CN104921971A - Flexible LED nail lacquer gel and preparing method thereof - Google Patents
Flexible LED nail lacquer gel and preparing method thereof Download PDFInfo
- Publication number
- CN104921971A CN104921971A CN201510389512.6A CN201510389512A CN104921971A CN 104921971 A CN104921971 A CN 104921971A CN 201510389512 A CN201510389512 A CN 201510389512A CN 104921971 A CN104921971 A CN 104921971A
- Authority
- CN
- China
- Prior art keywords
- flexible led
- acrylate
- led nail
- nail polish
- polish glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of ink, in particular to flexible LED nail lacquer gel and a preparing method thereof. The flexible LED nail lacquer gel comprises, by mass, 20-80 percent of acrylic ester low polymer (including urethane acrylate, polyester acrylate, polyether acrylate and the like), 10-15 percent of acrylate monomer, 1-10 percent of photoinitiator and 0.1-5 percent of assistant. The attachment effect on fingernails can be achieved, the gel can be directly stripped off manually very easily, organic solvent auxiliary stripping is avoided, and the nails are effectively prevented from being injured by removing of nail lacquer.
Description
Technical field
The present invention relates to technical field of ink, especially relate to a kind of flexible LED nail polish glue and preparation method thereof.
Background technology
Nial polish belongs to the large series products in color make-up series, has the function of beautifying and modifying fingernail.Common nial polish is the fingernail film former that a kind of NC Nitroncellulose of ester dissolubility is dissolved in certain high activity ester base solvents system, its formula also comparative maturity, main component is the volatile solvent of 70-80%, the nitrocellulose of about 15%, a small amount of oil-based solvent, Camphora, titanium dioxide and oily molten pigment etc.Nial polish forms the strong and glossiness thin film of tool after being applied to fingernail.
Current LED nail polish glue product on the market has a lot, but it is flexible poor, easy embrittlement, and adhesive force overwork, not easily take off from fingernail.
Summary of the invention
For existing LED nail polish glue is flexible poor on the market, easy embrittlement, and adhesive force overwork, not easily from the problem that fingernail is taken off, provide a kind of flexible LED nail polish glue and preparation method thereof, adhesive force is moderate, the adhesion effect on fingernail can be met, and can be easy to direct peel manually from, avoid with an organic solvent up-stripping, effectively prevent and unload the injury of nail polish to fingernail.
The technical solution adopted for the present invention to solve the technical problems is: a kind of flexible LED nail polish glue, its composition component and each constituent mass degree are: acrylate oligomer (comprising urethane acrylate, polyester acrylate, polyether acrylate etc.) 20-80%, acrylate monomer 10-50%, light trigger 1-10%, auxiliary agent 0.1-5%.
Wherein, acrylate oligomer comprises one or more in urethane acrylate, polyester acrylate, polyether acrylate; Light trigger comprises 184,907, one or more in TPO, 819; Auxiliary agent to comprise in organic silicon modified by polyether, polyester resin change properties of organic silicon, polydimethylsiloxane, organic-silicon-modified polysiloxanes one or more; Acrylate monomer is ethoxyquin trimethylolpropane triacrylate, trimethylolpropane triacrylate or ethoxylation tetramethylol methane tetraacrylate etc.
Detailed description of the invention
Describe the present invention below in conjunction with embodiment:
Embodiment 1
One, by following component proportion (mass percentage content):
Urethane acrylate 55%
Ethoxyquin trimethylolpropane triacrylate 25%
Polyester acrylate 14%
907 5%
Polyester resin change properties of organic silicon 1%
Two, preparation method
Step 1 takes each component in proportion;
The above-mentioned each component taken stirs by step 2, blender rotating speed 1000 revs/min;
After step 3 leaves standstill de-bubble, encapsulation is real.
Execute example 2
One, by following component proportion (mass percentage):
Urethane acrylate 65%
Trimethylolpropane triacrylate 30%
184 4%
Organic silicon modified by polyether 1%
Two, preparation method
Step 1 takes each component in proportion;
The above-mentioned each component taken stirs by step 2, blender rotating speed 1000 revs/min;
Step 3 encapsulates after leaving standstill de-bubble.
Embodiment 3
One, by following component proportion (mass percentage):
Polyester acrylate 40%
Urethane acrylate 25%
Ethoxylation tetramethylol methane tetraacrylate 30%
TPO 4%
Organic silicon modified by polyether 1%
Two, preparation method
Step 1 takes each component in proportion;
The above-mentioned each component taken stirs by step 2, blender rotating speed 1000 revs/min;
Step 3 encapsulates after leaving standstill de-bubble.
Claims (5)
1. a flexible LED nail polish glue, is characterized in that, component and each constituent mass degree of described flexible LED nail polish glue are: acrylate oligomer 20-80%, acrylate monomer 10-50%, light trigger 1-10%, auxiliary agent 0.1-5%.
2. flexible LED nail polish glue as claimed in claim 1, is characterized in that: described acrylate oligomer comprise in urethane acrylate, polyester acrylate, polyether acrylate one or more.
3. flexible LED nail polish glue as claimed in claim 1, is characterized in that: described light trigger comprises 184,907, one or more in TPO, 819.
4. flexible LED nail polish glue as claimed in claim 1, is characterized in that: described auxiliary agent to comprise in organic silicon modified by polyether, polyester resin change properties of organic silicon, polydimethylsiloxane, organic-silicon-modified polysiloxanes one or more.
5. the preparation method of the flexible LED nail polish glue as described in claim 1-4, is characterized in that, comprise the following steps:
Take each component in proportion;
The each component taken is stirred, blender rotating speed 1000 revs/min;
Encapsulate after leaving standstill de-bubble.