The content of the invention
The embodiment of the present invention provides a kind of preparation method of green sweater made of cotton yarns, is carried out for solving green bafta in the prior art
When dress designing is developed, green sweater made of cotton yarns has that green sweater made of cotton yarns feel is poor, poor, size is steady to obtain color depth according to conventional washing process
The technical problem of qualitative difference, reach improve green sweater made of cotton yarns feel, improve color depth and dimensional stability technique effect.
The application provides following technical scheme by an embodiment of the application:
A kind of preparation method of green sweater made of cotton yarns, during being applied to make green sweater made of cotton yarns by green cotton fiber, including:It is right
The green cotton fiber is arranged;The described green cotton fiber that will be put in order carries out spinning fabric, forms green bafta;Will be described green
Bafta carries out dress designing exploitation and composition, forms green sweater made of cotton yarns;The green sweater made of cotton yarns is immersed in the working solution for adding softening agent
In.
Further, it is described arrangement is carried out to the green cotton fiber to include:Pre-treatment is carried out to the green cotton fiber;To institute
Stating green cotton fiber carries out chloride treatment and soft treatment.
Further, the described green cotton fiber that will be put in order carries out spinning fabric, forms green bafta, including:Will
The green cotton fiber put in order carries out colour-spun yarns with white cotton.
Further, it is described that pre-treatment is carried out to the green cotton fiber, including:Being positioned over concentration to the green cotton fiber is
In the treatment fluid of 0.5~20g/L, process time is 10-120min, and treatment temperature is 10-150 DEG C, and treatment bath raio is 1:(5-
50)。
Further, it is described that chloride treatment and soft treatment are carried out to the green cotton fiber, including:Concentration is
The chloride of 0.5~20g/L, concentration are the hydrophilic organic silicone softener of 0.5~20g/L, and by plus acetic acid pH value be 4.5~
Within the scope of 7.5, and process time is 10-120min, and treatment temperature is 10-150 DEG C, and treatment bath raio is 1:(5-50).
Further, the green cotton fiber that will be put in order carries out colour-spun yarns with white cotton, including:The green cotton fiber is entered
The treatment of row stoving process;The green cotton fiber is carried out grabbing cotton PROCESS FOR TREATMENT;Mixed cotton PROCESS FOR TREATMENT is carried out to the green cotton fiber,
Form mixed cotton;Opener PROCESS FOR TREATMENT is carried out to the mixed cotton;Cotton feeding process treatment is carried out to the mixed cotton;The mixed cotton is carried out
Lap Technology treatment;Carding process treatment is carried out to the mixed cotton;Bar is carried out to the mixed cotton and PROCESS FOR TREATMENT is rolled up;To described mixed
Cotton carries out combing treatment;Drawing process treatment is carried out to the mixed cotton;Process of roving treatment is carried out to the mixed cotton;To institute
Stating mixed cotton carries out spinning process treatment;Winding process treatment is carried out to the mixed cotton.
Further, the green cotton fiber that will be put in order carries out colour-spun yarns with white cotton, including:By it is described put in order it is green
Cotton fiber and 10~70% white cotton carry out colour-spun yarns.
Further, the preparation method also includes:The green sweater made of cotton yarns is carried out into desizing or arrangement of deoiling, green cotton is formed
Final products.
Further, it is described to be immersed in the green sweater made of cotton yarns in the working solution for adding softening agent, including:It is hydrophilic by 3~8%
Silicone softening agent is diluted in a small amount of water, is subsequently adding in 40 DEG C of working solutions, adjusts PH4.5-7.5, and green sweater made of cotton yarns is put into,
Treatment 10~30 minutes, the ﹕ of bath raio 1 (10~20).
