CN104946030B - A kind of super hydrophobic coating composition - Google Patents
A kind of super hydrophobic coating composition Download PDFInfo
- Publication number
- CN104946030B CN104946030B CN201510348208.7A CN201510348208A CN104946030B CN 104946030 B CN104946030 B CN 104946030B CN 201510348208 A CN201510348208 A CN 201510348208A CN 104946030 B CN104946030 B CN 104946030B
- Authority
- CN
- China
- Prior art keywords
- parts
- hydrophobic
- coating
- primer
- super
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses such a super hydrophobic coating composition.It is poor to solve wearability existing for existing super hydrophobic coating, it is poor to the adhesive force of a variety of base materials such as plastics, glass, the problems such as using being restricted.The present invention takes primer:Its composition includes 10 30 parts of chlorinated polypropylenes, 38 parts of polypropylene micro mists, 30 70 parts of ethyl acetate;Coating materials:Its composition includes 15 30 parts of resin with low surface energy, 5 15 parts of hydrophobization nano particles, 30 70 parts of ethyl acetate.
Description
Technical field
The present invention relates to a kind of coating, more particularly to a kind of super hydrophobic coating being made up of primer and coating materials to combine
Thing.
Background technology
Super hydrophobic coating is as a emerging product, because it has excellent water proofing property, soil resistance and self-cleaning, in recent years
Constantly pursued.Super-hydrophobic product is widely used in the neck such as antifouling, steamer of exterior aerial, anticorrosion of steel structure, external wall waterproof
Domain.A kind of super-hydrophobicity, wearability and persistence are developed, and the super hydrophobic coating for having good adhesiveness to different substrate materials has
Make great sense.
Published super hydrophobic coating is mainly formed single with usual resins or resin with low surface energy combination hydrophobic granule
Hydrophobic coating, the wearability and persistence of this kind of hydrophobic coating are poor, and the applicability of different substrate materials is more limited to.
Chinese patent CN101143989 discloses a kind of that organosilan gel precursors and silicone oil and nanoparticle are molecular
Hydrophobic coating, the hydrophobic coating can produce super-hydrophobic interface under specific circumstances, but what it utilized is silane gel precursors, is prepared
Complex process and greater risk be present, the hydrophobic interfaces constructed change with the molecular weight of gel precursors, and hydrophobicity is unstable
Fixed and organic silicon coating is poor to the adhesive force of the base materials such as plastics, glass, and its scope of application has limitation.
One kind disclosed in Chinese patent CN101643622 and Chinese patent CN102453425 using furfuryl alcohol resin as binding agent,
Using single hydrophobic granule or micron powder particle as the super hydrophobic coating of filler, simple production process, certain dredge can be played
Water effect, but its hydrophobicity is poor, it is poor to the applicability of a variety of base materials such as plastics, glass.
Chinese patent CN102417773, Chinese patent CN102660182, Chinese patent CN103666173 and Chinese patent
CN103642378 discloses four kinds using fluoroacrylic resin as low-surface-energy binding agent, and hydrophobic nano-particles form for filler
Hydrophobic coating, under specific occasion, it can play preferable super-hydrophobic effect, but its wearability is poor, by of short duration wind
Erosion or friction will lose ultra-hydrophobicity, poor to the adhesive force of a variety of base materials such as plastics, glass, using being restricted.
The content of the invention
It is an object of the invention to overcome the shortcomings of the prior art, there is provided it is a kind of with super-hydrophobicity, it is good resistance to
Mill property and persistence, and all there is the super hydrophobic coating composition of good adhesiveness to various base materials.
For the above-mentioned purpose, a kind of super hydrophobic coating composition of the present invention is made up of primer and coating materials, primer bag
Include the composition of following mass fraction:10-30 part chlorinated polypropylenes, 3-8 part plastics micro mists, 30-70 part ethyl acetate;Face applies
Material includes the composition of following mass fraction:15-30 part resin with low surface energy, 5-15 part hydrophobic nanoparticles, 30-70 part acetic acid second
Ester.
Further, the chlorinity of described chlorinated polypropylene is 20%-25%.
Further, the plastics micro mist includes one or more of mixtures in PP, PET, PEEK, its particle diameter distribution
For 10-50 microns.
Further, the resin with low surface energy is siliceous modified fluorin resin, its single coating hydrophobic angle >=110 °, its point
Minor is:
CF3(CF2)n1CH(CF2)n2CH2CH2OCH2Si(OEt)3
︱
CH2OCOCH3
n1,n2=3-7。
Further, described hydrophobic nanoparticles include dewatering nano white carbon, hydrophobic nano-titanium dioxide and polytetrafluoro
One or more of mixtures in ethene micro mist, its particle diameter are 50-200 nanometers.
Further, described micron order polypropylene powder with nanoscale hydrophobic silicic aerogels by coating twice, in surface shape
Into micro-/ nano concaveconvex structure.
The construction technology of above-mentioned super hydrophobic coating, comprises the following steps:
(1)Remove the oils dunghill of substrate surface;
(2)Uniformly by primer sprays on base material, 10-20 minutes are dried;
(3)Uniformly coating materials are sprayed on primer, super-hydrophobic effect can be tentatively shown after drying several minutes.
Beneficial effects of the present invention are mainly manifested in:
1st, there is excellent super-hydrophobicity, wearability and persistence the invention provides a kind of, and to different substrate materials all
Super hydrophobic coating composition with good adhesiveness.
2nd, the present invention uses binding agent of the chlorinated polypropylene as primer, can be glued with a variety of substrate surfaces
Knot, or even have preferable adhesiveness to the difficult viscous material such as polypropylene plastics, glass.
