CN104945996A - Aqueous colorful wall paint - Google Patents
Aqueous colorful wall paint Download PDFInfo
- Publication number
- CN104945996A CN104945996A CN201510408564.3A CN201510408564A CN104945996A CN 104945996 A CN104945996 A CN 104945996A CN 201510408564 A CN201510408564 A CN 201510408564A CN 104945996 A CN104945996 A CN 104945996A
- Authority
- CN
- China
- Prior art keywords
- paint
- water
- emulsion
- aqueous colorful
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses aqueous colorful wall paint. The aqueous colorful wall paint comprises 30-40 g of waterproof protective glue, 20-30 g of ordinary base paint, 10-20 g of metal base paint and 20-40 g of polymer emulsion. The polymer emulsion comprises 30-40 g of emulsion, 2-4 g of anti-settling agent, 1-2 g of coalescing agent, 0-10 g of laser materials and 50-60 g of water. The metal base paint comprises 95-100 g of metal base paint body and 0-5 g of transparent color paste. The metal base paint body comprises emulsion, waterproof protective glue, other auxiliaries, aqueous pigment and water. The ordinary base paint comprises 95-100 g of ordinary base paint body and 0-5 g of color paste. The ordinary base paint body comprises emulsion, waterproof protective glue, other auxiliaries, pigments and water. According to the aqueous colorful wall paint, a good covering surface-free metallic texture granite texture effect can be achieved through cable-strayed painting; meanwhile, the aqueous colorful wall paint has excellent durability, washing tolerance and dirt resistance.
Description
Technical field
The present invention relates to wall paint technical field, specifically a kind of aqueous colorful wall paint.
Background technology
All the look grain point reaching grouan texture with inorganic or organic mill base (toner) on the market.The method is feasible for the grouan effect of imitating without metal-like, but the method cannot reach the grouan effect of metal-like.Traditional technology adopts the mode of facade vertical direct spraying to construct, and the grouan look grain point of product is evenly distributed on metope, can not into strips, thread distribution.Tradition multicolor finish uses as floating coat owing to adopting a large amount of wetting ability protecting glue and the general emulsion of pollution resistance, construction technology needs adopt cover technique to overcome above-mentioned shortcoming.
Summary of the invention
The object of the present invention is to provide and a kind of there is the good aqueous colorful wall paint of exempting from the metal-like grouan grain effect of cover.
For achieving the above object, the invention provides following technical scheme:
A kind of aqueous colorful wall paint, adopts the raw material of following combination: water tolerance protecting glue 30 ~ 40g, common base paint 20 ~ 30g, metal matrix paint 10 ~ 20g and polymer emulsion 20 ~ 40g;
Described polymer emulsion adopts the raw material of following combination: emulsion 30 ~ 40g, anti-settling agent 2 ~ 4g, film coalescence aid 1 ~ 2g, laserable material 0 ~ 10g and water 50 ~ 60g;
Described metal matrix paint adopts the raw material of following combination: metal foundation paint 95 ~ 100g and transparent mill base 0 ~ 5g, and described metal foundation paint adopts the raw material of following combination: emulsion 45 ~ 50g, water tolerance protecting glue 2 ~ 5g, other auxiliary agent 2 ~ 5g, water-based paint 10 ~ 15g and water 20 ~ 30g;
Described common base paint adopts the raw material of following combination: conventional foundation paint 95 ~ 100g and mill base 0 ~ 5g, and described conventional foundation paint adopts the raw material of following combination: emulsion 45 ~ 50g, water tolerance protecting glue 2 ~ 5g, other auxiliary agent 2 ~ 5g, pigment 10 ~ 15g and water 20 ~ 30g;
Other auxiliary agents described are one or more the mixture in sterilant, thickening material, flow agent and mould inhibitor.
As the further scheme of the present invention: described water-based paint is one or both the mixture in water-soluble pearlescent pigment and water-based metal pigment.
As the further scheme of the present invention: described mill base is one or both the mixture in inorganic mill base and organic mill base.