The embodiment of the present invention has the beneficial effect that:
A kind of preparation method of green sweater made of cotton yarns that one embodiment of the invention is provided, it is whole by carrying out to the green cotton fiber
Reason;Then, the described green cotton fiber that will be put in order carries out spinning fabric, forms green bafta;Subsequently, by the green bafta
Dress designing exploitation and composition is carried out, green sweater made of cotton yarns is formed;Finally, the green sweater made of cotton yarns is immersed in the working solution for adding softening agent
In, reach improve green sweater made of cotton yarns feel, improve color depth and dimensional stability technique effect.
Embodiment one
To enable those skilled in the art to understand the present invention in more detail, the present invention is retouched in detail below in conjunction with accompanying drawing
State.
As described in Figure 1, Fig. 1 is a kind of preparation method of green sweater made of cotton yarns in one embodiment of the invention, is applied to by green cotton
During fiber makes green sweater made of cotton yarns, including:
Step S110:The green cotton fiber is arranged;
Specifically, as shown in Fig. 2 step S110 carries out arrangement to the green cotton fiber includes:
Step S111:Pre-treatment is carried out to the green cotton fiber;
Step S112:Chloride treatment and soft treatment are carried out to the green cotton fiber.
Wherein, step S111 carries out pre-treatment to the green cotton fiber includes:
The green cotton fiber is positioned in the treatment fluid that concentration is 0.5~20g/L, process time is 10-120min, located
Reason temperature is 10-150 DEG C, and treatment bath raio is 1:(5-50).
Preferably, it is to the preferred embodiment that the green cotton fiber carries out pre-treatment:
The green cotton fiber is positioned in the treatment fluid that concentration is 3g/L, process time is 30min, and treatment temperature is 80
DEG C, treatment bath raio is 1:20.
Specifically, above-mentioned treatment fluid can be color cotton refining agent.Color cotton refining agent includes by weight percentage, 10-
25% secondary alkyl sulfonate, the isomeric alcohol polyethenoxy ether of 15-40%, the polyethers of 5-20%, the carboxylate chelating point of 1-2%
The water of powder and 30-65%.Secondary alkyl sulfonate is SAS salt or secondary alkyl sulfonic acid sylvite.Isomery alcohol polyoxyethylene
Ether is the polymer of isomery alcohol and oxirane, and structural formula is RO- (C2H4O) n H, R are C8, C11Or C13, n is 3,5,7 or 9.
Wherein, step S112:Chloride treatment and soft treatment are carried out to the green cotton fiber, including:
The hydrophilic organic silicone softener that concentration is the chloride of 0.5~20g/L, concentration is 0.5~20g/L, and lead to
Cross plus acetic acid pH value be 4.5~7.5 within the scope of, and process time be 10-120min, treatment temperature be 10-150 DEG C, treatment
Bath raio is 1:(5-50).
Specifically, above-mentioned chloride can be zinc chloride, and softening agent is selected for the routine techniques of those skilled in the art
It is capable of achieving, the application is not specifically limited.
Preferably, it is described to be to the preferred embodiment that the green cotton fiber carries out chloride treatment and soft treatment:
Chloride, hydrophilic organic silicone softener that concentration be 5g/L of the concentration for 3g/L, and by adding acetic acid pH value
Within the scope of for 6-7, and process time is 20min, and treatment temperature is 50 DEG C, and treatment bath raio is 1:20.
Step S120:The described green cotton fiber that will be put in order carries out spinning fabric, forms green bafta;
Specifically, the described green cotton fiber that step S120 will put in order carries out spinning fabric, forms green bafta, bag
Include:The green cotton fiber that will be put in order carries out colour-spun yarns with white cotton.
Specifically, the green cotton fiber put in order can carry out colour-spun yarns with 10~70% white cotton.Wherein, green cotton fiber is used
After this preparation method, after have passed through the sufficient color development of comparing, the characteristics of with color stability, and then mixed the white of different proportion is given
Cotton, can reach the product of various color and lusters.
