CN104926251A - 一种混凝土防护溶胶 - Google Patents
一种混凝土防护溶胶 Download PDFInfo
- Publication number
- CN104926251A CN104926251A CN201510279657.0A CN201510279657A CN104926251A CN 104926251 A CN104926251 A CN 104926251A CN 201510279657 A CN201510279657 A CN 201510279657A CN 104926251 A CN104926251 A CN 104926251A
- Authority
- CN
- China
- Prior art keywords
- parts
- concrete
- agent
- water
- protection sol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及混凝土防护材料技术领域,尤其是一种混凝土防护溶胶;所述防护溶胶的质量份组成如下:胶凝材料55-65份、溶胶态纳米二氧化硅10-40份、纳米水泥添加剂2-6份、引气减水剂2-10份、保水增稠剂0.5-1.0份、高分子聚合物0.5-1.2份、钙离子螯合剂0.2-1.2份、消泡剂0.3-0.6份、润湿分散剂0.3-0.6份、稳定剂0.5-1.2份、改性剂3-9份、去离子水120-150份。有益效果是:1、本发明中通过溶胶态纳米二氧化硅、纳米水泥添加剂以及改性剂和引气减水剂混合使用,既改善了混凝土中存在空隙紧实度低的不足,同时,渗透剂烷氧基烷基硅烷及其改性化合物能渗透到混凝土内部,改善了混凝土的结构,从根本上解决了混凝土开裂、强度低、使用寿命短等技术不足。
Description
技术领域
本发明涉及混凝土防护材料技术领域,尤其是一种混凝土防护溶胶。
背景技术
我国水泥混凝土建设的基础设施投资规模庞大,维修费用相当高,对修补材料的需求也非常大。目前对混凝土结构的防护多采用对混凝土外表面涂装保护材料的方法,在渗透型材料中,如:以硅酸钠为主成分的材料,通过在防水处和维修处涂布或注入以硅酸钠为主成分的材料,来达到保护混凝土结构的目的。但该材料存在因主体单硅酸钠而引起在混凝土中反应速度快,渗透性差及生成表面膜状物易磨损破坏等问题。
混凝土的防护应该从内在进行保护,混凝土保护剂的防水机理是与混凝土中的游离碱产生化学反应,生成稳定的枝蔓状晶体胶质,能有效的堵塞混凝土内部微细裂缝和毛细空隙,使混凝土结构具有持久的防水功能和更好地密实度及抗压强度。通常混凝土是由颗粒状的粗骨料、细骨料和水泥水化物组成,其在浇筑过程和使用过程中,由于各种各样的原因,经常会出现一些质量问题影响其使用寿命。在浇筑和养护过程中,由于水泥水化和水分蒸发易于引起混凝土开裂而导致混凝土强度发展不好。而且混凝土在实际工程中应用中,经常暴露于各种较为严酷的环境,如环境周围腐蚀性介质的侵入,环境温湿度的变化、冻融循环破坏以及部分混凝土工程经常处于重荷载磨损等,这些外部条件将会严重影响混凝土的使用寿命。因此,单纯的一种混凝土养护剂在浇筑时的使用难以实现混凝土保护功能。
发明内容
本发明要解决的技术问题是:克服现有技术中的不足,提供一种能有效提高混凝土的耐久性、耐腐蚀性、韧性的混凝土防护溶胶。
为解决上述技术问题,本发明采用的技术方案如下:
一种混凝土防护溶胶,所述防护溶胶的质量份组成如下:胶凝材料55-65份、溶胶态纳米二氧化硅10-40份、纳米水泥添加剂2-6份、引气减水剂2-10份、保水增稠剂0.5-1.0份、高分子聚合物0.5-1.2份、钙离子螯合剂0.2-1.2份、消泡剂0.3-0.6份、润湿分散剂0.3-0.6份、稳定剂0.5-1.2份、改性剂3-9份、去离子水120-150份。
进一步的,所述胶凝材料的质量份组成如下:石膏10-80份、无机胶凝20-60份、活性炭粉10-20份、工业纯碱8-20份。
进一步的,所述纳米水泥添加剂的质量份组成为:石灰1.2-2.5份、氯化钙1.2-2.5份、单分子双季铵盐1.5-2.8份、聚乙烯醇5-8份。
进一步的,所述保水增稠剂为链层状结构的含水富镁硅酸盐粘土矿物质。
进一步的,所述高分子聚合物为WPS型高分子聚合物。
进一步的,所述消泡剂为干粉类有机硅消泡剂。
进一步的,所述稳定剂为醇胺类化合物。
