CN104975231A - 一种消失模4Cr9Si2材料 - Google Patents
一种消失模4Cr9Si2材料 Download PDFInfo
- Publication number
- CN104975231A CN104975231A CN201510370577.6A CN201510370577A CN104975231A CN 104975231 A CN104975231 A CN 104975231A CN 201510370577 A CN201510370577 A CN 201510370577A CN 104975231 A CN104975231 A CN 104975231A
- Authority
- CN
- China
- Prior art keywords
- 4cr9si2
- lost foam
- present
- evaporative pattern
- surplus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种消失模4Cr9Si2材料,按质量百分含量计,其化学成分如下:Ce 1.0~1.5%、C 0.35~0.45%、Si 2.0~3.0%、Mn 0.5~0.7%、Cr 8.0~10.0%、P<0.035%、S≤0.02%,余量为Fe。与现有4Cr9Si2材料相比,本发明消失模4Cr9Si2材料具有良好的强度。
Description
技术领域
本发明涉及一种消失模4Cr9Si2材料。
背景技术
4Cr9Si2主要用于制造锅炉、汽轮机、动力机械、工业炉和航空、石油化工等工业部门中在高温下工作的零部件。这些部件除要求高温强度和抗高温氧化腐蚀外,根据用途不同还要求有足够的韧性、良好的可加工性和焊接性,以及一定的组织稳定性。
发明内容
本发明的目的是对现有4Cr9Si2进行改进,提供了一种消失模4Cr9Si2材料。
为了解决上述技术问题,本发明提供了如下的技术方案:
一种消失模4Cr9Si2材料,按质量百分含量计,其化学成分如下:Ce 1.0~1.5%、C 0.35~0.45%、Si 2.0~3.0%、Mn 0.5~0.7%、Cr 8.0~10.0%、P<0.035%、S≤0.02%,余量为Fe。
具体实施方式
以下对本发明的优选实施例进行说明,应当理解,此处所描述的优选实施例仅用于说明和解释本发明,并不用于限定本发明。
实施例1
一种消失模4Cr9Si2材料,按质量百分含量计,其化学成分如下:Ce 1.0%、C 0.35%、Si 3.0%、Mn 0.5%、Cr 8.0%、P<0.035%、S≤0.02%,余量为Fe。
实施例2
一种消失模4Cr9Si2材料,按质量百分含量计,其化学成分如下:Ce 1.5%、C 0.45%、Si 2.0%、Mn 0.7%、Cr 10.0%、P<0.035%、S≤0.02%,余量为Fe。
实施例3
一种消失模4Cr9Si2材料,按质量百分含量计,其化学成分如下:Ce 1.2%、C 0.40%、Si 2.6%、Mn 0.6%、Cr 9.0%、P<0.035%、S≤0.02%,余量为Fe。
对比例1
4Cr9Si2材料,按质量百分含量计,其化学成分如下:C 0.35%、Si 2.0%、Mn 0.6%、Cr 9.0%、P<0.035%、S≤0.02%,余量为Fe。
。
最后应说明的是:以上所述仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (1)
1.一种消失模4Cr9Si2材料,按质量百分含量计,其化学成分如下:Ce 1.0~1.5%、C 0.35~0.45%、Si 2.0~3.0%、Mn 0.5~0.7%、Cr 8.0~10.0%、P<0.035%、S≤0.02%,余量为Fe。