Wherein, as shown in figure 3, the preparation method that the green cotton fiber that will be put in order carries out colour-spun yarns with white cotton includes:
Step S121:Stoving process treatment is carried out to the green cotton fiber;
Step S122:The green cotton fiber is carried out grabbing cotton PROCESS FOR TREATMENT;
Step S123:Mixed cotton PROCESS FOR TREATMENT is carried out to the green cotton fiber, mixed cotton is formed;
Step S124:Opener PROCESS FOR TREATMENT is carried out to the mixed cotton;
Step S125:Cotton feeding process treatment is carried out to the mixed cotton;
Step S126:Lap Technology treatment is carried out to the mixed cotton;
Step S127:Carding process treatment is carried out to the mixed cotton;
Step S128:Bar is carried out to the mixed cotton and PROCESS FOR TREATMENT is rolled up;
Step S129:Combing treatment is carried out to the mixed cotton;
Step S1210:Drawing process treatment is carried out to the mixed cotton;
Step S1211:Process of roving treatment is carried out to the mixed cotton;
Step S1212:Spinning process treatment is carried out to the mixed cotton;
Step S1213:Winding process treatment is carried out to the mixed cotton.
Wherein, the PROCESS FOR TREATMENT of above-mentioned steps S121~step S1213 belongs to the routine techniques choosing of those skilled in the art
Select and be capable of achieving, therefore the application is no longer specifically described.
Step S130:The green bafta is carried out into dress designing exploitation and composition, green sweater made of cotton yarns is formed;
Specifically, the green bafta is carried out dress designing exploitation and composition by step S130, forms green sweater made of cotton yarns, is belonged to
The routine techniques selection of those skilled in the art is capable of achieving, therefore the application is no longer specifically described.
Step 140:The green sweater made of cotton yarns is immersed in the working solution for adding softening agent.
Specifically, the just described green sweater made of cotton yarns of step 140 is immersed in the working solution for adding softening agent, by present treatment
Technique can reach improve green sweater made of cotton yarns feel, improve color depth and dimensional stability technique effect.
Preferably, it is described by the green sweater made of cotton yarns be immersed in plus softening agent working solution in preferred embodiment be:
The hydrophilic organic silicone softener of 3~8% (o.w.f) dilutes in a small amount of water, is subsequently adding in 40 DEG C of working solutions, adjusts
Section PH4.5-7.5, green sweater made of cotton yarns is put into, and is processed 10~30 minutes, the ﹕ of bath raio 1 (10~20).Sweatshirt vision after washing is certainly
So clean, soft comfortable, color and luster is soft.Specifically, above-mentioned working solution can be water.Wherein described (o.w.f) is On
weight the fabric。
Step S150:The green sweater made of cotton yarns is carried out into desizing or arrangement of deoiling, green cotton final products are formed.
Specifically, the green sweater made of cotton yarns is carried out desizing or arrangement of deoiling by step S150, forms green cotton final products, category
It is capable of achieving in the routine techniques selection of those skilled in the art, therefore the application is no longer specifically described.
In sum, a kind of preparation method of green sweater made of cotton yarns that the embodiment of the present invention is provided has the following technical effect that:
A kind of preparation method of green sweater made of cotton yarns that one embodiment of the invention is provided, it is whole by carrying out to the green cotton fiber
Reason;Then, the described green cotton fiber that will be put in order carries out spinning fabric, forms green bafta;Subsequently, by the green bafta
Dress designing exploitation and composition is carried out, green sweater made of cotton yarns is formed;Finally, the green sweater made of cotton yarns is immersed in the working solution for adding softening agent
In, reach improve green sweater made of cotton yarns feel, improve color depth and dimensional stability technique effect, and indices reach GB
Requirement.
, but those skilled in the art once know basic creation although preferred embodiments of the present invention have been described
Property concept, then can make other change and modification to these embodiments.So, appended claims are intended to be construed to include excellent
Select embodiment and fall into having altered and changing for the scope of the invention.
Obviously, those skilled in the art can carry out various changes and modification without deviating from essence of the invention to the present invention
God and scope.So, if these modifications of the invention and modification belong to the scope of the claims in the present invention and its equivalent technologies
Within, then the present invention is also intended to comprising these changes and modification.