CN104927125A - Flange sealing gasket for chemical sewage pipe connection - Google Patents

Flange sealing gasket for chemical sewage pipe connection Download PDF

Info

Publication number
CN104927125A
CN104927125A CN201510312132.2A CN201510312132A CN104927125A CN 104927125 A CN104927125 A CN 104927125A CN 201510312132 A CN201510312132 A CN 201510312132A CN 104927125 A CN104927125 A CN 104927125A
Authority
CN
China
Prior art keywords
parts
aging agent
sealing gasket
warming
mixing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510312132.2A
Other languages
Chinese (zh)
Inventor
陈俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongzhi Qunsheng Chemical Equipment Co Ltd
Original Assignee
Dongzhi Qunsheng Chemical Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongzhi Qunsheng Chemical Equipment Co Ltd filed Critical Dongzhi Qunsheng Chemical Equipment Co Ltd
Priority to CN201510312132.2A priority Critical patent/CN104927125A/en
Publication of CN104927125A publication Critical patent/CN104927125A/en
Pending legal-status Critical Current

Abstract

The invention discloses a flange sealing gasket for chemical sewage pipe connection and relates to the technical field of sealing material production. The flange sealing gasket is prepared from raw materials in parts by mass as follows: 80-90 parts of NBR (nitrile butadiene rubber), 12-15 parts of nano glass fibers, 20-25 parts of polyphenylene sulfide, 15-20 parts of polyvinyl alcohol, 10-12 parts of kaolin, 8-11 parts of carboxymethyl chitosan, 5-8 parts of white carbon black, 4-7 parts of guar gum, 3-5 parts of sodium stearate, 1-3 parts of an anti-aging agent, 20-25 parts of polyethylene glycol and 25-30 parts of water. The NBR is modified with the nano glass fibers, multiple aids are used, the comprehensive performance of the sealing gasket is improved, and the prepared sealing gasket is applicable to corrosive chemical sewage at the temperature lower than 198 DEG C and is long in service life.

