CN105001560A - PVC hard non-toxic uvioresistant sheet - Google Patents
PVC hard non-toxic uvioresistant sheet Download PDFInfo
- Publication number
- CN105001560A CN105001560A CN201510539960.XA CN201510539960A CN105001560A CN 105001560 A CN105001560 A CN 105001560A CN 201510539960 A CN201510539960 A CN 201510539960A CN 105001560 A CN105001560 A CN 105001560A
- Authority
- CN
- China
- Prior art keywords
- uvioresistant
- percent
- nontoxic
- sheet material
- pvc hard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a sheet, in particular to a PVC hard non-toxic uvioresistant sheet, comprising the following materials by percentage: 55 to 65 percent of PVC resin powder, 13 to 20 percent of EVA ethylene-ethenyl ethanoate copolymer, 2 to 8 percent of LLDPE linear low-density polyethylene, 2 to 8 percent of PETG, 2 to 7 percent of MPE, 0.5 to 5 percent of methyl tin mercaptide, 0.5 to 5 percent of an enhancer, 0.5 to 5 percent of a stabilizer, 0.5 to 4 percent of a processing agent, 0.5 to 4 percent of calcium stearate, 0.1 to 3 percent of an internal lubricant, 0.1 to 3 percent of an external lubricant, and 0.1 to 3 percent of a colorant. The PVC hard non-toxic uvioresistant sheet being impact resistant, anti-aging, cold-resistant and alete is obtained, and achieves perfect effects in stretch resistance and cold resistance.
Description
Technical field
The present invention relates to a kind of sheet material, be specifically related to the nontoxic uvioresistant sheet material of a kind of PVC hard.
Background technology
Publication No. is the Chinese invention patent of CN 103131099 A, it discloses a kind of anti-ultraviolet PVC sheet, toxic substance can be prevented after being subject to uviolizing, but degree of aging is very fast in this sheet material use procedure, tensile strength is general, especially cold-resistant degree is poor, when sheet material lower ground just uses in temperature, easily occurs slight crack.Contriver improves on the basis of original formula, to overcome described defect.
Summary of the invention
The object of the present invention is to provide a kind of shock resistance, anti-aging, cold-resistant, the seamless nontoxic uvioresistant sheet material of PVC hard.
For achieving the above object, the present invention adopts following technical scheme:
The nontoxic uvioresistant sheet material of a kind of PVC hard, is made up of following material per-cent: PVC resin-oatmeal 55-65%; EVA ethene-vinyl acetate copolymer 13-20%; LLDPE linear low density polyethylene 2-8%; PETG2-8%; MPE2-7%; Thiol methyl tin 0.5-5%; Toughener 0.5-5%; Stablizer 0.5-5%; Processing aid 0.5-4%; Calcium stearate 0.5-4%; Internal lubricant 0.1-3%; External lubricant 0.1-3%; Tinting material 0.1-3%.
As preferred technical scheme: PVC resin-oatmeal 60%; EVA ethene-vinyl acetate copolymer 16%; LLDPE linear low density polyethylene 4%; PETG4%; MPE3.5%; Thiol methyl tin 2.5%; Toughener 2.5%; Stablizer 2.5%; Processing aid 1.5%; Calcium stearate 1.5%; Internal lubricant 0.5%; External lubricant 0.5%; Tinting material 1%.
The invention has the advantages that: EVA ethene-vinyl acetate copolymer improves the snappiness of product, shock resistance; LLDPE linear low density polyethylene adds the sticking power of later stage ink and colloid, the problem avoided deinking and come unstuck; The use of MPE can improve the tensile strength of sheet material.Comprehensive obtain a kind of shock resistance, anti-aging, resist cold, the seamless nontoxic uvioresistant sheet material of PVC hard, especially stretch-proof and cold-resistant in, achieve excellent effect especially.
embodiment:
adopt preparation method as follows in embodiment,
1) calendering stage;
Mainly comprise: batching, heat agitated, cold stirring, extrude, press saliva, stripping, press polish, cooling, traction;
2) the corona stage: the stage of removing electrostatic;
3) the ballingup stage.
