CN104944911A - 一种陶瓷滤水器滤芯及其制备方法 - Google Patents

一种陶瓷滤水器滤芯及其制备方法 Download PDF

Info

Publication number
CN104944911A
CN104944911A CN201510298096.9A CN201510298096A CN104944911A CN 104944911 A CN104944911 A CN 104944911A CN 201510298096 A CN201510298096 A CN 201510298096A CN 104944911 A CN104944911 A CN 104944911A
Authority
CN
China
Prior art keywords
filter core
water
orders
preparation
quartz
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510298096.9A
Other languages
English (en)
Inventor
黄克生
黄志发
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHAOZHOU HUAZHONG CERAMICS INDUSTRIES Co Ltd
Original Assignee
CHAOZHOU HUAZHONG CERAMICS INDUSTRIES Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHAOZHOU HUAZHONG CERAMICS INDUSTRIES Co Ltd filed Critical CHAOZHOU HUAZHONG CERAMICS INDUSTRIES Co Ltd
Priority to CN201510298096.9A priority Critical patent/CN104944911A/zh
Publication of CN104944911A publication Critical patent/CN104944911A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种陶瓷滤水器滤芯及其制备方法，由以下组分组成，按重量%：麦饭石：30～60%，粘土：18～25%，氧化钙：7～15%，石英：15～30%；其制备方法包括：（1）上述的各组分按比例配料，混合搅拌后经炼泥机炼制，制作成瓷泥；（2）制作成型；（3）烧成：烧成温度1050～1150℃，烧成时间4～6小时；（4）对滤芯表面进行磨光处理；（5）检验、包装、入库。实现本发明，由于陶瓷滤水器滤芯主要以麦饭石、粘土、氧化钙、石英为主要材料，既能吸附、过滤净化水质，且能活化及矿化水质，又具有抗菌、杀菌功能，并具有耐用、易清洗、使用方便等特点，能将普通水从酸性水变成弱碱性水，有益于人们的身体健康，是当前人们饮水中最健康的一种滤水器滤芯，应用该滤芯制成的饮水器，可广泛应用于家庭、酒店及公共场所。

