CN103030986A - 一种阻燃木塑复合材料的生产方法 - Google Patents
一种阻燃木塑复合材料的生产方法 Download PDFInfo
- Publication number
- CN103030986A CN103030986A CN2012105721873A CN201210572187A CN103030986A CN 103030986 A CN103030986 A CN 103030986A CN 2012105721873 A CN2012105721873 A CN 2012105721873A CN 201210572187 A CN201210572187 A CN 201210572187A CN 103030986 A CN103030986 A CN 103030986A
- Authority
- CN
- China
- Prior art keywords
- weight
- flame
- production method
- parts
- plastic composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种阻燃木塑复合材料的生产方法，涉及一种复合材料的生产方法，包括以下步骤：将红磷和十溴二苯醚按照一定比例混合得到复配型阻燃剂，然后然后与聚乙烯树脂、木粉、接枝物及加工助剂按组分和重量份数聚乙烯树脂20-30份，木粉50-70份，复配型阻燃剂20-30份，相容剂PE-g-MAH1-3份，抗氧剂10100.5-1份，抗氧剂1680.5-1份，润滑剂2-5份，抗紫外线剂0.5-1份，经混料、挤出机挤出造粒、挤出成型步骤得到一种阻燃木塑复合材料。本发明方法生产的阻燃木塑复合材料产品具有优异的阻燃性能，能够达到UL94垂直燃烧测试的V-0级阻燃级别。本发明工艺路线简单、产品质量稳定，适于工业化生产。
Description
技术领域
本发明涉及一种木塑复合材料的生产方法，特别是涉及一种阻燃木塑复合材料的生产方法。
背景技术
随着全球经济的发展，人们对生存环境提出了更高的要求，废旧塑料垃圾由于各种塑料制品产量和用量的不断增加而遍布全球，但其对人类居住的地球环境造成了极大的污染，再加上我国森林资源严重不足，政府己明令禁止滥伐森林。如何既满足人民的生活需求，又要保护森林资源，维护国家的可持续性发展，已成为需要急切解决的难题。另外，大量人造板材所造成的室内甲醛污染也成了现在人们所担心的重要问题。因此，在自然资源日渐缺乏、环保要求日益高涨的今天，研发一种新型复合材料来满足人们的需求不仅具有经济效益，更有深远的社会效益。木塑复合材料作为一种新型绿色环保材料便应运而生。
木塑复合材料是一种新型的复合材料，以木纤维为增强材料,基体材料可以是热固性和热塑性塑料，如聚乙烯、聚丙烯、聚氯乙烯、ABS树脂和聚苯乙烯等，前三者应用最广泛。木塑复合材料综合了木材和塑料两者的优点，尺寸稳定性好，耐腐蚀，耐虫蛀，耐老化，并且回收再利用。木塑复合材料采用木材加工剩余物(木屑、刨花等)和废旧塑料为原料生产，综合性能突出而且经济效益显著。但由于天然纤维和各种聚合物都是易燃物质，木塑复合材料十分容易燃烧，着火后不能自熄，属于易燃类材料，这使得它在应用过程中受到了限制，因此赋予木塑复合材料良好的阻燃性能是该材料应用发展的需要。
发明内容
本发明的目的在于提供一种阻燃木塑复合材料的生产方法。本方法生产的阻燃木塑复合材料产品具有优异的阻燃性能，能够达到垂直燃烧测试的V-0级阻燃级别，产品质量稳定，适于工业化生产。
本发明的目的是通过以下技术方案实现的：
一种阻燃木塑复合材料的生产方法，所述方法包括以下过程：将红磷和十溴二苯醚混合为红磷和十溴二苯醚的混合物，其中红磷的重量份数为5-10，十溴二苯醚的重量份数为10-20，得到复配型阻燃剂，然后与聚乙烯树脂、木粉、接枝物及加工助剂按组分和重量份数聚乙烯树脂20-30份，木粉50-70份，复配型阻燃剂20-30份，相容剂PE-g-MAH（聚乙烯接马来酸酐）1-3份，抗氧剂1010（四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯）0.5-1份，抗氧剂168（三(2,4-二叔丁基苯基)亚磷酸酯）0.5-1份，润滑剂2-5份，抗紫外线剂0.5-1份，经混料、挤出机挤出造粒、挤出成型步骤得到一种阻燃木塑复合材料。
本发明的优点与效果是：
1.本发明方法生产的阻燃木塑复合材料产品具有优异的阻燃性能，能够达到垂直燃烧测试的V-0级阻燃级别。
2.本发明工艺路线简单、产品质量稳定，适于工业化生产。
具体实施方式
下面结合实施例对本发明进行详细说明。
实施例1：
称取20公斤高密度聚乙烯树脂、50公斤木粉、5公斤加工助剂、8公斤红磷和17公斤十溴二苯醚，高混机中混料10min，经双螺杆挤出机在一定条件下挤出造粒，锥形双螺杆挤出机挤出成型，将产品取样制成标准样条进行垂直燃烧测试，样条离火自熄，全部能够达到UL94 V-0阻燃级别。
实施例2：
称取25公斤高密度聚乙烯树脂、55公斤木粉、6公斤加工助剂、10公斤红磷和20公斤十溴二苯醚，高混机中混料10min，经双螺杆挤出机在一定条件下挤出造粒，锥形双螺杆挤出机挤出成型，将产品取样制成标准样条进行垂直燃烧测试，样条离火自熄，全部能够达到UL94 V-0阻燃级别。
Claims (1)
1.一种阻燃木塑复合材料的生产方法，其特征在于，所述方法包括以下过程：将红磷和十溴二苯醚混合为红磷和十溴二苯醚的混合物，其中红磷的重量份数为5-10，十溴二苯醚的重量份数为10-20，得到复配型阻燃剂，然后与聚乙烯树脂、木粉、接枝物及加工助剂按组分和重量份数聚乙烯树脂20-30份，木粉50-70份，复配型阻燃剂20-30份，相容剂PE-g-MAH（聚乙烯接马来酸酐）1-3份，抗氧剂1010（四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯）0.5-1份，抗氧剂168（三(2,4-二叔丁基苯基)亚磷酸酯）0.5-1份，润滑剂2-5份，抗紫外线剂0.5-1份，经混料、挤出机挤出造粒、挤出成型步骤得到一种阻燃木塑复合材料。