CN104966546A - 一种晶体硅太阳能电池用背面银浆 - Google Patents

一种晶体硅太阳能电池用背面银浆 Download PDF

Info

Publication number
CN104966546A
CN104966546A CN201510397922.5A CN201510397922A CN104966546A CN 104966546 A CN104966546 A CN 104966546A CN 201510397922 A CN201510397922 A CN 201510397922A CN 104966546 A CN104966546 A CN 104966546A
Authority
CN
China
Prior art keywords
parts
silver
crystal silicon
weight
silicon solar
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510397922.5A
Other languages
English (en)
Other versions
CN104966546B (zh
Inventor
邱羽
刘金宁
陈斐
江琳沁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fuzhou Yangguang Fusi New Energy Technology Co Ltd
Original Assignee
Fuzhou Yangguang Fusi New Energy Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fuzhou Yangguang Fusi New Energy Technology Co Ltd filed Critical Fuzhou Yangguang Fusi New Energy Technology Co Ltd
Priority to CN201510397922.5A priority Critical patent/CN104966546B/zh
Publication of CN104966546A publication Critical patent/CN104966546A/zh
Application granted granted Critical
Publication of CN104966546B publication Critical patent/CN104966546B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种晶体硅太阳能电池用背面银浆，原料组分按重量份数计为：银粉50份、有机粘合剂43~47份、无铅玻璃粉1~5份和添加剂2份。无铅玻璃粉中氧化钙与氧化锌在高温中会形成少量结晶，从而对银浆中银颗粒形成一定的保护，提高抗老化效果，同时添加剂中的氧化锡在高温中会与银反应在膜层表面形成合金，从而降低焊带对背银在高温下的侵蚀，提高抗老化效果。