Description

A kind of chemical engineering sewage pipeline connecting flange gasket
Technical field:
The present invention relates to sealing material production technical field, be specifically related to a kind of chemical engineering sewage pipeline connecting flange gasket.
Background technology:
Chemical engineering sewage refers to the sewage such as processing wastewater, water coolant, discarded washing water, equipment and place wash-down water given off in chemical process.If these sewage discharge without process, different properties and the pollution in various degree of water body can be caused, thus the health of harm humans, affect the production of industrial or agricultural.
At present, the plastics tubing that the main use properties of conveying of chemical engineering sewage pipeline is stable, and the connection between pipeline adopts Flange joint mostly.During Flange joint, in order to improve stopping property, need to use gasket between the flanges.But due to the complicated component in chemical engineering sewage, there is very strong corrodibility or there is higher temperature, therefore can not use general flange gasket.In recent years, people put forth effort on the gasket of exploitation corrosion-and high-temp-resistant, but performance is undesirable, and work-ing life is shorter.
Summary of the invention:
Technical problem to be solved by this invention is to provide a kind of chemical engineering sewage pipeline connecting flange gasket of high temperature resistant, corrosion-resistant and long service life.
Technical problem to be solved by this invention adopts following technical scheme to realize:
A kind of chemical engineering sewage pipeline connecting flange gasket, be made up of the raw material of following mass fraction:
Paracril 80-90 part, nanometer glass fiber 12-15 part, polyphenylene sulfide 20-25 part, polyvinyl alcohol 15-20 part, cm-chitosan 8-11 part, kaolin 6-9 part, white carbon black 5-8 part, guar gum 4-7 part, sodium stearate 3-5 part, anti-aging agent 1-3 part, polyoxyethylene glycol 20-25 part, water 25-30 part;
Its preparation method is as follows:
(1) cm-chitosan, sodium stearate are fully dissolved in the water, make the aqueous solution;
(2) in reactor, add paracril, nanometer glass fiber and polyoxyethylene glycol, stir and be warming up to 100-110 DEG C of insulation 1-2h, after then cooling, obtain material I;
(3) in Banbury mixer, polyphenylene sulfide, polyvinyl alcohol and guar gum is added, be warming up to 65-70 DEG C of mixing 3-5min, then the aqueous solution prepared by material I and step (1) is added, continue to be warming up to 90-95 DEG C of mixing 6-8min, add kaolin, white carbon black and anti-aging agent again, send into vulcanizer after mixing 4-6min, make flange gasket according to user demand.
Described anti-aging agent is selected from one or more in antioxidant A W, anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD.
The invention has the beneficial effects as follows:
(1) utilize nanometer glass fiber to carry out modification to paracril, and be aided with multiple auxiliary agent, improve the over-all properties of gasket;
(2) obtained gasket has stronger high thermal resistance, erosion resistance, is applicable to less than 198 DEG C, has corrosive chemical engineering sewage;
(3) long service life, is generally 3-5;
(4) raw material is easy to get, preparation method is simple, is conducive to suitability for industrialized production.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
(1) 8kg cm-chitosan, 3kg sodium stearate are fully dissolved in 25kg water, make the aqueous solution;
(2) in reactor, add 80kg paracril, 12kg nanometer glass fiber and 20kg polyoxyethylene glycol, stir and be warming up to 100-110 DEG C of insulation 2h, after then cooling, obtain material I;
(3) in Banbury mixer, 20kg polyphenylene sulfide, 15kg polyvinyl alcohol and 4kg guar gum is added, be warming up to 65-70 DEG C of mixing 5min, then the aqueous solution prepared by material I and step (1) is added, continue to be warming up to 90-95 DEG C of mixing 8min, add 6kg kaolin, 5kg white carbon black and 1kg anti-aging agent again, send into vulcanizer after mixing 5min, make flange gasket according to user demand.
Embodiment 2
(1) 9kg cm-chitosan, 4kg sodium stearate are fully dissolved in 28kg water, make the aqueous solution;
(2) in reactor, add 85kg paracril, 13kg nanometer glass fiber and 22kg polyoxyethylene glycol, stir and be warming up to 100-110 DEG C of insulation 2h, after then cooling, obtain material I;
(3) in Banbury mixer, 23kg polyphenylene sulfide, 18kg polyvinyl alcohol and 6kg guar gum is added, be warming up to 65-70 DEG C of mixing 5min, then the aqueous solution prepared by material I and step (1) is added, continue to be warming up to 90-95 DEG C of mixing 8min, add 7kg kaolin, 6kg white carbon black and 2kg anti-aging agent again, send into vulcanizer after mixing 5min, make flange gasket according to user demand.
Embodiment 3
(1) 11kg cm-chitosan, 5kg sodium stearate are fully dissolved in 30kg water, make the aqueous solution;
(2) in reactor, add 90kg paracril, 15kg nanometer glass fiber and 25kg polyoxyethylene glycol, stir and be warming up to 100-110 DEG C of insulation 2h, after then cooling, obtain material I;
(3) in Banbury mixer, 25kg polyphenylene sulfide, 20kg polyvinyl alcohol and 7kg guar gum is added, be warming up to 65-70 DEG C of mixing 5min, then the aqueous solution prepared by material I and step (1) is added, continue to be warming up to 90-95 DEG C of mixing 8min, add 9kg kaolin, 8kg white carbon black and 3kg anti-aging agent again, send into vulcanizer after mixing 5min, make flange gasket according to user demand.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.

Claims (2)

1. a chemical engineering sewage pipeline connecting flange gasket, is characterized in that, is made up of the raw material of following mass fraction:
Paracril 80-90 part, nanometer glass fiber 12-15 part, polyphenylene sulfide 20-25 part, polyvinyl alcohol 15-20 part, cm-chitosan 8-11 part, kaolin 6-9 part, white carbon black 5-8 part, guar gum 4-7 part, sodium stearate 3-5 part, anti-aging agent 1-3 part, polyoxyethylene glycol 20-25 part, water 25-30 part;
Its preparation method is as follows:
(1) cm-chitosan, sodium stearate are fully dissolved in the water, make the aqueous solution;
(2) in reactor, add paracril, nanometer glass fiber and polyoxyethylene glycol, stir and be warming up to 100-110 DEG C of insulation 1-2h, after then cooling, obtain material I;
(3) in Banbury mixer, polyphenylene sulfide, polyvinyl alcohol and guar gum is added, be warming up to 65-70 DEG C of mixing 3-5min, then the aqueous solution prepared by material I and step (1) is added, continue to be warming up to 90-95 DEG C of mixing 6-8min, add kaolin, white carbon black and anti-aging agent again, send into vulcanizer after mixing 4-6min, make flange gasket according to user demand.
2. chemical engineering sewage pipeline connecting flange gasket according to claim 1, is characterized in that: described anti-aging agent is selected from one or more in antioxidant A W, anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD.
CN201510312132.2A 2015-06-08 2015-06-08 Flange sealing gasket for chemical sewage pipe connection Pending CN104927125A (en)