Implement one:
PVC resin-oatmeal 63%; EVA ethene-vinyl acetate copolymer 18%; LLDPE linear low density polyethylene 3%; PETG3%; MPE4%; Thiol methyl tin 1.5%; Toughener 1.5%; Stablizer 1.5%; Processing aid 0.9%; Calcium stearate 0.6%; Internal lubricant 1%; External lubricant 1%; Tinting material 1%.
Implement two:
PVC resin-oatmeal 55%; EVA ethene-vinyl acetate copolymer 14%; LLDPE linear low density polyethylene 6%; PETG4%; MPE3%; Thiol methyl tin 3%; Toughener 4%; Stablizer 4%; Processing aid 2%; Calcium stearate 2%; Internal lubricant 1%; External lubricant 1%; Tinting material 1%.
Implement three:
PVC resin-oatmeal 60%; EVA ethene-vinyl acetate copolymer 16%; LLDPE linear low density polyethylene 4%; PETG4%; MPE3.5%; Thiol methyl tin 2.5%; Toughener 2.5%; Stablizer 2.5%; Processing aid 1.5%; Calcium stearate 1.5%; Internal lubricant 0.5%; External lubricant 0.5%; Tinting material 1%.
Following table is patent test data contrast situation involved by the embodiment of the present invention and background technology:
Claims (10)
1. the nontoxic uvioresistant sheet material of PVC hard, is characterized in that, is made up of following material per-cent: PVC resin-oatmeal 55-65%; EVA ethene-vinyl acetate copolymer 13-20%; LLDPE linear low density polyethylene 2-8%; PETG2-8%; MPE2-7%; Thiol methyl tin 0.5-5%; Toughener 0.5-5%; Stablizer 0.5-5%; Processing aid 0.5-4%; Calcium stearate 0.5-4%; Internal lubricant 0.1-3%; External lubricant 0.1-3%; Tinting material 0.1-3%.
2. the nontoxic uvioresistant sheet material of a kind of PVC hard according to claim 1, is characterized in that: PVC resin-oatmeal 60%; EVA ethene-vinyl acetate copolymer 16%; LLDPE linear low density polyethylene 4%; PETG4%; MPE3.5%; Thiol methyl tin 2.5%; Toughener 2.5%; Stablizer 2.5%; Processing aid 1.5%; Calcium stearate 1.5%; Internal lubricant 0.5%; External lubricant 0.5%; Tinting material 1%.
3. the nontoxic uvioresistant sheet material of a kind of PVC hard according to claim 1 and 2, is characterized in that: described processing aid is ACR processing aid.
4. the nontoxic uvioresistant sheet material of a kind of PVC hard according to claim 1 and 2, is characterized in that: described internal lubricant is GLR internal lubricant.
5. the nontoxic uvioresistant sheet material of a kind of PVC hard according to claim 1 and 2, is characterized in that: described external lubricant is EBS external lubricant.
6. the nontoxic uvioresistant sheet material of a kind of PVC hard according to claim 1 and 2, is characterized in that: described tinting material is ultramarine 0.1-1%; Disperse mauve 0.1-1%; Transparent agent 0.1-1%; Titanium dioxide 0.1-1%.
7. the nontoxic uvioresistant sheet material of a kind of PVC hard according to claim 6, is characterized in that: described ultramarine 0.25%; Disperse mauve 0.25%; Transparent agent 0.25%; Titanium dioxide 0.25%.
8. the nontoxic uvioresistant sheet material of a kind of PVC hard according to claim 1 and 2, is characterized in that: described toughener is BTA717 toughener or MBS impact modifier.
9. the nontoxic uvioresistant sheet material of a kind of PVC hard according to claim 1 and 2, is characterized in that: the one that described stablizer is 316A stablizer, liquid barium zinc compound stabilizer, liquid calcium zinc complex stabilizer, liquid barium cadmium and liquid barium cadmium zinc compound appraise and decide agent.
10. the nontoxic uvioresistant sheet material of a kind of PVC hard according to claim 1 and 2, is characterized in that: preparation method is as follows,
1) calendering stage;
Mainly comprise: batching, heat agitated, cold stirring, extrude, press saliva, stripping, press polish, cooling, traction;
2) the corona stage: the stage of removing electrostatic;
3) the ballingup stage.