CN104988479A - 一种乳化柔韧金属表面处理剂及其制备方法 - Google Patents
一种乳化柔韧金属表面处理剂及其制备方法 Download PDFInfo
- Publication number
- CN104988479A CN104988479A CN201510411505.1A CN201510411505A CN104988479A CN 104988479 A CN104988479 A CN 104988479A CN 201510411505 A CN201510411505 A CN 201510411505A CN 104988479 A CN104988479 A CN 104988479A
- Authority
- CN
- China
- Prior art keywords
- add
- aniline
- surface treatment
- treatment agent
- metal surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种乳化柔韧金属表面处理剂,本发明的丙烯酸酯胶液粒子表面含有大量的羧基,将苯胺加入到丙烯酸酯胶液中,苯胺单体首先扩散到胶束内部,然后与羧基发生掺杂,随后在氧化剂的作用下,苯胺在乳胶粒子表面发生聚合反应,增大了聚苯胺涂层对水的接触角,提高了附着力和耐水性,该涂层可以通过电子转移作用和氧化还原作用,使金属表面钝化产生保护作用,而经硅烷化改性的氟钛酸,引入的无机组分Ti4+在加热固化过程中形成TiO2颗粒,均匀地填充在硅烷膜的空隙中,使整个膜层更加均匀致密,能有效抑制膜层表面的微电化学反应,从而耐腐蚀性能得到很大提高。
Description
技术领域
本发明涉及一种处理剂,尤其涉及一种乳化柔韧金属表面处理剂及其制备方法。
背景技术
聚苯胺是一类导电高分子材料,性能稳定,环境友好,且氧化还原电位远高于金属,其涂层在酸性或中性介质中可以通过电子转移作用和氧化还原作用,使金属表面钝化产生保护作用,是金属防腐蚀的良好材料,但是,聚苯胺分子链刚性强,不溶不熔,难以加工,通常要与其他成膜物质复合使用。丙烯酸酯树脂是常用的成膜物质,具有良好的成膜性和附着力。
目前,聚苯胺与丙烯酸酯树脂复合制膜的方式有3 种:聚苯胺涂层上涂覆丙烯酸酯面漆形成复合涂层,2种涂层各自发挥作用; 聚苯胺粉末作为填料直接分散在丙烯酸树脂中制备涂层;两者共溶于同一溶剂中再在金属上涂刷成膜。采用乳液互穿网络聚合法制备聚苯胺-丙烯酸树脂防腐蚀涂料,其涂层具有良好的防腐蚀性能。利用丙烯酸酯聚合物链上的羧基对苯胺的掺杂作用,采用原位聚合法合成了丙烯酸酯-苯胺共聚物; 但研究主要针对苯胺含量对共聚物介电性能的影响,没有讨论共聚物的防腐蚀性能。目前,关于丙烯酸酯与苯胺共聚制备防腐蚀材料的报道还很少。
发明内容
本发明提供了一种乳化柔韧金属表面处理剂及其制备方法。
本发明是通过以下技术方案实现的:
一种乳化柔韧金属表面处理剂,它是由下述重量份的原料组成的:
柠檬酸三丁酯0.7-2、sp-80 1.8-2、苯胺0.5-0.6、过硫酸钾0.38-0.4、丙烯酸丁酯40-50、碳酸氢钠0.16-0.2、双( γ-三乙氧基硅基丙基) 四硫化物20-30、70-75%的乙醇100-110、30%过氧化氢0.2-0.3、去离子水110-120、氟钛酸4-6、二羟基聚二甲基硅氧烷0.5-1、α-松油醇1-2、防锈剂t705 2-3、二水合磷酸氢钙1-2、辛苯昔醇1-2。