As the further scheme of the present invention: described water tolerance protecting glue is one or more the mixture in acrylic acid modified clay, cation emulsion and organic bentonite.
As the further scheme of the present invention: described anti-settling agent is one or more the mixture in silicon-dioxide, polyamide wax, polyethylene wax and magnesium aluminum silicate.
As the further scheme of the present invention: described film coalescence aid is one or more the mixture in alcohol ester 12, phenylcarbinol and alcohol ethers.
The preparation method of described aqueous colorful wall paint, comprises the following steps:
(1) preparation of conventional foundation paint: take emulsion, water tolerance protecting glue, other auxiliary agents, pigment and water in proportion, mixing, stirs and obtains conventional foundation paint, for subsequent use;
(2) preparation of metal foundation paint: take emulsion, water tolerance protecting glue, other auxiliary agents, water-based paint and water in proportion, mixing, stirs and obtains metal foundation paint, for subsequent use;
(3) preparation of common base paint: take mill base in proportion, the conventional foundation paint prepared with step (1) mixes, and stirs evenly and obtains common base paint, for subsequent use;
(4) preparation of metal matrix paint: take transparent mill base in proportion, the metal foundation paint prepared with step (2) mixes, and stirs evenly and obtains metal matrix paint, for subsequent use;
(5) preparation of polymer emulsion: take the mixing of emulsion, anti-settling agent, film coalescence aid, laserable material and water in proportion, stir evenly and obtain polymer emulsion, for subsequent use;
(6) preparation of aqueous colorful wall paint: take the polymer emulsion that the obtained metal matrix paint of the obtained common base paint of water tolerance protecting glue, step (3), step (4), step (5) are obtained in proportion; mixing, stirs and obtains aqueous colorful wall paint.
Compared with prior art, the invention has the beneficial effects as follows:
Contrast locating of the present invention is higher, selects raw material based on imported materials and items, and makes every effort to the environmental requirement of low smell, low VOC, so integral material cost adopts separately inorganic, organic mill base (toner) high than original.But be that usual way institute is inaccessiable in metal-like effect, there has been positive effect persistence and the pollution resistance aspect of paint film.Higher than multicolor finish product common on market on cost.
1, select inorganic mill base or toner, organic mill base or toner, weather-proof level water-soluble pearlescent pigment or weather-proof level water-based metal pigment, laserable material, transparent pigment as color development material, after making coating application, present the grouan grain effect of metal-like.
2, form of construction work working procedure adopting oblique pull spray, thus reach strip and thread grain effect.
3, adopt the polymer emulsion of water tolerance protecting glue and band functional groups as main film forming substance; functional groups is utilized to meet the UV-crosslinked principle of sunlight; make this wall paint have more excellent weather resistance, abrasion resistance and pollution resistance, thus remove common multicolor finish on market from and need the operation of cover.
The present invention not only facilitated coating material production to process, but also have the good metal-like grouan grain effect of exempting from cover, the final novel wall surface material forming comprehensive wall guard, decorative effect.
Embodiment
Below in conjunction with the embodiment of the present invention, be clearly and completely described the technical scheme in the embodiment of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, a kind of aqueous colorful wall paint, adopts the raw material of following combination: water tolerance protecting glue 30g, common base paint 30g, metal matrix paint 20g and polymer emulsion 20g; Polymer emulsion adopts the raw material of following combination: emulsion 40g, anti-settling agent 2g, film coalescence aid 1g, laserable material 0g and water 50g; Metal matrix paint adopts the raw material of following combination: metal foundation paint 100g and transparent mill base 0g, and metal foundation paint adopts the raw material of following combination: emulsion 45g, water tolerance protecting glue 5g, other auxiliary agent 5g, water-based paint 10g and water 30g; Common base paint adopts the raw material of following combination: conventional foundation paint 95g and mill base 5g, and conventional foundation paint adopts the raw material of following combination: emulsion 50g, water tolerance protecting glue 2g, other auxiliary agent 2g, pigment 15g and water 20g; Other auxiliary agents are sterilant.Water-based paint is water-soluble pearlescent pigment.Mill base is inorganic mill base.Water tolerance protecting glue is acrylic acid modified clay.Anti-settling agent is silicon-dioxide.Film coalescence aid is alcohol ester 12.