Description

一种晶体硅太阳能电池用背面银浆
技术领域
本发明属于太阳能电池技术领域，涉及一种晶体硅太阳能电池用电子浆料，具体涉及一种晶体硅太阳能电池用背面银浆。
背景技术
随着晶体硅太阳能电池片技术日趋成熟，对电池片的各个组成部分的技术要求在不停地提高。太阳能电池背面银浆是太阳能电池片的重要组成部分，必须要提供优良的附着力与可焊性，同时必须要满足老化要求，保证电池片组件的稳定可靠性。
太阳能电池背面银浆主要由银粉、无铅玻璃粉、添加剂、有机粘合剂组成。银粉作为浆料中的功能相，起到导电作用。而无铅玻璃粉与添加剂则起到提供附着力及老化等各项性能。
目前电池片的老化性能要求逐渐提高，太阳能电池背面银浆也必须做到抗老化性能，同时必须降低银含量，降低成本，现有的技术不能很好的满足这项技术要求。
发明内容
本发明的目的在于提供一种晶体硅太阳能电池用背面银浆，能显著提高其抗老化效果，并降低成本。
为实现上述目的，本发明采用如下技术方案：
一种晶体硅太阳能电池用背面银浆，原料组分按重量份数计为：银粉50份、有机粘合剂43~47份、无铅玻璃粉1~5份和添加剂2份。
所述的银粉纯度为99.9~99.99%、呈球状，平均粒径为1.5~3.0μm。
所述的有机粘合剂的原料组分按重量份数计为：松油醇40~65份、丁基卡必醇5~10份、丁基卡必醇醋酸酯15~20份、乙基纤维素3~10份、邻苯二甲酸二乙酯5~15份和山梨醇酐硬脂酸酯5份。
所述的无铅玻璃粉的原料组分按重量份数计为：Bi2O3 30~60份、B2O3 6~17份、CaO 6~10份、SiO2 12~21份、ZnO 6~11份、TiO2 1~5份、Al2O3 10~20份和NiO 3份。
所述的添加剂为氧化锡和氧化铜，两者的重量比为1:1。
本发明的显著优点在于：无铅玻璃粉中氧化钙与氧化锌在高温中会形成少量结晶，从而对银浆中银颗粒形成一定的保护，提高抗老化效果，同时添加剂中的氧化锡在高温中会与银反应在膜层表面形成合金，从而降低焊带对背银在高温下的侵蚀，提高抗老化效果。将氧化钙、氧化锌和氧化锡复配使用，发挥其协同效果，能显著提高背面银浆的抗老化性能，并降低银含量，从而降低成本。
具体实施方式
一种晶体硅太阳能电池用背面银浆，原料组分按重量份数计为：银粉50份、有机粘合剂43~47份、无铅玻璃粉1~5份和添加剂2份。
所述的银粉纯度为99.9~99.99%、呈球状，平均粒径为1.5~3.0μm。
所述的有机粘合剂的原料组分按重量份数计为：松油醇40~65份、丁基卡必醇5~10份、丁基卡必醇醋酸酯15~20份、乙基纤维素3~10份、邻苯二甲酸二乙酯5~15份和山梨醇酐硬脂酸酯5份。
所述的无铅玻璃粉的原料组分按重量份数计为：Bi2O3 30~60份、B2O3 6~17份、CaO 6~10份、SiO2 12~21份、ZnO 6~11份、TiO2 1~5份、Al2O3 10~20份和NiO 3份。
所述的添加剂为氧化锡和氧化铜，两者的重量比为1:1。
实施例1
所述银浆的原料组分及重量含量如下：银粉50份、有机粘合剂47份、无铅玻璃粉1份和添加剂2份；所述银粉纯度为99.9%、平均粒径为2.0μm的球状银粉；所述有机粘合剂的原料组分及重量含量如下：松油醇62份，丁基卡必醇5份、丁基卡必醇醋酸酯17份、乙基纤维素3份、邻苯二甲酸二乙酯8份和山梨醇酐硬脂酸酯5份；所述无铅玻璃粉的原料组分及重量含量如下，Bi2O3：50份、B2O3：5份、CaO：8份、SiO2：16份、ZnO：7份、TiO2：1份、Al2O3：10份、NiO：3份；所述添加剂的组分和重量比如下，SnO2：1份、CuO：1份。
实施例2
作为本发明的优选方案，所述银浆的原料组分及重量含量如下：银粉50份、有机粘合剂45份、无铅玻璃粉3份和添加剂2份；所述银粉纯度为99.9%、平均粒径为2.0μm的球状银粉；所述有机粘合剂的原料组分及重量含量如下：松油醇62份，丁基卡必醇5份、丁基卡必醇醋酸酯17份、乙基纤维素3份、邻苯二甲酸二乙酯8份和山梨醇酐硬脂酸酯5份；所述无铅玻璃粉的原料组分及重量含量如下，Bi2O3：50份、B2O3：5份、CaO：8份、SiO2：16份、ZnO：7份、TiO2：1份、Al2O3：10份、NiO：3份；所述添加剂的组分和重量比如下，SnO2：1份、CuO：1份。
实施例3
所述银浆的原料组分及重量含量如下：银粉50份、有机粘合剂45份、无铅玻璃粉3份和添加剂2份；所述银粉纯度为99.9%、平均粒径为2.0μm的球状银粉；所述有机粘合剂的原料组分及重量含量如下：松油醇62份，丁基卡必醇5份、丁基卡必醇醋酸酯17份、乙基纤维素3份、邻苯二甲酸二乙酯8份和山梨醇酐硬脂酸酯5份；所述无铅玻璃粉的原料组分及重量含量如下，Bi2O3：44份、B2O3：5份、CaO：10份、SiO2：16份、ZnO：11份、TiO2：1份、Al2O3：10份、NiO：3份；所述添加剂的组分和重量比如下，SnO2：1份、CuO：1份。
以上所述仅为本发明的较佳实施例，凡依本发明申请专利范围所做的均等变化与修饰，皆应属本发明的涵盖范围。

Claims (5)

1.一种晶体硅太阳能电池用背面银浆，其特征在于：原料组分按重量份数计为：银粉50份、有机粘合剂43~47份、无铅玻璃粉1~5份和添加剂2份。
2.根据权利要求1所述的晶体硅太阳能电池用背面银浆，其特征在于：所述的银粉纯度为99.9~99.99%、呈球状，平均粒径为1.5~3.0μm。
3.根据权利要求1所述的晶体硅太阳能电池用背面银浆，其特征在于：所述的有机粘合剂的原料组分按重量份数计为：松油醇40~65份、丁基卡必醇5~10份、丁基卡必醇醋酸酯15~20份、乙基纤维素3~10份、邻苯二甲酸二乙酯5~15份和山梨醇酐硬脂酸酯5份。
4.根据权利要求1所述的晶体硅太阳能电池用背面银浆，其特征在于：所述的无铅玻璃粉的原料组分按重量份数计为：Bi2O3 30~60份、B2O3 6~17份、CaO 6~10份、SiO2 12~21份、ZnO 6~11份、TiO2 1~5份、Al2O3 10~20份和NiO 3份。
5.根据权利要求1所述的晶体硅太阳能电池用背面银浆，其特征在于：所述的添加剂为氧化锡和氧化铜，两者的重量比为1:1。
CN201510397922.5A 2015-07-09 2015-07-09 一种晶体硅太阳能电池用背面银浆 Active CN104966546B (zh)