进一步的,所述防护溶胶的质量份组成如下:胶凝材料60份、溶胶态纳米二氧化硅25份、纳米水泥添加剂4份、引气减水剂6份、保水增稠剂0.75份、高分子聚合物0.8份、钙离子螯合剂0.7份、消泡剂0.5份、润湿分散剂0.5份、稳定剂0.8份、改性剂6份、去离子水135份。
采用本发明的技术方案的有益效果是:
1、本发明中通过溶胶态纳米二氧化硅、纳米水泥添加剂以及改性剂和引气减水剂混合使用,既改善了混凝土中存在空隙紧实度低的不足,同时,渗透剂烷氧基烷基硅烷及其改性化合物能渗透到混凝土内部,改善了混凝土的结构,从根本上解决了混凝土开裂、强度低、使用寿命短等技术不足。
2、本发明中将引气减水剂、润湿分散剂和稳定剂共同使用,提高了混凝土的自流平性能,在重力作用下自流平即可,施工简单,节约了施工成本。
具体实施方式
下面结合具体实施例对本发明做进一步说明。
一种混凝土防护溶胶,所述防护溶胶的质量份组成如下:胶凝材料55-65份、溶胶态纳米二氧化硅10-40份、纳米水泥添加剂2-6份、引气减水剂2-10份、保水增稠剂0.5-1.0份、高分子聚合物0.5-1.2份、钙离子螯合剂0.2-1.2份、消泡剂0.3-0.6份、润湿分散剂0.3-0.6份、稳定剂0.5-1.2份、改性剂3-9份、去离子水120-150份。
所述胶凝材料的质量份组成如下:石膏10-80份、无机胶凝20-60份、活性炭粉10-20份、工业纯碱8-20份。
所述纳米水泥添加剂的质量份组成为:石灰1.2-2.5份、氯化钙1.2-2.5份、单分子双季铵盐1.5-2.8份、聚乙烯醇5-8份。
所述保水增稠剂为链层状结构的含水富镁硅酸盐粘土矿物质。
所述高分子聚合物为WPS型高分子聚合物。
所述消泡剂为干粉类有机硅消泡剂。
所述稳定剂为醇胺类化合物。
实施例1-6的原料组成及数据见表1。
实施例3为最佳实施方式。
实施例1-6中胶凝材料的质量份组成见表2。
原料 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 实施例6 |
石膏 | 10 | 20 | 40 | 50 | 60 | 80 |
无机胶凝 | 20 | 25 | 30 | 40 | 50 | 60 |
活性炭粉 | 10 | 12 | 16 | 18 | 18 | 20 |
工业纯碱 | 8 | 10 | 12 | 15 | 18 | 20 |
实施例3为最佳实施方式。
实施例1-6中纳米水泥添加剂的质量份组成见表3。
实施例3为最佳实施方式。
尽管上述实施例已对本发明的技术方案进行了详细地描述,但是本发明的技术方案并不限于以上实施例,在不脱离本发明的思想和宗旨的情况下,对本发明的技术方案所做的任何改动都将落入本发明的权利要求书所限定的范围。
Claims (8)
1.一种混凝土防护溶胶,其特征在于所述防护溶胶的质量份组成如下:胶凝材料55-65份、溶胶态纳米二氧化硅10-40份、纳米水泥添加剂2-6份、引气减水剂2-10份、保水增稠剂0.5-1.0份、高分子聚合物0.5-1.2份、钙离子螯合剂0.2-1.2份、消泡剂0.3-0.6份、润湿分散剂0.3-0.6份、稳定剂0.5-1.2份、改性剂3-9份、去离子水120-150份。
2.根据权利要求1所述的一种混凝土防护溶胶,其特征在于所述胶凝材料的质量份组成如下:石膏10-80份、无机胶凝20-60份、活性炭粉10-20份、工业纯碱8-20份。
3.根据权利要求1所述的一种混凝土防护溶胶,其特征在于所述纳米水泥添加剂的质量份组成为:石灰1.2-2.5份、氯化钙1.2-2.5份、单分子双季铵盐1.5-2.8份、聚乙烯醇5-8份。
4.根据权利要求1所述的一种混凝土防护溶胶,其特征在于所述保水增稠剂为链层状结构的含水富镁硅酸盐粘土矿物质。
5.根据权利要求1所述的一种混凝土防护溶胶,其特征在于所述高分子聚合物为WPS型高分子聚合物。
6.根据权利要求1所述的一种混凝土防护溶胶,其特征在于所述消泡剂为干粉类有机硅消泡剂。
7.根据权利要求1所述的一种混凝土防护溶胶,其特征在于所述稳定剂为醇胺类化合物。
8.根据权利要求1所述的一种混凝土防护溶胶,其特征在于所述防护溶胶的质量份组成如下:胶凝材料60份、溶胶态纳米二氧化硅25份、纳米水泥添加剂4份、引气减水剂6份、保水增稠剂0.75份、高分子聚合物0.8份、钙离子螯合剂0.7份、消泡剂0.5份、润湿分散剂0.5份、稳定剂0.8 份、改性剂6份、去离子水135份。