The preparation method of described aqueous colorful wall paint, comprises the following steps:
(1) preparation of conventional foundation paint: take emulsion, water tolerance protecting glue, other auxiliary agents, pigment and water in proportion, mixing, stirs and obtains conventional foundation paint, for subsequent use;
(2) preparation of metal foundation paint: take emulsion, water tolerance protecting glue, other auxiliary agents, water-based paint and water in proportion, mixing, stirs and obtains metal foundation paint, for subsequent use;
(3) preparation of common base paint: take mill base in proportion, the conventional foundation paint prepared with step (1) mixes, and stirs evenly and obtains common base paint, for subsequent use;
(4) preparation of metal matrix paint: take transparent mill base in proportion, the metal foundation paint prepared with step (2) mixes, and stirs evenly and obtains metal matrix paint, for subsequent use;
(5) preparation of polymer emulsion: take the mixing of emulsion, anti-settling agent, film coalescence aid, laserable material and water in proportion, stir evenly and obtain polymer emulsion, for subsequent use;
(6) preparation of aqueous colorful wall paint: take the polymer emulsion that the obtained metal matrix paint of the obtained common base paint of water tolerance protecting glue, step (3), step (4), step (5) are obtained in proportion; mixing, stirs and obtains aqueous colorful wall paint.
Embodiment 2
In the embodiment of the present invention, a kind of aqueous colorful wall paint, adopts the raw material of following combination: water tolerance protecting glue 35g, common base paint 25g, metal matrix paint 15g and polymer emulsion 30g; Polymer emulsion adopts the raw material of following combination: emulsion 35g, anti-settling agent 3g, film coalescence aid 1.5g, laserable material 5g and water 55g; Metal matrix paint adopts the raw material of following combination: metal foundation paint 97g and transparent mill base 3g, and metal foundation paint adopts the raw material of following combination: emulsion 48g, water tolerance protecting glue 3g, other auxiliary agent 4g, water-based paint 12g and water 27g; Common base paint adopts the raw material of following combination: conventional foundation paint 98g and mill base 2g, and conventional foundation paint adopts the raw material of following combination: emulsion 47g, water tolerance protecting glue 4g, other auxiliary agent 3g, pigment 13g and water 24g; Other auxiliary agents are thickening material.Water-based paint is water-based metal pigment.Mill base is organic mill base.Water tolerance protecting glue is organic bentonite.Anti-settling agent is polyethylene wax.Film coalescence aid is phenylcarbinol.
The preparation method of described aqueous colorful wall paint, comprises the following steps:
(1) preparation of conventional foundation paint: take emulsion, water tolerance protecting glue, other auxiliary agents, pigment and water in proportion, mixing, stirs and obtains conventional foundation paint, for subsequent use;
(2) preparation of metal foundation paint: take emulsion, water tolerance protecting glue, other auxiliary agents, water-based paint and water in proportion, mixing, stirs and obtains metal foundation paint, for subsequent use;
(3) preparation of common base paint: take mill base in proportion, the conventional foundation paint prepared with step (1) mixes, and stirs evenly and obtains common base paint, for subsequent use;
(4) preparation of metal matrix paint: take transparent mill base in proportion, the metal foundation paint prepared with step (2) mixes, and stirs evenly and obtains metal matrix paint, for subsequent use;
(5) preparation of polymer emulsion: take the mixing of emulsion, anti-settling agent, film coalescence aid, laserable material and water in proportion, stir evenly and obtain polymer emulsion, for subsequent use;
(6) preparation of aqueous colorful wall paint: take the polymer emulsion that the obtained metal matrix paint of the obtained common base paint of water tolerance protecting glue, step (3), step (4), step (5) are obtained in proportion; mixing, stirs and obtains aqueous colorful wall paint.