2、一种如权利要求1所述的乳化柔韧金属表面处理剂的制备方法,其特征在于包括以下步骤:
(1)取上述过硫酸钾重量的40-50%、sp-80重量的80-90%,与碳酸氢钠混合,加入去离子水重量的70-75%,搅拌均匀,得引发剂乳液;
(2)取剩余去离子水重量的30-36%,加入辛苯昔醇,搅拌均匀后加入柠檬酸三丁酯、防锈剂t705,在50-60℃下保温搅拌8-10分钟,得防锈酯;
(3)取上述引发剂乳液重量的45-50%,升高温度为80-86℃,滴加剩余的引发剂乳液与丙烯酸丁酯的混合液,滴加完毕后加入上述防锈酯,60-100转/分搅拌10-20分钟,保温反应1-2小时,得丙烯酸酯胶液;
(4)取剩余去离子水重量的50-60%,加入二水合磷酸氢钙,搅拌均匀后加入α-松油醇、剩余的sp-80,搅拌均匀,得乳化钙;
(5)将剩余的过硫酸钾加入到剩余的去离子水中,搅拌均匀,得引发剂溶液;
(6)取上述70-75%的乙醇,加入双( γ-三乙氧基硅基丙基) 四硫化物、二羟基聚二甲基硅氧烷,调节PH为3-4,加入氟钛酸、30%过氧化氢,搅拌反应6-7小时,得氟化硅烷;
(7)将苯胺、乳化钙、丙烯酸酯胶液混合,搅拌均匀,滴加引发剂溶液,滴加完毕后在10-15℃下反应8-10小时,送入65-70℃的水浴中,加入氟化硅烷,保温搅拌反应1-2小时,得硅烷化丙烯酸-苯胺共聚乳液;
(8)将上述硅烷化丙烯酸-苯胺共聚乳液与剩余各原料混合,800-1000转/分搅拌40-50分钟,得所述乳化柔韧金属表面处理剂。
本发明的优点是:
本发明的丙烯酸酯胶液粒子表面含有大量的羧基,将苯胺加入到丙烯酸酯胶液中,苯胺单体首先扩散到胶束内部,然后与羧基发生掺杂,随后在氧化剂的作用下,苯胺在乳胶粒子表面发生聚合反应,增大了聚苯胺涂层对水的接触角,提高了附着力和耐水性,该涂层可以通过电子转移作用和氧化还原作用,使金属表面钝化产生保护作用,加入的丙二醇苯醚可以增强涂层的稳定性和成膜性,有效的抑制了腐蚀介质浸入后腐蚀的过程;
而经硅烷化改性的氟钛酸,引入的无机组分Ti4 + 在加热固化过程中形成TiO2颗粒,均匀地填充在硅烷膜的空隙中,使整个膜层更加均匀致密,能有效抑制膜层表面的微电化学反应,从而耐腐蚀性能得到很大提高;
本发明的表面剂经过涂覆后,可以形成柔韧的涂膜,稳定性强,抗擦拭性好。
具体实施方式
下面结合实施例对本发明作进一步详细描述:
实施例1:
一种乳化柔韧金属表面处理剂,其特征在于它是由下述重量份的原料组成的:
柠檬酸三丁酯0.7、sp-80 1.8、苯胺0.6、过硫酸钾0.38、丙烯酸丁酯40、碳酸氢钠0.16、双( γ-三乙氧基硅基丙基) 四硫化物30、75%的乙醇110、30%过氧化氢0.3、去离子水120、氟钛酸4-6、二羟基聚二甲基硅氧烷0.5、α-松油醇2、防锈剂t705 2、二水合磷酸氢钙1、辛苯昔醇2。
一种乳化柔韧金属表面处理剂的制备方法,包括以下步骤:
(1)取上述过硫酸钾重量的50%、sp-80重量的90%,与碳酸氢钠混合,加入去离子水重量的75%,搅拌均匀,得引发剂乳液;
(2)取剩余去离子水重量的36%,加入辛苯昔醇,搅拌均匀后加入柠檬酸三丁酯、防锈剂t705,在60℃下保温搅拌10分钟,得防锈酯;
