concrete refers to the compression strength of concrete, and one of leading indicator of concrete quality is exactly pressure resistance
Degree, at present, the concrete of in the market is mainly common concrete, and the defect that there is low intensity, the quality of concrete is poor,
Needs are improved.
The content of the invention
Of poor quality, low intensity defect the invention aims to solve concrete of the prior art, there is provided one
Strong concrete and preparation method thereof is planted to solve the above problems.
To achieve these goals, technical scheme is as follows：The invention discloses a kind of strong concrete, press
According to mass percent, it is prepared from the following components：Cement 4%-12%, flyash 1%-5%, miberal powder 1%-5%, sand 2%-8%, stone
Sub- 35%-45%, haydite 15%-25%, carbon fiber 2%-8%, iron powder 4%-12%, water 4%-12%.
Preferably, the invention discloses a kind of strong concrete, according to mass percent, by following components preparation
Into：Cement 12%, flyash 1%, miberal powder 5%, sand 8%, stone 35%, haydite 25%, carbon fiber 2%, iron powder 4%, water 8%.
Preferably, the invention discloses a kind of strong concrete, according to mass percent, by following components preparation
Into：Cement 10%, flyash 4%, miberal powder 1%, sand 2%, stone 45%, haydite 15%, carbon fiber 2%, iron powder 12%, water 9%.
Preferably, the invention discloses a kind of strong concrete, according to mass percent, by following components preparation
Into：Cement 8%, flyash 3%, miberal powder 3%, sand 5%, stone 40%, haydite 20%, carbon fiber 5%, iron powder 8%, water 8%.
Preferably, the particle diameter of described stone is 5-31.5mm.
The present invention also provides a kind of preparation method of above-mentioned strong concrete, comprises the following steps：
According to above-mentioned mass percent, cement, flyash, miberal powder, sand, stone, haydite, iron powder are added in mixer,
Compound is prepared after stirring, to water is added in compound, strong concrete is prepared after stirring.
The present invention has advantages below compared to existing technology：The present invention is by cement, flyash, miberal powder, sand, stone
And on the basis of water these raw materials, haydite, carbon fiber, iron powder are with the addition of, the intensity of concrete is effectively raised, preparation
The quality of concrete is significantly improved.
Specific embodiment
Embodiments of the invention are elaborated below, the present embodiment is carried out under premised on technical solution of the present invention
Implement, give detailed implementation method and specific operating process, but protection scope of the present invention is not limited to following implementations
Example.
Embodiment 1
The invention discloses a kind of strong concrete, according to mass percent, it is prepared from the following components：Cement 12%, powder
Coal ash 1%, miberal powder 5%, sand 8%, stone 35%, haydite 25%, carbon fiber 2%, iron powder 4%, water 8%.
The particle diameter of described stone is 30.5mm.
The present invention also provides a kind of preparation method of above-mentioned strong concrete, comprises the following steps：
According to above-mentioned mass percent, cement, flyash, miberal powder, sand, stone, haydite, iron powder are added in mixer,
Compound is prepared after stirring, to water is added in compound, strong concrete is prepared after stirring.
Embodiment 2
The invention discloses a kind of strong concrete, according to mass percent, it is prepared from the following components：Cement 10%, powder
Coal ash 4%, miberal powder 1%, sand 2%, stone 45%, haydite 15%, carbon fiber 2%, iron powder 12%, water 9%.
The particle diameter of described stone is 28.5mm.
The present invention also provides a kind of preparation method of above-mentioned strong concrete, comprises the following steps：
According to above-mentioned mass percent, cement, flyash, miberal powder, sand, stone, haydite, iron powder are added in mixer,
Compound is prepared after stirring, to water is added in compound, strong concrete is prepared after stirring.
Embodiment 3
The invention discloses a kind of strong concrete, according to mass percent, it is prepared from the following components：Cement 8%, powder
Coal ash 3%, miberal powder 3%, sand 5%, stone 40%, haydite 20%, carbon fiber 5%, iron powder 8%, water 8%.
The particle diameter of described stone is 24.5mm.
The present invention also provides a kind of preparation method of above-mentioned strong concrete, comprises the following steps：
According to above-mentioned mass percent, cement, flyash, miberal powder, sand, stone, haydite, iron powder are added in mixer,
Compound is prepared after stirring, to water is added in compound, strong concrete is prepared after stirring.
Table 1 is the performance indications of the strong concrete that embodiment 1-3 is prepared
As shown in Table 1, the strong concrete Performance comparision that the present invention is prepared is excellent.
General principle of the invention, principal character and advantages of the present invention has been shown and described above.The technology of the industry
Personnel it should be appreciated that the present invention is not limited to the above embodiments, the simply present invention described in above-described embodiment and specification
Principle, various changes and modifications of the present invention are possible without departing from the spirit and scope of the present invention, these change and
Improvement is both fallen within the range of claimed invention.The protection domain of application claims by appending claims and its
Equivalent is defined.
Claims (6)
1. a kind of strong concrete, it is characterised in that：According to mass percent, it is prepared from the following components：Cement 4%-
12%th, flyash 1%-5%, miberal powder 1%-5%, sand 2%-8%, stone 35%-45%, haydite 15%-25%, carbon fiber 2%-8%, iron powder
4%-12%, water 4%-12%.
2. a kind of strong concrete according to claim 1, it is characterised in that：According to mass percent, by with the following group
Divide and be prepared from：Cement 12%, flyash 1%, miberal powder 5%, sand 8%, stone 35%, haydite 25%, carbon fiber 2%, iron powder 4%, water
8%。
3. a kind of strong concrete according to claim 1, it is characterised in that：According to mass percent, by with the following group
Divide and be prepared from：Cement 10%, flyash 4%, miberal powder 1%, sand 2%, stone 45%, haydite 15%, carbon fiber 2%, iron powder 12%, water
9%。
4. a kind of strong concrete according to claim 1, it is characterised in that：According to mass percent, by with the following group
Divide and be prepared from：Cement 8%, flyash 3%, miberal powder 3%, sand 5%, stone 40%, haydite 20%, carbon fiber 5%, iron powder 8%, water
8%。
5. according to a kind of any described strong concretes of claim 1-4, it is characterised in that：The particle diameter of described stone is
5-31.5mm。
6. according to a kind of preparation method of any described strong concretes of claim 1-4, it is characterised in that：Including following
Step：
According to above-mentioned mass percent, cement, flyash, miberal powder, sand, stone, haydite, iron powder are added in mixer,
Compound is prepared after stirring, to water is added in compound, strong concrete is prepared after stirring.