CN105017735A - 一种乒乓球用纳米改性高分子材料及其制造方法 - Google Patents
一种乒乓球用纳米改性高分子材料及其制造方法 Download PDFInfo
- Publication number
- CN105017735A CN105017735A CN201510414469.4A CN201510414469A CN105017735A CN 105017735 A CN105017735 A CN 105017735A CN 201510414469 A CN201510414469 A CN 201510414469A CN 105017735 A CN105017735 A CN 105017735A
- Authority
- CN
- China
- Prior art keywords
- nano
- table tennis
- modified polymer
- polymer material
- poly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种乒乓球用纳米改性高分子材料，按质量分数包括：50-75%的聚丁二酸丁二醇酯或聚乳酸；3%-7%的木质素纤维；1%-2%的植物纤维；15-18%的增塑剂；0.5-3%的二氧化钛和二氧化硅纳米材料，其制造步骤：第一步，原料混合，同时增加0.5%的聚氯乙烯和聚丙烯纳米微粉混合物，搅拌1-1.5h。第二步，挤压机挤压成片材；第三步，裁断机将片材裁切成小片，供乒乓球制造用。本发明提供的一种乒乓球用纳米改性高分子材料，相比赛璐璐材料，具有生产安全，可生物降解，环境污染少的优点，同时制成的乒乓球各项性能指标优良，部分性能超过赛璐璐。
Description
技术领域
本发明具体涉及体育用品技术领域，具体为一种乒乓球用纳米改性高分子材料及其制造方法。
背景技术
现有技术乒乓球多采用赛璐璐作为原材料制造，而赛璐璐制成的乒乓球虽然性能优良，但是赛璐璐易燃易爆，运输生产困难，安全系数低，同时其制造成本较高，工艺较复杂，对环境的危害较大。市场上也出现一批代替赛璐璐的新材料，但是这些新材料，普遍在性能上达不到赛璐璐的性能水平，同时制造成本居高不下，因此如何开发一种运输生产安全，对环境危害小，性能与赛璐璐相当或者超过的材料，是所有乒乓球制造领域人员需要攻克的难关。
发明内容
针对上述问题，
本发明第一目的在于提供一种乒乓球用纳米改性高分子材料。
本发明第二目的在于提供上述乒乓球用纳米改性高分子材料的制备方法。
一种乒乓球用纳米改性高分子材料，所述材料主要成分按质量分数比包括：
50-75%的聚丁二酸丁二醇酯或聚乳酸；3%-7%的木质素纤维；1%-2%的植物纤维；15-18%的增塑剂；0.5-3%的二氧化钛和二氧化硅纳米材料。
作为优选，所述材料中还包括聚氯乙烯和聚丙烯纳米微粉。
作为优选，所述材料成分按质量百分比包括：聚氯乙烯：2%；聚丙烯纳米微粉：6%；聚丁二酸丁二醇酯或聚乳酸：65%；木质素纤维：5%；植物纤维：2%；增塑剂：17%；二氧化钛纳米材料：1%二氧化硅纳米材料：2%。
作为优选，所述增塑剂的成分包括：领苯甲酸丁二酯。
上述一种乒乓球用纳米改性高分子材料的制造方法，步骤如下：
第一步，原料混合，按权利要求1中主要成分比例，按质量分数混合，同时增加0.5%的聚氯乙烯和聚丙烯纳米微粉混合物，搅拌1-1.5h。
第二步，挤压机挤压成片材；所述挤压机的料筒温度范围为100~120度，塑化区温度为180-190度。
第三步，裁断机将片材裁切成小片，供乒乓球制造用。
本发明提供的一种乒乓球用纳米改性高分子材料，相比赛璐璐材料，具有生产安全，可生物降解，环境污染少的优点，同时制成的乒乓球各项性能指标优良，部分性能超过赛璐璐。
具体实施方式
下面通过具体实施例，对本发明的技术方案作进一步具体说明。
实施例1。
一种乒乓球用纳米改性高分子材料，所述材料主要成分按质量分数比包括：
50-75%的聚丁二酸丁二醇酯或聚乳酸；3%-7%的木质素纤维；1%-2%的植物纤维；15-18%的增塑剂；0.5-3%的二氧化钛和二氧化硅纳米材料。所述材料中还包括聚氯乙烯和聚丙烯纳米微粉，且其总的质量分数比例为0.5-8%。增塑剂的成分包括：领苯甲酸丁二酯。也可以使用其他常见增塑剂。
实施例2
所述材料成分按质量百分比包括：聚氯乙烯：2%；聚丙烯纳米微粉：6%；
聚丁二酸丁二醇酯或聚乳酸：65%；木质素纤维：5%；植物纤维：2%；增塑剂：17%；二氧化钛纳米材料：1%二氧化硅纳米材料：2%。
实施例3。
上述一种乒乓球用纳米改性高分子材料的制造方法，步骤如下：
第一步，原料混合，按权利要求1中主要成分比例，按质量分数混合，同时增加0.5%的聚氯乙烯和聚丙烯纳米微粉混合物，搅拌1-1.5h。
第二步，挤压机挤压成片材；所述挤压机的料筒温度范围为100~120度，塑化区温度为180-190度。
第三步，裁断机将片材裁切成小片，供乒乓球制造用。
本发明提供的一种乒乓球用纳米改性高分子材料，相比赛璐璐材料，具有生产安全，可生物降解，环境污染少的优点，同时制成的乒乓球各项性能指标优良，部分性能超过赛璐璐。
以上所述的实施例只是本发明的一种较佳的方案，并非对本发明作任何形式上的限制，在不超出权利要求所记载的技术方案的前提下还有其它的变体及改型。
Claims (5)
1.一种乒乓球用纳米改性高分子材料，其特征在于，所述材料主要成分按质量分数比包括：
50-75%的聚丁二酸丁二醇酯或聚乳酸；
3%-7%的木质素纤维；
1%-2%的植物纤维；
15-18%的增塑剂；
0.5-3%的二氧化钛和二氧化硅纳米材料。
2.如权利要求1 所述的一种乒乓球用纳米改性高分子材料，其特征在于，所述材料中还包括聚氯乙烯和聚丙烯纳米微粉。
3.如权利要求2所述的一种乒乓球用纳米改性高分子材料，其特征在于，所述材料成分按质量百分比包括：
聚氯乙烯：2%；
聚丙烯纳米微粉：6%；
聚丁二酸丁二醇酯或聚乳酸：65%；
木质素纤维：5%；
的植物纤维：2%；
增塑剂：17%；
二氧化钛纳米材料：1%
二氧化硅纳米材料：2%。
4.如权利要求1 所述的一种乒乓球用纳米改性高分子材料，其特征在于，
所述增塑剂的成分包括：领苯甲酸丁二酯。
5.如权利要求1-4任一项所述的一种乒乓球用纳米改性高分子材料的制造方法，其特征在于，步骤如下：
第一步，原料混合，按权利要求1中主要成分比例，按质量分数混合，同时增加0.5%的聚氯乙烯和聚丙烯纳米微粉混合物，搅拌1-1.5h；
第二步，挤压机挤压成片材；所述挤压机的料筒温度范围为100~120度，塑化区温度为180-190度；
第三步，裁断机裁切成小片，供乒乓球制造用。