Embodiment 3
In the embodiment of the present invention, a kind of aqueous colorful wall paint, adopts the raw material of following combination: water tolerance protecting glue 40g, common base paint 20g, metal matrix paint 10g and polymer emulsion 40g; Polymer emulsion adopts the raw material of following combination: emulsion 30g, anti-settling agent 4g, film coalescence aid 2g, laserable material 10g and water 60g; Metal matrix paint adopts the raw material of following combination: metal foundation paint 95g and transparent mill base 5g, and metal foundation paint adopts the raw material of following combination: emulsion 50g, water tolerance protecting glue 2g, other auxiliary agent 2g, water-based paint 15g and water 20g; Common base paint adopts the raw material of following combination: conventional foundation paint 100g and mill base 0g, and conventional foundation paint adopts the raw material of following combination: emulsion 45g, water tolerance protecting glue 5g, other auxiliary agent 5g, pigment 10g and water 30g; Other auxiliary agents are mould inhibitor.Water-based paint is the mixture of water-soluble pearlescent pigment and water-based metal pigment.Mill base is the mixture of inorganic mill base and organic mill base.Water tolerance protecting glue is cation emulsion.Anti-settling agent is magnesium aluminum silicate.Film coalescence aid is alcohol ethers.
The preparation method of described aqueous colorful wall paint, comprises the following steps:
(1) preparation of conventional foundation paint: take emulsion, water tolerance protecting glue, other auxiliary agents, pigment and water in proportion, mixing, stirs and obtains conventional foundation paint, for subsequent use;
(2) preparation of metal foundation paint: take emulsion, water tolerance protecting glue, other auxiliary agents, water-based paint and water in proportion, mixing, stirs and obtains metal foundation paint, for subsequent use;
(3) preparation of common base paint: take mill base in proportion, the conventional foundation paint prepared with step (1) mixes, and stirs evenly and obtains common base paint, for subsequent use;
(4) preparation of metal matrix paint: take transparent mill base in proportion, the metal foundation paint prepared with step (2) mixes, and stirs evenly and obtains metal matrix paint, for subsequent use;
(5) preparation of polymer emulsion: take the mixing of emulsion, anti-settling agent, film coalescence aid, laserable material and water in proportion, stir evenly and obtain polymer emulsion, for subsequent use;
(6) preparation of aqueous colorful wall paint: take the polymer emulsion that the obtained metal matrix paint of the obtained common base paint of water tolerance protecting glue, step (3), step (4), step (5) are obtained in proportion; mixing, stirs and obtains aqueous colorful wall paint.
Contrast locating of the present invention is higher, selects raw material based on imported materials and items, and makes every effort to the environmental requirement of low smell, low VOC, so integral material cost adopts separately inorganic, organic mill base (toner) high than original.But be that usual way institute is inaccessiable in metal-like effect, there has been positive effect persistence and the pollution resistance aspect of paint film.Higher than multicolor finish product common on market on cost.
1, select inorganic mill base or toner, organic mill base or toner, weather-proof level water-soluble pearlescent pigment or weather-proof level water-based metal pigment, laserable material, transparent pigment as color development material, after making coating application, present the grouan grain effect of metal-like.
2, form of construction work working procedure adopting oblique pull spray, thus reach strip and thread grain effect.
3, adopt the polymer emulsion of water tolerance protecting glue and band functional groups as main film forming substance; functional groups is utilized to meet the UV-crosslinked principle of sunlight; make this wall paint have more excellent weather resistance, abrasion resistance and pollution resistance, thus remove common multicolor finish on market from and need the operation of cover.
The present invention not only facilitated coating material production to process, but also have the good metal-like grouan grain effect of exempting from cover, the final novel wall surface material forming comprehensive wall guard, decorative effect.
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and when not deviating from spirit of the present invention or essential characteristic, the present invention can be realized in other specific forms.Therefore, no matter from which point, all should embodiment be regarded as exemplary, and be nonrestrictive, scope of the present invention is limited by claims instead of above-mentioned explanation, and all changes be therefore intended in the implication of the equivalency by dropping on claim and scope are included in the present invention.