(3)取上述引发剂乳液重量的50%,升高温度为86℃,滴加剩余的引发剂乳液与丙烯酸丁酯的混合液,滴加完毕后加入上述防锈酯,100转/分搅拌20分钟,保温反应1小时,得丙烯酸酯胶液;
(4)取剩余去离子水重量的60%,加入二水合磷酸氢钙,搅拌均匀后加入α-松油醇、剩余的sp-80,搅拌均匀,得乳化钙;
(5)将剩余的过硫酸钾加入到剩余的去离子水中,搅拌均匀,得引发剂溶液;
(6)取上述75%的乙醇,加入双( γ-三乙氧基硅基丙基) 四硫化物、二羟基聚二甲基硅氧烷,调节PH为4,加入氟钛酸、30%过氧化氢,搅拌反应7小时,得氟化硅烷;
(7)将苯胺、乳化钙、丙烯酸酯胶液混合,搅拌均匀,滴加引发剂溶液,滴加完毕后在15℃下反应10小时,送入70℃的水浴中,加入氟化硅烷,保温搅拌反应1小时,得硅烷化丙烯酸-苯胺共聚乳液;
(8)将上述硅烷化丙烯酸-苯胺共聚乳液与剩余各原料混合,1000转/分搅拌40-50分钟,得所述乳化柔韧金属表面处理剂。
性能测试:
吸水率:按照上述方法将本发明的表面处理剂涂覆于尺寸为5cm×6cm的钢板表面,在25 ℃的去离子水中浸泡48 h,测得吸水率为16.2%;
附着力:1级;
耐腐蚀性:中性盐雾试验72小时,被腐蚀面积2.3 %;
硬度:3H。
Claims (2)
1.一种乳化柔韧金属表面处理剂,其特征在于它是由下述重量份的原料组成的:
柠檬酸三丁酯0.7-2、sp-80 1.8-2、苯胺0.5-0.6、过硫酸钾0.38-0.4、丙烯酸丁酯40-50、碳酸氢钠0.16-0.2、双( γ-三乙氧基硅基丙基) 四硫化物20-30、70-75%的乙醇100-110、30%过氧化氢0.2-0.3、去离子水110-120、氟钛酸4-6、二羟基聚二甲基硅氧烷0.5-1、α-松油醇1-2、防锈剂t705 2-3、二水合磷酸氢钙1-2、辛苯昔醇1-2。
2.一种如权利要求1所述的乳化柔韧金属表面处理剂的制备方法,其特征在于包括以下步骤:
(1)取上述过硫酸钾重量的40-50%、sp-80重量的80-90%,与碳酸氢钠混合,加入去离子水重量的70-75%,搅拌均匀,得引发剂乳液;
(2)取剩余去离子水重量的30-36%,加入辛苯昔醇,搅拌均匀后加入柠檬酸三丁酯、防锈剂t705,在50-60℃下保温搅拌8-10分钟,得防锈酯;
(3)取上述引发剂乳液重量的45-50%,升高温度为80-86℃,滴加剩余的引发剂乳液与丙烯酸丁酯的混合液,滴加完毕后加入上述防锈酯,60-100转/分搅拌10-20分钟,保温反应1-2小时,得丙烯酸酯胶液;
(4)取剩余去离子水重量的50-60%,加入二水合磷酸氢钙,搅拌均匀后加入α-松油醇、剩余的sp-80,搅拌均匀,得乳化钙;
(5)将剩余的过硫酸钾加入到剩余的去离子水中,搅拌均匀,得引发剂溶液;
(6)取上述70-75%的乙醇,加入双( γ-三乙氧基硅基丙基) 四硫化物、二羟基聚二甲基硅氧烷,调节PH为3-4,加入氟钛酸、30%过氧化氢,搅拌反应6-7小时,得氟化硅烷;
(7)将苯胺、乳化钙、丙烯酸酯胶液混合,搅拌均匀,滴加引发剂溶液,滴加完毕后在10-15℃下反应8-10小时,送入65-70℃的水浴中,加入氟化硅烷,保温搅拌反应1-2小时,得硅烷化丙烯酸-苯胺共聚乳液;
(8)将上述硅烷化丙烯酸-苯胺共聚乳液与剩余各原料混合,800-1000转/分搅拌40-50分钟,得所述乳化柔韧金属表面处理剂。