3rd, for the present invention using chlorinated polypropylene as primer, surface still has certain viscosity after film forming, can
The hydrophobic granule of coating materials is adhered to, increases its wearability and persistence.
4th, primer of the present invention uses micron order PP GRANULES, and coating materials use nanoscale hydrophobic granule, by twice
Coating, micro-/ nano concaveconvex structure is formed on surface, coordinates the resin with low surface energy of coating materials, forms super-hydrophobic interface, static state is hated
Water angle >=150 °, roll angle≤5 °.
The present invention is described in detail in embodiment embodiment described below.In these embodiments, except as otherwise saying
Bright outer, all parts and percentages are by weight.
Embodiment 1:
It is prepared by primer:10 parts of chlorinated polypropylenes are dissolved in 30 parts of ethyl acetate solvents, by 3 parts of PP micro mist high-speed stirrings
Mix and be dispersed in chlorinated polypropylene solution;
It is prepared by coating materials:15 parts of siliceous modified fluorin resins are mixed with 30 parts of ethyl acetate, it is white to add 5 parts of dewatering nanos
Carbon black, high-speed stirred are scattered 30 minutes;
Embodiment 2:
It is prepared by primer:15 parts of chlorinated polypropylenes are dissolved in 45 parts of ethyl acetate solvents, by 3 parts of PP micro mists and 4 parts
PET micro mist high-speed stirreds are dispersed in chlorinated polypropylene solution;
It is prepared by coating materials:20 parts of siliceous modified fluorin resins are mixed with 60 parts of ethyl acetate, add 15 parts of dewatering nanos
Titanium dioxide, high-speed stirred are scattered 30 minutes;
Embodiment 3:
It is prepared by primer:12 parts of chlorinated polypropylenes are dissolved in 45 parts of ethyl acetate solvents, by 6 parts of PET micro mists at a high speed
It is dispersed with stirring in chlorinated polypropylene solution;
It is prepared by coating materials:25 parts of siliceous modified fluorin resins are mixed with 70 parts of ethyl acetate, 10 parts of nanoscales is added and gathers
Tetrafluoroethene micro mist, high-speed stirred are scattered 30 minutes;
Embodiment 4:
It is prepared by primer:25 parts of chlorinated polypropylenes are dissolved in 70 parts of ethyl acetate solvents, by 5 parts of PP micro mists and 1 part
PEEK micro mist high-speed stirreds are dispersed in chlorinated polypropylene solution;
It is prepared by coating materials:18 parts of siliceous modified fluorin resins are mixed with 60 parts of ethyl acetate, it is white to add 3 parts of dewatering nanos
Carbon black and 9 parts of nanoscale ptfe micropowders, high-speed stirred are scattered 30 minutes;
Embodiment 5:
It is prepared by primer:19 parts of chlorinated polypropylenes are dissolved in 65 parts of ethyl acetate solvents, by 6 parts of PEEK micro mists at a high speed
It is dispersed with stirring in chlorinated polypropylene solution;
It is prepared by coating materials:23 parts of siliceous modified fluorin resins are mixed with 45 parts of ethyl acetate, add 2 parts of dewatering nanos two
Titanium oxide and 7 parts of nanoscale ptfe micropowders, high-speed stirred are scattered 30 minutes;
Embodiment 6:
It is prepared by primer:30 parts of chlorinated polypropylenes are dissolved in 70 parts of ethyl acetate solvents, by 8 parts of PP micro mist high-speed stirrings
Mix and be dispersed in chlorinated polypropylene solution;
It is prepared by coating materials:30 parts of siliceous modified fluorin resins are mixed with 70 parts of ethyl acetate, it is white to add 5 parts of dewatering nanos
Carbon black and 10 parts of Nano titanium dioxides, high-speed stirred are scattered 30 minutes;
It is as shown in the table that embodiment corresponds to technical indicator:
Hydrophobic angle | Roll angle | Adhesive force | |
Embodiment 1 | 150° | 5° | 1 grade |
Embodiment 2 | 150° | 5° | 1 grade |
Embodiment 3 | 152° | 4° | 1 grade |
Embodiment 4 | 151° | 4° | 1 grade |
Embodiment 5 | 153° | 4° | 1 grade |
Embodiment 6 | 150° | 4° | 1 grade |
Primer | 20° | Nothing | 1 grade |
Coating materials | 120° | 30° | 7 grades |
Claims (2)
1. a kind of super hydrophobic coating composition, it is characterised in that it is made up of following weight parts:
A. primer:Its composition includes 10-30 part chlorinated polypropylenes, 3-8 part polypropylene micro mists, 30-70 part ethyl acetate;
B. coating materials:Consisting of 15-30 part resin with low surface energy, 5-15 part hydrophobization nano particles, 30-70 part acetic acid second
Ester;
Wherein, described its particle diameter distribution of polypropylene micro mist is 10-50 microns;The hydrophobic nanoparticles include dewatering nano hard charcoal
One or more of mixtures in black, hydrophobic nano-titanium dioxide and ptfe micropowder, its particle diameter distribution are received for 50-200
Rice;The resin with low surface energy is siliceous modified fluorin resin, its single coating hydrophobic angle >=110 °, and its molecular formula is:
CF3(CF2)n1CH(CF2)n2CH2CH2OCH2Si(OEt)3
︱
CH2OCOCH3
n1,n2=3-7;
And the construction technology of the super hydrophobic coating, comprise the following steps:
(1)Remove the oils dunghill of substrate surface;
(2)Uniformly by primer sprays on base material, 10-20 minutes are dried;
(3)Uniformly coating materials are sprayed on primer, super-hydrophobic effect can be tentatively shown after drying several minutes.
A kind of 2. super hydrophobic coating composition according to claim 1, it is characterised in that:The chlorinated polypropylene
Chlorinity is 20%-25%.