In addition, be to be understood that, although this specification sheets is described according to embodiment, but not each embodiment only comprises an independently technical scheme, this narrating mode of specification sheets is only for clarity sake, those skilled in the art should by specification sheets integrally, and the technical scheme in each embodiment also through appropriately combined, can form other embodiments that it will be appreciated by those skilled in the art that.
Claims (7)
1. an aqueous colorful wall paint, is characterized in that, adopts the raw material of following combination: water tolerance protecting glue 30 ~ 40g, common base paint 20 ~ 30g, metal matrix paint 10 ~ 20g and polymer emulsion 20 ~ 40g;
Described polymer emulsion adopts the raw material of following combination: emulsion 30 ~ 40g, anti-settling agent 2 ~ 4g, film coalescence aid 1 ~ 2g, laserable material 0 ~ 10g and water 50 ~ 60g;
Described metal matrix paint adopts the raw material of following combination: metal foundation paint 95 ~ 100g and transparent mill base 0 ~ 5g, and described metal foundation paint adopts the raw material of following combination: emulsion 45 ~ 50g, water tolerance protecting glue 2 ~ 5g, other auxiliary agent 2 ~ 5g, water-based paint 10 ~ 15g and water 20 ~ 30g;
Described common base paint adopts the raw material of following combination: conventional foundation paint 95 ~ 100g and mill base 0 ~ 5g, and described conventional foundation paint adopts the raw material of following combination: emulsion 45 ~ 50g, water tolerance protecting glue 2 ~ 5g, other auxiliary agent 2 ~ 5g, pigment 10 ~ 15g and water 20 ~ 30g;
Other auxiliary agents described are one or more the mixture in sterilant, thickening material, flow agent and mould inhibitor.
2. aqueous colorful wall paint according to claim 1, is characterized in that, described water-based paint is one or both the mixture in water-soluble pearlescent pigment and water-based metal pigment.
3. aqueous colorful wall paint according to claim 1, is characterized in that, described mill base is one or both the mixture in inorganic mill base and organic mill base.
4. aqueous colorful wall paint according to claim 1, is characterized in that, described water tolerance protecting glue is one or more the mixture in acrylic acid modified clay, cation emulsion and organic bentonite.
5. aqueous colorful wall paint according to claim 1, is characterized in that, described anti-settling agent is one or more the mixture in silicon-dioxide, polyamide wax, polyethylene wax and magnesium aluminum silicate.
6. aqueous colorful wall paint according to claim 1, is characterized in that, described film coalescence aid is one or more the mixture in alcohol ester 12, phenylcarbinol and alcohol ethers.
7. a preparation method for the aqueous colorful wall paint as described in as arbitrary in claim 1-6, is characterized in that, comprise the following steps:
(1) preparation of conventional foundation paint: take emulsion, water tolerance protecting glue, other auxiliary agents, pigment and water in proportion, mixing, stirs and obtains conventional foundation paint, for subsequent use;
(2) preparation of metal foundation paint: take emulsion, water tolerance protecting glue, other auxiliary agents, water-based paint and water in proportion, mixing, stirs and obtains metal foundation paint, for subsequent use;
(3) preparation of common base paint: take mill base in proportion, the conventional foundation paint prepared with step (1) mixes, and stirs evenly and obtains common base paint, for subsequent use;
(4) preparation of metal matrix paint: take transparent mill base in proportion, the metal foundation paint prepared with step (2) mixes, and stirs evenly and obtains metal matrix paint, for subsequent use;
(5) preparation of polymer emulsion: take the mixing of emulsion, anti-settling agent, film coalescence aid, laserable material and water in proportion, stir evenly and obtain polymer emulsion, for subsequent use;
(6) preparation of aqueous colorful wall paint: take the polymer emulsion that the obtained metal matrix paint of the obtained common base paint of water tolerance protecting glue, step (3), step (4), step (5) are obtained in proportion; mixing, stirs and obtains aqueous colorful wall paint.