Description

一种陶瓷滤水器滤芯及其制备方法
技术领域
本发明属于一种陶瓷制品及其制备方法的应用领域，具体来说是涉及一种陶瓷滤水器滤芯及其制备方法。
背景技术
水是生命之源，万物之本。随着世界经济的快速发展，水已经成为主宰和制约人类社会发展的重要因素之一。这些年来因水而引发的问题层出不穷，一方面是我国淡水资源的严重短缺、河流湖泊的富营养化、工业及医疗废水的污染问题、化肥农药对地下水的污染问题等，另一方面是受到各种直接或间接的污染导致水质下降、日常饮用水的净化消毒不彻底以及由此引发的食品安全问题等。日趋加剧的水污染，已对人类的生存安全构成重大威胁，成为人类健康、经济和社会可持续发展的重大障碍。据世界权威机构调查，在发展中国家，各类疾病有8％是因为饮用了不卫生的水而传播，因此，水污染被称作“世界头号杀手”。为了应对水污染问题，目前市面上有很多种类的净水设备，如RO膜净水器、PP棉水过滤机、木炭裸粒的净水器等等；但RO膜净水器过滤的水是一种电解水、纯净水，没有人体所需矿物质，对人们的生活健康带来盲区；PP棉水过滤机其本身质地是软化，初用期肉眼就能看到过滤效果，但一段时间后由于PP棉是一种软化化学品，经过水分解后将破坏其物理结构，造成孔径大，会把原来过滤的沉淀物聚集一次性还原给人们饮用，造成人们身体更不健康。
发明内容
为克服上述不足，本发明的目的在于提供一种既能过滤净化水质、活化及矿化水质，且有抗菌、杀菌功能，将普通水从酸性水变成弱碱性水的陶瓷滤水器滤芯及其制备方法。
本发明是这样实现的：
一种陶瓷滤水器滤芯，由以下组分组成，按重量%：
麦饭石：30～60%，粘土：18～25%，氧化钙：7～15%，石英：15～30%
上述组分中，麦饭石为300～500目，粘土为300～500目，氧化钙为200～300目，石英为50～120目。
上述陶瓷滤水器滤芯，其优选配方由以下组分组成，按重量%：
麦饭石：38～50%，粘土：20～25%，氧化钙：10～12%，石英：20～25%
上述组分中，麦饭石为400～500目，粘土为400～500目，氧化钙为200～300目，石英为80～120目。
本发明陶瓷滤水器滤芯的制备方法，其工艺步骤包括：
将上述各组分按比例配料，然后混合搅拌后经炼泥机炼制，制作成瓷泥；
（2）按所需的滤芯形状制作成型；
（3）将制作成型的滤芯进入窑炉烧制，烧成温度1050～1150℃，烧成时间4～6小时；
（4）将烧制后的滤芯表面进行磨光处理；
（5）检验、包装、入库。
其工艺步骤（2）所述制作成型为滚压成型。
其工艺步骤（2）所述滤芯形状为直筒形、桶形或碗形。
实现本发明，由于陶瓷滤水器滤芯主要以麦饭石、氧化钙、石英为主要材料，既能吸附、过滤净化水质，且能活化及矿化水质，又具有抗菌、杀菌功能，并具有耐用、易清洗、使用方便等特点，能将普通酸性水变成弱碱性水，有益于人们的身体健康，是当前人们饮水中最健康的一种滤水器滤芯，应用该滤芯制成的饮水器，可广泛应用于家庭、酒店及公共场所。
具体实施方式
实施例１：
陶瓷滤水器滤芯，由以下组分组成，按重量%：
麦饭石：（400～500目）40%，粘土：（400～00目）25%，氧化钙：（200～300目）10%，石英：（80～120目）25%。
上述陶瓷滤水器滤芯的制备方法，其工艺步骤包括：
（1）将上述的各组分按比例配料，然后混合搅拌后经炼泥机炼制，制作成瓷泥；
（2）制作成型：采用滚压成型制作成直筒形状滤芯；
（3）将制作成型的滤芯进入窑炉烧制，烧成温度 1120℃，烧成时间5.2小时；
（4）将烧制后的滤芯表面进行磨光处理；
（5）检验、包装、入库。
实施例2：
陶瓷滤水器滤芯，由以下组分组成，按重量%：
麦饭石：（400～500目）45%，粘土：（400～500目）20%，氧化钙：（200～300目）15%，石英：（80～120目）20%。
上述陶瓷滤水器滤芯的制备方法，其工艺步骤包括：
（1）将上述的各组分按比例配料，然后混合搅拌后经炼泥机炼制，制作成瓷泥；
（2）制作成型：采用滚压成型制作成桶形状滤芯；
（3）将制作成型的滤芯进入窑炉烧制，烧成温度 1150℃，烧成时间5.0小时；
其它工艺步骤与实施例1相同。
实施例3：
陶瓷滤水器滤芯，由以下组分组成，按重量%：
麦饭石：（400～500目）50%，粘土：（400～500目）20%，氧化钙：（200～300目）7%，石英：（80～120目）23%。
上述陶瓷滤水器滤芯的制备方法，其工艺步骤包括：
（1）将上述的各组分按比例配料，然后混合搅拌后经炼泥机炼制，制作成瓷泥；
（2）制作成型：采用滚压成型制作成碗形状滤芯；
（3）将制作成型的滤芯进入窑炉烧制，烧成温度 1100℃，烧成时间  5.5小时；
其它工艺步骤与实施例1相同。

Claims (5)

1.一种陶瓷滤水器滤芯，其特征在于：由以下组分组成，按重量%：
麦饭石：30～60%，粘土：18～25%，氧化钙：7～15%，石英：15～30%
上述组分中，麦饭石为300～500目，粘土为300～500目，氧化钙为200～300目，石英为50～120目。
2.根据权利要求１所述陶瓷滤水器滤芯，其特征在于：由以下组分组成，按重量%：
麦饭石：38～50%，粘土：20～25%，氧化钙：10～12%，石英：20～25%
上述组分中，麦饭石为400～500目，粘土为400～500目，氧化钙为200～300目，石英为80～120目。
3.一种陶瓷滤水器滤芯的制备方法，其特征在于：其工艺步骤包括：
（1）将权利要求1或2所述的各组分按比例配料，然后混合搅拌后经炼泥机炼制，制作成瓷泥； 
（2）按所需的滤芯形状制作成型；
（3）将制作成型的滤芯进入窑炉烧制，烧成温度1050～1150℃，烧成时间4～ 6小时；
（4）将烧制后的滤芯表面进行磨光处理；
（5）检验、包装、入库。
4.根据权利要求3所述陶瓷滤水器滤芯的制备方法，其特征在于：其工艺步骤（2）所述制作成型为滚压成型。
5.根据权利要求3所述陶瓷滤水器滤芯的制备方法，其特征在于：其工艺步骤（2）所述滤芯形状为直筒形、桶形或碗形。
CN201510298096.9A 2015-06-04 2015-06-04 一种陶瓷滤水器滤芯及其制备方法 Pending CN104944911A (zh)